RESUMO
Objective: to evaluate the marginal fit and microleakage of monolithic zirconia crowns cemented by bio-active cements (Ceramir) compared to that cemented with glass ionomer cement, and to evaluate the effect of thermocycling on marginal fit. Material and Methods: Twenty sound human molar teeth were prepared to receive monolithic zirconia crowns. Teeth were divided randomly into two equal groups according to the type of luting cement: Group I (glass ionomer cement) and group II (Ceramir cement). After cementation, the vertical marginal gap was assessed using stereomicroscope before and after thermocycling. Twenty equidistant measurement points were taken for each crown. Leakage assessment was carried out using Fuchsin dye penetration followed by digital photography under a stereomicroscope. Data were analyzed by Mann-Whitney U test to compare between the two luting cements. Wilcoxon signed-rank test was used to evaluate the effect of thermocycling on the marginal fit (P ≤ 0.05). Results: Whether before or after thermocycling, the results showed no significant difference between the marginal gap values of the two tested groups. For both groups, there was a significant increase in marginal gap values after thermocycling. Also, there was no significant difference between leakage scores of the two tested groups. Conclusion: Similarity in the physical properties and chemical composition of the two cements resulted in a nonsignificant effect on the vertical marginal fit and the extent of microleakage of translucent zirconia crowns. Thermocycling had a negative impact on the vertical marginal gap of the two tested luting agents. (AU)
Objetivo: avaliar a adapatação marginal e a microinfiltração de coroas monolíticas de zircônia cimentadas com cimentos bioativos (Ceramir) em comparação com o cimento de ionômero de vidro e avaliar o efeito da termociclagem na adaptação marginal. Material e Métodos: Vinte molares humanos sadios foram preparados para receber coroas monolíticas de zircônia. Os dentes foram divididos aleatoriamente em dois grupos iguais, de acordo com o tipo de cimento: Grupo I (cimento de ionômero de vidro) e grupo II (cimento Ceramir). Após a cimentação, a adaptação marginal vertical foi avaliada com estereomicroscópio antes e após a termociclagem. Vinte pontos de medição equidistantes foram obtidos para cada coroa. A avaliação da infiltração foi realizada utilizando a penetração do corante de fucsina, seguida de fotografia digital sob estereomicroscópio. Os dados foram analisados pelo teste de Mann-Whitney para comparação entre os dois cimentos. O teste de Wilcoxon foi usado para avaliar o efeito da termociclagem na adaptação marginal (P ≤ 0,05). Resultados: Antes ou depois da termociclagem, os resultados não mostraram diferença significativa entre os valores de fenda marginal dos dois grupos testados. Para ambos os grupos, houve um aumento significativo nos valores de fenda marginal após a termociclagem. Além disso, não houve diferença significativa entre os escores de infiltração dos dois grupos testados. Conclusão: A similaridade nas propriedades físicas e na composição química dos dois cimentos resultou em um efeito não significativo na adaptação marginal vertical e na extensão da microinfiltração de coroas translúcidas de zircônia. A termociclagem teve um impacto negativo na fenda marginal vertical dos dois agentes de cimentação testados. (AU)
Assuntos
Humanos , Zircônio , Adaptação Marginal Dentária , Coroas , Cimentos Dentários , Infiltração Dentária , Temperatura , Técnicas In Vitro , Distribuição Aleatória , Cimentos de Ionômeros de Vidro , Dente MolarRESUMO
