Extrusion and hot compressing molding processes were used to create bio-polyethylene (BioPE) composites reinforced with argan byproducts (shell, pulp, and argan cake) as bio-fillers. The thermal stability of the composites wass analyzed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Dynamical mechanical analysis and rheological testing were used to investigate their mechanical properties. The morphological results showed a good adhesion between the argan and BioPE matrix. More efficient mechanical properties have been distinguished in the case of argan byproduct-based composite. A higher Young's modulus was noted for all the biocomposites compared to pure BioPE. Thermal analysis revealed that the addition of bio-filler to polymer reduced decomposition temperatures. This study provides an ecological alternative for upgrading the valorization of abundant and underutilized Moroccan biomass. Furthermore, the possibility of using argan byproducts in composite manufacturing will help open up new markets for what is currently considered waste.
RESUMO
Argan pulp is an abundant byproduct from the argan oil process. It was investigated to study the feasibility of second-generation bioethanol production using, for the first time, enzymatic hydrolysis pretreatment. Argan pulp was subjected to an industrial grinding process before enzymatic hydrolysis using Viscozyme L and Celluclast 1.5 L, followed by fermentation of the resulting sugar solution by Saccharomyces cerevisiae. The argan pulp, as a biomass rich on carbohydrates, presented high saccharification yields (up to 91% and 88%) and an optimal ethanol bioconversion of 44.82% and 47.16% using 30 FBGU/g and 30 U/g of Viscozyme L and Celluclast 1.5 L, respectively, at 10%w/v of argan biomass.