Reliability and lifetime of lithium disilicate, 3Y-TZP, and 5Y-TZP zirconia crowns with different occlusal thicknesses.

OBJECTIVES: To assess the probability of survival of crowns made with a 3Y-TZP, a 5Y-TZP, and a lithium disilicate. MATERIALS AND METHODS: CAD-CAM premolar crowns with occlusal thicknesses of 1.0 mm or 1.5 mm and cemented on a metal dye. Step-stress accelerated life testing (SSALT) was performed to access the use level probability Weibull curves and reliability were calculated for the completion of a mission of 100,000 cycles at 300 to 1200 N. RESULTS: All ceramics showed a high probability of survival (87-99%) at 300 N, irrespective of thickness. 3Y-TZP shows no significant decrease in the probability of survival up to 1200 N (83-96%). Lithium disilicate presented lower reliability than zirconia under the 600 N mission. 5Y-TZP showed lower reliability than 3Y-TZP at 1200 N. There was no significant difference in the Weibull modulus (3.23-7.12). 3Y-TZP had the highest characteristic strength (2483-2972 N), followed by 5Y-TZP (1512-1547 N) and lithium disilicate (971-1154 N). CONCLUSION: Zirconia ceramics have a high probability of survival (up to 900 N-load), while lithium disilicate survives up to 300 N load only, irrespective of the thickness (1.0 mm or 1.5 mm). CLINICAL RELEVANCE: The probability of survival of posterior crowns made with zirconia ceramics resists extreme loads while glass ceramics resist normal chewing loads. In addition, crowns with thinner occlusal face showed sufficient mechanical behavior.

Efeito antimicrobiano e propriedades mecânicas da zircônia translúcida revestida por vidros experimentais / Antimicrobial effect and mechanical properties of translucent zirconia coated with experimental glasses

Objetivos: Avaliar as propriedades mecânicas, atividade antimicrobiana e citocompatibilidade da zircônia translúcida 5Y-PSZ revestida por vidros experimentais contendo boro e prata. Métodos: Discos 5Y-PSZ (KATANA UTML™, Kuraray Noritake) foram processados e divididos em quatro grupos: polido, sem nenhum revestimento (Controle), aplicação de glaze comercial (Glaze) e vidros experimentais contendo prata (AgCoat) e boro (BCoat). As amostras foram submetidas aos testes de dureza Vickers, testes de flexão biaxial, análise fractográfica e rugosidade através de perfilometria óptica. O potencial antimicrobiano foi caracterizado usando biofilmes de espécie única de Streptococcus mutans e Candida albicans. Foi realizada a quantificação de unidades viáveis formadoras de colônias (UFC), atividade metabólica (CV), ensaios de matriz polissacarídica extracelular (EPS) e biovolume. Biofilmes foram visualizados por microscópio eletrônico de varredura (MEV) e microscopia confocal de varredura a laser (CLSM). A citocompatibilidade foi determinada usando os testes WST-1 e LIVE&DEAD usando células-tronco do ligamento periodontal (PDLSCs) por 24 h. Todas as caracterizações biológicas foram realizadas em triplicatas técnicas e biológicas usando amostras independentes. As análises estatísticas foram realizadas por ANOVA de uma via, teste de Tukey, análise de Weibull e análise de correlação de Pearson. Resultados: BCoat, AgCoat e Glaze alcançaram dureza semelhante, que foi menor que o Controle. BCoat teve a maior resistência à flexão e parâmetros de Weibull (m = 11,5, sF 625 MPa, s0 620) seguido por AgCoat (m = 5,3; sF 464 MPa, s0 478 MPa). BCoat diminuiu significativamente a formação de biofilmes, conforme mostrado pela menor UFC (5,94 log-UFC/mm2) e atividade metabólica (0,17 a.u.) em comparação com os outros grupos (AgCoat: 6,44 log-UFC/mm2, 0,89 a.u.; Glaze: 6,81 log UFC/mm2, 1,21 a.u.; Controle: 6,82 logUFC/mm2, 1,25 a.u.). BCoat e AgCoat apresentaram os menores valores de EPS (0,11 a.u.), seguidos por Glaze e Controle (0,13 a.u.; 0,14 a.u., respectivamente). MEV e CLSM revelaram que os biofilmes no BCoat eram finos, esparsos, com menor biovolume, enquanto os outros grupos produziram biofilmes robustos com maior biovolume. Os ensaios de viabilidade celular não mostraram toxicidade para PDLSCs para todos os grupos. Conclusão: 5Y-PSZ revestida por vidro experimental contendo boro surge como uma estratégia potencial para melhorar as propriedades mecânicas e antimicrobianas do material (AU).

Objectives: To evaluate the mechanical and antimicrobial properties of boroncontaining coating on translucent zirconia (5Y-PSZ). Methods: 5Y-PSZ discs (Control) were coated with a glaze (Glaze), silver- (AgCoat), or boron-containing (BCoat) glasses. The coatings' antimicrobial potential was characterized using S. mutans and C. albicans biofilms through viable colony-forming units (CFU), metabolic activity (CV), and the extracellular polysaccharide matrix (EPS). Biofilm architectures were imaged under scanning electron and confocal laser scanning microscopies (SEM and CLSM). Cytocompatibility was determined at 24 h via WST-1 and LIVE&DEAD assays using periodontal ligament stem cells (PDLSCs). The coatings' effects on mechanical properties were characterized by Vickers hardness, biaxial bending tests, and fractography analysis. Statistical analyses were performed via one-way ANOVA, Tukey's tests, Weibull analysis, and Pearson's correlation analysis. Results: BCoat significantly decreased biofilm formation, having the lowest CFU and metabolic activity compared with the other groups. BCoat and AgCoat presented the lowest EPS, followed by Glaze and Control. SEM and CLSM images revealed that the biofilms on BCoat were thin and sparse, with lower biovolume. In contrast, the other groups all yielded similarly robust biofilms with higher biovolume without compromising PDLSC viability. BCoat, AgCoat, and Glaze also presented similar hardness significantly lower than Control. BCoat had the highest flexural strength, characteristic strength and Weibull parameters (sF : 625 MPa; s0: 620 MPa; m = 11.5), followed by AgCoat (sF : 464 MPa; s0: 478 MPa; m = 5.3). Significance: BCoat is a cytocompatible glass with promising antimicrobial properties that can improve the mechanisms and reliability of 5Y-PSZ (AU).

