Restauração classe II com resina composta: avaliação da técnica de Pollack / Restoration class II with composite resin: evaluation of the Pollack technique

Apesar do notável aumento de restaurações posteriores com resinas compostas nos últimos anos, ainda existem dificuldades quanto à técnica restauradora em se tratando de cavidades com envolvimento da face proximal. Considera-se que a intensidade de luz que atinge os incrementos da resina na face cervical do preparo é menor do que a intensidade próxima à superfície, podendo comprometer as propriedades mecânicas e o sucesso da restauração. Objetivo: Investigar a resistência compressiva dos incrementos de resina composta de uso direto na profundidade da caixa proximal de restaurações classe II em diferentes extensões ocluso-cervicais utilizando- se a técnica incremental proposta por Pollack (1988). Métodos: Foram obtidos 40 espécimes (blocos) de resina composta, com 2 mm de dimensão ocluso-cervical, confeccionados a partir de restaurações classe II em três molares inferiores de manequim (Prodens) com dimensões de 4 mm vestíbulo-lingual, 2 mm mésio-distal e profundidades ocluso-cervical de 2 mm (G1 e G2), 4 mm (G3) e 6 mm (G4), formando 4 grupos (n=10). Para G1 (grupo controle) foi utilizada a resina autoativada (Alpha Plast) e demais grupos resina fotoativada (Z100, 3M ESPE), todos com espessura de 2mm. Após, os espécimes foram armazenados em soro fisiológico durante 30 dias e, posteriormente,submetidos ao teste de resistência à compressão em máquina universal de ensaios EMIC DL-2000, composta por um dispositivo metálico de base plana de 15mm, com célula de carga de 490N e velocidade de 0,5mm/min, aplicada sobre a face oclusal dos espécimes até a fratura.Os resultados foram analisados pelo teste ANOVA. Resultados: A média dos valores de resistência à fratura (MPa), foram: 52,86; 48,55; 44,89; 42,67 para G1, G2, G3 e G4, respectivamente. Conclusão: Não houve diferença significativa (p>0,05) na resistência à compressão entre incrementos de resina composta inseridas na base da face proximal de preparos do tipo classe II em diferentes profundidades utilizando-se o protocolo adotado.(AU)

In spite of the remarkable increase of posterior restorations with composite resins in the last years, there are still difficulties regarding the restorative technique when dealing with cavities with involvement of the proximal face. It is considered that the light intensity that reaches the resin increments in the cervical face of the preparation is smaller than the intensity close to the surface, which may compromise the mechanical properties and the success of the restoration. Objective: To investigate the compressive strength of the composite resin increments of direct use in the depth of the proximal box of class II restorations in different occlusalcervical extensions using the incremental technique proposed by Pollack (1988). Methods: 40 composite resin specimens with 2 mm occlusal-cervical dimensions were made from class II restorations in three lower molars of the manikin (Prodens) with 4 mm vestibullary, 2 mm mesio- Distal and occlusal-cervical depths of 2 mm (G1 and G2), 4 mm (G3) and 6 mm (G4), forming 4 groups (n = 10). For G1 (control group) the autoactivated resin (Alpha Plast) and other photoactivated resin groups (Z100, 3M ESPE) were used, all with a thickness of 2mm. Afterwards, the specimens were stored in saline solution for 30 days and then submitted to the compressive strength test in a universal EMIC DL-2000 test machine, consisting of a 15mm flat base metal device with a 490N load cell And velocity of 0.5 mm / min, applied on the occlusal face of the specimens until the fracture.The results were analyzed by the ANOVA test. Results: The average values of fracture resistance (MPa) were: 52.86; 48.55; 44.89; 42.67 for G1, G2, G3 and G4, respectively. Conclusion: There was no significant difference (p> 0.05) in the compressive strength between increments of composite resin inserted at the base of the proximal face of class II type preparations at different depths using the protocol adopted.(AU)

