Early Peri-Implant Bone Healing on Laser-Modified Surfaces with and without Hydroxyapatite Coating: An In Vivo Study.

(1) Objective: The aim of this study was to assess the biological behavior of bone tissue on a machined surface (MS) and modifications made by a laser beam (LS) and by a laser beam incorporated with hydroxyapatite (HA) using a biomimetic method without thermic treatment (LHS). (2) Methods: Scanning electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM/EDX) was performed before and after installation in the rabbit tibiae. A total of 20 Albinus rabbits randomly received 30 implants of 3.75 × 10 mm in the right and left tibias, with two implants on each surface in each tibia. In the animals belonging to the 4-week euthanasia period group, intramuscular application of the fluorochromes calcein and alizarin was performed. In implants placed mesially in the tibiofemoral joint, biomechanical analysis was performed by means of a removal torque (N/cm). The tibias with the implants located distally to the joint were submitted for analysis by confocal laser microscopy (mineral apposition rate) and for histometric analysis by bone contact implant (%BIC) and newly formed bone area (%NBA). (3) Results: The SEM showed differences between the surfaces. The biomechanical analysis revealed significant differences in removal torque values between the MSs and LHSs over a 2-week period. Over a 4-week period, both the LSs and LHSs demonstrated removal torque values statistically higher than the MSs. BIC of the LHS implants were statistically superior to MS at the 2-week period and LHS and LS surfaces were statistically superior to MS at the 4-week period. Statistical analysis of the NBA of the implants showed difference between the LHS and MS in the period of 2 weeks. (4) Conclusions: The modifications of the LSs and LHSs provided important physicochemical modifications that favored the deposition of bone tissue on the surface of the implants.

A self-etch bonding system with potential to eliminate selective etching and resist proteolytic degradation.

OBJECTIVES: Bonded restorations using self-etch (SE) systems exhibit a limited lifespan due to their susceptibility to hydrolytic, enzymatic or fatigue degradation and poor performance on enamel. This study was conducted to develop and assess the performance of a two-step SE system using a functional monomer bis[2-(methacryloyloxy)ethyl]phosphate (BMEP) and demonstrate a strategy to enhance stability of bonded resin composite restorations to both enamel and dentine. METHODS: A two-step SE system was formulated with a primer containing BMEP, with an adhesive with or without BMEP, and compared to a commercial 10-MDP-containing system, ClearfilTM SE Bond 2 (CFSE). The systems were evaluated on enamel for surface roughness and microshear bond strength (µSBS) and on dentine for microtensile bond strength (µTBS), nanoleakage, MMP inhibition and cyclic flexural fatigue. RESULTS: Whilst all bonding systems resulted in statistically similar µSBS, BMEP-based primers yielded greater enamel surface roughness than the CFSE primer. The BMEP-free adhesives resulted in statistically similar or higher µTBS and lower nanoleakage compared to CFSE. In situ zymography revealed minimal to no MMP activity within the hybrid layer of BMEP-based systems. The BMEP-free adhesive exhibited flexural strength and fatigue resistance statistically similar to CFSE. CONCLUSIONS: Incorporation of BMEP in the primer led to satisfactory bond strengths with both enamel and dentine, potentially eliminating the need for selective enamel etching. Combined with an adhesive formulation that is solvent-free and hydrophobic, and confining the acidic functional monomer in the primer resulted in minimal interfacial leakage, and resistance to proteolytic degradation and the cyclic nature of chewing. CLINICAL SIGNIFICANCE: The SE bonding system containing BMEP combines the potent etching of phosphoric acid with the therapeutic function of the phosphate-based monomer in creating a homogenous hybrid layer with protection against endogenous proteolytic enzymes. This strategy may overcome current challenges that arise during selective enamel etching.

Etching time and bonding of adhesive systems to dentin of primary teeth: A systematic review and meta-analysis.

BACKGROUND: Due to the chemical and morphological differences between primary vs. permanent teeth, the time reduction of the acid etching or acidic primer can result in higher values of bond strength. AIM: To assess through a systematic review and meta-analysis the influence of the reducing etching (acid etching or acidic primer) time on the bond strength of adhesive systems to primary dentin. DESIGN: A systematic search was carried out in 3 databases: PubMed, Web of Science and Scopus. Studies that evaluated the effect of reducing the etching time on the bond strength of adhesive systems to primary dentin were included. Meta-analyses were performed using a random-effects model, with subgroups for etch-and-rinse and self-etching adhesives, with a significance level of P < .05. The risk of bias and heterogeneity between studies (Cochrane and I2 tests) were assessed. RESULTS: Eight studies were included in the systematic review and seven in the meta-analyses. The shortening etching time did not influence the immediate dentin bond strength for etch-and-rinse (Z = 0.07, P = .95) and self-etching adhesives (Z = 0.41, P = .69). After ageing, however, the shorting etching time improved the bond strength for etch-and-rinse adhesives (Z = 2.01, P = .04). All studies presented high bias risk. CONCLUSIONS: Reducing the acid-etching time to primary dentin improves the long-term bond strength to this substrate.

