Contemporary Concepts of Adhesive Cementation of Glass-Fiber Posts: A Narrative Review.

(1) Background: Cementation of glass fiber posts to root canals has been associated with various failures, especially debonding. This narrative review aims to present the contemporary concepts concerning the adhesive cementation of glass fiber post and to discuss the optimal management of these factors. (2) Methods: Electronic search was performed in MEDLINE/Pub Med and Google Scholar using selected keywords examining the parameters post length, surface treatment of glass fiber posts, post space preparation and dentin pretreatment, resin cement selection, adhesive systems and hybrid layer formation, and clinical techniques. (3) Results: The search led to the selection of 44 articles. Epoxy resin-based endodontic sealers are recommended and the use of temporary cement in the root canal should be avoided. The minimum length of a glass fiber post adhesively cemented to a root canal is 5 mm. Irrigating the root canals with chlorhexidine, MTAD, or EDTA (alone or in combination with NaOCl) after post space preparation seems to enhance the bond strength. Silane application on the surface of the post seems to be beneficial. Concerning resin cements and adhesive systems, the results were rather inconclusive. Finally, resin cement should be applied inside the root canal with an elongation tip and photoactivation should be delayed. (4) Conclusions: Contemporary concepts of adhesive cementation of glass fiber posts can indeed improve the bond between glass fiber posts, resin cement, and root canal dentin, however, evidence coming from long-term randomized prospective clinical trials is needed in order to obtain safer conclusions.

Ultrasonic activation of adhesive systems increases bond strength and intratubular penetration of resin cement in root dentin subjected to radiation therapy.

OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.

Three Self-Adhesive Resin Cements and Their Influence on the Marginal Adaptation of Zirconia-Reinforced Lithium Silicate Single Crowns: An In Vitro Scanning Electron Microscope Evaluation.

Background: In everyday dentistry, monolithic single crowns can be cemented with self-adhesive resin cements. The aim of this in vitro study was to evaluate how the marginal adaptation of full monolithic zirconia-reinforced lithium silicate (ZLS) single crowns is influenced by three different self-adhesive resin cements. Methods: Forty-five typodont teeth fully prepared for full monolithic crowns were divided into three groups (fifteen each) for the use of three different self-adhesive resin cements. A fourth control group (Temp-bond) was created by taking five teeth from each group before cementation with self-adhesive resin cements. All forty-five abutments were scanned using a Primescan intra-oral scanner (IOS), followed by computer-aided design (CAD) and computer-aided manufacturing (CAM) of zirconia-reinforced lithium silicate (ZLS) full crowns using a four-axis machine. Initially, the crowns of the control group were fixed to the abutments using Temp-bond, and the marginal gap was evaluated using a scanning electron microscope (SEM). After removing the control group crowns from the abutments, fifteen crowns in each group were cemented using a different self-adhesive resin cement and observed under SEM for evaluation of the marginal gap. A Kolmogorov-Smirnov test was performed, indicating no normal distribution (p < 0.05), followed by Mann-Whitney tests (α = 0.05). Results: The total mean marginal gap of the temp-bond control group was significantly lower compared to all three groups of self-adhesive resin cement (p < 0.0005). The total mean marginal gap of the G-cem ONE group was significantly lower compared to the TheraCem group (p < 0.026) and RelyX U200 group (p < 0.008). The total mean marginal gap of the TheraCem group was significantly higher than the G-cem ONE group (p < 0.026) but showed no significant difference with the RelyX U200 group (p > 0.110). Conclusions: All four groups showed a clinically acceptable marginal gap (<120 microns). Although all three groups of self-adhesive resin cement showed a significant increase in the marginal gap compared to the temp-bond control group, they were within the limits of clinical acceptability. Regarding the marginal gap, in everyday dentistry, it is acceptable to use all three self-adhesive resin cements, although the G-cem ONE group exhibited the lowest marginal gap for ZLS single crowns.

