Endocrown: A Conservative Approach in the Management of Endodontically Treated Teeth.

The outcome of an endodontic procedure determines the clinical success of the treated tooth. A post-endodontic restoration will restore the tooth's form, function, and aesthetics while preserving and safeguarding its existing tooth structure. To restore endodontically treated teeth with the best possible tissue preservation, the least invasive preparation is the aim. Full-coverage crowns are still more popular than partial-coverage crowns. Conservative dental procedures such as inlays, overlays, and endocrowns maximize the amount of tooth structure that is intact while minimizing the amount of tooth structure that is removed. Compared to posts, cores, and crowns, endocrowns offer several advantages in terms of ease of preparation, application, and reduced clinical visits and time. Endocrown is a simple, minimally invasive preparation usually given when margins are supragingival, which makes it self-cleansable and maintains natural tooth contact, preventing interference with periodontal tissue. This case report focuses on managing endodontically treated teeth with the fabrication of endocrown using computer-aided design (CAD) and computer-assisted manufacturing (CAM) techniques.

Effect of margin designs and loading conditions on the stress distribution of endocrowns: a finite element analysis.

BACKGROUND: Margin designs and loading conditions can impact the mechanical characteristics and survival of endocrowns. Analyzing the stress distribution of endocrowns with various margin designs and loading conditions can provide evidence for their clinical application. METHODS: Three finite element analysis models were established based on the margin designs: endocrown with a butt-joint type margin (E0), endocrown with a 90° shoulder (E90), and endocrown with a 135° shoulder (E135). The E0 group involved lowering the occlusal surface and preparing the pulp chamber. The E90 group created a 90° shoulder on the margin of model E0, measuring 1.5 mm high and 1 mm wide. The E135 group featured a 135° shoulder. The solids of the models were in fixed contact with each other, and the materials of tooth tissue and restoration were uniform, continuous, isotropic linear elasticity. Nine static loads were applied, with a total load of 225 N, and the maximum von Mises stresses and stress distribution were calculated for teeth and endocrowns with different margin designs. RESULTS: Compared the stresses of different models under the same loading condition. In endocrowns, when the loading points were concentrated on the buccal side, the maximum von Mises stresses were E0 = E90 = E135, and when there was a lingual loading, they were E0 < E90 = E135. In enamel, the maximum von Mises stresses under all loading conditions were E0 > E90 > E135. In dentin, the maximum von Mises stresses of the three models were basically similar except for load2, load5 and load9. Compare the stresses of the same model under different loading conditions. In endocrowns, stresses were higher when lingual loading was present. In enamel and dentin, stresses were higher when loaded obliquely or unevenly. The stresses in the endocrowns were concentrated in the loading area. In enamel, stress concentration occurred at the cementoenamel junction. In particular, E90 and E135 also experienced stress concentration at the shoulder. In dentin, the stresses were mainly concentrated in the upper section of the tooth root. CONCLUSION: Stress distribution is similar among the three margin designs of endocrowns, but the shoulder-type designs, especially the 135° shoulder, exhibit reduced stress concentration.

The fracture resistance of pulpotomized primary molars restored with zirconia crowns, lithium disilicate or resin based ceramic endocrowns.

BACKGROUND: Endocrown in pediatric dentistry was rooted in the fundamental principles of preserving healthy dental tissues, leveraging contemporary adhesive methodologies. AIM: This research aimed on assessing and comparing the fracture resistance of pulpotomized primary molars when rehabilitated with zirconia crowns and two distinct types of endocrowns, namely E-Max and Brilliant Crios. METHODS: The study involved thirty, anonymized, freshly extracted second primary molars that underwent pulpotomy. These teeth were then evenly divided into three groups, each consisting of ten specimens: the zirconia crown, the E-Max endocrown, and the Brilliant Crios endocrown groups. Post-pulpotomy, the teeth were prepared for their respective restorations. Subsequent to this preparation, the zirconia crowns, E-Max endocrowns, and Brilliant Crios endocrowns were secured. To evaluate the fracture resistance using a computer-controlled testing machine (Instron), a progressively increasing load was applied to each group until fracture occurred. The gathered data were then analyzed for outliers and subjected to normality testing using the Shapiro-Wilk and/or Kolmogorov-Smirnov tests, with a significance threshold set at 0.05. RESULTS: There was no statistically significant difference in fracture resistance of pulpotomized primary molars among lithium disilicate (E-Max) group (mean=1367.59N), Brilliant Crios group (mean=1349.73N) and zirconia group (mean=1240.82N). CONCLUSION: Endocrowns can be considered a promising restoration for pulpotomized primary molars.

