BACKGROUND: Evaluation of adhesion of Streptococcus mutans on recycled orthodontic brackets is significant, as Streptococcus mutans is the main causative factor in enamel demineralization and many clinicians, in their practice, resort to reconditioning of brackets, as it is cost-effective. Thus, this study aimed to evaluate and compare the adhesion of Streptococcus mutans on new brackets of three different companies (Group I, Group II, and Group III) and brackets recycled by three different recycling methods (RC I: flame heating followed by acid bath; RC II: flame heating followed by ultrasonic cleaning and electropolishing; RC III: flame heating followed by sandblasting and electropolishing). Materials and methods: A total of 10 brackets from each group were incubated with 108 colony-forming units (CFUs) of Streptococcus mutans in trypticase soy broth overnight. The brackets were then washed with phosphate-buffered saline and treated with 0.25% trypsin for 20 minutes followed by vertexing the solution to remove the adhered bacteria and then the solution was plated on the blood agar and incubated overnight. The total viable count of bacteria was quantified. RESULTS: Comparing all the three groups and recycling methods, Group II brackets showed significantly more adhesion, Group I brackets showed lesser adhesion, and Group III brackets showed intermediate adhesion. When comparing recycling methods, all the three methods of recycling with all the three groups showed more bacterial adhesion than the control brackets, which was statistically insignificant (P > 0.05). CONCLUSION: Recycled brackets showed more bacterial adhesion and electropolishing resulted in reduced bacterial adhesion.
RESUMO
Objective:To evaluate the surface free energy and Streptococcus mutans(S.mutans)adhesion on the surfaces of Co-Cr al-loy specimens fabricated by selective laser sintering(SLS)and casting method(SG and W280)respectively.Methods:The specimens of three groups were polished by SiC sandpaper.Surface morphology test,surface contact angle test and surface adhesion test of S.mu-tans were performed.Results:With the same surface roughness value,the surface contact angle of group SLS,W280 and SG was 66.200 ±3.112,74.212 ±3.206 and 67.238 ±2.047(P >0.05),the surface adhesion of S.mutans colone was 8.88 ±2.90,9.25 ± 2.05 and 8.50 ±1.85(P >0.05),respectively.Conclusion:The cobalt chromium alloy fabricated by SLS and casting method have similar surface performance.