Effects of argon plasma and aging on the mechanical properties and phase transformation of 3Y-TZP zirconia

Abstract To evaluate the flexural strength (FS) and flexural modulus (FM) of a commercial 3Y-TZ0P ceramic after artificial aging and either without or with two application times of non-thermal plasma treatments (NTP). In addition, changes in crystalline phase transformation and surface nano-topography after NTP application, during different aging periods, were evaluated. Ninety 3Y-TZP bars (45x4x3 mm) were made for FS and FM testing, and assigned to nine groups (n=10): no NTP/no aging (Control); no NTP/4h aging; no NTP/30h aging; 10s NTP/no aging; 10s NTP/4h aging; 10s NTP/30h aging; 60s NTP/no aging; 60s NTP/4h aging and 60s NTP/30h aging. Artificial accelerated aging was simulated using an autoclave (134º C at 2 bar) for up to 30h. FS and FM were assessed using a universal testing machine and data analyzed using a ANOVA and Tukey test (α=0.05). The volume change in zirconia monoclinic phase (MPV) was evaluated using X-ray diffraction and surface nano-topography was assessed using atomic force microscopy (baseline until 30h-aging). NTP application did not influence the FS and FM of zirconia. Compared to the Control (no NTP/no aging), the FS of zirconia samples treated for 30 hours in autoclave ("no NTP/30h aging" group) increased. Artificial aging for 30 hours significantly increased the FM of zirconia, regardless of NTP application. MPV tended to increase following the increase in aging time, which might result in the surface irregularities observed at 30h-aging. NTP did not alter the zirconia properties tested, but 30h-aging can change the zirconia FS, FM and MPV.

Resumo Avaliar a resistência à flexão (FS) e o módulo de flexão (FM) de uma cerâmica comercial 3Y-TZP após envelhecimento artificial, e com ou sem dois tempos de aplicação de plasma não térmico (NTP). Além disso, a transformação de fase cristalina e a nano-topografia de superfície após a aplicação de NTP, durante diferentes períodos de envelhecimento, foram avaliadas. Noventa barras 3Y-TZP (45x4x3 mm) foram feitas para testes de FS e FM, e distribuídas em nove grupos (n=10): sem NTP/sem envelhecimento (Controle); sem NTP/4h de envelhecimento; sem NTP/30h de envelhecimento; 10sNTP/sem envelhecimento; 10sNTP/4h; 10sNTP/30h; 60sNTP/sem envelhecimento; 60sNTP/4h e 60sNTP/30h. O envelhecimento artificial acelerado foi simulado em autoclave (134º C a 2 bar) por até 30 horas. FS e FM foram avaliados em máquina de ensaio universal e os dados analisados ​​pela ANOVA e teste de Tukey (α = 0,05). A mudança de volume da fase monoclínica de zircônia (MPV) foi avaliada usando difração de raios-X e nano-topografia de superfície foi avaliada utilizando microscopia de força atômica (baseline até 30h). A aplicação do NTP não influenciou a FS e FM da zircônia. Comparado ao Controle ("sem NTP/sem envelhecimento"), a FS das amostras de zircônia tratadas por 30 horas em autoclave ("sem NTP/30h de envelhecimento") aumentou. O envelhecimento artificial por 30 horas aumentou significativamente a FM da zircônia, independente do tempo de aplicação do NTP. O MPV tendeu a aumentar em função do aumento do tempo de envelhecimento para todos os grupos, que pode ter resultado nas irregularidades superficiais observadas com 30 horas de envelhecimento. O NTP não afetou as propriedades da zircônia testadas, mas o envelhecimento por 30 horas pode alterar a FS, FM e MPV da zircônia.

Influência do uso da proantocianidina em um adesivo autocondicionante: avaliação da resistência de união / Influence of the use of proanthocyanidinin a self-etching adhesive: evaluation of bond strength / Influenciadel uso de proantocianidinaem um adesivo autograbante: evaluación de la fuerza de unión

Introdução:Os sistemas adesivos possibilitama execução de restaurações estéticas e minimamente invasivas, sendo, portanto,objeto de pesquisas para contornar os problemas que se apresentam no procedimento restaurador.Objetivo:Avaliar in vitroa resistência de união de um sistema adesivo autocondicionante, e deste modificado com soluções extrativas de semente de uva.Metodologia:Duas soluções extrativas foram preparadas comextrato de semente de uva em pó dissolvido em acetona e etanol. A partir delas e de umadesivo,seis sistemas adesivos autocondicionantes experimentais foram preparados, diferindo quanto aosolvente utilizado eàsproporções entre adesivo puro e solução extrativa(7,5%, 15% e 30%). Setenta incisivos bovinos hígidos tiveram as raízes removidas com disco de carborundum e as faces vestibulares desgastadas comlixas d'água de granulação 120, 240, 600 e 1200 sob refrigeração até expor a dentina superficial. Os dentes foram distribuídos aleatoriamenteem sete grupos distintos: Controle; A7,5; A15; A30; E7,5; E15; e E30, contendo 10 elementos cada. A aplicação dos adesivos foi executada de acordo com as recomendações do fabricante do adesivo controle. A restauração foi realizada com uma matriz de silicone com dimensões 2mm de altura e 4mm de diâmetro e inserido o material restaurador em incremento único e fotopolimerizado por 40s. Após três meses armazenados em água destilada, os espécimes foram submetidos ao teste de resistência de união. Foi empregado ométodo estatísticoTeste Paramétrico Anova 1 Fator e pós-teste de Tamhane (p<0,05). Resultados:Os grupos A7,5, E7,5 e E30 não apresentaram diferença em relação ao grupo Controle; A15 e A30 mostraram desempenho estatisticamente semelhante entre si; e E15 não apresentou diferença estatística em relação aos outros adesivos.Conclusões:A adição de proantocianidina teve efeitos diferentes,dependendodos solventes e das concentrações utilizadas, mas sem alterar significativamente o desempenho do adesivo (AU).

Introduction:Adhesive systems make it possible to perform aestheticand minimally invasive restorations, being the subject of research to circumvent the problems that arise in the restorative procedure.Objective:Evaluate in vitrothe bond strength of a self-etching adhesive system,and modified with extractive grape seed solutions. Methodology:Two extractive solutions were prepared with powdered grape seed extract dissolved in acetone and ethanol. From them and an adhesive, six experimental self-etching adhesive systems were prepared, differing in terms of the solvent used and the proportions between pure adhesive and extractive solution(7.5%, 15% and 30%). Seventy healthy bovine incisors had their roots removed with carborundum disc and the vestibular faces were worn with sandpaper with granulation water 120, 240, 600 and 1200 under refrigeration until the superficial dentin was exposed. The teeth were randomly assigned to seven different groups: Control; A7.5; A15; A30; E7.5; E15; and E30, containing 10 elements each. The application of the adhesives was carried out according to the recommendations of the manufacturer of the control adhesive. The restoration was performed with a silicone matrix with dimensions 2mm high and 4mm indiameter and the restorative material was inserted in a single increment and light cured for 40s. After three months stored in distilled water, the specimens were submitted to the bond strength test. The statistical method Parametric Test Anova 1 Factor and Tamhane post-test (p<0.05) were used. Results:Groups A7.5, E7.5 and E30 showed no difference in relation to the Control group; A15 and A30 showed a statistically similar performance; and E15 showed no statistical difference in relation to the other adhesives. Conclusions:The addition of proanthocyanidin had different effects, depending on the solvents and concentrations used, but without significantly altering the performance ofthe adhesive (AU).

