Metastable 11 K superconductor Na(1-y)Fe(2-x)As2.

The topochemical deintercalation of Na(+) ions from solid NaFeAs at room temperature in THF with iodine yields the superconducting phase Na(1-y)Fe(2-x)As(2) (T(c) ≈ 11 K). This metastable iron arsenide decomposes at 120 °C and is not accessible by high-temperature solid-state synthesis. X-ray powder diffraction confirms the ThCr(2)Si(2)-type structure, but reveals very small coherently scattering domains with a mean composition Na(0.9(2))Fe(1.7(1))As(2). HRTEM investigations show crystalline as well as strongly distorted areas with planar defects. The latter are probably due to sodium loss and disorder which is also detected by (23)Na solid state NMR. The (57)Fe-Mössbauer spectrum of Na(1-y)Fe(2-x)As(2) shows one type of iron atoms in tetrahedral coordination. All results point to one crystallographic phase with very small domains due to fluctuations of the chemical composition. From electronic reasons we suggest the superconducting phase is presumably NaFe(2)As(2) in the ordered fractions of the sample.

Unprecedented zeolite-like framework topology constructed from cages with 3-rings in a barium oxonitridophosphate.

A novel oxonitridophosphate, Ba(19)P(36)O(6+x)N(66-x)Cl(8+x) (x ≈ 4.54), has been synthesized by heating a multicomponent reactant mixture consisting of phosphoryl triamide OP(NH(2))(3), thiophosphoryl triamide SP(NH(2))(3), BaS, and NH(4)Cl enclosed in an evacuated and sealed silica glass ampule up to 750 °C. Despite the presence of side phases, the crystal structure was elucidated ab initio from high-resolution synchrotron powder diffraction data (λ = 39.998 pm) applying the charge flipping algorithm supported by independent symmetry information derived from electron diffraction (ED) and scanning transmission electron microscopy (STEM). The compound crystallizes in the cubic space group Fm ̅3c (no. 226) with a = 2685.41(3) pm and Z = 8. As confirmed by Rietveld refinement, the structure comprises all-side vertex sharing P(O,N)(4) tetrahedra forming slightly distorted 3(8)4(6)8(12) cages representing a novel composite building unit (CBU). Interlinked through their 4-rings and additional 3-rings, the cages build up a 3D network with a framework density FD = 14.87 T/1000 Å(3) and a 3D 8-ring channel system. Ba(2+) and Cl(-) as extra-framework ions are located within the cages and channels of the framework. The structural model is corroborated by (31)P double-quantum (DQ) /single-quantum (SQ) and triple-quantum (TQ) /single-quantum (SQ) 2D correlation MAS NMR spectroscopy. According to (31)P{(1)H} C-REDOR NMR measurements, the H content is less than one H atom per unit cell.