RESUMO
OBJECTIVE: To evaluate the physical and biological properties of different types of flowable resin composites and their bonding ability to dentin, comparing the performance of self-adhesive and bulk-fill materials with a conventional control. METHODS AND MATERIALS: Four flowable resin composites were tested: two self-adhesive (Y-flow [SA_YF]; and Dyad Flow [SA_DF]); one bulk-fill (Filtek Bulk Fill Flow [BF]); and one conventional composite (Opallis Flow [OF]). The microshear bond strength (µSBS) to dentin (bovine samples) was investigated at 24 hours and 6 months of storage. The materials were also characterized by degree of conversion, cross-link density, water contact angle, color stability, and cell viability (ISO 10993-5/2009) analyses. Data were analyzed using Analysis of Variance and Tukey tests (α=0.05). RESULTS: The µSBS values were higher for control specimens at 24 hours, whereas the resin-dentin bonds were similarly distributed among the groups after aging. Adhesive failure was the most frequent pattern observed at both time intervals. SA_YF was the only material that increased the bond strength over time. Degree of conversion increased in the following order: SA_YF (28.6±1.4%) < BF (49.7±0.8%) < OF (60.0±2.0%) = SA_DF (63.6±2.3%). Cross-link density was similar among all materials. The self-adhesive composites were more hydrophilic than the other types, with BF showing the lowest water contact angle and the greatest color alteration. All resin composites had a biocompatible behavior. CONCLUSION: Chemical composition appeared to be an influential factor affecting the physico-mechanical and biological behavior of the materials tested.