Introducción: Sistemas adhesivos permiten realizar restauraciones estéticas y mínimamente invasivas, siendo objeto de investigación para sortear problemas que surgen en elprocedimiento restaurador. Objetivo: Evaluar in vitrola fuerza de unión de un sistema adhesivoautograbante y modificado con soluciones extractivas de semilla de uva. Metodología: Se prepararon dos soluciones extractivas con extracto de semilla de uva en polvo disuelto en acetona y etanol. A partir de ellos y de un adhesivo, se prepararon seis sistemas experimentales de adhesivos autograbantes, que se diferencian en cuanto al solvente utilizado y las proporciones entre adhesivo puro y solución extractiva (7,5%, 15% y 30%). Setenta incisivos bovinos sanos fueron removidos con un disco de carborundo y las caras vestibulares fueron usadas com lija de agua de granulación 120, 240, 600 y 1200 bajo refrigeración hasta que la dentina superficial quedo expuesta. Los dientes se asignaron aleatoriamente a siete grupos diferentes: Control; A7,5; A15; A30; E7,5; E15; y E30, que contiene 10 elementos cada uno. La aplicación de los adhesivos se realizó siguiendo las recomendaciones del fabricante del adhesivo de control. La restauración se realizó con matriz de silicona con 2mm de altura y 4mm de diámetro y el material restaurador se insertó en un solo incremento y se fotopolimerizó durante 40s. Tres meses después, almacenados em agua destilada, las muestras se sometieron a la prueba de resistencia de la unión. Se utilizó el método estadístico Prueba Paramétrica Factor Anova 1 y post-prueba de Tamhane (p<0,05). Resultados: Los grupos A7,5, E7,5 y E30 no mostraron diferencias em relación con el grupo Control; A15 y A30 mostraron un desempeño estadísticamente similar; y E15 no mostró diferencia estadística en relación con los otros adhesivos. Conclusiones: La adición de proantocianidina tuvo diferentes efectos, dependiendo de los disolventes y concentraciones utilizadas, pero sin alterar significativamente el rendimiento del adhesivo (AU).

Hardness, compressive strength and resilience of complete denture lining materials: an in situ study / Dureza, resistência à compressão e resiliência de materiais de reembasamento para próteses totais: estudo in situ

ABSTRACT Objective The aim of this study was to evaluate the in situ hardness, compressive strength and resilience of soft lining materials used in total removable prostheses in different time intervals Methods total of 48 rectangular test specimens (10 x 3 x 2 mm) were fabricated of each of the polyvinylsiloxane-based soft liner (Mucopren Soft) and acrylic resin-based material (Trusoft), which were placed on total removable prostheses bases of 12 volunteers (n = 12). The hardness (Shore A), compressive strength (in MPa) and resilience (in Kgf/cm2) were evaluated in different time intervals: 0, 7, 30 and 60 days, at three different locations of the specimens surface. Results The two-way ANOVA and Tukey test showed that the polyvinylsiloxane-based soft liner presented higher hardness values (p = 0.0113) and higher compressive strength (p=0.0252) than the acrylic resin-based material at immediate and 7 days evaluations. The polyvinylsiloxane-based soft liner presented higher resilience values than the acrylic resin-based material at all times (p = 0.0133). Hardness and compressive strength were similar for both materials at 30 and 60 days evaluations. Conclusions For both materials,there was a tendency for an increase of hardness, compressive strength and resilience over time, influenced by the composition of the tissue conditioner. The polyvinylsiloxane-based soft liner presented higher hardness, compressive strength and resilience than the acrylic resin-based material, specially considering a long-term evaluation up to 60 days.

RESUMO Objetivo O objetivo deste estudo foi avaliar in situ a dureza, resistência à compressão e resiliência de materiais para reembasamento utilizadas em próteses totais removíveis em diferentes intervalos de tempo. Métodos Um total de 48 corpos de prova retangulares (10 x 3 x 2 mm) foram confeccionados de cada uma dos reembasadores a base de polivinilsiloxano (Mucopren Soft, Kettenbach GmbH & Co) e resina acrílica (Trusoft, Bosworth), os quais foram posicionados na base de próteses totais removíveis de 12 voluntários (n = 12). A dureza (Shore A), resistência à compressão (em MPa) e resiliência (em Kgf/cm2) foram avaliadas em diferentes intervalos de tempo: 0, 7, 30 e 60 dias, em três diferentes localizações da superfície do corpo de prova. Resultados A ANOVA a dois critérios e o teste de Tukey mostraram que o reembasador a base de polivinilsiloxano apresentou maiores valores de dureza (p = 0,0113) e maior resistência à compressão (p=0,0252) do que o a base de resina acrílica nas avaliações nos tempos imediato e 7 dias. O reembasador a base de polivinilsiloxano apresentou maior resiliência que o a base de resina acrílica em todos os tempos (p = 0,0133). Dureza e resistência à compressão foram semelhantes para ambos os materiais nos tempos 30 e 60 dias de avaliação. Conclusões Para ambos os materiais, houve tendência de aumento da dureza, resistência à compressão e resiliência com o passar do tempo, influenciado pela composição dos materiais de rembasamento tecidual. O reembasador a base de polivinilsiloxano apresentou maior dureza, resistência à compressão e resiliência que o a base de resina acrílica, considerando-se especialmente o tempo de avaliação de 60 dias.

Fatiga cíclica de cuatro sistemas reciprocantes en una canaleta dinámica de raíces simuladas / Cyclical fatigue of four reciprocating systems in a dynamic dump of simulating roots / Fadiga cíclica de quatro sistemas reciprocantes em uma com canais simulados

En conductos radiculares curvos, la utilización de limas que eviten desvíos y fracturas del instrumento por fatiga y que mantengan curvaturas originales son aspectos importantes en el tratamiento endodóntico. Ob-jetivo: Se evaluó la resistencia a la fatiga cíclica de cuatro sistemas reciprocantes en una canaleta dinámica que simuló tres curvaturas diferentes. Materiales y Método: Estudio in vitro; la muestra con 48 limas se dividió en cuatro grupos (n= 12/grupo): WaveOne® (WO), WaveOne® Gold (WOG), Reciproc® (R) y Reciproc® Blue (RB), cuatro limas de cada sistema se usaron en una canaleta que simuló tres angulaciones 45°, 60° y 90°; montadas en un motor X-Smart Plus®, las limas se introdujeron 23 mm en los conductos para ser activadas continuamente a 300/500 oscilaciones/minuto hasta que se produjo la fractura. Se registró tiempo y zona de fractura. Se realizó el test Kruskal Wallis con un nivel de confianza del 95% para las comparaciones. Resul-tados: RB presentó mayor resistencia a la fatiga cíclica que WO y WOG en todas las angulaciones y que R a 90° (p= <0,05). R presentó mayor resistencia que WOG a 45° y 60°, sin embargo, a 90° WOG fue superior que R y WO (p<0,05). No hubo diferencias en cuanto a la zona de fractura que aconteció en la porción apical. Conclusiones: La resistencia se reduce cuando aumenta el grado de curvatura. RB fue significativamente más resistente a la fatiga cíclica que WO y WOG en todas las angulaciones y que R a 90°. La zona de fractura se produjo en la porción apical de las limas.