Metal Marvels: Revolutionizing Endodontic Restoration With a Novel Endocrown Approach.

This case report explores the innovative application of the endocrown technique for restoring a severely damaged mandibular molar (tooth #46) in a 28-year-old male patient. With a recent root canal treatment history, the patient presented with a dislodged prosthesis. Due to financial constraints, a base metal alloy was chosen for the endocrown restoration. The unique preparation process involved reducing the occlusal surface by 2 mm, creating a shoulder cervical margin, and preserving enamel walls. The endocrown, crafted from a base metal alloy, demonstrated a semi-conservative approach, providing cost-effectiveness and minimal tooth preparation. The case adheres to the 2013 CAse REport (CARE) guidelines. The discussion highlights the biomechanical benefits of the endocrown, emphasizing stress resistance, stability, and superior performance compared to traditional treatments. Materials like ceramic, resin nanoceramic, and polyetheretherketone are briefly discussed, focusing on the promising success rates of endocrowns, mainly through computer-aided designing/computer-aided manufacturing systems. The report provides valuable insights for clinicians considering this endocrown technique in reconstructing severely damaged molars and premolars.

Clinical and laboratorial performance of rehabilitation of endodontically treated teeth: A systematic review.

OBJECTIVE: This systematic review aimed to analyze the clinical (survival rate, failure risk, or fracture) and laboratory performance (fracture mode or failure) of rehabilitations of endodontically treated teeth, with and without posts. MATERIALS AND METHODS: A systematic search was conducted in the Pubmed, Scopus, Web of Science, Embase, Cochrane Library, and OpenGrey databases up to March 2023, according to PRISMA guidelines. In vitro and clinical studies that compared the clinical and laboratory performance of endodontically treated teeth with and without intraradicular posts were included. Studies selection, data extraction, and risk of bias analysis were performed. RESULTS: Thirty-one in vitro and 7 clinical studies were included. For in vitro studies, fiberglass post (n = 24) was the most mentioned. The follow-up time of the clinical studies ranged from 1 to 17 years, with the fiber-reinforced composite post (n = 3) being the most evaluated, and only failure risk proved to be more favorable for using intraradicular posts. CONCLUSION: Rehabilitations of endodontically treated teeth with and without intraradicular retainers showed no difference in fracture resistance and failure mode, evaluated by in vitro studies. Clinical studies showed no difference in survival rate, but failure risk proved to be more favorable for the use of posts. CLINICAL SIGNIFICANCE: This analysis revealed significant variability between results, however, most laboratory and clinical studies revealed no difference with using the post. Furthermore, it is important to emphasize the need to evaluate the coronary remnant and the general characteristics of the tooth in each situation.

Comparison of Clinical Efficacy of CAD/CAM Endocrowns Made of Feldspathic, Zirconia Lithium Silicate, and Lithium Disilicate: A Two-year Mixed Cohort Study.

