Review of microstructure and properties of low temperature lead-free solder in electronic packaging.

Low temperature solder (In-based, Sn-Bi, Sn-Zn) has great advantages in aerospace and through-hole technology assemblies in IBM mainframe due to its unique low temperature characteristics. The review evaluates the effects of alloying elements, rare earth elements and nanoparticles on the wettability, microstructure, mechanical properties and oxidation resistance of the low-temperature solders.

Cu6Sn5 Whiskers Precipitated in Sn3.0Ag0.5Cu/Cu Interconnection in Concentrator Silicon Solar Cells Solder Layer.

Cu6Sn5 whiskers precipitated in Sn3.0Ag0.5Cu/Cu interconnection in concentrator silicon solar cells solder layer were found and investigated after reflow soldering and during aging. Ag3Sn fibers can be observed around Cu6Sn5 whiskers in the matrix microstructure, which can play an active effect on the reliability of interconnection. Different morphologies of Cu6Sn5 whiskers can be observed, and hexagonal rod structure is the main morphology of Cu6Sn5 whiskers. A hollow structure can be observed in hexagonal Cu6Sn5 whiskers, and a screw dislocation mechanism was used to represent the Cu6Sn5 growth. Based on mechanical property testing and finite element simulation, Cu6Sn5 whiskers were regarded as having a negative effect on the durability of Sn3.0Ag0.5Cu/Cu interconnection in concentrator silicon solar cells solder layer.

Effects of CuZnAl Particles on Properties and Microstructure of Sn-58Bi Solder.

With the purpose of improving the properties of the Sn-58Bi lead-free solder, micro-CuZnAl particles ranging from 0 to 0.4 wt % were added into the low temperature eutectic Sn-58Bi lead-free solder. After the experimental testing of micro-CuZnAl particles on the properties and microstructure of the Sn-58Bi solders, it was found that the wettability of the Sn-58Bi solders was obviously improved with addition of CuZnAl particles. When the addition of CuZnAl particles was 0.2 wt %, the wettability of the Sn-58Bi solder performed best. At the same time, excessive addition of CuZnAl particles led to poor wettability. However, the results showed that CuZnAl particles changed the melting point of the Sn-58Bi solder slightly. The microstructure of the Sn-58Bi solder was refined by adding CuZnAl particles. When the content of CuZnAl addition was between 0.1 and 0.2 wt %, the refinement was great. In addition, the interfacial IMC layer between new composite solder and Cu substrate was thinner than that between the Sn-58Bi solder and Cu substrate.