In the curved canals, the use of files that avoid deviations and fractures of the instrument due to fatigue and that maintain original curvatures are important aspects in endodontic treatment. Objective: The resistance to cyclic fatigue of four reciprocating systems was evaluated in a dynamic gutter that stimulated three different curvatures. Materials and Method: In vitro study, the sample with 48 files was divided into four groups (n = 12 /group): WaveOne® (WO), WaveOne® Gold (WOG), Reciproc® (R) and Reciproc® Blue (RB), four files from each system were used in a gutter that simulated three angulations 45o , 60 o and 90 o . The files which were mounted on an X-smart Plus® were inserted 23 mm into the conduits to be continuously activated at 300/500 oscillations per minute until the fracture occurred. Time and fracture zone were recorded. The Krustal Wallis test was performed with a 95% confidence level for the comparisons. Results: RB presented greater resis-tance to cyclic fatigue than WO and WOG at 45o and 60o, however, at 90o WOG was higher than R and WO (p<0.05). There were no differences regarding the fracture zone occurred in the apical portion. Conclusions: The resistance decreases when the degree of curvature increases. RB was significantly more resistance to cyclic fatigue than WO and WOG at all angulations and R at 90o. The fracture zone occurred in the apical portion of the files.

Em canais radiculares curvos, o uso de limas que evitem desvios e fraturas do instrumento devido à fadiga e que mantêm as curvaturas originais são aspectos importantes no tratamento endodôntico. Objetivo: avaliar a resistência à fadiga cíclica de quatro sistemas reciprocantes em uma canaleta artificial que simula três curva-turas diferentes. Materiais e Método: estudo in vitro; a amostra com 48 limas foi dividida em quatro grupos (n = 12 / grupo): WaveOne® (WO), WaveOne® Gold (WOG), Reciproc® (R) e Reciproc® Blue (RB), quatro limas de cada sistema foram usadas em uma canaleta que simulo três angulações 45 °, 60 ° e 90 °; se montaram em um motor X Smart Plus®, as limas foram inseridas 23 mm nos condutos para serem ativadas continuamente a 300/350 oscilações / minuto até ocorrer uma fratura. O tempo e a zona de fratura foram registrados. O teste de Kruskal Wallis foi realizado com um nível de confiança de 95% para as comparações. Resultados: O RB apresenta maior resistência à fadiga cíclica que o WO e o WOG em todas as angulações e que R a 90 ° (p = <0,05). R apresentou maior resistência que WOG a 45 ° e 60 °, no entanto, a 90 ° WOG foi maior que R e WO (p <0,05). No existiu diferença na zona de fratura que ocorreu na porção apical. Conclusões: a resistência diminui quando o grau de curvatura aumenta. RB foi significativamente mais resistente à fadiga cíclica do que WO e WOG em todos os ângulos e R a 90 °. A zona de fratura ocorre na parte apical das limas.

Influência da solução de irrigação sobre a resistência adesiva de um cimento resinoso de dupla polimerização / Influence of solution of irrigation on the resistance of and adhesive resin cement double polymerization

Objetivo: Avaliar a influência de diferentes soluções de irrigação cavitária sobre a resistência de união de um cimento resinoso de dupla polimerização. Material e Método: A partir de incisivos bovinos, foram obtidos 4 grupos (n=15), divididos aleatoriamente de acordo com a solução irrigadora empregada na limpeza cavitária, sendo: G0 - soro fisiológico + condicionamento ácido; G1 ­ EDTA + condicionamento ácido; G2 - Clorexidina 2% + condicionamento ácido + clorexidina 2% e G3 - soro fisiológico + condicionamento ácido + clorexidina 2%. Foram confeccionados cilindros de cimento resinoso para cada coroa, utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e altura de 2 mm. O teste de resistência adesiva por microcisalhamento foi realizado após 3 meses de armazenamento dos espécimes em soro fisiológico a 37ºC. Os dados foram submetidos ao teste de Kruskall-Wallis, seguido do teste de Dunn (p<0,05). Resultados: Os grupos G0, G1 e G3 não apresentaram diferenças significativas entre si (p>0,05). Os menores valores foram observados no grupo G2 (p<0,05). Conclusões: As soluções irrigadoras EDTA e soro fisiológico utilizadas previamente ao condicionamento ácido da dentina não interferiram, significativamente, na resistência de união, porém, a solução de clorexidina utilizada após o condicionamento ácido influenciou negativamente nos valores de resistência de união.

Objectives: This study aimed to evaluate the influence of different cavity irrigation solutions on the bond strength of a dual-curing resin cement. Methods: From bovine incisors, 4 groups (n=15), were randomly divided according to the irrigating solution for cavity cleaning: G0 ­ saline + acid etching; G1 ­ EDTA + acid etching; G2: Chlorhexidine 2% + acid etching + Chlorhexidine 2%; and G3 ­ Saline + acid etching + Chlorhexidine 2%. Resin cement cylinders were made for each crown, using a Tygon matrix with internal diameter of 1 mm and height of 2 mm. The specimens were stored for 3 months at 37oC, and then subjected to microshear tests. Data were statistically analyzed by Kruskal-Wallis test followed by Dunn (p<0.05). Results: There were no statistically significant differences between G0, G1 and G3 groups (p>0.05). The lowest values were observed in G2 group (p<0.05). Conclusion: The irrigation solutions EDTA and saline used before to the acid etching of dentin did not interfere, significantly, in the bond strength, however, the solution of chlorhexidine used after the acid etching influenced negatively.

In vitro study of a modified sagittal split osteotomy fixation technique of the mandible: a mechanical test.

This study was performed to evaluate the compressive mechanical strength of rigid internal fixation (RIF) using 1.5-mm L-shaped plates fixed with monocortical screws in sagittal split osteotomy (SSO). Thirty synthetic hemimandibles, which had all undergone a 5-mm advancement, were divided into three groups: three 12-mm bicortical titanium screws were placed in an inverted L pattern in group A; one straight 2.0-mm system spaced titanium plate fixed with four 5-mm monocortical screws was used in group B; two 1.5-mm system L-shaped titanium plates, each fixed with four 5-mm monocortical screws, were used in group C. The models were subjected to compressive and progressive mechanical tests with forces applied in the area between the second premolar and first molar to verify resistance in Newtons (N). A displacement speed of 1mm/min was applied, with a maximum 10mm displacement of the distal segment or until disruption of the fixation. The deformity and/or eventual rupture of the plates were evaluated, and consequently their technical stability was determined. The results showed that the modified fixation technique tested in this study on synthetic mandibles resulted in adequate stability and superior mechanical behaviour compared to simulated osteosynthesis with the use of a straight 2.0-mm titanium plate.

