[Influence of static flow (CREEP) on amalgam hardness. Effect of alloys and measured areas]. / Influência do escoamento estático (CREEP) na dureza do amálgama. Efeito de ligas e regióes de medida.

The authors studied the CREEP of 5 amalgam alloys (1 conventional and 4 with high cooper) by the application os static load of 36 MPa in 478 mm specimens, 7 days old. After CREEP test, the samples were included in acrylic resin and Vickers hardness determined by three penetrations for each portion (cervical, medium and occlusal). Samples not submitted to the creep test was used with control. They concluded that no statistic difference was found in creep test but in Vickers test all the studied materials showed different hardness averages. The load application to samples increased the hardness of all the studied materials.

[Influence of different bonding agents on traction resistance of metal alloys to dentin]. / Influência de diferentes agentes de fixação na resistência de união, por tração, de ligas metálicas fixadas à dentina.

They were casted pieces using three kinds of alloy (Ni-Cr, Ag-Sn and Cu-Al) with circular and smooth surface. They were cemented to human teeth, on occlusal surface, grounded at dentin level, through three different materials kind (zinc polycarboxylate cement, glassionomer cement and composite). After 24 hours storing, the samples were subjected to the tensile test. The results showed that the samples cemented with composite and the casts made with Ag-Sn alloy had higher bond strength.

[Penetration of calcium hydroxide based cements by dental enamel conditioning acids]. / Estudo da penetração de agentes ácidos para o condicionamento do esmalte dental em cimentos à base de hidróxido de cálcio.

It was verified the penetration of phosphoric acid into 3 commercial calcium hydroxide-based cements (Life, Renew and Prisma VLC Dycal). The colorimetric method employed permitted the identidication of phosphorus amount in representative samples of 6 successive layers 0.1 mm thick of each material. The acid etching used were the commercial products Scotchbond Etching Gel--3M at 36.114% by weight and Solução Condicionadora--Johnson & Johnson at 36.054% by weight. The contact time was 60 seconds. The result showed that layers 0.1 mm tick for Life and Prisma VLC Dycal and 0.2 mm thick for Renew were able to block the penetration of phosphoric acid solution whereas layers 0.1 mm thick for the 3 cements were able to block the penetration of phosphoric acid gel.