The Influence of Retreated Lithium Slag with a High Content of Alkali, Sulfate and Fluoride on the Composition and the Microstructure of Autoclaved Aerated Concrete.

In this paper, the possibility of retreated lithium slag (RTLS) with a high content of alkali, sulfate and fluoride as a partial replacement for fly ash (FA) to produce autoclaved aerated concrete (AAC) was investigated. The influence of the RTLS dosage on the AAC performance were examined. The composition and microstructure of hydrates as well as the microstructure of the RTLS-FA-based AAC compositions were determined by XRD, FTIR, TG-DSC and SEM. The results illustrated that the incorporation of RTLS changed the crystal structure and the microstructure of the tobermorite. With increased RTLS contents, the morphology of tobermorite was changed, and the grass-like tobermorite gradually transformed into network-like tobermorite. The newly formed tobermorite improved the mechanical performance of the AAC. Compared with the RTLS10, the content of tobermorite in the RTLS30 increased by 8.6%.

Performance and Nanostructure Simulation of Phosphogypsum Modified by Sodium Carbonate and Alum.

This paper presents a new modification of the nanostructure of CaSO4·2H2O crystals containing nanopores. This nanoporous structure was achieved in phosphogypsum samples that were modified by sodium carbonate and alum. The effects of sodium carbonate and alum on the properties of phosphogypsum were studied. X-ray diffraction (XRD) and scanning electron microscopy (SEM) methods were used to explore the micro-mechanism of the composite system. Subsequently, molecular dynamics simulations were used to study the nanopore structures of the modified CaSO4·2H2O. The results show that the addition of sodium carbonate and alum reduced the absolute dry density by 23.1% compared with the original phosphogypsum sample, with a bending strength of 2.1 MPa and compressive strength of 7.5 MPa. In addition, new hydration products, sodium sulfate and sodium aluminum sulfate, were formed in the sample doped with sodium carbonate and alum. A new nanostructure of CaSO4·2H2O crystal containing nanopores was formed. Molecular simulations show that the hydration products were responsible for the surface nanopore formation, which was the main factor leading to an increase in mechanical strength. The presented nanopore structure yields lightweight and high strength properties in the modified phosphogypsum.