OBJECTIVE: Endocrowns can be fabricated from various materials as a treatment option for endodontically treated teeth. This mixed cohort study aimed to demonstrate the clinical efficacy of endocrowns made of feldspathic, zirconia lithium silicate, and lithium disilicate ceramics using a chairside CAD/CAM system. METHODS: The present study compared the clinical outcomes of 141 endocrown restorations in posterior teeth of 85 patients in a two-year follow-up. The efficacy of restorations was evaluated in three aspects: esthetics, biological response, and function, with the aid of the FDI guideline, and presented as descriptive analyses. Additionally, the data were analyzed using Chi-square and Spearman correlation tests. The significance level was set at p = 0.05. RESULTS: The study findings revealed that the type of restorations (feldspathic, zirconia lithium silicate, and lithium disilicate) (p > 0.05) and underlying teeth (molars and premolars) (p > 0.05) play no part in restorations' failure. Caries' recurrence is primarily responsible for the failure of the endocrowns. Secondary caries and radiolucency were observed in four teeth (2.83%). The clinical efficacy of 126 restorations (89.36%) fell into the category of "clinically excellent" and "clinically good." Ten restorations (7.09%) were classified as "clinically sufficient/satisfactory," and only five restorations (3.54%) needed replacement due to having "clinically unsatisfactory" and "clinically poor" quality. CONCLUSIONS: With endocrowns made of the mentioned ceramics showing a high success rate and durability in the short term, they can be considered a safe choice for restoring endodontically treated teeth. It is worth noting that caries were the most common reason for the failure of the restorations. CLINICAL SIGNIFICANCE: Endocrowns made of different ceramics have been proven reliable restorations for endodontically treated molars and premolars.

Comparison of color changes, fracture strengths, and failure modes of conventional endocrowns and endocrowns with different design modifications.

BACKGROUND: Endocrowns (ECs) are alternatives for rebuilding severely damaged teeth and show superior efficacy in molars over premolars. OBJECTIVE: The objective of this in vitro study is to evaluate the effects of different preparation designs with short pulp chambers on the mean color change (Δ⁢E), fracture resistance, and failure types of mandibular molar ECs. METHOD: A total of 40 extracted mandibular molars were treated endodontically and divided into four groups. Samples in groups 1, 2, 3, and 4 had occlusal preparation depths of 5 mm, 3 mm, 3 mm with ferrule, and 3 mm with boxes, respectively. The samples were immersed in coffee and their Δ⁢E values were measured by using the Commission Internationale de l'Eclairage color system. They were also subjected to a fracture test. Next, all specimens were examined visually under a stereomicroscope to evaluate their failure modes and identify their fracture origins. Data were entered and analyzed by using Statistical Package for Social Sciences. RESULTS: Among all groups, group 4 (3 mm + boxes) presented the highest Δ⁢E (4.15) after immersion in coffee. Moreover, ANOVA revealed that the Δ⁢E of group 4 (occlusal preparation depth of 3 mm with boxes) was significantly different (p< 0.05) from that of group 2 (3 mm + ferrule, 3.07). The EC with a 3 mm chamfer and ferrule showed the highest maximum load of 2847.68 ± 693.27 N, whereas that with a 5 mm chamfer finish line had a marginally reduced load at fracture of 2831.52 ± 881.83 N. The EC with a 3 mm chamber and boxes had a slightly increased maximum load of 2700.75 ± 436.40 N, whereas that with the 3 mm chamber had the lowest maximum load at fracture of 2385.97 ± 465.61 N. One-way ANOVA showed that different EC preparation designs had no effect on maximum fracture load (F [3,16] = 0.550, p= 0.6). CONCLUSION: The recorded Δ⁢E values of ECs in all groups were equal or marginally higher than the acceptable values. The EC with a 3 mm chamfer and ferrule displayed the highest mean maximum load. The EC with a 5 mm chamfer finish line had a marginally lower maximum load at fracture than other ECs. Failures, such as ceramic fracture, split fracture, and ceramic and tooth splitting above the cemento-enamel junction (CEJ) or vertically were predominant in samples with occlusal preparation depths of 3 mm with ferrule and 5 mm.

Fracture resistance of CAD/CAM endocrowns made from different materials in maxillary premolar interproximal defects.