Objective: the purpose of the study was to evaluate the micro-shear bond strength of different cements to translucent zirconia before and after thermocycling aging. Material and methods: Twelve translucent zirconia ceramic discs were used in the study. Specimens were sandblasted using 50 µm aluminum oxide (Al2 O3 ) particles. The specimens were divided into three groups (n = 4) according to the cement type: Panavia resin cement (control group), resin modified glass ionomer (RMGI), and Activa bioactive cement. Each group was further sub-divided into two equal subgroups (n = 2) according to whether the specimens were subjected to thermocycling or not. Thermocycling was performed in distilled water at 5000 cycles between 5 o C - 55 o C. The micro-shear bond strength test (µSBS) was measured using universal testing machine. Kruskal-Wallis test was used to compare between the three cements. Dunn's test was used for pair-wise comparisons when Kruskal-Wallis test is significant. Mann-Whitney U test was used to compare between micro-shear bond strength before and after thermocycling P ≤ 0.05. Results: In non-aged subgroups, there was no significant difference between Panavia and Activa; both showed significantly the highest mean µSBS values (22.9 MPa, 31.3 MPa respectively). While, RMGI showed the lowest µSBS values (4.7 MPa). In thermocycled subgroups, Panavia showed significantly the highest mean µSBS values (32.2 MPa). There was no significant difference between RMGI and Activa; both showed the lowest significant mean µSBS values (3.2 MPa and 8.7 MPa respectively). Conclusions: RMGI and Activa couldn't be considered long-term reliable materials for cementing zirconia. However, Panavia provided the most durable bond to zirconia. (AU)
Objetivo: O objetivo do estudo foi avaliar a resistência de união ao microcisalhamento de diferentes cimentos à zircônia translúcida antes e após o envelhecimento da termociclagem. Material e métodos: Doze discos de zircônia translúcidos foram utilizados no estudo. As amostras foram jateadas com partículas de óxido de alumínio de 50 µm (Al2 O3 ). Os espécimes foram divididos em três grupos (n = 4), de acordo com o tipo de cimento: cimento resinado Panavia (grupo controle), ionômero de vidro modificado por resina (RMGI) e cimento bioativo Activa. Cada grupo foi subdividido em dois subgrupos iguais (n = 2), dependendo se as amostras foram submetidas ou não a termociclagem. A termociclagem foi realizada em água destilada a 5000 ciclos entre 5°C - 55°C. O teste de resistência de união por microcisalhamento (µSBS) foi medido usando uma máquina de teste universal. O teste de Kruskal-Wallis foi utilizado para comparar os três cimentos. O teste de Dunn foi usado para comparações entre pares quando o teste de Kruskal-Wallis foi significativo. O teste U de Mann-Whitney foi utilizado para comparar a resistência de união ao microcisalhamento antes e após a termociclagem (P ≤ 0,05). Resultados: Nos subgrupos sem envelhecimento por termociclagem, não houve diferença significativa entre Panavia e Activa; ambos mostraram significativamente os maiores valores médios de µSBS (22,9 MPa, 31,3 MPa, respectivamente). Por sua vez, o RMGI apresentou os menores valores de µSBS (4,7 MPa). Nos subgrupos termociclados, Panavia mostrou significativamente os maiores valores médios de µSBS (32,2 MPa). Não houve diferença significativa entre RMGI e Activa; ambos apresentaram os menores valores médios significativos de µSBS (3,2 MPa e 8,7 MPa, respectivamente). Conclusões: RMGI e Activa não puderam ser considerados materiais confiáveis para cimentação à zircônia a longo prazo. No entanto, a Panavia apresentou a ligação mais durável à zircônia. (AU)
Assuntos
Cimentos de Resina , Cimentos de Ionômeros de VidroRESUMO
Objective: The aim of this study was to evaluate the effect of decontamination methods on shear bond strength of resin cement to translucent monolithic zirconia. Material and Methods: Eighty 4-mol yttria-stabilized tetragonal zirconia polycrystal specimens were fabricated. All specimens were subjected to saliva contamination and divided into four groups (n = 20) according to the decontamination methods: 70% isopropanol (AL); zirclean (ZC); 5.25% sodium hypochlorite (NaOCL); and no cleaning (NC). All specimens were bonded by using self-adhesive resin cement. Half of the specimens in each group (n = 10) were subjected to aging. All specimens were subjected to shear bond strength test in a universal testing machine. Failure modes were evaluated by using a scanning electron microscope (SEM). The data obtained were statistically analyzed by using one-way ANOVA followed by the HSD Tukey test (p < 0.05). Results: ANOVA test revealed a significant difference among the different decontamination methods (p < 0.05). No significant differences were found among NaOCL, ZC, and AL groups as revealed by the HSD Tukey test (p > 0.05). The effect of aging was significantly different in all groups (p < 0.05); whereas, no significant difference was found in group ZC (p > 0.05). The (SEM) analysis showed mixed failures in all groups, except in group NC where only adhesive failure was observed. Conclusion: Saliva contamination during clinical evaluation significantly decreases the shear bond strength between self-adhesive resin cement and translucent monolithic zirconia. The cleaning methods have an impact on improving the bond strength between resin cement and translucent monolithic zirconia (AU)
Objetivo: O objetivo deste estudo foi avaliar o efeito dos métodos de descontaminação na resistência ao cisalhamento entre cimento resinoso e zircônia monolítica translúcida. Material e métodos: Foram fabricados oitenta espécimes policristalinos de zircônia tetragonal estabilizada com ítria a 4 mol. Todas as amostras foram submetidas à contaminação salivar e divididas em quatro grupos (n = 20) de acordo com os métodos de descontaminação: isopropanol a 70% (AL); zircleano (ZC); Hipoclorito de sódio a 5,25% (NaOCL); e sem limpeza (NC). Todas as amostras foram cimentadas utilizando um cimento resinoso autoadesivo. Metade das amostras de cada grupo(n = 10) foram submetidas ao envelhecimento. Todas as amostras foram submetidas ao teste de resistência ao cisalhamento em uma máquina de teste universal. Os módulos de falha foram avaliados usando um microscópio eletrônico de varredura (MEV). Os dados obtidos foram analisados estatisticamente utilizando ANOVA de uma via, seguida pelo teste de HSD Tukey (p < 0,05). Resultados: O teste ANOVA revelou diferença significativa entre os diferentes métodos de descontaminação (p < 0,05). Não foram encontradas diferenças significativas entre os grupos NaOCl, ZC e AL, conforme revelado pelo teste HSD Tukey (p> 0,05). O efeito do envelhecimento foi significativamente diferente em todos os grupos (p < 0,05); enquanto nenhuma diferença significativa foi encontrada no grupo ZC (p > 0,05). A análise (SEM) mostrou falhas mistas em todos os grupos, exceto no grupo NC, onde apenas foi observada falha adesiva. Conclusão: A contaminação por saliva durante a avaliação clínica diminui significativamente a resistência ao cisalhamento entre o cimento resinoso autoadesivo e a zircônia monolítica translúcida. Os métodos de limpeza têm um impacto na melhoria da resistência da união entre o cimento resinoso e a zircônia monolítica translúcida. (AU)
Assuntos
Hipoclorito de Sódio , Descontaminação , Cimentos de Resina , 2-Propanol , Resistência ao CisalhamentoRESUMO
O presente estudo tem como objetivo avaliar a influência do modo de sinterização nas propriedades superficiais e no limite de fadiga de uma nova cerâmica de zircônia (Y-TZP). 50 discos de cerâmica à base de óxido de zircônio (IPS e.max ZirCAD LT) para CAD/CAM (Computer Aided Design/Computer Aided Manufacture) foram confeccionados de acordo com a norma ISO 6872:2015. Os discos foram divididos em dois grupos, de acordo com o modo de sinterização do material: MP (modo padrão) e MR (modo rápido). Os discos do grupo MP foram sinterizados conforme o programa padrão (n=25), enquanto os discos do grupo MR foram sinterizados utilizando o programa rápido (n=25). Por se tratar de um novo material, previamente ao ensaio de fadiga, cinco amostras de cada grupo foram confeccionadas de forma semelhante e utilizadas para as seguintes avaliações: rugosidade superficial, perfilometria, microscopia eletrônica de varredura (MEV), sistema de energia dispersiva (EDS), difração de raios-X e mensuração da cor e translucidez. Cinco discos de cada grupo foram submetidos ao teste monotônico de flexão biaxial com célula carga de 50 kgf e velocidade de 0,5 mm/min até o momento da fratura para