An alternative specimen preparation technique for 3-point bending tests on dual-cured dental resin cements / Técnica alternativa de confecção de espécimes para testes de flexão de 3 pontos em cimentos de resina dentária de dupla ativação

The proper mechanical properties of resin cements are essential to the longevity of indirect restoration, whereas the 3-point bending test is recommended for measuring the flexural strength. The ISO 4049 specification requires light-curing of specimens in three consecutive points; however, this approach cannot be used for dual-cured resin cements. The aim of this study was to investigate the effect of two different specimen preparation techniques on the flexural strength and elastic modulus of experimental dual-cured resin cements immediately or 5 after minutes light curing. Experimental dual-cured resin cements were formulated, and the specimens of these cements were confectioned with the dimension of ISO 4049 specification. Light-activation was performed at one or three points immediately or 5 minutes after the insertion of cement into the matrix (n=7), resulting in four experimental conditions (2 methods × 2 moments of light-activation). The three-point bending test was performed and the values of the flexural strength and elastic modulus were recorded. Data were individually analyzed using 2-way ANOVA followed by the Tukey's post hoc test (P<0.05). Regardless of the points of light-activation, the specimens that were light-cured at 3 points showed the highest values of flexural strength. Only for light-activation at 1 point did the time before the light-activation affect the elastic modulus, whereas delayed light-activation had the highest values. In conclusion, the number of lightcuring points on specimen preparation for the 3-point bending test seems to affect the mechanical properties of dual-cured resin cements.

Cimentos resinosos com propriedades mecânicas adequadas são essenciais para a longevidade de restaurações indiretas, sendo que o ensaio de flexão de 3 pontos é recomendado para mensurar a resistência flexural. A especificação ISO 4049 requer a fotoativação das amostras em três pontos consecutivos, entretanto, esta abordagem não pode ser usada para cimentos resinosos duais. O objetivo deste estudo foi investigar o efeito e duas diferentes técnicas de preparo de amostras na resistência flexural e módulo de elasticidade de cimentos resinosos duais experimentais fotoativados imediatamente ou após 5 minutos. Cimentos resinosos duais experimentais foram formulados, e amostras destes cimentos foram confeccionadas com as dimensões da especificação ISO 4049. A fotoativação foi realizada em um ou três pontos imediatamente ou após 5 minutos da inserção do cimento na matriz (n=7), resultando em quatro condições experimentais (2 métodos × 2 tempos antes da fotoativação). O teste de flexão de três pontos foi realizado e os valores de resistência flexural e módulo de elasticidade mensurados. Os dados foram individualmente analisados por ANOVA de dois fatores seguido pelo teste de Tukey (P<0,05). Em relação aos pontos de fotoativação, as amostras que foram fotoativadas em três pontos mostraram os maiores valores de resistência flexural. Apenas para a fotoativação em um ponto, o tempo antes da fotoativação afetou o módulo de elasticidade, sendo que a fotoativação tardia apresentou maiores valores. Em conclusão, o número de pontos de fotoativação no preparo das amostras para teste de flexão de 3 pontos parece afetar as propriedades mecânicas dos cimentos resinosos.

Efeito de diferentes espessuras, técnicas de aplicação e protocolos de resfriamento na resistência à fratura da cerâmica de cobertura aplicada sobre infraestrutura de y-tzp / Effects of different thicknesses, application techniques, and cooling protocols on fracture resistance of a veneering ceramic applied to Y-TZP infrastructures