Sports supplement induces dental structure corrosion: an in vitro pilot study / El suplemento deportivo induce corrosión en la estructura dental: un estudio piloto in vitro

Dietary supplements are being consumed with an increasingly high frequency among sports practitioners, whether at professional and/or amateur level. The supplements contain some nutritional properties in their composition, so they can dissolute the hydroxyapatite crystals of the enamel and favor the process of dental corrosion. The objective was to measure the corrosive power of protein-based supplementation (Whey Protein), under conditions that resemble the use of the supplement by the athletes, increasing the ecological validity of the study. The teeth of the test group (TG) were placed in contact with the Whey protein solution and then exposed to artificial saliva. And the teeth of the control group (CG) were exposed only to artificial saliva. The analysis occurred in natural healthy molar teeth, so that each tooth of the TG was immersed in 50 mL of supplement for 1.5 minutes and then placed in contact with the artificial saliva for 30 seconds. The same procedure was performed 5 times a day for 30, 60, 90, 120, 150 and 180 days. Each group, in its time (TG0 to TG180), underwent analysis of superficial roughness with the aid of optical profilometer (Talysurf CCI®, 3D model). The control group (CG) did not change its superficial roughness. Half of the teeth of the test group (TG) suffered loss of enamel surface. The values, in micrometers, of surface loss of the TG samples were 1.21; 2.1; 2.0; 1.04; 0.97; 0.8; 0.53; 1.14; 1.9; 2.0; 1.66; 1.80. The dietary supplement (Whey protein®) may be a potential cause of the dental corrosion process, considering the demineralization of hydroxyapatite that occurs along with the surface enamel loss.

Los suplementos dietéticos se consumen con una frecuencia cada vez más alta entre los practicantes de deportes, sea a nivel profesional y / o aficionado. Los suplementos contienen algunas propiedades nutricionales en su composición, por lo que pueden disolver los cristales de hidroxiapatita del esmalte y favorecer el proceso de corrosión dental. El objetivo fue medir el poder corrosivo de la suplementación a base de proteínas (proteína de suero), en condiciones que se asemejan al uso del suplemento por parte de los atletas, aumentando la validez ecológica del estudio. Los dientes del grupo de prueba (TG) se pusieron en contacto con la solución de proteína de suero y luego se expusieron a saliva artificial. Y los dientes del grupo de control (CG) estuvieron expuestos solo a saliva artificial. El análisis se realizó en dientes molares sanos naturales, cada diente del TG se sumergió en 50 ml de suplemento durante 1,5 minutos y luego se puso en contacto con la saliva artificial durante 30 segundos. El mismo procedimiento se realizó 5 veces al día durante 30, 60, 90, 120, 150 y 180 días. Cada grupo, en su momento (TG0 a TG180), se sometió a un análisis de rugosidad superficial con la ayuda de un perfilómetro óptico (Talysurf CCI®, modelo 3D). El grupo de control (CG) no cambió su rugosidad superficial. La mitad de los dientes del grupo de prueba (TG) sufrieron pérdida de la superficie del esmalte. Los valores, en micrómetros, de pérdida de superficie de las muestras de TG fueron 1.21; 2.1; 2,0; 1.04; 0,97; 0.8; 0,53; 1.14; 1.9; 2,0; 1,66; 1.80. El suplemento dietético (Whey protein®) puede ser una causa potencial del proceso de corrosión dental, considerando la desmineralización de la hidroxiapatita que ocurre junto con la pérdida de esmalte superficial.

Deproteinization of primary enamel with sodium hypochlorite before phosphoric acid etching.

