One-Step Low Temperature Synthesis of CeO2 Nanoparticles Stabilized by Carboxymethylcellulose.

An elegant method of one-pot reaction at room temperature for the synthesis of nanocomposites consisting of cerium containing nanoparticles stabilized by carboxymethyl cellulose (CMC) macromolecules was introduced. The characterization of the nanocomposites was carried out with a combination of microscopy, XRD, and IR spectroscopy analysis. The type of crystal structure of inorganic nanoparticles corresponding to CeO2 was determined and the mechanism of nanoparticle formation was suggested. It was demonstrated that the size and shape of the nanoparticles in the resulting nanocomposites does not depend on the ratio of the initial reagents. Spherical particles with a mean diameter 2-3 nm of were obtained in different reaction mixtures with a mass fraction of cerium from 6.4 to 14.1%. The scheme of the dual stabilization of CeO2 nanoparticles with carboxylate and hydroxyl groups of CMC was proposed. These findings demonstrate that the suggested easily reproducible technique is promising for the large-scale development of nanoceria-containing materials.

Synthesis of Magneto-Controllable Polymer Nanocarrier Based on Poly(N-isopropylacrylamide-co-acrylic Acid) for Doxorubicin Immobilization.

In this work, the preparation procedure and properties of anionic magnetic microgels loaded with antitumor drug doxorubicin are described. The functional microgels were produced via the in situ formation of iron nanoparticles in an aqueous dispersion of polymer microgels based on poly(N-isopropylacrylamide-co-acrylic acid) (PNIPAM-PAA). The composition and morphology of the resulting composite microgels were studied by means of X-ray diffraction, Mössbauer spectroscopy, IR spectroscopy, scanning electron microscopy, atomic-force microscopy, laser microelectrophoresis, and static and dynamic light scattering. The forming nanoparticles were found to be ß-FeO(OH). In physiological pH and ionic strength, the obtained composite microgels were shown to possess high colloid stability. The average size of the composites was 200 nm, while the zeta-potential was -27.5 mV. An optical tweezers study has demonstrated the possibility of manipulation with microgel using external magnetic fields. Loading of the composite microgel with doxorubicin did not lead to any change in particle size and colloidal stability. Magnetic-driven interaction of the drug-loaded microgel with model cell membranes was demonstrated by fluorescence microscopy. The described magnetic microgels demonstrate the potential for the controlled delivery of biologically active substances.

Transparent Polymer Blends of Poly(methyl methacrylate) and Poly(propylene glycol).

Polymer blends, obtained by polymerization of methyl methacrylate in the presence of poly(propylene glycol), are investigated. Poly(propylene glycol) acts as a plasticizer, significantly lowering poly(methyl methacrylate)'s glass transition temperature and decreasing its elasticity modulus and yield stress. The mixture of methyl methacrylate with poly(propylene glycol) is more stable than its mixture with currently used poly(ethylene glycol), which leads to more uniform distribution and higher possible content of the plasticizer. Unlike low molecular weight plasticizers, poly(propylene glycol) is less prone to migration and exudation during manufacturing process and in use, and has low toxicity. Dynamic mechanical thermal analysis, compression testing and X-ray diffraction were used to investigate how the properties of the material depend on the content and molecular weight of the poly(propylene glycol) in the polymer blend. It was shown that the dependence of the glass transition temperature of methyl methacrylate polymerized in the presence of poly(propylene glycol) on the molar fraction of propylene glycol units is linear, and poly(propylene glycol) with lower molecular weight affects properties of the material stronger than poly(propylene glycol) with higher molecular weight. Therefore, the addition of poly(propylene glycol) allows to control the properties of poly(methyl methacrylate) easily and within wide range.

A Dramatic Change in Rheological Behavior of a Clay Material Caused by a Minor Addition of Hydrophilic and Amphiphilic Polyelectrolytes.

Wide usage of clay-based materials in industry requires investigations concerning efficient modification techniques to control their mechanical behavior in aqueous media. The challenging problem in this field involves minimization of the modifying agent content to provide marked changes in the operating characteristics of the material. In this work, the physicochemical, mechanical and structural aspects of the interaction of capillary water-saturated kaolinite with polyelectrolytes were studied. Modification of kaolinite with a negligible amount (0.1 wt.%) of hydrophilic and amphiphilic polyelectrolytes provides the control for rheological parameters of kaolinite suspensions such as storage and loss modulus in the range of three orders of magnitude. The results obtained reveal the wide possibilities for the production of a spectrum of clay materials using minor amounts of polymer modifying agents.