O objetivo desta pesquisa foi avaliar, in vitro, a influência do resfriamento, da técnica de aplicação e do efeito da espessura da cerâmica de cobertura na carga de fratura de coroas totalmente cerâmicas com infraestrutura de zircônia. Foram confeccionadas 100 infraestruturas de zircônia (Y-TZP) com 1,0 mm de espessura. 80 infraestruturas foram divididas em 8 grupos (n = 10) para confecção de 80 coroas de acordo com os fatores “técnica de aplicação” (estratificada e prensada), “espessura” (1 mm e 2 mm) e “protocolo de resfriamento” (lento e rápido) da cerâmica de cobertura. Com as outras 20 infraestruturas foram confeccionadas 20 coroas pela técnica CAD/CAM/Rapid Layer e divididas em 2 grupos (n = 10) de acordo com o fator “espessura da cerâmica de cobertura” (1 mm e 2 mm) e foi realizada Análise de Elementos Finitos. Todos os espécimes foram ciclados mecanicamente (200 N; 2 x 106 ciclos; 3,0 Hz; água/ 37 °C). A presença de chipping foi avaliada através de análise em estereomicroscópio após a ciclagem mecânica. Em seguida, todos os espécimes foram submetidos ao teste de resistência à fratura em compressão axial (0,5 mm/minuto; 10 kN). As coroas foram analisadas para determinar a possível origem da falha. Os dados (N) obtidos foram submetidos à análise estatística, com o Teste de Dunnett, teste t-Student, para a técnica CAD/CAM/Rapid Layer, e ANOVA 3-fatores e teste de Tukey para as demais técnicas. A carga de fratura das coroas confeccionadas pela técnica CAD/CAM/Rapid Layer, independente da espessura, foi menor em relação às outras duas técnicas (p < 0,05), mas houve diferença significativa entre as duas espessuras das coroas confeccionadas por esta técnica. Houve influência dos fatores resfriamento (p = 0,0058) e técnica de aplicação (p = 0,0001) na análise das técnicas estratificada e prensada. O resfriamento lento diferiu do resfriamento rápido na técnica prensada de aplicação da cerâmica, porém, esta diferença não foi ..

The aim of this study was to evaluate the in vitro influence of cooling protocols and application techniques and the effect of the thickness of veneering ceramics on the fracture resistance of prosthetic crowns. For this purpose, 100 ‘zirconia partially stabilized by yttrium oxide’ frameworks (1 mm thick) were made. Eighty frameworks were divided into 8 groups (n = 10) according to the application technique (stratified or pressed), thickness (1 or 2 mm), and the cooling protocol (slow or fast) of the veneering ceramic. With the remaining 20 frameworks, 20 crowns were prepared by the CAD/CAM/Rapid Layer technique and were divided into 2 groups (n = 10) according to the veneering ceramic thickness (1 or 2 mm); these were also evaluated by Finite Element Analysis. All specimens were mechanically cycled (200 N, 2 x 106 cycles; 3.0 Hz; water at 37 °C). Chipping presence was evaluated by stereomicroscopy after mechanical cycling. All specimens were tested for compressive strength (0.5 mm/minute; 10 kN). We analyzed crowns to determine the possible beginning of the failures. Data, in N, were statistically analyzed with Dunnett’s, t-test, 3-way ANOVA, and Tukey's tests. The fracture load of the CAD/CAM/Rapid Layer crowns was lower, regardless of ceramic thickness, when compared with the other two application techniques tested (p < 0.05). We observed an influence of the cooling protocol (p = 0.0058) and the application technique (p = 0.0001) in the analysis of stratified and pressed techniques. Slow cooling differed from rapid cooling in the pressed ceramic crowns; however, this difference was not observed for the stratified crowns, regardless of the thickness of the veneering ceramic. Failures in the CAD/CAM/Rapid Layer crowns began predominantly at the interface between the resin cement and veneering ceramic, resulting in delaminations of the veneering ceramic, while the other techniques showed chipping of the veneering ceramic beginning ..