The aim of this study was to evaluate the deproteinization of primary enamel by analyzing etching pattern types, with and without the application of 5% NaOCl before acid etching with 37% H3PO4. Fifteen extracted human primary molars were randomly selected for the present in vitro study; 1mm x 1mm blocks were prepared and divided into two groups (n = 21). These groups were treated as follows: Group A- Acid Etching with 37% H3PO4 gel for 15 s; Group B- 5% NaOCl for 60 s + Acid Etching with 37% H3POfor 15 s. The specimens were prepared for scanning electron microscopy analysis. The images were evaluated for quality types I and II etching of the enamel surface using ImageJ software. Datasets were checked for normality by Kolgomorv-Smirnov test and the nonparametric unpaired Mann-Whitney test was applied. The mean surface area of type I and II etching pattern values was 1922.314 µm2for Group A and 3840.473 µm2Group B. We conclude that deproteinization with 5% NaOCl prior to acid etching can be used to increase the area of adhesion and the quality of the etching pattern.

El objetivo del estudio fue evaluar la desproteinización del esmalte primario a través de los tipos de patrones de grabado, con y sin NaOCl 5% utilizado antes del grabado ácido con H3PO4 37%. Quince dientes primarios humanos extraídos se seleccionaron al azar para el presente estudio in vitro, se prepararon bloques de 1mm x 1 mm y se dividieron en dos grupos (n = 21). Estos grupos se trataron de la siguiente manera: Grupo A: Grabado ácido con H3PO4 37% en gel durante 15 segundos; Grupo B: NaOCl 5% durante 60 segundos + Grabado ácido con H3PO4 37% durante 15 segundos. Las muestras se prepararon para el análisis de microscopía electrónica de barrido. Las imágenes obtenidas se evaluaron principalmente por la calidad de los grabados tipo I y II de la superficie del esmalte primario, utilizando el software Image J. Los datos se analizaron en cuanto a su normalidad mediante la prueba de Kolgomorv-Smirnov, se utilizó pruebas no paramétricas: Prueba de Mann-Whitney no pareada. Como resultado, se encontró que el área de superficie media de los valores de patrón de grabado de tipo I y II para el Grupo A era 1922,314 µm2 y el Grupo B era 3840,473 µm2. Finalmente, llegamos a la conclusión de que se puede usar la desproteinización con NaOCl 5% antes del grabado ácido para aumentar el área de adhesión y la calidad del patrón de grabado.

Deproteinization of primary enamel with sodium hypochlorite before phosphoric acid etching

The aim of this study was to evaluate the deproteinization of primary enamel by analyzing etching pattern types, with and without the application of 5% NaOCl before acid etching with 37% H3PO4. Fifteen extracted human primary molars were randomly selected for the present in vitro study; 1mm x 1mm blocks were prepared and divided into two groups (n = 21). These groups were treated as follows: Group AAcid Etching with 37% H3PO4 gel for 15 s; Group B5% NaOCl for 60 s + Acid Etching with 37% H3PO4for 15 s. The specimens were prepared for scanning electron microscopy analysis. The images were evaluated for quality types I and II etching of the enamel surface using ImageJ software. Datasets were checked for normality by KolgomorvSmirnov test and the nonparametric unpaired MannWhitney test was applied. The mean surface area of type I and II etching pattern values was 1922.314 µm2for Group A and 3840.473 µm2Group B. We conclude that deproteinization with 5% NaOCl prior to acid etching can be used to increase the area of adhesion and the quality of the etching pattern (AU)

El objetivo del estudio fue evaluar la desproteinización del esmalte primario a través de los tipos de patrones de grabado, con y sin NaOCl 5% utilizado antes del grabado ácido con H3PO4 37%. Quince dientes primarios humanos extraídos se seleccionaron al azar para el presente estudio in vitro, se prepararon bloques de 1mm x 1 mm y se dividieron en dos grupos (n = 21). Estos grupos se trataron de la siguiente manera: Grupo A: Grabado ácido con H3PO4 37% en gel durante 15 segundos; Grupo B: NaOCl 5% durante 60 segundos + Grabado ácido con H3PO4 37% durante 15 segundos. Las muestras se prepararon para el análisis de microscopía electrónica de barrido. Las imágenes obtenidas se evaluaron principalmente por la calidad de los grabados tipo I y II de la superficie del esmalte primario, utilizando el software Image J. Los datos se analizaron en cuanto a su normalidad mediante la prueba de KolgomorvSmirnov, se utilizó pruebas no paramétricas: Prueba de MannWhitney no pareada. Como resultado, se encontró que el área de superficie media de los valores de patrón de grabado de tipo I y II para el Grupo A era 1922,314 µm2 y el Grupo B era 3840,473 µm2. Finalmente, llegamos a la conclusión de que se puede usar la desproteinización con NaOCl 5% antes del grabado ácido para aumentar el área de adhesión y la calidad del patrón de grabado (AU)