Fitting of Different Intraradicular Composite Posts to Oval Tooth Root Canals: A Preliminary Assessment.

The purpose of the present study was to perform a preliminary analysis of the fitting of different fiber-reinforced composite (GFRC) posts to tooth root canals and determine the resin cement layer thickness. The following GFRC posts were assessed: bundle posts (Rebilda GTTM, VOCO, Germany), sleeve system (SAPTM, Angelus Ind, Brazil), and accessory posts (ReforpinTM, Angelus, Brazil). Twenty-four freshly extracted mandibular single-rooted pre-molars were endodontically treated and divided into six groups, according to the type of GFRC post and resin cement (self-adhesive or conventional dual-cured). Then, specimens were cross-sectioned and inspected by optical microscopy regarding the cement layer thickness and presence of defects such as pores, voids, or fissures were assessed. Bundle and accessory posts revealed a regular distribution of resin cement with a lower number of voids than found with sleeve systems. The sleeve system posts showed poor fitting at the apical portion of the root canals. The type of resin cement did not affect the thickness of the interface, although both bundle and accessory posts allow a better distribution of resin cement and fibers. The present preliminary study reveals interesting insights on the fitting of bundle and accessory posts to root dentin and resin cement layer thickness in oval-shape root canals. The sleeve system posts showed adequate fitting only at the coronal portion of the canals.

[Impact of chemical surface treatment of samples made of domestic zirconium dioxide on adhesive strength]. / Vliyanie khimicheskikh metodov podgotovki poverkhnosti obraztsov iz otechestvennogo dioksida tsirkoniya na pokazateli adgezionnoi prochnosti.

Ceramic based on zirconium dioxide (ZD) is a modern, durable material for the manufacture of dentures. It is known that ZD is not etched as glass-ceramic, making it difficult to prepare this material before fixing. OBJECTIVE: To study the impact of various methods of surface treatment of ZD-based ceramic on adhesive strength. MATERIALS AND METHODS: Sandblasting with Al2O3 particles sized 50 µm and application of primers with 10-MDP phosphate monomer were used. Adhesive strength values for following 4 groups of samples were obtained: 1st group - RelyX U200 + sandblasting + Compofix new primer (n=9); 2nd group - Compofix + sandblasting + Compofix new primer (n=9); 3rd group - Panavia F 2.0 + sandblasting (n=9); 4th group (control) - Variolink Esthetic DC + sandblasting + Monobond Plus primer (n=9). RESULTS: The highest strength of adhesion was in the 4th group - 48.71±5.71MPa, the smallest in the 3rd group - 9.49±35.24 MPa. Fully domestic components used in the 2nd group allowed to obtain values of 42.50±9.79 MPa. Adhesive strength in the 1st group was 34.11±4.78 MPa. CONCLUSION: The absence of the 10-MDP-based primers application in the preparation of ZD ceramic reduces the adhesive strength between resin cement and its surface. The domestic set for fixation of dentures can be effectively used for ZD on the same basis as European analogue.

Application of near-infrared-to-blue upconversion luminescence for the polymerization of resin cements through zirconia discs.

OBJECTIVES: To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs. METHODS: Lava zirconia discs of different thicknesses (0.5-2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF4:Yb3+/Tm3+ upconversion phosphor (UP) powder was milled into 0.5-µm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type. RESULTS: The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm. SIGNIFICANCE: NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.

The effects of monomer type, filler size, and filler content of three resin cements on the color stability of laminate veneers exposed to accelerated aging.