Avaliação de cimentos de ionômero de vidro modificados por resina frente à incorporação de nanopartículas de vitrocerâmica bioativa / Resin modified glass ionomer cements evaluation with additional bioactive glass-ceramics nanoparticles

Os materiais bioativos são materiais sintéticos que possuem superfícies ativas em que os minerais presentes em tecidos duros podem se ligar quimicamente. Há alguns estudos em Odontologia, onde partículas desses materiais foram incorporadas aos Cimentos de Ionômero de Vidro (CIVs) e Cimentos de Ionômero de Vidro modificados por resina (CIVMRs) com o objetivo de se obter bioatividade, e conseqüente remineralização dentária. O presente estudo teve como objetivo avaliar os efeitos da incorporação de nanopartículas de vitrocerâmica bioativa nas propriedades de resistência à compressão e rugosidade de CIVMRs. Fuji II LC e Vitremer foram considerados os grupos controles. Materiais experimentais foram feitos através da incorporação de 2, 5 e 10% em peso de Biosilicato nestes CIVMRs. Seis corpos-de-prova de cada material foram confeccionados para o teste de resistência à compressão, que foi realizado em máquina de ensaios universal (Emic), a uma velocidade de 1,0 mm/min, depois de mantidos por 24 horas em água destilada a 37°C. Para análise da rugosidade, foram confeccionados dois corpos-de-prova de cada material, armazenados em água destilada por sete dias, para terem suas superfícies analisadas por meio de Microscopia de Força Atômica. Os dados da resistência à compressão e rugosidade foram submetidos à análise estatística por meio da Análise de Variância (ANOVA) a dois critérios e para comparações múltiplas foi aplicado o teste de Tukey, com nível de significância de 5%. Apenas os cimentos com 2% de nanopartículas de vitrocerâmica bioativa obtiveram resistência à compressão semelhante ao grupo controle, as demais concentrações contribuíram para a diminuição dessa resistência. A incorporação de 5% de nanopartículas de vitrocerâmica bioativa aumentou a rugosidade superficial dos CIVMRs estudados.

Bioactive materials are synthetic materials that have active surfaces that are capable to chemically bond to dental structures. There are some studies where particles of these materials were incorporated in Glass-ionomer cements (GIC) and Resin-modified glass-ionomer cements (RMGIC) trying to achieve bioactivity and dental remineralization. The aim of this study was to evaluate the effects of the incorporation of bioactive glass-ceramics nanoparticles on the compressive strength and roughness of RMGIC. Fuji II LC and Vitremer were considered the control groups. Experimental materials were made adding 2, 5 and 10% (weight) of Biosilicate into these RMGIC. Six specimens of each material were made to be tested on compressive strength performed with a universal testing machine (Emic) at a crosshead speed of 1.0 mm / min, after they were stored in distilled water for 24 hour at 37°C. To roughness analysis, two specimens of each material were made and stored in distilled water for 7 days and their surfaces were analyzed with a Atomic Force Microscope. Data of compressive strength and roughness were statistically analyzed by ANOVA and Tukey test for multiple comparisons. Only the RMGICs with 2% of bioactive glass-ceramic nanoparticles obtained compressive strength similar to the control RMGICs, the other concentrations decreased their compressive strength values. The incorporation of 5% of bioactive glass-ceramic nanoparticles increased the roughness of the RMGICs.

Compressive strength of glass ionomer cements used for atraumatic restorative treatment / Resistência à compressão de cimentos de ionômero de vidro utilizados no tratamento restaurador atraumático

Purpose: This study evaluated the compressive strength of five glass ionomer cements (Ketac Molar, Fuji IX, Magic Glass, Vidrion R, and Vitro Molar) as a function of storage period (1 hour and 24 hours). Methods: Sixteen specimens of each material were fabricated according to ISO/DP #7489 Specification using a 6x12 mm (diameter and height) matrix. After setting, specimens were stored in distilled water at 37 ºC. Eight specimens per cement were subjected to the compressive strength test in a universal testing machine after 1 hour, and the other eight specimens were tested after 24 hours. Data were analyzed by ANOVA and Tukey's test (α=5%). Results: The compressive strength mean values (kgf) after 1 and 24 hours were: Ketac Molar: 218.75 and 297.88; Fuji IX: 335.75 and 350.88; Magic Glass: 61.50 and 140.13; Vidrion R: 142.38 and 230.88; and Vitro Molar: 183.38 and 297.50. After 1 hour Fuji IX had the highest compressive strength. All materials but Fuji IX showed higher compressive strength in 24 hours than in 1 hour. After 24 hours, no significant differences were found among Fuji IX, Ketac Molar, and Vitro Molar. Magic Glass had the lowest compressive strength in both storage periods. Conclusion: Fuji IX showed the best results after 1 hour. After 24-hour storage, Fuji IX, Ketac Molar, and Vitro Molar had similar performance.

