RESUMO
Supplementary cementitious materials are considered a viable and affordable way to reduce CO2 emissions from the cement industry's perspective since they can partially or nearly entirely replace ordinary Portland cement (OPC). This study compared the impact of adding spent coffee grounds (SCGs), fly ash (FA), and volcanic ash (VA) to two types of cement: OPC and calcium sulfoaluminate cement (CSA). Cement samples were characterized using compressive strength measurements (up to 210 days of curing), scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction (XRD), attenuated total reflection infrared spectroscopy, and hydration temperature measurements. In all the studied systems, the presence of SCGs reduced compressive strength and delayed the hydration process. CSA composite cement containing 3.5% SCGs, 30% FA, and 30% VA showed compressive strength values of 20.4 MPa and 20.3 MPa, respectively, meeting the minimum requirement for non-structural applications. Additionally, the results indicate a formation of cementitious gel, calcium silicate hydrate (C-S-H) in the OPC-based composite cements, and calcium alumino-silicate hydrate (C-A-S-H) as well as ettringite in the CSA-based composite cements.
RESUMO
OBJECTIVE: To assess light irradiance (LI) delivered by two light-curing units (LCU's) and to measure the degree of conversion (DC) of three composite cements, when cured through different thicknesses of two novel CAD-CAM block materials. METHODS: 100-µm-thick films of a dual-curable composite cement (G-CEM LinkAce, GC), a light-curable flowable resin-based composite (RBC) (G-ænial Universal Flo, GC) and a micro-hybrid RBC (G-ænial Posterior, GC) were investigated as luting agents. Two 'polymer-ceramic' CAD-CAM blocks (Cerasmart, GC; Enamic, Vita Zahnfabrik) were sectioned in slabs with different thicknesses (1, 3 and 5mm). LI at the bottom of the specimens was measured using a calibrated spectrometer, while being light-cured through the CAD-CAM block slabs for 40s with a low- (±500mW/cm2) or high- (±1,600mW/cm2) irradiance LCU (n=5). After light-curing, micro-Raman spectra of the composite films were acquired to determine DC at 5min, 10min, 1h and 24h. LI data were statistically analyzed by Kruskal-Wallis followed by post-hoc comparisons, while a linear mixed-effect model was applied for the DC analysis. In addition, the CAD-CAM blocks ultrastructure was characterized upon argon-ion slicing using scanning transmission electron microscopy (STEM). Finally, light transmission (LT) through each CAD-CAM block material was assessed using a spectrophotometer. RESULTS: Curing-light attenuation and DC were significantly influenced by thickness and type of the overlying material. LCU only had a significant effect on DC of the micro-hybrid RBC. DC significantly increased over time for all composite cements. CAD-CAM block structural analysis revealed a relatively small and homogenous filler configuration (mean filler size of 0.2-0.5µm) for Cerasmart, while Enamic contained ceramic grains varying in shape and size (1-10µm), which were interconnected by the polymer-based network. LT was much higher at a wavelength range of 300-800nm for Cerasmart than for Enamic. SIGNIFICANCE: Light-curable composite cements can be cured through a restoration up to 2.7-mm thickness, depending on the kind of CAD-CAM material. A high-irradiance LCU only has a limited effect on the maximum thickness of the polymer-ceramic CAD-CAM material that can be cured through.