Tailoring Nylon 6/Acrylonitrile-Butadiene-Styrene Nanocomposites for Application against Electromagnetic Interference: Evaluation of the Mechanical, Thermal and Electrical Behavior, and the Electromagnetic Shielding Efficiency.

Nylon 6/acrylonitrile-butadiene-styrene nanocomposites were prepared by mixing in a molten state and injection molded for application in electromagnetic interference shielding and antistatic packaging. Multi-wall carbon nanotubes (MWCNT) and maleic anhydride-grafted ABS compatibilizer were incorporated to improve the electrical conductivity and mechanical performance. The nanocomposites were characterized by oscillatory rheology, Izod impact strength, tensile strength, thermogravimetry, current-voltage measurements, shielding against electromagnetic interference, and scanning electron microscopy. The rheological behavior evidenced a severe increase in complex viscosity and storage modulus, which suggests an electrical percolation phenomenon. Adding 1 to 5 phr MWCNT into the nanocomposites produced electrical conductivities between 1.22 × 10-6 S/cm and 6.61 × 10-5 S/cm. The results make them suitable for antistatic purposes. The nanocomposite with 5 phr MWCNT showed the highest electromagnetic shielding efficiency, with a peak of -10.5 dB at 9 GHz and a value around -8.2 dB between 11 and 12 GHz. This was possibly due to the higher electrical conductivity of the 5 phr MWCNT composition. In addition, the developed nanocomposites, regardless of MWCNT content, showed tenacious behavior at room temperature. The results reveal the possibility for tailoring the properties of insulating materials for application in electrical and electromagnetic shielding. Additionally, the good mechanical and thermal properties further widen the application range.

Influence of Small Amounts of ABS and ABS-MA on PA6 Properties: Evaluation of Torque Rheometry, Mechanical, Thermomechanical, Thermal, Morphological, and Water Absorption Kinetics Characteristics.

In this work, polyamide 6 (PA6) properties were tailored and improved using a maleic anhydride-grafted acrylonitrile-butadiene-styrene terpolymer (ABS-MA). The PA6/ABS-MA blends were prepared using a co-rotational twin-screw extruder. Subsequently, the extruded pellets were injection-molded. Blends were characterized by torque rheometry, the Molau test, Fourier transform infrared spectroscopy (FTIR), impact strength, tensile strength, Heat Deflection Temperature (HDT), Differential Scanning Calorimetry (DSC), Thermogravimetry (TG), Contact Angle, Scanning Electron Microscopy (SEM), and water absorption experiments. The most significant balance of properties, within the analyzed content range (5, 7.5, and 10 wt.%), was obtained for the PA6/ABS-MA (10%) blend, indicating that even low concentrations of ABS-MA can improve the properties of PA6. Significant increases in impact strength and elongation at break have been achieved compared with PA6. The elastic modulus, tensile strength, HDT, and thermal stability properties of the PA6/ABS-MA blends remained at high levels, indicating that maleic anhydride interacted with amine end-groups of PA6. Torque rheometry, the Molau test, and SEM analysis suggested interactions in the PA6/ABS-MA system, confirming the high properties obtained. Additionally, there was a decrease in water absorption and the diffusion coefficient of the PA6/ABS-MA blends, corroborating the contact angle analysis.