OBJECTIVES: This in vitro study aims to compare the fracture resistance of three CAD/CAM materials used in endocrown restoration of interproximal defects in maxillary premolars. MATERIALS AND METHODS: 45 maxillary premolars extracted as part of orthodontic treatment were included. Following standardized root canal treatment, all teeth were prepared into Mesial-Occlusal (MO) cavity types. The samples were then randomly divided into three groups: LD [repaired with lithium disilicate glass ceramics (IPS e.max CAD)], VE [treated with polymer-infiltrated ceramics (Vita Enamic)], and LU [repaired with resin-based nanoceramics (Lava Ultimate)]. Axial static loading was applied using a universal testing machine at 1 mm/min until fracture, and fracture resistance and failure modes were recorded. RESULTS: Regarding Fracture Resistance Values (FRVs), the LD group exhibited significantly higher values than the other two groups, VE (P = 0.028) and LU (P = 0.005), which showed no significant difference (P = 0.778). On the other hand, regarding failure modes, the LD group had a higher prevalence of irreparable fractures compared to the other two groups, VE (P < 0.001) and LU (P < 0.001), which showed no significant difference. CONCLUSIONS: Although lithium disilicate glass ceramics exhibited higher FRVs, they had a lower repair probability. In contrast, polymer-infiltrated ceramics and resin-based nanoceramics contributed to tooth structure preservation. CLINICAL RELEVANCE: For maxillary premolars with interproximal defects following root canal treatment, resin ceramic composites are recommended for restoration to enhance abutment teeth protection.

Impact of CAD/CAM Material Thickness and Translucency on the Polymerization of Dual-Cure Resin Cement in Endocrowns.

The objective of this study is to evaluate the impact of the thickness and translucency of various computer-aided design/computer-aided manufacturing (CAD/CAM) materials on the polymerization of dual-cure resin cement in endocrown restorations. Three commercially available CAD/CAM materials-lithium disilicate glass (e.max CAD), resin composite (CERASMART), and a polymer-infiltrated ceramic network (ENAMIC)-were cut into plates with five different thicknesses (1.5, 3.5, 5.5, 7.5, and 9.5 mm) in both high-translucency (HT) and low-translucency (LT) grades. Panavia V5, a commercial dual-cure resin cement, was polymerized through each plate by light irradiation. Post-polymerization treatment was performed by aging at 37 °C for 24 h under light-shielding conditions. The degree of conversion and Vickers hardness measurements were used to characterize the polymerization of the cement. The findings revealed a significant decrease in both the degree of conversion and Vickers hardness with increasing thickness across all CAD/CAM materials. Notably, while the differences in the degree of conversion and Vickers hardness between the HT and LT grades of each material were significant immediately after photoirradiation, these differences became smaller after post-polymerization treatment. Significant differences were observed between samples with a 1.5 mm thickness (conventional crowns) and those with a 5.5 mm or greater thickness (endocrowns), even after post-polymerization treatment. These results suggest that dual-cure resin cement in endocrown restorations undergoes insufficient polymerization.

Effect of ceramic materials and tooth preparation design on computer-aided design and computer-aided manufacturing endocrown adaptation and retentive strength: An in vitro study.

OBJECTIVES: To evaluate how various tooth preparation designs impact the adaptation-both at the margins and internally-and the retentive strength of computer-aided design and computer-aided manufacturing (CAD/CAM) produced endocrowns. MATERIALS AND METHODS: 60 extracted human mandibular first molars were endodontically treated and assigned into three groups (n = 20) according to the tooth preparation design: Group N: butt joint design, Group F and F1 received 1- and 2-mm circumferential ferrule preparation, respectively. Endocrowns were milled using either lithium disilicate glass-ceramic (IPS emax ceramic) or monolithic zirconia. The internal and marginal adaptation of the endocrowns were evaluated using the replica technique. After cementation, the endocrowns of all test groups were dislodged axially at 0.5 mm/min using a universal testing machine. A 2-way ANOVA and the independent samples t-test (α = .05) were performed to statistically analyze the data. RESULTS: The effect of changing the design of the tooth preparation (butt joint, ferrule) on the marginal and internal gap was shown to be statistically significant (p < .05); the lower gap values were recorded at the axial followed by cervical, marginal, and pulpal floor walls in both ceramic groups regardless of the teeth preparation design. The ANOVA test revealed similar average removal forces and stresses for the two types of tested ceramic materials. CONCLUSION: IPS emax ceramic adapted better than monolithic zirconia ceramic, regardless of the preparation design. Ferrule preparation design is more retentive than butt joint preparation, regardless of the type of ceramic material used.