STATEMENT OF PROBLEM: Commercially available resin cements consist of various filler sizes, filler content and monomers, and it is unclear which of these factors have the greatest effect on the color stability of laminate veneers. OBJECTIVES: To evaluate the color stability of lithium disilicate-reinforced laminate veneers inserted with three commercial resin cements with various filler sizes/contents and monomers upon accelerated aging. METHODS: Veneers were fabricated and cemented on resin abutments using three commercially available resin cements comprised of two different monomers and varying filler sizes/contents: 1) triethylene glycol dimethacrylate, TEGDMA (RelyX™ Veneer = 0.6 µm/66 %, Calibra® Esthetic Light Cure =1.2 µm/65 %); and 2) urethane dimethacrylate, UDMA (Variolink Esthetic LC = 0.1 µm/38 %). A total of 60 specimens were fabricated (n = 20 for each cement). The relative number of particles (N) and relative surface area (A) were calculated for each filler size/content. Color coordinates (L*, a*, b*) were measured, and color change (ΔE00) was calculated after cementation and following aging at 150, 300, 450, and 600 h using xenon light. Differences in color coordinates and color change were determined using repeated measures ANOVA followed by Tukey's post hoc test (α = .05). A post-hoc power analysis was performed to confirm reliability of the results. RESULTS: Based on a post-hoc power analysis of a repeated measures ANOVA with two between-factors and 1 within-factor, we had 89 % power to detect a difference of effect by cement type, 10 % power to detect a difference by shade, and 100 % power to detect a difference of effect by aging. The UDMA-based cement (0.1 µm/38 %) was least affected by aging, despite having the largest number of particles (N = 1010) and largest particle surface area (A = 7.02). The TEGDMA-based cements exhibited a significant color change, with 0.6 µm/66 % (A = 2.03, N = 8.12) producing a larger ΔE00 than 1.2 µm/65 % (A = 1.00, N = 1.00). CONCLUSIONS: Among the commercial cements tested, UDMA-based resin (0.1 µm/38 %) provided better color stability than TEGDMA-based resin cements. The color change after aging was affected by the relative surface area and relative number of particles for the TEGDMA-based resin cement (0.6 µm/66 % and 1.2 µm/65 %), with a larger surface area and a higher relative number of particles, accelerated color change with aging. The present study demonstrates a novel approach to determine color stability for any resin cement with particulate filler. CLINICAL IMPLICATIONS: The dental practitioner should be selective in choosing a commercial light cure cementation product for laminate veneers, as UDMA containing resin cement is more resistant to color changes over time than TEGDMA, regardless of the filler size/content.

Corrigendum: The possibility of clinical bonding between metal/ceramic brackets to zirconia: in vitro study.

[This corrects the article DOI: 10.3389/fbioe.2024.1354241.].

Effect of water glass treatment for zirconia and silane coupling on bond strength of resin cement.

OBJECTIVE: To evaluate the ability of the water glass treatment to penetrate zirconia and improve the bond strength of resin cement. MATERIAL AND METHODS: Water glass was applied to zirconia specimens, which were then sintered. The specimens were divided into water-glass-treated and untreated zirconia (control) groups. The surface properties of the water-glass-treated specimens were evaluated using surface roughness and electron probe micro-analyser (EPMA) analysis. A resin cement was used to evaluate the tensile bond strength, with2 and without a silane-containing primer. After 24 h in water storage at 37 °C and thermal cycling, the bond strengths were statistically evaluated with t-test, and the fracture surfaces were observed using SEM. RESULTS: The water glass treatment slightly increased the surface roughness of the zirconia specimens, and the EPMA analysis detected the water glass penetration to be 50 µm below the zirconia surface. The application of primer improved the tensile bond strength in all groups. After 24 h, the water-glass-treated zirconia exhibited a tensile strength of 24.8 ± 5.5 MPa, which was significantly higher than that of the control zirconia (17.6 ± 3.5 MPa) (p < 0.05). After thermal cycling, the water-glass-treated zirconia showed significantly higher tensile strength than the control zirconia. The fracture surface morphology was mainly an adhesive pattern, whereas resin cement residue was occasionally detected on the water-glass-treated zirconia surfaces. CONCLUSION: The water glass treatment resulted in the formation of a stable silica phase on the zirconia surface. This process enabled silane coupling to the zirconia and improved the adhesion of the resin cement.

Light Polymerization through Glass-ceramics: Influence of Light-polymerizing Unit's Emitted Power and Restoration Parameters (Shade, Translucency, and Thickness) on Transmitted Radiant Power.