determinação da carga a ser utilizada no teste de fadiga staircase. Setenta por cento do valor médio da carga máxima (MPa) registrada na fratura de cada espécime foi utilizado como carga inicial para o teste de fadiga. A carga foi aplicada sobre o espécime por 20.000 ciclos, a uma frequência de 20 Hz. As análises fractográficas dos espécimes foi realizada e amostras representativas foram submetidas à MEV para avaliação da origem da fratura. Comprovada a normalidade dos dados, os resultados de rugosidade superficial, limite de fadiga e leituras de cor foram avaliados através de ANOVA 1 fator seguido pelo teste de Tukey, ambos com significância de 5%. O limite médio da fadiga em flexão biaxial foi calculado de acordo com o método de Collins (1993). As imagens de MEV e perfilometria foram avaliadas qualitativamente. ANOVA revelou não haver diferença para Ra, Rz e RSm (p>0.05) entre MP (0,13±0,02; 1.21±0,26; 24,91±2,19) e MR (0,14±0,03; 1,32±0,25; 24,68±2,26). As microscopias confirmaram similaridade na morfologia superficial dos grupos. DRX apresentou semelhantes fases. A resistência à fadiga foi semelhante entre MP (512 MPa; 464.39 560.06) e MR (542 MPa; 472.49 - 611.51) e a fractografia apresentou a origem das falhas no lado de tração, independentemente do modo de sinterização dos discos. Os valores de coordenadas L* (p = 0,000) e a* (p = 0,001) foram superiores para o grupo MR enquanto a coordenada b* (p = 0,977) foi semelhante entre os modos de sinterização. E, um valor de ΔE = 2 foi observado. Já a translucidez foi semelhante entre os grupos (p = 0,788) (AU)
The present study aims to evaluate the influence of sintering mode on surface properties and fatigue limit of a new zirconia ceramic (Y-TZP). 50 zirconium oxide (IPS e.max ZirCAD LT) ceramic discs for CAD/CAM (Computer Aided Design/Computer Aided Manufacture) were prepared based on ISO 6872:2015. The discs were divided into two groups according to the material sintering mode: MP (standard mode) and MR (fast mode). MP group discs were sintered according to the standard program (n = 25), while MR group discs were sintered using the fast program (n = 25). As it is a new material, before the fatigue test, five samples from each group were similarly made and used for the following evaluations: surface roughness, profilometry, scanning electron microscopy (SEM), dispersive energy system (EDS), X-ray diffraction and color and translucency measurements. Five discs from each group were submitted to the monotonic biaxial flexion test with a load cell of 50 kgf and 0.5 mm/min speed until the fracture moment to determine the load to be used in the staircase fatigue test. Seventy percent of the mean maximum strength (MPa) recorded during fracture of each specimen was used as the initial load for the fatigue test. The load was applied to the specimen for 20,000 cycles at a frequency of 20 Hz. Fractographic analyzes of the specimens were performed and representative samples were submitted to SEM to assess the origin of the fracture. Once the data normality was verified, the results of surface roughness, fatigue limit and color readings were evaluated by one-way ANOVA followed by Tukey 's test, both with 5% significance. The mean limit of biaxial flexion fatigue was calculated according to the Collins method (1993). SEM and profilometry images were qualitatively evaluated. ANOVA revealed no difference for Ra, Rz and RSm (p> 0.05) between MP (0.13 ± 0.02; 1.21 ± 0.26; 24.91 ± 2.19) and MR (0.14 ± 0, 03, 1.32 ± 0.25; 24.68 ± 2.26). The microscopies confirmed similarity in the superficial morphology of the groups. XRD presented similar phases. Fatigue strength was similar among MP (512 MPa; 464.39 - 560.06) and MR (542 MPa; 472.49 - 611.51) and fractography showed the failure origin on the tensile side, regardless of the sintering mode of the discs. The L * (p = 0.000) and a * (p = 0.001) coordinate values were higher for the MR group while the b * coordinate (p = 0.977) was similar within the sintering modes and a value of ΔE = 2 was observed. Translucency was similar between groups (p = 0.788) (AU)