Corrosion Activity of Stainless Steel SS430 and Carbon Steel B450C in a Sodium Silicate Modified Limestone-Portland Cement Extract.

Stainless steel SS430 and carbon steel B450C were exposed for 30 days to the aqueous extract of sodium silicate-modified limestone-Portland cement as an alternative for the partial replacement of the Portland cement clinker. The initial pH of 12.60 was lowered and maintained at an average of 9.60, associated with air CO2 dissolution and acidification. As a result, the carbon steel lost its passive state, and the corrosion potential (OCP) reached a negative value of up to 296 mV, forming the corrosion layer of FeO, and FeOOH. In the meaning time, on the stainless steel SS430 surface, a passive layer of Cr2O3 grew in the presence of FeO, Fe2O3 and Cr(OH)3 corrosion products; thus, the OCP shifted to more positive values of +150 mV. It is suggested that a self-repassivation process took place on the SS430 surface due to the accumulation of alkaline sulfates on the interface. Because of the chloride attack, SS430 presented isolated pits, while on B450C, their area was extended. The quantitative analysis of EIS Nyquist and Bode diagrams revealed that the Rp of the corrosion process for SS430 was 2500 kΩcm2, ≈32 times lower in magnitude than on B450C, for which the passive layer tended to disappear, while that on SS430 was ≈0.82 nm.

Materials for Production of High and Ultra-High Performance Concrete: Review and Perspective of Possible Novel Materials.

This review article proposes the identification and basic concepts of materials that might be used for the production of high-performance concrete (HPC) and ultra-high-performance concrete (UHPC). Although other reviews have addressed this topic, the present work differs by presenting relevant aspects on possible materials applied in the production of HPC and UHPC. The main innovation of this review article is to identify the perspectives for new materials that can be considered in the production of novel special concretes. After consulting different bibliographic databases, some information related to ordinary Portland cement (OPC), mineral additions, aggregates, and chemical additives used for the production of HPC and UHPC were highlighted. Relevant information on the application of synthetic and natural fibers is also highlighted in association with a cement matrix of HPC and UHPC, forming composites with properties superior to conventional concrete used in civil construction. The article also presents some relevant characteristics for the application of HPC and UHPC produced with alkali-activated cement, an alternative binder to OPC produced through the reaction between two essential components: precursors and activators. Some information about the main types of precursors, subdivided into materials rich in aluminosilicates and rich in calcium, were also highlighted. Finally, suggestions for future work related to the application of HPC and UHPC are highlighted, guiding future research on this topic.