Background: This in vitro study assessed light transmission through ceramic discs varying in shade, translucency, and thickness using light-polymerizing units with different radiant power/flux (RP) outputs. Methods: Disc-shaped specimens (0.5 mm, 1.0 mm, and 2.0 mm) were made from high and low-translucency glass-ceramic ingots (IPS e.max Press) in shades A1 and A4, totaling 60 discs. Two light-polymerizing units with different power outputs were used, and their emission spectra were verified. The transmitted RP values for each ceramic specimen were measured and irradiance and radiant energy influx were calculated. Differences between the light-polymerizing units and the influence of the three ceramic parameters were evaluated using an independent-samples t-test and three-way analysis of variance (ANOVA) tests (α = 0.05). Results: A statistically significant difference was observed in the mean transmitted RP values between the two light-polymerizing units. Furthermore, the three-way ANOVA test showed a significant effect of shade, translucency, and thickness, as well as a significant interaction between each pair of variables and all three variables on the transmitted RP (P < 0.05). Conclusions: Despite the significant attenuation in the transmitted RP, especially in ceramics with higher shade chromaticity and thickness and lower translucency, the calculated minimal irradiance values for both light-polymerizing units (their emitted power ≥ 500 mW) were greater than the minimum recommended irradiance threshold (100 mW/cm2). However, the exposure duration needs to be increased to provide the resin with sufficient radiant exposure for adequate polymerization.

Effect of universal adhesive pretreatments on the bond strength durability of conventional and adhesive resin cements to zirconia ceramic.

PURPOSE: This study aimed to evaluate the effect of pretreatment of three different universal adhesives (Single Bond Universal [SBU], All-Bond Universal [ABU], and Prime&Bond universal [PBU]) on the bonding durability of an adhesive (Panavia F 2.0, PF) and a conventional (Duo-Link, DL) resin cements to air-abraded zirconia. MATERIALS AND METHODS: Rectangular-shaped zirconia specimens were prepared. The chemical composition and surface energy parameters of the materials were studied by Fourier transform infrared spectroscopy and contact angle measurement, respectively. To evaluate resin bonding to the zirconia, all the bonding specimens were immersed in water for 24 h and the specimens to be aged were additionally thermocycled 10000 times before the shear bond strength (SBS) test. RESULTS: The materials showed different surface energy parameters, including the degree of hydrophilicity/hydrophobicity. While the DL/CON (no pretreatment) showed the lowest SBS and a significant decrease in the value after thermocycling (P < .001), the PF/CON obtained a higher SBS value than the DL/CON (P < .001) and no decrease even after thermocycling (P = .839). When the universal adhesives were used with DL, their SBS values were higher than the CON (P < .05), but the trend was adhesive-specific. In conjunction with PF, the PF/SBU produced the highest SBS followed by the PF/ABU (P = .002), showing no significant decrease after thermocycling (P > .05). The initial SBS of the PF/PBU was similar to the PF/CON (P = .999), but the value decreased after thermocycling (P < .001). CONCLUSION: The universal adhesive pretreatment did not necessarily show a synergistic effect on the bonding performance of an adhesive resin cement, whereas the pretreatment was beneficial to bond strength and durability of a conventional resin cement.

Micro-shear bond strength of a novel resin-modified glass ionomer luting cement (eRMGIC) functionalized with organophosphorus monomer to different dental substrates.