Application of one-piece endodontic crowns fabricated with CAD-CAM system to molars.

Computer-aided design-computer-aided manufacturing (CAD-CAM) systems have been widely used as a fabrication method for restorations because of their high efficiency and accuracy, which significantly reduces fabrication time. However, molars with insufficient clearance or short clinical crown lengths require retention holes or grooves on the preparation, making it difficult to replicate the shapes with the CAM milling system. In these cases, restorations using the lost-wax method are selected. This article focuses on one-piece endodontic crowns (endocrowns) fabricated with a CAD-CAM system (CAD-CAM endocrowns), in which their posts and crowns are integrated. Articles from July 2012 to August 2023 were searched in PubMed with the keyword "endocrown". This review discusses the application of CAD-CAM endocrowns to molars from the viewpoint of model experiment (fracture resistance, adaptation) and clinical research. This technique, which allows margins and internal gaps to be set within the clinically acceptable range, is reported to be an effective way of restoring molars with high survival rates in clinical research.

Construction of metal endocrown for a short clinical second molar crown.

This case highlights where a metal endocrown was used as a novel technique. The metal endocrown showed promising outcomes during the 5-year follow-up, utilizing a resin base to preserve tissue and act as a stress breaker. This approach was used to preserve the tooth and avoid extraction or periodontal surgery.

Clinical performance of computer-aided design/computer-aided manufacture lithium disilicate ceramic endocrown restorations: A 2-year study.

Context: Optimal restoration methods for endodontically treated teeth (ETTs) have always remained an ongoing discussion among physicians in this day and age. ETTs have a tendency to fracture when chewing, compared to initial teeth. From the perspective of biology, preserving and restoring tooth structure is critical to maintaining biomechanical, functional, and esthetic harmony. Dental bonding techniques have lessened the necessity for post-and-core restorations in ETTs with severe substance loss. A minimally invasive endodontic restoration technique called "endocrown" was initially introduced by Bindl and Mörmann in 1999. Aims: The aim of the study was to clinically evaluate all-ceramic mandibular molar endocrowns made using computer-aided design/computer-aided manufacturing (CAD/CAM) following 2 years of follow-up. Subjects and Methods: This unblinded study contains 56 patients with 56 mandibular molars, which had severe substance loss. After teeth preparation, lithium disilicate ceramic endocrowns were manufactured with the CEREC CAD/CAM system, and cementation was performed using a composite luting agent. The endocrowns were assessed using the modified United States Public Health Service criteria at baseline, 6 months, 1 year, and 2 years following placement. Patient satisfaction was evaluated using a questionnaire. Statistical Analysis Used: This study used descriptive statistics, including mean, standard deviation, and 95% confidence intervals. Data were processed using STATA version 14.0 (StataCorp LLC, USA). Results: Two endocrowns (3.6%) failed throughout the period of observation. The high clinical rating criteria (96.4%, count of 54) and the increased satisfaction percentage (94.6%, count of 53) remained practically stable during the follow-up assessments at 6 months and after 1-2 years. Conclusions: Endocrown offers a less invasive treatment option that may be a better method for endodontically treated mandibular molars. With contemporary CAD/CAM technology and new materials, time in the chair and esthetics optimally improved, bringing satisfaction to the patient.

Influence of Cementation Mode and Ferrule Design on the Fatigue Resistance of Monolithic Zirconia Endocrowns.

