Pronounced Size Dependence in Structure and Morphology of Gas-Phase Produced, Partially Oxidized Cobalt Nanoparticles under Catalytic Reaction Conditions.

It is generally accepted that optimal particle sizes are key for efficient nanocatalysis. Much less attention is paid to the role of morphology and atomic arrangement during catalytic reactions. Here, we unravel the structural, stoichiometric, and morphological evolution of gas-phase produced and partially oxidized cobalt nanoparticles in a broad size range. Particles with diameters between 1.4 and 22 nm generated in cluster sources are size selected and deposited on amorphous alumina (Al2O3) and ultrananocrystalline diamond (UNCD) films. A combination of different techniques is employed to monitor particle properties at the stages of production, exposure to ambient conditions, and catalytic reaction, in this case, the oxidative dehydrogenation of cyclohexane at elevated temperatures. A pronounced size dependence is found, naturally classifying the particles into three size regimes. While small and intermediate clusters essentially retain their compact morphology, large particles transform into hollow spheres due to the nanoscale Kirkendall effect. Depending on the substrate, an isotropic (Al2O3) or anisotropic (UNCD) Kirkendall effect is observed. The latter results in dramatic lateral size changes. Our results shed light on the interplay between chemical reactions and the catalyst's structure and provide an approach to tailor the cobalt oxide phase composition required for specific catalytic schemes.

Combined temperature-programmed reaction and in situ x-ray scattering studies of size-selected silver clusters under realistic reaction conditions in the epoxidation of propene.

The catalytic activity and dynamical shape changes in size-selected nanoclusters at work are studied under realistic reaction conditions by using a combination of simultaneous temperature-programmed reaction with in situ grazing-incidence small angle x-ray scattering. This approach allows drawing a direct correlation between nanocatalyst size, composition, shape, and its function under realistic reaction conditions for the first time. The approach is illustrated in a chemical industry highly relevant selective partial oxidation of propene on a monodisperse silver nanocatalyst. The shape of the catalyst undergoes rapid change already at room temperature upon the exposure to the reactants, followed by a complex evolution of shape with increasing temperature. Acrolein formation is observed around 50 degrees C while the formation of the propylene oxide exhibits a sharp onset at 80 degrees C and is leveling off at 150 degrees C. At lower temperatures acrolein is produced preferentially to propylene oxide; at temperatures above 100 degrees C propylene oxide is favored.