The aim of this study was to evaluate the influence of surface topography of gutta-percha (GP) cones and plasticized disks of GP on the initial adhesion of Enterococcus faecalis (E. faecalis). The GP cones (Tanari and Dentsply brands) were cut 3 mm from the apical portion and fixed on a glass slide. To make the disks, the cones were thermoplasticized in standardized molds. The specimens were divided into groups according to the shape of the GP and the presence or absence of the bacteria. For contamination, the strain of E. faecalis (ATCC 29212) was used. The surface topography was analyzed using an atomic force microscope (AFM). The surface, roughness, and waviness parameters were evaluated by the Kruskal-Wallis and Dunn test. The comparison between disks and cones showed significant differences, where the cones were rougher, with a higher value attributed to the Dentsply cone (DC group). The same was observed for the waviness. After contamination, there was greater bacterial accumulation in cones, especially in their valleys, but both the surface and the topography became more homogeneous and smoother, with no differences between disks and cones of both brands. The topographic surface of the GP, at the micro and nanoscale, influences the initial adhesion of E. faecalis, with a greater tendency for contamination in regions associated with the presence of roughness and waviness. In this context, plasticization of GP is indicated, as it reduces surface irregularities compared to cones, contributing to less retention of bacteria.
RESUMO
The objective of the present study was to investigate the pH, volumetric alteration, antimicrobial action, and effect on biofilm matrix polysaccharides of calcium hydroxide (CH) pastes with different vehicles available in endodontics: CH + propylene glycol (CHP), UltraCal XS®, Metapaste®, and Metapex®. The pH was analyzed at different time intervals using a pH meter. For volumetric alteration, a microtomographic assay was performed before and after immersion in water. Enterococcus faecalis was chosen for microbiological tests. The bacterial viability and extracellular matrix were quantified with direct contact evaluation (dentin blocks) and at the intratubular level (dentin cylinders) using LIVE/DEAD BacLight and Calcofluor White dyes via confocal laser scanning microscopy (CLSM). Kruskal-Wallis and Dunn's tests were used to analyze pH and direct contact assays, while one-way ANOVA and Tukey tests were used to analyze volumetric alteration and intratubular decontamination (α = 0.05). Higher pH values were obtained during the initial days. Volumetric alterations were similar in all groups. Lower bacterial viability was obtained for dentin blocks and cylinders when CH pastes were used. UltraCal XS and Metapex had lower values for the extracellular matrix. The pH of all CH pastes decreased with time and did not promote medium alkalization for up to 30 days. CH paste can reduce bacterial viability through direct contact and at an intratubular level; however, UltraCal XS and Metapex are involved with lower volumes of extracellular matrices.