Previous research evidence suggests that microRNAs (miRNAs) play an indispensable role in onset and progression of bladder cancer (BCa). Here, we explored the functions and mechanisms of miR-5581-3p in BCa. miR-5581-3p, as a tumor suppressor in BCa, was detected at a lower expression level in BCa tissue and cells in contrast with the non-malignant bladder tissue and cells. Over-expression of miR-5581-3p remarkably dampened the migration and proliferation of BCa in vitro and in vivo. SMAD3 and FTO were identified as the direct targets of miR-5581-3p by online databases prediction and mRNA-seq, which were further verified. SMAD3 as a star molecule in modulating EMT progress of BCa had been formulated in former studies. Meanwhile, FTO proved as an N6-methyladenosine (m6A) demethylase in decreasing m6A modification was confirmed to regulate the migration and proliferation in BCa. In addition, we conducted rescue experiments and confirmed overexpressing miR-5581-3p partially rescued the effects of the overexpressing SMAD3 and FTO in BCa cells. In conclusion, our studies exhibit that miR-5581-3p is a novel tumor inhibitor of BCa.
RESUMO
In this work, the morphology and properties of graphene modified natural rubber (NR) was studied. Graphite oxide was chemically reduced with poly(sodium 4-styrenesulfonate) as a stabilizer, then the obtained graphene was blended with NR using latex technique. It is observed that a stable graphene suspension was fabricated by chemical reduction of graphite oxide in the presence of surfactant, while graphene was dispersed homogeneous in NR matrix as tested by WAXD and TEM. Dynamic mechanical analysis showed that storage modulus enhanced dramatically after the incorporation of graphene due to the high surface area of graphene and the exfoliated structure of graphene in NR. The electrical property and thermal conductive properties of NR/graphene nanocomposites improved significantly following the increase in graphene concentration.