Ultramorphology of pre-treated adhesive interfaces between self-adhesive resin cement and tooth structures / Ultramorfologia de interfaces adesivas entre cimento resinoso auto-adesivo e estruturas dentárias pré-tratadas

Introduction: Convencional resin cements can be used in combination with a total-etch system in a conventional mode or as self-adhesive resin cements. The latter are less technique sensitive and able to bond to dental tissues without previous treatment or adhesive layer and requires only a single step to be applied to dental structures. Objective: To compare qualitatively the adhesive interfaces of two self-adhesive resin cements and one conventional resin cement after different tooth surface treatments under scanning electron microscopy. Material and method: 42 crowns of bovine incisors were sectioned and flattened exposing enamel (E) or dentine (D) substrate. Subgroups were defined according to conditioning type and time: E1—no treatment, E2—37% phosphoric acid for 15 seconds, E3—37% phosphoric acid for 30 seconds; D1—no treatment, D2—37% phosphoric acid for 5 seconds; D3—11.5% polyacrylic acid for 15 seconds. A resin block was bonded to each substrate using the self-adhesive resin cements RelyX U100 (3M ESPE) and RelyX U200 (3M ESPE). As a reference hybrid layer, six resin blocks were luted with RelyX ARC and Scotchbond Multi-Purpose adhesive system (3M ESPE) (enamel—EA; dentine—DA). After aging for 7 days in a moist environment at 37±1°C, samples were prepared for microscopy analysis. Result and Discussion: In the ARC specimens, there was hybrid layer formation in both EA and DA. U100 E1 showed gaps at the adhesive interface, while E2 and E3 showed interaction for both self-adhesive cements. There was superficial interaction with bothU100 and U200 in D1, while in D2 and D3, resin tags were only observed in the case of U100. Conclusion: It was concluded that substrate conditioning may enhance the interaction between self-adhesive resin cements and dental tissues, although this is not the case for RelyX U200 and dentine.

Introdução: Restaurações estéticas indiretas são preferencialmente cimentadas utilizando-se cimentos resinosos convencionais e sistema adesivo de condicionamento total ou cimentos resinosos autoadesivos. Estes últimos são tecnicamente menos sensíveis e aderem aos tecidos dentários sem tratamento prévio ou aplicação de adesivo, com um único passo para sua aplicação aos tecidos dentários. Objetivo: Comparar qualitativamente as interfaces adesivas de dois cimentos resinosos autoadesivos e um cimento resinoso convencional, sob microscopia eletrônica de varredura. Material e método: 42 coroas de incisivos bovinos foram seccionadas e as faces vestibulares planificadas expondo esmalte (E) ou dentina (D). Os subgrupos foram definidos de acordo com o tipo e tempo de condicionamento: E1-sem tratamento, E2-37% de ácido fosfórico por 15 segundos, E3-37% de ácido fosfórico por 30 segundos; D1-sem tratamento, D2-37% de ácido fosfórico durante 5 segundos; D3-11,5% de ácido poliacrílico durante 15 segundos. Um bloco de resina foi unido a cada substrato usando os cimentos resinosos autoadesivos RelyX U100 e RelyX U200 (3M ESPE) (n=3). Como referência de camada híbrida, foram cimentados seis blocos de resina com RelyX ARC e o sistema adesivo Scotchbond Multi-Purpose(esmalte-EA, dentina-DA). Após armazenamento (7 dias, umidade, 37±1°C), as amostras foram preparadas para análise microscópica. Resultado: Nos espécimes ARC, houve formação de camada híbrida em EA e DA. U100 E1 mostrou lacunas na interface adesiva, enquanto E2 e E3 apresentaram boa interação para ambos os cimentos autoadesivos. Houve interação superficial com U100 e U200 em D1, enquanto em D2 e ​​D3, foram observadas tags de resina apenas para U100. Conclusão: Concluiu-se que o condicionamento do substrato pode aumentar a interação entre cimentos resinosos autoadesivos e os tecidos dentários, embora este não seja o caso do RelyX U200 e da dentina.

