RESUMO
Abstract The aim of this study was to evaluate the influence of the coefficient of thermal expansion (CTE or α) and glass transition temperature (Tg) of three veneering ceramics used with zirconia frameworks of full-arch fixed prostheses. The generation of residual stresses and linear contraction after the simulation of the cooling process and mechanical loading were measured. The analysis was based on the finite element method in three-dimensional model of a maxillary full-arch fixed prosthesis with zirconia framework (e.max ZirCAD) and veneer by felsdpathic ceramics (GEC - IPS e.max Ceram, GVM - Vita VM9 and GLC - Lava Ceram). The linear contraction simulation was performed by cooling the structures from the Tg of each veneer ceramic at room temperature (25°C). A loading of 100 N on the occlusal region of the first molar was performed. The magnitude of the maximum principal stress (smax) and linear contraction were evaluated. The levels of CTE mismatch between veneering ceramics and framework showed no relevant influence on smax and linear contraction. The Tg values of the veneer ceramic showed to be directly proportional to amount of smax and linear contraction. The GEC presented the highest values of smax and linear contraction. The GVM and GLC did not present significant differences between them. In conclusion, GVM was similar to GLC, while GEC presented differences in relation to other veneer ceramics in terms of residual stress and linear contraction.
Resumo O objetivo neste estudo foi avaliar a influência do coeficiente de expansão térmica (CET) e da temperatura de transição vítrea (Tg) de três cerâmicas feldspáticas utilizadas para o recobrimento da infraestrutura de zircônia em prótese total fixa. A tensão residual e contração linear após a simulação do processo de esfriamento e carga oclusal foram mensuradas. A análise foi efetuada pelo método por elementos finitos num modelo tridimensional de uma prótese total maxilar com infraestrutura em zircônia (e.max ZirCAD) recoberta por três cerâmicas felsdpáticas (GEC - IPS e.max Ceram, GVM - Vita VM9 ou GLC - Lava Ceram). A simulação da contração linear foi realizada pelo esfriamento da estrutura a partir da Tg de cada cerâmica de cobertura até a temperatura ambiente (25 °C). Em seguida, um carregamento de 100 N foi realizado na região oclusal de primeiro molar. A magnitude da tensão máxima principal (smax) e contração linear foram avaliadas. Os níveis de diferença de CTE entre cerâmica de cobertura e infraestrutura não apresentaram influência significante na smax e na contração linear. Os valores da Tg da cerâmica de cobertura foram diretamente proporcionais à quantidade de smax e contração linear. O grupo GEC apresentou os maiores valores de smax e contração linear, enquanto os grupos GVM e GLC com menores valores não apresentaram diferenças significantes entre si. Em conclusão, o grupo GVM foi similar ao GLC, enquanto o grupo GEC apresentou diferenças em relação a outras cerâmicas de cobertura quanto à tensão residual e contração linear.
Assuntos
Zircônio/química , Cerâmica , Análise do Estresse Dentário , Facetas Dentárias , Teste de Materiais , Análise de Elementos FinitosRESUMO
OBJECTIVES: Recently all-ceramic restorative systems have been introduced that use CAD/CAM technology to fabricate both the Y-TZP core and veneer-ceramic layers. The aim was to identify whether the CAD/CAM approach resulted in more favourable stressing patterns in the veneer-ceramic when compared with a conventionally sintered Y-TZP core/veneer-ceramic. METHODS: Nominally identical Vita VM9 veneer-ceramic disc-shaped specimens (0.7mm thickness, 12mm diameter) were fabricated. 20 specimens received a surface coating of resin-cement (Panavia 21); 20 specimens were bonded with the resin-cement to fully sintered Y-TZP (YZ Vita Inceram Vita) discs (0.27mm thickness, 12mm diameter). A final series of 20 Y-TZP core/veneer-ceramic specimens were manufactured using a conventional sintering route. Biaxial flexure strength was determined in a ball-on-ring configuration and stress at the fracture origin calculated using multilayer closed-form analytical solutions. Fractography was undertaken using scanning electron microscopy. The experimental test was simulated using Finite Element Analysis. Group mean BFS were compared using a one-way ANOVA and post hoc Tukey tests at a 95% significance level. RESULTS: Resin cement application resulted in significant strengthening of the veneer-ceramic and further significant strengthening of the veneer-ceramic (p<0.01) occurred following bonding to the Y-TZP core. The BFS calculated at the failure origin for conventionally sintered specimens was significantly reduced when compared with the adhesively bonded Y-TZP/veneer-ceramic. CONCLUSIONS: Under the test conditions employed adhesive cementation between CAD/CAM produced Y-TZP/veneer-ceramic layers appears to offer the potential to induce more favourable stress states within the veneer-ceramic when compared with conventional sintered manufacturing routes. CLINICAL SIGNIFICANCE: The current investigation suggests that the stressing patterns that arise in all-ceramic restorations fabricated using CAD/CAM for both the core and veneer-ceramic layers differ from those that occur in conventionally sintered bilayer restorations. Further work is required to ascertain whether such differences will translate into improved clinical outcomes.