Background: Classic endocrowns made of dental ceramics are considered a promising alternative to traditional post-endodontic restorations. The use of circular ferrules in endocrowns is a topic of controversial discussion. Therefore, the present study aims to evaluate the effect of ferrule design and cementation mode on the fatigue resistance of zirconia endocrowns. Methods: Eighty human molars were divided into four groups (n = 20): NFC (no-ferrule, conventional cementation), NFA (no-ferrule, adhesive luting), FC (ferrule, conventional cementation) and FA (ferrule, adhesive luting). Both the classic and the modified endocrown preparation with a two-millimeter ferrule design were carried out. Endocrowns were fabricated from zirconia using the CEREC system. After thermocycling, specimens were loaded according to the step-stress test up to 1500 N. Results: Failure rate was low; 88.8% of total specimens passed the step-stress test. Fractures were distributed between all groups; no significant differences in fatigue resistance were detected for preparation design and cementation mode. Conclusions: Endocrowns appear to be a promising concept for endodontically treated molars. Ferrule and also cementation mode have only a minor influence on fatigue resistance of zirconia endocrowns. However, at very high forces, the marginal area of the ferrule represents a weak point.

Fracture strength of endocrowns after thermomechanical aging.

This in-vitro study aimed to evaluate the fracture strength (FS; N) of composite, feldspathic, and glass-ceramic computer-aided design/computer-aided manufacturing (CAD/CAM) endocrowns after thermomechanical aging. Seventy non-carious human molars were randomly divided into seven groups, according to the CAD/CAM material used for endocrown fabrication. Intact molars without cavity preparations were used as control (n = 10). Following endodontic treatment, standardized endocrown cavities were prepared and endocrowns were fabricated using composite (Cerasmart270, CS and Grandio Blocs, GB), fired and milled zirconia-reinforced lithium silicate (Celtra Duo, CD), leucite-reinforced feldspar ceramic (LRF Initial, LRF), and feldspathic (Cerec Blocks, CE) materials which were luted with universal adhesive (Futurabond U; Voco) and dual-cure resin cement (Bifix QM). Following thermocycling for 20,000 cycles and 480,000 load cycles in a chewing simulator (CS-4.2, SD Mechatronik), FS was evaluated (Instron). Data were analyzed with one-way ANOVA and post hoc Tukey's tests (p < 0.05). FS was significantly influenced by the tested material (p = 0.00). CS had the highest FS, which was not significantly different from intact molars and fired CD (p > 0.05). There were no significant differences in FS between LRF, GB, and CD, which were significantly higher than CE. Most of the failure modes of CS, CD, and GB were repairable, whereas those of CE were irreparable. All the tested materials withstood clinically relevant axial forces. Composite endocrowns exhibited more favorable fracture pattern, whereas feldspathic and leucite-reinforced feldspar ceramic endocrowns exhibited mostly irreparable fractures.

Biomechanical behavior and Weibull survival of CAD-CAM endocrowns with different marginal designs: A 3D finite element analysis.

OBJECTIVES: To evaluate and compare the effect of tooth preparation designs and different CADCAM. materials on stress distribution and Weibull survival probability of endocrowns. applied to root canal-treated lower first permanent molar using the 3D finite element. analysis method. METHODS: A root canal-treated lower first permanent molar was prepared for endocrowns with a. butt joint or with a ferrule design by placing, circumferentially, a 1-mm wide shoulder. finish line. The prepared molar was scanned for the two designs and modeled on a 3D. Finite element model. Monolithic zirconia (IPS e.max ZirCAD MT, FCZ), lithium. disilicate (IPS e.max CAD, EX), and nano-ceramic resin composite (Lava Ultimate, LU). CAD-CAM materials were used for each preparation to design the virtual endocrown. A. total of six models were built according to the different tooth preparation designs and. endocrown materials. An occlusal load of 600 N and a transverse load of 20 N in. magnitude that simulates the average occlusal load was directed toward the occlusal. surfaces. von Mises and maximum principle values were evaluated Weibull risk-ofrupture. analysis was used to analyze the survival probability of the restorations and. tooth in the different models. RESULTS: The highest von Mises were found in the butt joint design for FCZ, EX, and LU (45.3. MPa, 35.2 MPa, and 24.2 MPa, respectively) compared to the ferrule design for the. same materials (42.6 MPa, 31.2 MPa, and 23.6 MPa, respectively). For von Mises. stress distribution in the remaining part of tooth structure (dentin), the highest stresses. were found in LUFerrule which was closely similar to LUButt joint (135.4 MPa and. 134.7 MPa, respectively), followed by EXFerrule and FCZFerrule (132.2 MPa and. 131.7 MPa, respectively), while the lowest stresses were found in EXButt joint and. FCZButt joint (129.0 MPa and 128.4 MPa, respectively). Shear stresses within the. resin cement were the highest in FCZ and EX compared to LU. EX was found to be the. most reliable material with the highest survival probability, while FCZ showed the. lowest survival probability according to the Weibull risk-of-fracture results. SIGNIFICANCE: Materials with high elastic modulus transfer more stresses to the endocrown and less. to the remaining tooth structure. Endocrown tooth preparation with ferrule design has. better stress distribution and magnitude compared to the butt joint design.