Efficiency in bracket bonding with the use of pretreatment methods to tooth enamel before acid etching: sodium hypochlorite vs. hydrogen peroxide techniques

Bond failures are produced by the existence of biofilm on the tooth surface. Because biofilm is impermeable, it prevents contact in many areas, reducing the etching effect which selectively dissolves calcified tissues but does not seem to eliminate biofilm from the tooth surface, and thus the bond between the tooth and the bracket is not strong enough. The aim of this study is to compare bracket bonding efficiency with two dental surface pretreatments: sodium hypochlorite vs. hydrogen peroxide techniques. This was a cross-sectional, comparative, in vitro study. Seventy-five premolars extracted for orthodontic purposes were evaluated. They were divided into three groups of 25 teeth and assigned randomly toone of the pretreatment techniques (5.25%sodium hypochlorite or 3.5% hydrogen peroxide) or to a control group. The most efficient pretreatment technique for bonding to brackets was sodium hypochlorite, with an average of 17.15 (kg/F). Significant differences were observed between groups (p=0.0001). The post hoc bond strength test showed statistically significant differences between the sodium hypochlorite technique and the control group (p=0.0001). The sodium hypochlorite technique improves bracket adhesion to tooth enamel.

Las fallas de adhesion se producen por la existencia de la biopelicula en la superficie del organo dental, ya que es impermeable y no permite el contacto en muchas areas, de manera que disminuye el efecto del grabado acido; el cual tiene la capacidad de disolver selectivamente los tejidos calcificados, pero no parece eliminar la biopelicula en la superficie dental, por lo tanto, no se lleva a cabo la suficiente fuerza de adhesion en la interfase diente-bracket. El objetivo es comparar la eficiencia en la adhesion de los brackets con el empleo de dos metodos de pre-tratamientos de la superficie del esmalte, el hipoclorito de sodio vs. peroxido de hidrogeno. Estudio comparativo, transversal, in vitro. Se evaluaron 75 premolares extraidos con fines ortodoncicos, tres grupos de 25 dientes, asignados aleatoriamente con alguna de las dos tecnicas de pre-tratamiento al esmalte, hipoclorito de sodio al 5.25%, peroxido de hidrogeno al 3.5% y un grupo control. La tecnica de pre-tratamiento al esmalte mas eficiente para la fuerza de adhesion a los brackets fue el hipoclorito de sodio, con una media de 17.15 (Kg/F), se observaron diferencias significativas inter-grupos (p= 0.001). Las pruebas post hoc para las fuerzas de adhesion mostraron diferencia estadistica - mente significativa para la tecnica de hipoclorito de sodio/ grupo control (p=.001). La utilizacion de hipoclorito de sodio ayuda a mejorar la adhesion de los brackets en la superficie del esmalte.

Shear bond strength of self-etch and total-etch bonding systems at different dentin depths

The purpose of this study was to evaluate the dentin shear bond strength of four adhesive systems (Adper Single Bond 2, Adper Prompt L-Pop, Magic Bond DE and Self Etch Bond) in regards to buccal and lingual surfaces and dentin depth. Forty extracted third molars had roots removed and crowns bisected in the mesiodistal direction. The buccal and lingual surfaces were fixed in a PVC/acrylic resin ring and were divided into buccal and lingual groups assigned to each selected adhesive. The same specimens prepared for the evaluation of superficial dentin shear resistance were used to evaluate the different depths of dentin. The specimens were identified and abraded at depths of 0.5, 1.0, 1.5 and 2.0 mm. Each depth was evaluated by ISO TR 11405 using an EMIC-2000 machine regulated at 0.5 mm/min with a 200 Kgf load cell. We performed statistical analyses on the results (ANOVA, Tukey and Scheffé tests). Data revealed statistical differences (p < 0.01) in the adhesive and depth variation as well as adhesive/depth interactions. The Adper Single Bond 2 demonstrated the highest mean values of shear bond strength. The Prompt L-Pop product, a self-etching adhesive, revealed higher mean values compared with Magic Bond DE and Self Etch Bond adhesives, a total and self-etching adhesive respectively. It may be concluded that the shear bond strength of dentin is dependent on material (adhesive system), substrate depth and adhesive/depth interaction.

Evaluation "in situ" of tag formation in dental enamel submitted to microabrasion technique: Effect of two etching times

The objective of this study was to analyze the formation of resin tags on enamel surfaces submitted or not to enamel microabrasion technique. Thirteen undergraduate dental students received removable acrylic palatal appliances on which four sections from intact premolars were fixed, measuring 4.0 mm X 4.0 mm. Two sections received the application of a microabrasive system and the remaining sections did not receive any surface treatment. The patients were instructed to wear the acrylic palatal appliances for 4 months during the day. After this time, the sections were etched with 37% phosphoric acid for 15 seconds (sections 1 and 2) and 60 seconds (sections 3 and 4), followed by adhesive system and composite resin applications. All the sections were prepared for light microscopy analysis to observe the degree of resin penetration (x400). The results were submitted to a three-way analysis of variance with a significance level of 5%. The difference between groups was verified by the Tukey test, at a significance level of 5%. The results showed that microabraded enamel required a longer period of acid etching for longer resin tags.