Effect of thermocycling aging on the flexural strength of feldspathic ceramic / Efeito da termociclagem na resistência flexural de uma cerâmica feldspática

Objective: The aim of the study was to evaluate the effect of aging through different thermocycling protocols on the flexural strength of a feldspathic ceramic. Material and Methods: Fifty ceramic bars, Vitablock Mark II (VITA), with dimensions of 18X4X2mm were prepared. The bars were randomly distributed to the groups (n = 10), which were defined according to the number of thermal cycles (TCy): G0 - no TCy; G500 - 500 cycles of TCy; G6000 - 6000 TCy; G10000 - 10000 TCy; G15000 - 15000 TCy. After aging, the specimens were subjected to the three point bending test in a universal testing machine (EMIC DL 1000), under 0.5mm/min speed and loading of 50kgf, until catastrophic failure. A sample of each group was evaluated for topographic morphology under Scanning Electron Microscopy. Results: For mechanical testing, the following mean values and standard deviation (MPa) were obtained: G0 (99.78 ± 5.07); G500 (101.64 ± 5.59); G6000 (98.13 ± 4.95); G10000 (91.77 ± 9.68); G15000 (101.51 ± 4.22). An analysis of variance by regression equation (p = 0.387) was performed, demonstrating a weak and non-significant correlation between flexural strength and number of thermal cycles. Conclusion: It can be concluded that aging in water solely by different numbers of temperature cycles did not influence on the flexural strength of a feldspathic ceramic. (AU)

Objetivo: O objetivo do estudo foi avaliar o efeito do envelhecimento por meio de diferentes protocolos de ciclos térmicos na resistência à flexão de uma cerâmica feldspática. Material e Métodos: Cinquenta barras de cerâmica, Vitablock Mark II (VITA), com dimensões de 18X4X2mm foram preparadas. As barras foram distribuídas aleatoriamente pelos grupos (n = 10), os quais foram definidos de acordo com o número de ciclos térmicos (CT): G0 ­ nenhum; G500 - 500 CT; G6000 - 6000 CT; G10000 ­ 10000 CT; G15000 - 15000 CT. Após envelhecimento, as amostras foram submetidas ao ensaio de flexão de três pontos em uma máquina de ensaios universal (EMIC DL 1000), sob a velocidade de 0,5 mm / min e célula de carga de 50kgf, até uma falha catastrófica. Uma amostra de cada grupo foi avaliada quanto à morfologia topográfica sob microscopia eletrônica de varredura. Resultados: Para os testes mecânicos, foram obtidos os seguintes valores médios e desvio padrão (MPa): G0 (99,78 ± 5,07); G500 (101,64 ± 5,59); G6000 (98,13 ± 4,95); G10000 (91,77 ± 9,68); G15000 (101,51 ± 4,22). Uma análise de variância pela equação de regressão (p = 0,387) foi realizada, o que demonstra uma correlação fraca e não significativa entre a resistência à flexão e do número de ciclos térmicos. Conclusão: Pode-se concluir que o envelhecimento somente em água por diferentes números de ciclos térmicos não influenciou na resistência à flexão de uma cerâmica feldspática (AU)

Avaliação da resistência flexural de resinas compostas convencionais e do sistema bulkfill / Evaluation of the flexural strength between conventional composite resins and bulk fill system

O constante aprimoramento dos materiais odontológicos é impulsionado pelas pesquisas científicas que, por sua vez,são incentivadas pelo mercado consumidor que busca tratamentos estéticos e duráveis. Objetivo: avaliar a resistência flexuralde duas resinas compostas convencionais e uma resina composta do sistema bulkfill. Metodologia: foram utilizadas as resinas compostas: Z100TM (microhíbrida), FiltekTM Z350 XT (nanoparticulada) e a FiltekTM Bulk fill (sistema bulkfill). Foram confeccionados dez corpos de prova de cada compósito (25x2x2mm). Testes mecânicos para avaliação da resistência flexural foram realizados, os valores de força obtidos para fratura do corpo de prova foram, então, transformados em MPa. Resultados: o valor médio de resistência flexural médio encontrado para o grupo Z100TM=108,43MPa, para o grupo FiltekTM Bulk Fill=133,30MPa e para o grupo FiltekTM XT Z350=172,53MPa. Conclusões: a resina composta convencional denanoparticulaFiltekTM XT Z350 apresentou os maiores valores de resistência flexural, seguida da resina FiltekTMBulk fill. A resina Z100TM apresentou os menores valores médios de resistência flexural.

The constant improvement of dental materials is driven by scientific research which, in turn, is encouraged by the consumer market seeking aesthetic and durable treatments.Aim: to evaluate the flexural strength between two conventional composite resins and a composite resin of the bulk fill system. Methodology: composite resins were used: Z100TM (microhybrid), FiltekTM XT Z350 (nanoparticulate) and FiltekTM Bulk fill (bulk fill system). Ten specimens of each composite (25X2X2mm) were made. Mechanical tests for evaluation of flexural strength were performed, strength values obtained for fracture of the specimen were, then, transformed into MPa.Results: the mean value for the Z100TM group = 108.43MPa, for the FiltekTM Bulk Fill group = 133.30MPa and the FiltekTM XT Z350 group = 172.53MPa. Conclusions: the conventional composite resin of FiltekTM XT Z350 showed the highest values of flexural strength, followed by FiltekTM Bulk fill resin. Z100TM resin showed the lowest values of flexural strength.

Influence of Cusp Inclination and Type of Retention on Fracture Load of Implant-Supported Crowns

Abstract There are few informations about the influence of cusp inclination on the fracture strength of implant-supported crowns. The study aimed to evaluate the influence of cusp inclination and retention type on fracture load in implant-supported metal-ceramic single crowns. Sixty crowns were made, classified as cemented and screw-retained with screw access hole (SAH) sealed or not. Standard (33°) and reduced (20°) cusp inclinations were tested for each group (n=10). To support crowns of a mandibular second molar, analogs of external hexagon implants 5.0 were used. The fracture load was measured in a universal testing machine EMIC DL2000 (10 kN load cell; 0.5 mm/min). Two-way ANOVA (retention and cusp inclination) followed by post hoc Tukey’s honest significant difference test was used for the statistical analyses (a=0.05). Crowns with reduced cusp inclination exhibited significantly higher fracture load (p<0.01) than crowns with standard cusp inclination. Cemented crowns showed significantly higher fracture load (p<0.01) than screw-retained crowns. The interaction among these factors was not significant (p>0.05) for the fracture load. The sealing of SAH did not influence the fracture load of screw-retained crowns (p>0.05). In conclusion, fracture load of implant-supported metal-ceramic crowns was influenced by retention and cusp inclination, and there was no influence of the sealing of SAH.