The fracture strength and the failure mode of lithium disilicate or resin nano ceramics as a crown, overlay, or endocrown restoration on endodontically treated teeth.

INTRODUCTION: Different materials and restorative concepts have been proposed over the years to restore endodontically treated teeth (ETT). Monolithic ceramic and composite restoration can be lute to the tooh, without the use of a post. However, little is known how the material stiffness and presence of a composite core will affect the survival and failure mode. The objective of this in-vitro study was to evaluate the fracture strength and failure mode of endodontically treated molars, restored with ceramic or hybrid composite monolithic restoration, in the presence of absence of a composite core. MATERIALS AND METHODS: Sixty depulped molars were restored with a lithium-disilicate (e.max CAD) or hybrid composite (Cerasmart) restoration. Both materials were used in a monolithic approach, but with 3 different designs: (a) monolithic endocrown, (b) crown with a separate composite core, and (c) overlay without core buildup or pulpal extension. Ten sound teeth were used as control group. All groups were thermocycled (10,000 cycles), subsequently loaded in a chewing simulator (100,000 cycles) and finally loaded until fracture. RESULTS: Peak fracture loads and failure modes were registered. No significant differences were seen between the groups in terms of fracture load. Failure modes were statistically significantly different among groups with significant correlation between restoration type and material. (p < 0.001 and p = 0.033, respectively). No group presented significantly higher fracture resistance. Although ceramic crowns and overlays presented the highest repairability, all restored ETT were within the range of the intact tooth' fracture strength. CONCLUSION: No restoration presented significant different fracture loads. However, the type of restoration and material choice were correlated to the fracture mode.

[In vitro analysis of the influence of different tooth positions and retention depths of the pulp cavity on the accuracy of digital impression of the endocrown].

OBJECTIVE: To evaluate the influence of tooth position and retention depth of the dental pulp cavity on the accuracy of intraoral digital impression of endocrown preparation. METHODS: Dental pulp cavities with retention depths of 2, 3, 4 and 5 mm were prepared on 8 auatomic resin tooth models, including 4 right maxillary first molar (16) and 4 right mandibular first molar (46).Each cavity were scanned for 10 times using 3shape trios3, with micro-CT scans as the reference.All the scan data were exported, and the reference models were obtained by 3D reconstruction with Mimics 2021 software.Gomagic Wrap 2017 was used to analyze the 3D models.The average absolute deviation values were calculated to evaluate the accuracy of the digital models. RESULTS: There was no significant difference in the authenticity and precision between models 16 and 46.The mean maximum positive and negative deviations of the model 16 were less than those of the model 46(P<0.05), and for both the models 16 and 46, the mean maximum positive deviation was significantly greater than the mean maximum negative deviation (P<0.05).The authenticity of the 5 mm group was lower than that of the 2 mm, 3 mm and 4 mm groups (P<0.05).The precision was higher in 2 mm group than in 4 mm and 5 mm groups (P<0.05), and higher in 3 mm group than in 5 mm group (P<0.05).The mean maximum positive and negative deviations in 2 mm group were lower than those in 5 mm group (P<0.05). CONCLUSION: The position of teeth has little influence on intraoral digital impression of the endocrown.The retention depth of the dental pulp cavity affects the accuracy of intraoral digital impression of the endocrown, and a greater depth results in a greater deviation.