O objetivo deste estudo foi analisar a formacao de tags resinosos em esmalte dental submetido ou nao a tecnica de microabrasao. Treze estudantes de Odontologia receberam a aplicacao de um aparelho ortodontico removivel contendo quatro seccoes de esmalte com dimensoes de 4.0 mm X 4.0 mm. Duas secoes receberam a aplicacao de um composto microabrasivo e as demais nao receberam nenhum tratamento. Os pacientes foram instruidos a usar os aparelhos ortodonticos durante o dia e por quatro meses. Apos este periodo, as seccoes foram condicionadas com acido fosforico 37% por 15 segundos (secoes 1 e 2) e por 60 segundos (seccoes 3 e 4), seguido pela aplicacao do sistema adesivo e de resina composta. Todas as seccoes foram preparadas para analise em microscopia optica comum para observar o grau de penetracao do material resinoso (x400). Os resultados foram submetidos a analise de variancia a tres criterios, ao nivel de 5%. A diferenca entre os grupos foi verificada pelo teste de Tukey, ao nivel de 5%. Os resultados mostraram que maiores tempos de condicionamento acido do esmalte dental sao exigidos para uma maior penetracao do sistema adesivo.

Microleakage in conservative cavities varying the preparation method and surface treatment

OBJECTIVE: To assess microleakage in conservative class V cavities prepared with aluminum-oxide air abrasion or turbine and restored with self-etching or etch-and-rinse adhesive systems. Materials and Methods: Forty premolars were randomly assigned to 4 groups (I and II: air abrasion; III and IV: turbine) and class V cavities were prepared on the buccal surfaces. Conditioning approaches were: groups I/III - 37 percent phosphoric acid; groups II/IV - self-priming etchant (Tyrian-SPE). Cavities were restored with One Step Plus/Filtek Z250. After finishing, specimens were thermocycled, immersed in 50 percent silver nitrate, and serially sectioned. Microleakage at the occlusal and cervical interfaces was measured in mm and calculated by a software. Data were subjected to ANOVA and Tukey's test (α=0.05). RESULTS: Marginal seal provided by air abrasion was similar to high-speed handpiece, except for group I. There was SIGNIFICANT difference between enamel and dentin/cementum margins for to group I and II: air abrasion. The etch-and-rinse adhesive system promoted a better marginal seal. At enamel and dentin/cementum margins, the highest microleakage values were found in cavities treated with the self-etching adhesive system. At dentin/cementum margins, high-speed handpiece preparations associated with etch-and-rinse system provided the least dye penetration. CONCLUSION: Marginal seal of cavities prepared with aluminum-oxide air abrasion was different from that of conventionally prepared cavities, and the etch-and-rinse system promoted higher marginal seal at both enamel and dentin margins.

Shear bond strength of orthodontic brackets bonded using halogen light and light-emitting diode at different debond times

The aim of this in vitro study was to compare the photoactivation effects of QTH (Quartz-Tungsten-Halogen) and LED (Light-Emitting Diode) on the SBS (Shear Bond Strength) of orthodontic brackets at different debond times. Seventy-two bovine lower incisors were randomly divided into two groups according to the photoactivation system used (QTH or LED). The enamel surfaces were conditioned with Transbond self-etching primer, and APC (Adhesive Pre-Coated) brackets were used in all specimens. Group I was cured with QTH for 20 s and Group II with LED for 10 s. Both groups were subdivided according to the different experimental times after bonding (immediately, 24 h and 7 days). The specimens were tested for SBS and the enamel surfaces were analyzed according to the Adhesive Remnant Index (ARI). The statistical analysis included the Tukey's test to evaluate the main effects of photoactivation and debond time on SBS. The Chi-square test was used to compare the ARI values found for each group, and no statistically significant difference was observed. The debond time of 7 days for QTH photoactivation showed statistically greater values of SBS when compared to the immediate and 24 h periods. There was no statistically significant difference between the QTH and LED groups immediately and after the 24 h period. In conclusion, bonding orthodontic brackets with LED photoactivation for 10 s is suggested because it requires a reduced clinical chair time.