Objetivo: Este estudo avaliou a resistência à compressão de 5 cimentos de ionômero de vidro (Ketac Molar, Fuji IX, Vitro Molar, Magic Glass e Vidrion R), em dois tempos de armazenagem (1 h e 24 h). Metodologia: Foram confeccionados 16 corpos-de-prova (CP) para cada material (n=8), seguindo as especificações da ISO/DP 7489. Os materiais foram manipulados e inseridos numa matriz desmontável (6 mm de diâmetro e 12 mm de altura). Após a presa os CP foram armazenados em água destilada a 37 ºC. Metade dos CP de cada material foi submetida a ensaio de compressão após 1 h e a outra metade foi testada após 24 h. Os resultados foram analisados por ANOVA e teste de Tukey (α=5%). Resultados: Os valores médios de resistência à compressão (kgf) após 1 h e 24 h foram: Ketac Molar: 218,75 e 297,88; Fuji IX:335,75 e 350,88; Magic Glass:61,50 e 140,13; Vidrion R:142,38 e 230,88, e Vitro Molar:183,38 e 297,50. Em 1 h o Fuji IX apresentou a maior resistência à compressão. Com exceção do Fuji IX, todos os ionômeros apresentaram maior resistência em 24h do que em 1 h. Em 24 h não houve diferença entre Fuji IX, Ketac Molar e Vitro Molar. O cimento Magic Glass apresentou os menores valores nos 2 tempos. Conclusão: O cimento Fuji IX apresentou os melhores resultados após 1 h. Após 24 h de armazenamento, Fuji IX, Ketac Molar e Vitro Molar tiveram desempenho similar.

An in-vitro study of the physico-mechanical properties of a new esthetic restorative versus dental amalgam / Estudo in vitro das propriedades mecânicas de uma nova restauração estética versus amálgama dentário

OBJECTIVES: The aim of this study was to determine the compressive strength (CS), diametraltensile strength (DTS), surface hardness (SH), and surface roughness (SR) of a ceramic-reinforcedglass ionomer in comparison to a high-copper dental amalgam. The microstructure was alsoexamined. MATERIAL AND METHODS: A ceramic-reinforced glass ionomer (AmalgomerCR), and a spherical high-copper dental amalgam (GS.80) were used in this study. Specimens werefabricated from the tested materials according to the instructions of each manufacturer. The CS,DTS, SH, and SR were measured after storing the specimens for 1 day and 1 week in water at 37oC. Independent-samples t-test and paired–samples t-test were used to determine which specimengroups were significantly different for each test. One representative specimen of each materialwas prepared and examined for microstructure using scanning electron microscopy (SEM).RESULTS: At 1 day, ceramic-reinforced glass ionomer exhibited significantly-higher CS and DTS,lower SR. At 1 week, it exhibited significantly-higher CS and lower SR. The results of SH were notsignificantly different between the tested materials at both storage periods. CONCLUSION: Thephysico-mechanical properties of the tooth-colored ceramic-reinforced glass ionomer were soclose and sometimes significantly superior to dental amalgam.