Resumo Existem poucas informações sobre a influência da inclinação de cúspide na resistência à fratura de coroas implantossuportadas. O objetivo do estudo foi avaliar a influência da inclinação de cúspide e do tipo de retenção na carga de fratura de coroas unitárias metalocerâmicas implantossuportadas. Sessenta coroas foram confeccionadas, classificadas como cimentadas e parafusadas com orifício de acesso ao parafuso selado ou não. Cúspides com inclinação padrão (33°) e reduzida (20°) foram testadas para cada grupo (n=10). Para suportar as coroas de um segundo molar inferior, análogos de implante hexágono externo 5.0 foram utilizados. A carga de fratura foi mensurada em máquina de ensaios universais EMIC DL2000 (célula de carga de 10 kN; 0,5 mm/min). ANOVA dois fatores (retenção e inclinação da cúspide) seguido do pós-teste de Tukey da diferença honestamente significativa foi utilizada para análise estatística (a=0,05). Coroas com inclinação de cúspide reduzida exibiram carga de fratura significativamente maior (p>0,05) que coroas com cúspides de inclinação padrão. Coroas cimentadas apresentaram carga de fratura significativamente maior (p<0,01) que coroas parafusadas. A interação entre os dois fatores não foi significante (p>0,05) para a carga de fratura. O selamento do orifício de acesso ao parafuso não influenciou a carga de fratura das coroas parafusadas (p>0,05). Concluindo, a carga de fratura de coroas metalocerâmicas implantossuportadas foi influenciada pelo tipo de retenção e inclinação da cúspide, e não houve influência do selamento do orifício de acesso ao parafuso

Estudo da resistência coesiva de cimentos resinosos convencionais e autoadesivos / Study of the cohesive strength of conventional and selfadhesive resin cements

O presente estudo teve como objetivo avaliar a resistência coesiva e o módulo de elasticidade de cimentos resinosos à tração e compressão. Os 15 espécimes foram divididos em 3 grupos: G1: AllCem, G2: Rely X U100, G3: Rely X ARC e submetidos a dois testes mecânicos: tração e compressão. Foram obtidos os resultados de resistência e módulo de elasticidade à tração e compressão dos cimentos resinosos. Os resultados foram avaliados estatisticamente por meio da ANOVA e múltiplas comparações de Games-Howell. Para a tração, a ANOVA revelou diferenças significativas entre os valores médios segundo o cimento (p<0.05). O teste de múltiplas comparações de Games-Howell para a tensão de ruptura mostrou que o cimento resinoso Rely X U100 apresentou os menores valores (21.91 ± 4.97 MPa), seguido pelo AllCem (23.13 ± 5.51 MPa) e pelo Rely X ARC (36.10 ± 8.27 MPa), onde o Rely X ARC diferiu estatisticamente doRely X U100 e doAllCem. ORely X U100 e AllCemnão revelaram diferenças entre si (p<0.05). No teste de compressão, o cimento Rely X U100 também apresentou os menores valores (134.57 ± 48.93 MPa), seguido do Rely X ARC (145.64 ± 32.76 MPa) e AllCem (243.71 ± 29.75 MPa), onde os cimentos Rely X U100 e Rely X ARC diferiram estatisticamente do AllCem e não revelaram diferenças entre si (p<0.05). Concluiu-se que os cimentos resinosos duais convencionais estudados apresentaram maiores valores de resistência à tração quando comparados ao cimento resinoso dual autoadesivo. A resistência coesiva à compressão foi maior que à tração para todos os cimentos resinosos estudados (AU).

The aim of the present study was to evaluate the cohesive strength and elastic modulus of resin cements subjected to the tensile and compression strength. Fifteen specimens were divided into 3 groups: G1: Allcem, G2: Rely X U100, G3: Rely X ARC, and subjected to two mechanical testing: tensile and compression. Strength and elastic modulus results of tension and compression tests of resin cements were obtained. The results were statistically analyzed by ANOVA and multiple comparisons of Games-Howell. For tensile test, the ANOVA revealed significant differences between the mean values according to the cement (p <0.05). The test multiple Games-Howell comparisons for the break to tensile showed that the resin cement Rely X U100 showed the lowest values (21.91 ± 4.97 MPa), followed by Allcem (23:13 ± 5:51 MPa) and the Rely X ARC (36.10 ± 8.27 MPa ), where the Rely X ARC differed from Rely X U100 and Allcem. The Rely X U100 and Allcem revealed no differences (p<0.05). In the compression test, Rely X U100 cement also had the lowest values (134.57 ± 48.93 MPa), followed by Rely X ARC (145.64 ± 32.76 MPa) and Allcem (243.71 ± 29.75 MPa), where cement Rely X U100 and Rely X ARC differed from the Allcem and revealed no differences (p <0.05). It was concluded that conventional dual resin cements studied showed higher tensile strength when compared to the dual-cured self-adhesive cement. The cohesive compressive strength was greater than to tensile for all resin cements studied (AU).

Analysis of resistance to fatigue between straight solid and anatomic abutments of Morse taper system / Análise da resistência à fadiga entre pilares retos e anatômicos do sistema cone Morse

Background: The study of the phenomenon of fatigue is essential because implant failures usually are caused by this process. Purpose: The objective of this study was to examine the fatigue resistance of straight and anatomical abutments joints that were submitted to cyclic loads. Material and method: We used 37 Morse taper implants and 37 abutments, divided into two groups (n= 16: straight abutment, n= 21 anatomical abutment). The sets were submitted to cyclic loading (5 million) using servo-hydraulic equipment. Three sets from each group were subjected to bending tests to determine the maximum load resistance, which served as the parameter for comparison of the cyclic tests. We evaluated number of cycles, load and bending moment. Result: Of the 31 abutments cyclically tested, 17 (54.8%) fractured in fewer than 5 million cycles; 8 (25.8%) of these were straight abutments, and 9 (29%) were anatomical. A total of 14 samples (45.2%) resisted the cyclic loading. According to Fisher's exact test, there was no difference between groups as the fracture. Conclusion: Despite of the straight abutments have higher average load and bending moment on the anatomical, both types of abutments showed similar performance as the fracture strength in vitro.

Contexto: O estudo do fenômeno de fadiga é essencial porque as falhas de implantes geralmente são causadas por este processo. Objetivo: O objetivo deste estudo foi analisar a resistência à fadiga de conjuntos de pilares retos e anatômicos que foram submetidos a cargas cíclicas. Material e método: Foram utilizados 37 implantes cone Morse e 37 pilares, divididos em dois grupos (n = 16: pilares retos, n = 21: pilares anatômicos). Os conjuntos foram submetidos à carga cíclica (5.000.000) usando o equipamento servo-hidráulico. Três conjuntos de cada grupo foram submetidos a testes de flexão para determinar a resistência de carga máxima, o que serviu de parâmetro para comparação dos testes cíclicos. Foram avaliados número de ciclos, carga e momento de flexão. Resultado: Dos 31 pilares ciclicamente testados, 17 (54,8%) fraturaram em menos de 5 milhões de ciclos; 8 (25,8%) destes eram pilares retos, e 9 (29%) eram anatômicos. Um total de 14 amostras (45,2%) resistiu à carga cíclica. De acordo com o teste exato de Fisher, não houve diferença entre os grupos quanto à fratura. Conclusão: Apesar dos pilares retos terem maior carga média e momento de flexão que os anatômicos, os dois tipos de pilares apresentaram desempenho semelhante quanto a resistência à fratura in vitro.