Assessment of Level of Awareness, Current State of Knowledge, and Skills on Endocrown Technique Among Senior Saudi Dental Students and Interns.

Background Awareness and knowledge about the endocrown technique contribute to the delivery of quality dental care and restorative long-term success. Dentists must be aware and knowledgeable about endocrowns as they offer a conservative approach, aid in maintaining tooth integrity, and have become a promising option in use recently. Aim This study evaluated the current state of knowledge, and the understanding of the endocrown technique as post-endodontic management among senior undergraduate dental students and interns who have studied the theoretical and laboratory procedures of endocrown as part of the curriculum. Materials and methods This cross-sectional investigation was conducted through an online questionnaire consisting of 21 questions in three parts. The first part consisted of demographic information; the second encompassed knowledge and attitude; and the third part evaluated skills regarding endocrown technique. A total of 164 voluntary dental students and dental intern questionnaires were evaluated. Factor analysis was used to identify the domains for knowledge and skill. Results In this study, the knowledge and skills of undergraduate dental students toward endocrowns were assessed. The reliability statistics showed favorable internal consistency (Cronbach's alpha values: 0.513 for knowledge and 0.729 for skill component 1). Significant correlations were noticed between knowledge component 1 and skill component 1 (r = 0.647, p < 0.001), knowledge component 1 and skill component 2 (r = 0.333, p < 0.001), and knowledge component 1 and skill component 3 (r = 0.260, p = 0.001). These findings emphasize the importance of evaluating students' understanding of endocrown. Significant differences were found among intern participants, fifth- and sixth-year dental students in component 1 of the knowledge (p-value<0.001), and all skills components. Conclusion Dental students have varying levels of knowledge and skills related to endocrown. Gaps in knowledge and skills have been detected, which dictates intervention actions, including curricular changes and training workshops.

Fracture strength of endocrown maxillary restorations using different preparation designs and materials.

PURPOSE: This study investigated the impact of preparation design and material types on fracture strength in maxillary premolars endocrowns after thermodynamic aging. MATERIALS AND METHODS: Eighty two-rooted maxillary premolar crowns underwent endodontic treatment (N = 80, n = 10). The teeth were categorized into ten groups (4-mm deep with no intracanal extension lithium disilicate glass ceramic & multilayer zirconia endocrowns (LE0 & ZE0); 4-mm deep with 4-mm intracanal extension in one canal (LE1 & ZE1); 4-mm deep with 2-mm intracanal extensions in both canals (LE2 & ZE2); flat overlays with no endocore (LO & ZO); glass fiber reinforced post & core and crown (LC & ZC)). After cementation, all specimens were subjected to 1500 thermocycles and 1,200,000 chewing cycles with an axial occlusal load of 49 N. A static loading test was performed at a non-axial 45° loading using a universal testing machine and failure modes (Type I: restoration debonding; Type II: restoration fracture; Type III: restoration/tooth complex fracture above bone level; Type IV: restoration/tooth complex fracture below bone level) were evaluated using a stereoscope. Data were ananalzed using 2-way ANOVA and Tukey's tests (alpha = 0.05). RESULTS: The endocrowns manufactured from multilayered zirconia and pressed lithium disilicate glass ceramic exhibited a fracture load ranging between 1334 ± 332 N and 756 ± 150 N, with ZC presenting the highest and LE2 the lowest values. The differences were not statistically significant (p > 0.05). CONCLUSION: All endocrowns tested in this study performed similar considering the different designs and materials tested. The distribution of fracture modes did not differ significantly depending on the design of the restoration and the type of material used.