OBJETIVOS: O propósito deste estudo foi determinas a resistência à compressão, resistência àtensão diametral, dureza de superfície e aspereza de superfície de um ionômero de vidro reforçadocom cerâmica em comparação com amálgama dentário com alto conteúdo de cobre. Amicroestrutura foi também examinada. MATERIAL E MÉTODO: Um ionômero de vidroreforçado com cerâmica (Amalgomer CR) e um amálgama com limalha esférica com alto conteúdode cobre (GS.80) foram utilizados neste estudo. Os corpos de prova foram produzidos com osmateriais testados, de acordo com instruções dos fabricantes. O CS, DTS, SH e SR foram medidosapós estocagem dos corpos de prova por um dia e uma semana em água a 37 o C. Amostrasforam testadas (t-test e t-test emparceiradas), usadas para determinar qual grupo de corpos deprova foram diferentes significativamente para cada teste. Um espécime representativo de cadamaterial foi preparado para avaliação da microestrutura utilizando microscopia eletrônica (SEM).RESULTADOS: Após um dia, o ionômero de vidro reforçado por cerâmica exibiusignificativamente maiôs CS e DTS e menor SR. Após uma semana, exibiu significativamentemaior CS e menor SR. Os resultados do SH não foram significativamente diferentes entre osmateriais testados em ambos os períodos de estocagem. CONCLUSÃO: As propriedades físicomecânicasdo ionômero de vidro com cor de dente, reforçado com cerâmica, foram semelhantes ealgumas vezes superiores ao amálgama dentário.

Estudo da dureza e da resistência à compressão de resinas compostas indiretas: efeitos da imersão em água destilada / Hardness and compressive strength of indirect composite resin: effects on immersion in distilled water

Nos últimos anos, tem sido introduzidos no mercado odontológico, materiais especificamente destinados à confecção de restaurações estéticas indiretas com o objetivo de suprir lacunas deixadas pela técnica direta em restaurações, como o maior efeito da contração de polimerização na interface adesivo/dente, a dificuldade de obtenção de contornos oclusal e proximal satisfatórios e a impossibilidade de se empregar métodos complementares de polimerização com o objetivo de se obter maior grau de conversão. Entretanto, embora tais materiais apresentem resultados iniciais animadores, há a necessidade de comprovações adicionais, clínicas e laboratoriais, para que possam ser utilizados em larga escala. Motivado pela ação adversa da água em polímeros e compósitos orgânicos, o presente trabalho tem como propósito avaliar o efeito da imersão em água sobre as propriedades mecânicas de dureza e de resistência à compressão dos compósitos indiretos Artglass (Heraeus/Kulzer), Solidex (Shofu) e Targis (Ivoclar), comparando-os à resina composta Z100 (3M) e a uma cerâmica feldspática (Noritake). Os ensaios de dureza foram realizados em aparelho WOLPERT, com diamante Vickers, e cargas de 50 gramas e 200 gramas respectivamente para os compósitos e a cerâmica, aplicadas por 30 segundos antes e após 30, 60, 90 e 180 dias de imersão. Os ensaios de resistência à compressão foram realizados em máquina de ensaios mecânicos "Material Test System-MTS 810", equipada com célula de carga de 100 kN e a velocidade de 0,5 mm/min. antes e após 180 dias de imersão. Os resultados mostraram que: 1- o material cerâmico Noritake (553,6520 VHN) apresentou o maior valor de dureza, seguido dos compósitos na seguinte ordem decrescente: Z100 (87,2140 VHN) > Artglass (37,6172 VHN) > Solidex (31,324 VHN) > Targis (26,5344 VHN); 2- o material cerâmico não apresentou redução de dureza até o período de 180 dias de imersão. Para todos os compósitos houve redução da dureza, com estabilização após 30 dias para os materiais Artglass e Solidex, após 60 dias para Z100, e após 90 dias para o Targis; 3- apenas o material Solidex (276,520 MPa) apresentou resistência à compressão estatisticamente similar a da resina composta Z100 (279,885 MPa). Os demais materiais testados (Artglass- 212,4249 MPa; Noritake- 212,9549 MPa e Targis- 179,0450 MPa) apresentaram-se similares entre si e inferiores a Z100 e Solidex; 4- para todos os materiais os valores iniciais de resistência à compressão sem imersão em água foram estatisticamente semelhantes aos valores obtidos após 180 dias de imersão