Effect of Glaze Cooling Rate on Mechanical Properties of Conventional and Pressed Porcelain on Zirconia

Abstract The aim of this study was to characterize a conventional and a pressed porcelain for zirconia core as to biaxial flexural strength (BFS), apparent fracture toughness (FT) and microstructure composition, and to investigate the effect of glaze cooling rate on the BFS of the zirconia/porcelain bilayers. Monolayers of conventional porcelain Vita VM9 and pressed porcelain Vita PM9 (n=15) (12 mm diameter x 1.2 mm thick) were prepared for the BFS test (MPa). Apparent fracture toughness (MPa.m1/2) was measured by indentation technique (n=15). t-Student test was performed for statistical analysis. Scanning electron microscopy and x-ray diffraction were used to analyze the porcelain's microstructure. For the BFS of bilayers, zirconia discs (12 mm diameter x 1 mm thick) (Vita In-Ceram YZ) were veneered with the two porcelains (1 mm thick). After the glaze firing simulation, the specimens were submitted to fast or slow cooling (n=15). Apparent fracture toughness (MPa.m1/2) was measured on the porcelain surface of bilayers (n=15) and residual stress was calculated. Two-way ANOVA (porcelain and cooling method) was used for the bilayer analysis (a=0.05). Vita PM9 monolayer exhibited significantly higher BFS (p<0.01), but there was no significant difference (p=0.41) in the FT between the porcelains. For bilayer specimens, the two-way ANOVA for BFS was significant for the porcelain variable only (p<0.01) better for Vita PM9/zirconia. Two-way ANOVA for the FT for the bilayers was not significant for any variable. All groups showed compressive residual stresses. The pressed porcelain seems to be mechanically more effective for zirconia veneering.

Resumo Este estudo teve como objetivo caracterizar uma porcelana convencional e uma prensada indicadas para infraestrutura de zircônia em termos de resistência à flexão biaxial (RFB), tenacidade à fratura aparente (TF) e composição microestrutural, e investigar o efeito da taxa de resfriamento do ciclo de glaze na RFB de espécimes bicamada de zircônia/porcelana. Espécimes monocamada de porcelana convencional Vita VM9 e porcelana prensada Vita PM9 (n=15) (12 mm de diâmetro x 1,2 mm de espessura) foram preparados para o ensaio de RFB (MPa). Tenacidade à fratura aparente (MPa.m1/2) foi mensurada pela técnica da indentação (n=15). O teste de t-Student foi aplicado para as análises estatísticas. Microscopia eletrônica de varredura e difração de raios-X foram utilizadas para análise microestrutural da porcelana. Para o ensaio de RFB nos bicamadas, discos de zircônia (12 mm de diâmetro x 1 mm de espessura) (Vita In-Ceram YZ) foram recobertos com as duas porcelanas (1 mm de espessura). Após a simulação da queima de glaze, os espécimes foram submetidos ao método de resfriamento rápido ou lento (n=15). A tenacidade à fratura aparente (MPa.m1/2) foi mensurado na superfície da porcelana dos bicamadas (n=15) e o estresse residual foi calculado. Foi utilizado ANOVA a dois fatores (porcelana e método de resfriamento) para análise estatística dos espécimes bicamada (a=0,05). Monocamadas de Vita PM9 exibiram valores de resistência à flexão biaxial significativamente maiores (p<0,01), mas não houve diferença estatística (p=0,41) em relação à TF entre as porcelanas. Para os espécimes bicamada, ANOVA a dois fatores para RFB foi significante apenas para a variável porcelana (p<0,01), com superioridade para Vita PM9/zircônia. ANOVA a dois fatores para TF dos espécimes bicamadas não apresentou significância para nenhuma variável. Todos os grupos apresentaram estresse residual de compressão. Porcelanas prensadas parecem ser mecanicamente mais efetivas para recobrimento de zircônia.

Pilares cerâmicos utilizados na Odontologia: revisão de literatura / Ceramic abutments used in Dentistry: a literature review

A busca pela excelência estética e funcional nas reabilitações com próteses implantossuportadas necessita que a restauração tenha harmoniosa integração visual da coroa protética com a arcada dentária, além de ter a capacidade de suportar carga funcional. Para isso, a seleção do pilar protético é fundamental, permitindo similaridade de cor e translucidez em relação à estrutura dentária natural. Embora os pilares de titânio sejam considerados padrão ouro para a reabilitação implantossuportada, estes podem interferir negativamente na estética fnal do caso, pois, em algumas situações, é possível visualizar o metal através da margem da gengiva. A fm de solucionar esse problema, surgem os pilares de cerâmica, desempenhando um papel fundamental na capacidade de mimetizar o elemento dental natural equivalente. Nesse sentido, o objetivo deste estudo foi, através de uma revisão da literatura, discutir os principais aspectos relacionados aos pilares cerâmicos utilizados em reabilitações implantossuportadas

To achieve aesthetic and functional excellence in rehabilitation with implant prostheses, the restorations should have harmonious visual integration of the prosthetic crown with the dental arch, and have the ability to withstand functional load. For this, the selection of the abutment is essential, allowing similarity of color and translucency in relation to natural tooth structure. Although the titanium abutments are considered the gold standard for implant-supported rehabilitation, they can adversely affect the fnal aesthetics of the case because, in some situations, the metal through the gingival margin may be seen. In order to solve this problem, ceramic abutments play a key role in the ability to mimic the natural dental element. In this context, the objective of this study was, through a literature review, discuss the main aspects related to ceramic abutments used in implant-suported rehabilitation

Biomechanical comparison of four mandibular angle fracture fixation techniques.

The aim of this study was to make a comparison of the biomechanical behavior of four different internal fixation systems for mandibular angle fractures. A total of 40 polyurethane mandible replicas were employed with different fixation methods: group 1SP, one 2.0-mm four-hole miniplate; group 2PPL, two 2.0-mm four-hole parallel miniplates; group 3DP, one 3D 2.0-mm four-hole miniplate; and group 3DPP, one 3D 2.0-mm eight-hole miniplate. Each group was subjected to incisal or homolateral molar region loading. The load resistance values were measured at load application causing tip displacement of 1, 3, and 5 mm, and at the time at which the system achieves its maximum strength (MS). Means and standard deviations were compared among groups using analysis of variance and the Tukey test. Group 2PPL showed higher strength for all the displacements. For incisal loading, no statistically significant differences were found between groups 1SP, 3DP, and 3DPP. For molar loading, group 1SP and 3DPP showed statistically significant differences. For MS testing, group 1SP and 2PPL showed statistically significant differences in incisal loading; group 1SP and 3DP showed no statistically significant differences; and group 3DPP showed lower values of strength. Two parallel miniplates provide the most favorable mechanical behavior under the conditions tested.

