RESUMO
The gasification of microalgae Chlorella vulgaris under an atmosphere of argon and water vapor was investigated by thermogravimetric analysis. The data were interpreted by using conventional isoconversional methods and also by the independent parallel reaction (IPR) model, in which the degradation is considered to happen individually to each pseudo-component of biomass (lipid, carbohydrate and protein). The IPR model allows obtaining the kinetic parameters of the degradation reaction of each component. Three main stages were observed during the gasification process and the differential thermogravimetric curve was satisfactorily fitted by the IPR model considering three pseudocomponents. The comparison of the activation energy values obtained by the methods and those found in the literature for other microalgae was satisfactory. Quantification of reaction products was performed using online gas chromatography. The major products detected were H2, CO and CH4, indicating the potential for producing fuel gas and syngas from microalgae.
Assuntos
Biocombustíveis , Chlorella vulgaris/química , Microalgas/química , Biomassa , Cromatografia Gasosa , Cinética , Modelos Químicos , TermogravimetriaRESUMO
En este trabajo se analizó la degradación del poli(etilen tereftalato) variando la temperatura y la concentración de hidróxido de potasio en 1-butanol, manteniendo constante el tamaño y peso de la muestra. El intervalo de temperatura utilizada fue de 110 ºCa 150 ºC y las concentraciones de hidróxido de potasio en 1-butanol en el intervalo 0,4 a 4,4 molar. Para estas condiciones de concentración y temperatura se observó la degradación de un 99% de poli(etilen tereftalato) en un tiempo de una hora. Se obtuvieron dos fases: una orgánica y una sólida. La fase sólida es un polvo soluble en soluciones ácidas. Este producto degradado corresponde probablemente al tereftalato de potasio. A una temperatura de 150 ºC y una concentración de 3,34 M se estudió la cinética de degradación del poli(etilen tereftalato) en función del tiempo. A partir de los resultados y comparando con modelos matemáticos de degradación encontrados en la literatura, se propone que la degradación del poli(etilen tereftalato) sigue un modelo de degradación de power law.
In this work the degradation of poly(ethylene terephthalate) was analyzed by varying the temperature and the concentration of potassium hydroxide in 1-butanol holding constant the size and weight of the sample. The temperature range used was from 110ºC to 150ºC and concentrations of potassium hydroxide in 1-butanol in the range of 0,4 to 4,4 molar, obtaining 99% degradation of poly(ethylene terephthalate) in one hour. The temperature of 150°C and the concentration of 3,34 M were used to study the degradation of poly(ethylene terephthalate) as a function of time. We obtained two phases, an organic phase and solid phase. The solid phase is a soluble in acidic solutions. The solid phase probably corresponds to the of potassium terephthalate. From the results and comparing with models of degradation found in the literature this work suggests that poly(ethylene terephthalate) degradation reaction occurs type power law.
Neste trabalho, se analisou a degradação de poli(tereftalato de etileno) através da variação da temperatura e da concentração de hidróxido de potássio em 1-butanol, segurando o tamanho e o peso constante da amostra. A faixa de temperatura utilizada foi 110° C a 150° C e concentrações de hidróxido de potássio em 1-butanol, intervalo de 0,4-4,4 molar. Para que essas variações são 99% de degradação do poli(teref-talato de etileno) em um tempo de uma hora. Foram obtidas duas fases: uma fase orgânica e uma fase sólida. A fase sólida é um pó solúvel em soluções ácidas. Isso provavelmente corresponde ao produto degradado de tereftalato de potássio. Foram utilizadas uma temperatura de 150 °C e uma concentração de 3,34 M para estudar a cinética de degradação do poli(teref-talato de etileno) como uma função do tempo. A partir dos resultados e comparando com modelos matemáticos de degradação encontrados na literatura, se sugere que a degradação do poli(tereftalato de etileno) é um modelo de degradação do tipo lei de potência.