New materials have been specifically indicated as esthetic indirect restorative materials to supply clinical disadvantages of direct technique including the effect of the polymerisation shrinkage, difficulty to obtain occlusal and interproximal contour and the impossibility of expose the composite resin to a complementary polymerisation. Although the initial clinical results appear to be satisfactory, further clinical and laboratory investigations are necessary before any general expansion in the indication of these materials. Based on the adverse effect of water in organic polymers and composites, the aim of this study was to evaluate the effect of ageing in water through the hardness and compressive strength tests on the indirect composites- Artglass (Heraeus/Kulzer), Solidex (Shofu) and Targis (Ivoclar) compared with a composite resin Z100 (3M) and a feldspatic ceramic (Noritake). The hardness tests were conducted on WOLPERT equipment using Vickers diamond and a load of 50g or 200g respectively for composites and ceramic, applied for 30 seconds, before and after immersion for 30, 60, 90 and 180 days. The compressive strength experiments were conducted on "Material Test System- MTS 810" (MTS System Corporation, U.S.A.) with 100 kN load cell and crosshead speed of 0,5 mm/min. before and after 180 immersion days. The results demonstrated that: 1- the Noritake ceramic specimens (553,6520 VHN) showed higher hardness values than the composities in the following decrescent order: Z100 (87,2140 VHN) > Artglass (37,6172 VHN) > Solidex (31,324 VHN) > Targis (26,5344 VHN); 2- the ceramic material not showed decrease in hardness after immersion. All composites showed decrease in hardness after immersion, stabilised after 30 days to Solidex and Artglass, 60 days to Z100, and 90 days to Targis; 3- only Solidex (276,520 MPa) exhibited compressive strength statistically similar to composite Z100. The order materials tested (Artglass - 276,520 MPa; Noritake- 212,9549 MPa and Targis- 179,0450 MPa) showed values similar and lowr than Z100 and Solidex; e 4- the immersion in water not affected significantly the values of compressive strength for all tested materials

Avaliação do creep e da resistência à compressão de 3 composições de amálgama enriquecidas por cobre em função do tipo de amalgamador / Evaluation of creep and of the resistance to the compression of 3 enriched compositions of amalgam for copper in function of the type of amalgamator

A finalidade do presente trabalho foi quantificar a resistência mecânica à compressão após 1 hora e 24 horas e medir a porcentagem do "creep" de amálgamas submetidos à trituração mecânica em diferentes aparelhos. Foram selecionadas as ligas Dispersalloy, Tytin e DFL Alloy. Os amalgadores foram o Deltronix, Silamat e Ultramat. 2. Os resultados mostraram que o Tytin alcançou os maiores valores, seguido pelo DFL Alloy e Dispersalloy. Com relação aos amalgamadores, o aparelho Deltronix promoveu baixos valores de resistência de 1 hora, sendo que os materiais DFL Alloy e Dispersalloy não alcançaram o valor mínimo estipulado pela ADA. Já o equipamento Ultramat 2 gerou as maiores médias, ficando o Silamat numa posição intermediária. Em relação ao "creep", todas as médias obtidas ficaram bem abaixo do valor máximo permitido pela ADA. Tanto os amálgamas quanto os amalgamadores não mostraram significância estatística

The objective of the present study was to evaluate quantitatively the mechanical resistance to compression after a 1-hour period and a 24-hour period and measure the percentage of creep of dental alloys submitted to mechanical trituration in different appliances. The Dispersal, Tytin and DFL alloys were chosen. The amalgamators chosen were Deltronix, Silamat and Ultramat 2. The results indicate that Tytin reached the best values, followed by DFL Alloy and Dispersalloy. As for the amalgamators, the Deltronix promoted low resistance values after the 1-hour period and the DFL Alloy and Dispersalloy did not reach the minimum value set by the ADA. The Ultramat 2 generated the best results, and the Silamat achieved an intermediate result. In relation to the creep, all values obtained from this study were set below the maximum value allowed by ADA. Both the alloys and amalgamators showed no statistical significance