Análise da resistência à fratura entre pilares retos e angulados do sistema cone Morse / Analysis of resistance to fracture between straight and angled abutments of Morse taper system

Objetivo: Analisar a resistência à fratura por fadiga dos conjuntos implante-pilar, nos tipos reto e angulado, submetidos a cargas cíclicas similares às mastigatórias. Material e método: Foram utilizados 32 implantes (3,75 × 11 mm) com sistema cone Morse e 32 pilares, separados em dois grupos: pilares retos e angulados (n=16) (Neodent, Curitiba, PR, Brasil). Os conjuntos foram submetidos a testes cíclicos em equipamento servo-hidráulico, fixando-se o número de ciclos em cinco milhões. Foram avaliados: número de ciclos, carga e momento de força das amostras. O Teste de Fisher e o Teste ANOVA foram aplicados (p<0,005). Amostras fraturadas foram analisadas em microscopia eletrônica de varredura (MEV). Resultado: Dos pilares retos, quatro resistiram ao número de ciclos estabelecidos, suportando cargas entre 470 N e 510 N. No grupo dos angulados, nove amostras resistiram a cargas entre 570 N e 890 N. Quanto às amostras fraturadas abaixo do número de ciclos, no grupo pilar reto, nove fraturaram com cargas entre 470 N e 630 N. No grupo pilar angulado, cinco amostras fraturaram com cargas entre 760 N e 890 N. Foi calculado, para cada conjunto implante-pilar, o momento de força (Médias: Grupo reto - 4.335,2 Nmm, Grupo angulado - 3.923,3 Nmm). Conclusão: Os dois tipos de pilares (retos e angulados), em condições in vitro, comportaram-se estatisticamente de forma semelhante, sendo aceita a hipótese nula de que não há diferença de resistência à fratura entre os grupos.

Objective: The aim of this study was to verify the fatigue fracture resistance of the implant-abutment joint, in straight and angled types, subject to cyclic loads similar to chewing. Material and method: It was used 32 implants system (3.75 × 11mm) with Morse taper and 32 abutment, divided in two groups: abutment straight and angled (n = 16) (Neodent, Curitiba, PR, Brazil). The sets were submitted to cyclic testing using servo-hydraulic equipment, fixing the number of cycles at 5 million. It was evaluated the number of cycles, load and moment force of the samples. The Fisher test and ANOVA were applied (p<0,005). Fractured samples were analyzed in the scanning electron microscopy (SEM). Result: Straight abutment, four resisted the cycles number established, supporting loads between 470N and 510N. Angled abutment: nine resisted to loads between 570N and 890N. Regarding the fractured samples below the number of cycles, in the straight abutment, nine fractured with loads between 470N and 630N. In the angled abutment, five fractured with loads ranging from 760N and 890N. The moment of the force was calculated for each joint implant-abutment (Averages: Straight Group - 4335,23Nmm, angled Group - 3923,37Nmm). Conclusion: Two types of abutments (straight and angled), in vitro conditions, statistically behaved similarly, and accepts the null hypothesis that there is no difference in fracture resistance between groups. .

A castor oil-containing dental luting agent: effects of cyclic loading and storage time on flexural strength

Favorable results in the use of castor oil polyurethane (COP) as pulp capping, membrane material, sealer, mouthwash and in bone repair, associated with the fact that Ricinus communis is not derived from petroleum and it is abundant in Brazil, encourage researches in the development of luting agents. Objectives This study compared the flexural strength (FS) of a castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate (COP10) with RelyX ARC (RX) after mechanical cycling (MC) and distilled water storage. Material and Methods Sixty-four specimens (25x2x2 mm) were fabricated and divided into two groups, COP10 and RX (control). Each group was divided into 4 subgroups (n=8) according to the storage time, 24 hours (24 h) or 60 days (60 d), and the performance (MC+FS) or not (only FS) of the mechanical cycling test. The FS (10 kN; 0.5 mm/min) and MC tests (10,000 cycles, 5 Hz, 0.5 mm/min) were carried out using an MTS-810 machine. The data were analyzed using ANOVA (α=0.05). Results The obtained FS (MPa) values were: COP10 24h- 19.04±2.41; COP10 60d- 17.92±3.54; RX 24h- 75.19±3.43; RX 60d- 88.77±6.89. All the RX specimens submitted to MC fractured, while the values for COP10 after MC were as follows: COP10 24h- 17.90±1.87 and COP10 60d- 18.60±1.60. Conclusions A castor oil-containing dental luting agent with a weight percentage of 10% (wt%) of calcium carbonate is resistant to mechanical cycling without decreases in flexural strength. However, mean COP10 showed only about 25% of the RelyX ARC mean flexural strength. .

Influence of the powder/liquid ratio and storage time of conventional glass ionomer cements in diametral tensile strength

Introduction: The Glass Ionomer Cements (GICs) are the most versatile dental material with extensive clinical indication. However, the mechanical strength of conventional GICs (C-GICs) is still unsatisfactory under areas of masticatory forces. Objective: To evaluate the influence of C-GIC proportioning system (powder-liquid and encapsulated) and storage period (1h, 24h and 7 days) on Diametral Tensile Strength (DTS). Material and methods: The two variables were tested in relation to C-GIC (Riva Self Cure, SDI, Australia). The following proportioning systems were tested: powder-liquid by weight (g:g) and powder-liquid by volume (flat scoop: drop) and encapsulated system (pre-dosed capsules). Five C-GIC specimens were prepared, according to ISO specification #9917 for each variable to be studied. The specimens were stored in plastic containers containing distilled water and kept at 37ºC and 100% humidity until the mechanical testing in a universal testing machine (Instron Corp., USA) at a speed 0.5 mm/min. The data were submitted to two-way ANOVA and Tukey test for multiple comparisons (α = 0.05). Results: The proportioning system (P < 0.0001) and storage time (P < 0.0001) were significant predictors of DTS, however with no interaction between these factors. Conclusion: The DTS of C-GICs was influenced by storage time (1 hour < 24 hours < 7 days) and by the proportioning system only for the initial period of its setting reaction.

Strength of 3Y-TZP and feldspathic porcelain subjected to different cooling methods

AIM: To investigate the effect of the cooling rate on flexural strength of monolayer and bilayer porcelain/zirconia (Y-TZP) bars. METHODS: Forty-five specimens were made for each design group: (PM) monolithic specimens of veneer porcelain Vita VM9 (Vita, Germany); (ZM) monolithic specimens of zirconia (ZiHP; ProtMat, Brazil); (PB) bilayer specimens zirconia/porcelain with porcelain on lower surface; and (ZB) bilayer specimens porcelain/zirconia with zirconia on lower surface. Each group was cooled by three different methods after porcelain sintering: slow specimens were cooled inside the turned-off furnace; normal specimens were removed from the furnace and cooled in air at room temperature; and fast specimens were removed from the furnace at 910°C and cooled by compressed air for 10 s. Specimens were polished and flexural strength was measured in water at 37 °C (n=15). Maximum load at fracture was recorded, and equations for simple (monolayer) and composite (bilayer) structures were used to calculate the flexural strength. RESULTS were analyzed using one-way ANOVA (p<0.05) and Tukey test separately for each design. RESULTS: The results of one-way ANOVA were statistically significant only for the PB group. The post-hoc Tukey test showed the highest flexural strength for fast cooling and the lowest for slow cooling; the normal cooling was statistically similar to both. CONCLUSIONS: Cooling methods affected only the flexural strength of bilayer specimens with porcelain on low surface (under tension) when the slow cooling method was used...