The effect of extracellular polymeric substances on MICP solidifying rare earth slags and stabilizing Th and U.

Microbially induced carbonate precipitation (MICP) has been used to cure rare earth slags (RES) containing radionuclides (e.g. Th and U) and heavy metals with favorable results. However, the role of microbial extracellular polymeric substances (EPS) in MICP curing RES remains unclear. In this study, the EPS of Lysinibacillus sphaericus K-1 was extracted for the experiments of adsorption, inducing calcium carbonate (CaCO3) precipitation and curing of RES. The role of EPS in in MICP curing RES and stabilizing radionuclides and heavy metals was analyzed by evaluating the concentration and morphological distribution of radionuclides and heavy metals, and the compressive strength of the cured body. The results indicate that the adsorption efficiencies of EPS for Th (IV), U (VI), Cu2+, Pb2+, Zn2+, and Cd2+ were 44.83%, 45.83%, 53.7%, 61.3%, 42.1%, and 77.85%, respectively. The addition of EPS solution resulted in the formation of nanoscale spherical particles on the microorganism surface, which could act as an accumulating skeleton to facilitate the formation of CaCO3. After adding 20 mL of EPS solution during the curing process (Treat group), the maximum unconfined compressive strength (UCS) of the cured body reached 1.922 MPa, which was 12.13% higher than the CK group. The contents of exchangeable Th (IV) and U (VI) in the cured bodies of the Treat group decreased by 3.35% and 4.93%, respectively, compared with the CK group. Therefore, EPS enhances the effect of MICP curing RES and reduces the potential environmental problems that may be caused by radionuclides and heavy metals during the long-term sequestration of RES.

Properties and mechanisms of steel slag strengthening microbial cementation of cyanide tailings.

The advantages of microbial induced carbonate precipitation (MICP) as bio-cementation technology for tailings-solidification are under extensive investigation. In order to improve performance of bio-cementation, many strengthening materials were applied to the bio-cementation of tailings. Steel slag (SS) is a kind of industrial solid waste, its chemical composition and mineral composition are similar to cement, and it has a certain application prospect as an auxiliary cementing material. In this study, the properties and mechanism of SS strengthening MICP cementation of cyanide tailings (CT) were investigated. The results showed that Sporosarcina pasteurii growth is not inhibited by SS, and Sporosarcina pasteurii can promote the hydration reaction of SS, providing a suitable alkaline environment and Ca2+, promoting the production of more CaCO3 in the MICP process. When 200 mL of CT leachate was added 1.4 g SS (200-400 mesh), the adsorption of Cu, Pb, Zn, Cd, total cyanide (T-CN), and free cyanide (F-CN) reached 48.05%, 44.28%, 36.25%, 16.67%, 79.05%, and 67.20%, respectively. The maximum unconfined compressive strength（UCS） of the cemented body (with 5%, 150 mesh SS) was 1.97 MPa, which was 3.396 times as high as that without SS. The cemented body with the addition of SS (5%, 150 mesh) contained more carbonate bound Cu (2.75%), Pb (4.89%), Zn (5.37%), and Cd (5.75%), and less exchangeable Cu (3.65%), Pb (6.85%), Zn (2.27%), and Cd (4.42%) than that without SS. In summary, the addition of SS improved the UCS of cemented bodies and the stability of heavy metals and cyanide, reduced the environmental risks existing in the process of CT storage. Meanwhile, it also provides new ideas for resource utilization of industrial solid waste SS and improvement of mine filling materials.