RESUMO
Objective: was to evaluate fracture resistance of zirconia monolithic restorations after aging procedures. Material and methods: Monolithic translucent zirconia 3-unit FPDs were fabricated using Cerec inLab CAD/CAM system on 2 stainless steel dies with a uniform 120 degrees circumferential deep chamfer finish line of 1 mm width. FPDs were divided into 2 groups, first group (Group A) was subjected to aging procedures in an autoclave at hydrothermal conditions 134 oC /2 bars for 5 hours. Second group (Group B) was not subjected to any aging procedures (control group). All specimens of each group were loaded compressively in a universal testing machine at cross head speed 0.5 mm/min until fracture occurred. The percentage of monoclinic (m) phase was detected by XRD device. Scanning electron microscope (SEM) was used to examine the fractured surfaces for Aged TZI (Group A) and Non-aged TZI (Group B). Student's t-test was used to compare between fracture resistances of both groups. The significance level was set at P ≤ 0.05. Results: The fracture resistance mean (SD) values of non-aged TZI (Group B) was 2406.9 ± 306.8 N which showed statistically significantly higher than that of aged group (Group A) which was 1964.5 ± 234.5 N. The percentage of monoclinic (m) phase detected by XRD device software in non-aged TZI (Group B) was nearly 0 weight % and in aged TZI (Group A) was about 42 weight %. Conclusions:Accelerated artificial aging decreases the fracture resistance of monolithic TZI FPDs. (AU)
Objetivo: Foi avaliar a resistencia à fratura de restaurações de zircônia monolítica após procedimentos de envelhecimento.Material e Métodos: 3 unidades de FPDs de zircônia monolítica translucida foram fabricadas utilizando o sistema Cerec inLab CAD/CAM com 2 matrizes de aço inoxidável com uma linha de acabamento de chanfro profundo circunferencial de 120 graus de largura de 1 mm. As FPDs foram divididos em dois grupos, primeiro grupo (Grupo A) foi submetido a procedimentos de envelhecimento em autoclave em condições hidrotérmicas de 134 °C /2 bars por 5 horas. O segundo grupo (Grupo B) não foi submetido a nenhum processo de envelhecimento (grupo controle). Todos os espécimes de cada grupo foram carregados compressivamente em uma maquina de teste universal na velocidade de 0.5 mm/min até a fratura ocorrer. A porcentagem da fase monoclínica (m) foi detectada pelo dispositivo XRD. O microscópio eletrônico de varredura (MEV) foi utilizado para examinar as superfícies fraturadas para TZI envelhecido (Grupo A) e TZI não envelhecido (Grupo B). O teste t de estudantes foi usado para comparar as resistências à fraturas de ambos os grupos. O nível de significância foi estabelecido em P ≤ 0.05. Resultados: Os valores médios de resistência à fratura (SD) do TZI não envelhecido (Grupo B) foi 2406.9±306.8 N, o qual se mostrou estatisticamente significativamente maior do que o grupo envelhecido (Grupo A), que foi 1964.5±234.5 N. A porcentagem da fase monoclínica (m) detectada pelo software do dispositivo XRD em TZI não envelhecido (Grupo B) foi próximo de 0% em peso e em TZI envelhecido (Grupo A) foi cerca de 42% em peso. Conclusão: O envelhecimento artificial acelerado diminui a resistência à fratura de FPDs TZI monolítico (AU)
Assuntos
Microscopia Eletrônica de Varredura , Resistência à FlexãoRESUMO
Objective: The objective of the present in-vitro study was to verify the efficacy of two spectrophotometer-based shade matching systems for color matching of ceramics after artificial accelerated aging (AAA). Material and Methods: The ceramics used were porcelain laminated veneers. Seventy standard-shaped discs (thickness x diameter: 0.5 mm x 10 mm) of B1 shades were used. Based upon the type of resin cement used, the specimens were divided into seven groups (10/group). The following light-cured cements were used: RelyX-Veneer (L-RV), Variolink-Veneer (L-VV), and Variolink-Esthetic (L-VE). The dual-cured cements were: RelyX Ultimate (D-RU), RelyX-Unicem (D-RC), and Variolink-Esthetics DC (D-VE). The control group consisted of ceramic only. All specimens were thermocycled in water for 3,500 cycles between 5 oC -55 oC, with dwell times of 30 s in each bath and a transfer time of 10 s between baths. All specimens were thermocycled in water for 3,500 cycles between 5 oC and 55 oC, and color measurement was done using the VITA Easyshade and ColorEye spectrophotometers. Baseline color reading was performed 24-hours after cementation. Differences in color (DE) of EasyShade and ColorEye before and after AAA were determined and compared statistically. Group comparisons were done using the paired t-tests. Level of significance was set at P< 0.05. Results: The mean differences in color (ΔE) values obtained from EasyShade spectrophotometer for light- and dual-cured cements, were 0.843±0.89 (L-RV ), 4.11±0.69 (L-VV) and 0.833±0.47 (L-VE); and 2.22±0.64 (D-RU), 3.37±0.83 (D-RC) and 0.38±0.92 (D-VE), respectively. The mean differences in color (ΔE) values obtained from ColorEye spectrophotometer for light- and dual-cured cements, were 0.68±0.86 (L-RV ), 4.55±0.83 (L-VV) and 2.68±0.26 (L-VE); and 2.06±0.84 (D-RU), 1.8±1.08 (D-RC) and 0.96±0.71 (D-VE), respectively. There was no significant difference in the mean DE values among the groups. Conclusion: The VITA Easyshade and ColorEye shade matching systems are comparable in terms of their efficacy for color matching of cerammics after AAA.(AU)
Objetivos: O objetivo do presente estudo in vitro foi verificar a eficácia de dois espectrofotômetros baseados em escalas de cor para avaliação de cor de cerâmicas após envelhecimento artificial acelerado (EAA). Material e Métodos: As cerâmicas utilizadas foram laminados cerâmicos. Foram usados setenta discos de formato padrão (0,5mm de espessura x 10 mm de diâmetro) de tonalidades B1. Com base no tipo de cimento resinoso utilizado, os corpos-de-prova foram divididos em sete grupos (10 / grupo). Foram utilizados os seguintes cimentos fotopolimerizáveis: RelyX-Veneer (L-RV), Variolink-Veneer (L-VV) e Variolink-Esthetic (L-VE). Os cimentos de cura dual foram: RelyX Ultimate (D-RU), RelyX-Unicem (D-RC) e Variolink-Esthetics DC (D-VE). O grupo controle consistia apenas de cerâmica. Todos os corpos-de-prova foram termociclados em água por 3.500 ciclos entre 5oC-55oC, com tempos de permanência de 30s em cada banho e um tempo de transferência de 10s entre os banhos. A medição da cor foi feita usando os espectrofotômetros VITA Easyshade e ColorEye. A leitura da cor inicial foi realizada 24 horas após a cimentação. As diferenças na cor (ΔE) do EasyShade e ColorEye antes e depois do EAA foram determinadas e comparadas estatisticamente. As comparações dos grupos foram feitas usando o teste t pareados. O nível de significância foi estabelecido em p <0,05. Resultados: os valores médios de diferenças na cor (ΔE) obtidos no espectrofotômetro EasyShade para cimentos fotopolimerizáveis e duais foram de 0,843 ± 0,89 (L-RV), 4,11 ± 0,69 (L-VV) e 0,833 ± 0,47 (L-VE ); e 2,22 ± 0,64 (D-RU), 3,37 ± 0,83 (D-RC) e 0,38 ± 0,92 (D-VE), respectivamente. os valores médios de diferenças na cor (ΔE) obtidos no espectrofotômetro ColorEye para cimentos fotopolimerizáveis e duais foram de 0,68 ± 0,86 (L-RV), 4,55 ± 0,83 (L-VV) e 2,68 ± 0,26 (L-VE); e 2,06 ± 0,84 (D-RU), 1,8 ± 1,08 (D-RC) e 0,96 ± 0,71 (D-VE), respectivamente. Não houve diferença significativa nos valores médios de ΔE entre os grupos. Conclusão: Os sistemas de combinação de cores VITA Easyshade e ColorEye são comparáveis em termos de eficácia para avaliação de cores de cerâmicas após EAA. (AU)
Assuntos
Técnicas In Vitro , Espectrofotômetros , Materiais Dentários , Facetas DentáriasRESUMO
Objetivo: O objetivo deste trabalho foi avaliar a influência do envelhecimento artificial acelerado na resistência à compressão de resinas compostas. Metodologia: Foram avaliadas cinco marcas comerciais de resinas compostas: Z250®, 4Seasons®, P60®, Z100® e Charisma®. Para cada resina foram obtidos 16 corpos de prova, divididos em dois grupos de oito, sendo um grupo submetido ao sistema envelhecimento acelerado para não metálicos CUV e o outro, à análise de resistência à compressão 24 horas após sua obtenção. Posteriormente, os corpos de prova envelhecidos foram submetidos ao ensaio de compressão. As médias das leituras de resistência à compressão de cada corpo de prova foram submetidas ao teste Kolmogorov-Smirnov (p > 0,05), Anova e teste de Tukey (p < 0,05). Resultados: A análise dos fatores apresentou diferenças significantes entre as marcas de resina composta quanto à resistência à compressão (F = 40,31, p < 0,0001). Com relação ao mesmo material antes e depois do envelhecimento, nota-se que esse processo não influenciou na resistência a compressão de nenhuma das resinas compostas (F = 2,82, p = 0,09). Nota-se que houve interação entre os fatores marca da resina composta e envelhecimento (F = 3,20, p < 0,004). Conclusão: Independentemente do tipo de resina, o envelhecimento artificial acelerado não influenciou na resistência à compressão. No entanto, houve diferença significante entre as marcas de resina quanto a essa propriedade.