Objectives: This study aims to assess and compare the micro-shear bond strength (µSBS) of a novel resin-modified glass-ionomer luting cement functionalized with a methacrylate co-monomer containing a phosphoric acid group, 30 wt% 2-(methacryloxy) ethyl phosphate (2-MEP), with different substrates (dentin, enamel, zirconia, and base metal alloy). This assessment is conducted in comparison with conventional resin-modified glass ionomer cement and self-adhesive resin cement. Materials and methods: In this in vitro study, ninety-six specimens were prepared and categorized into four groups: enamel (A), dentin (B), zirconia (C), and base metal alloys (D). Enamel (E) and dentin (D) specimens were obtained from 30 human maxillary first premolars extracted during orthodontic treatment. For zirconia and metal alloys, 48 disks were manufactured using IPS e.max ZirCAD through dry milling and Co-Cr powder alloy by selective laser milling. Each group was further subdivided into three subgroups (n = 8) according to the luting cement used: (1) Fuji PLUS resin-modified glass ionomer luting cement (FP) as a control cement, (2) modified control cement (eRMGIC), and (3) RelyX U 200 (RU 200) self-adhesive resin cement. The two-way analysis of variance and Tukey's HSD were used to assess the data obtained from measuring the µSBS of the samples. Results: The results of this study showed that the mean µSBS values of eRMGIC were statistically higher compared to FP in all tested groups (p < 0.001). The mean µSBS results of eRMGIC were non-significantly different from those recorded by RU 200 for all substrates except for the dentin substrate, where the RU200 cement produced significantly higher strength (p < 0.001). The failure modes were limited to a combination of mixed and adhesive failures without pure cohesive failure. Significance: The functionalization of FP with an organophosphorus co-monomer (2-MEP) directly affects the adhesion performance of the functionalized cement, which may be utilized to develop a new type of acid-base cement. It exhibited a performance comparable to that of resin-based cement and should serve well under different clinical conditions.

Effect of dentin surface conditions and curing mode of resin cement on the dentin bond strength.

This study investigates the effects of dentin's drying time, roughness, and curing modes of resin cement on bond strength. Forty human teeth were divided into eight groups based on three experimental factors: dentin's roughness by 240-or 600-grit SiC paper (coarse or fine), dentin wetness with air-drying time (5-s or 10-s), and Single Bond Universal adhesive's curing mode by co-curing with RelyX Ultimate cement or light-curing separately (co-curing or light-curing). The micro-tensile bond strength of fifteen resin-dentin stikcs per groups was measured. Failure mode and adhesive layers were observed using stereoscopic and confocal laser scanning microscopy, respectively. The curing mode of the adhesive layer affected the bond strength of the dentin-resin cement (p<0.05). In particular, the light-curing mode exhibited a significantly higher bond strength than the co-curing one (p<0.05). The bond strength between the resin cement and dentin was improved in the 5-s drying groups than in the 10-s drying groups.

Effect of Luting Materials on the Accuracy of Fit of Zirconia Copings: A Non-Destructive Digital Analysis Method.

The marginal accuracy of fit between prosthetic restorations and abutment teeth represents an essential aspect with regard to long-term clinical success. Since the final gap is also influenced by the luting techniques and materials applied, this study analyzed the accuracy of the fit of single-tooth zirconia copings before and after cementation using different luting materials. Forty plaster dies with a corresponding zirconia coping were manufactured based on a single tooth chamfer preparation. The copings were luted on the plaster dies (n = 10 per luting material) with a zinc phosphate (A), glass-ionomer (B), self-adhesive resin (C), or resin-modified glass-ionomer cement (D). The accuracy of fit for each coping was assessed using a non-destructive digital method. Intragroup statistical analysis was conducted using Wilcoxon signed rank tests and intergroup analysis by Kruskal-Wallis and Mann-Whitney U tests (α = 0.05). Accuracy of fit was significantly different before/after cementation within A (0.033/0.110 µm) and B (0.035/0.118 µm; p = 0.002). A had a significantly increased marginal gap compared to C and D, and B compared to C and D (p ≤ 0.001). Significantly increased vertical discrepancies between A and B versus C and D (p < 0.001) were assessed. Of the materials under investigation, the zinc phosphate cement led to increased vertical marginal discrepancies, whereas the self-adhesive resin cement did not influence the restoration fit.

Long-Term Bonding Efficacy of CAD/CAM Hybrid Restorative Materials and Universal Adhesives.

OBJECTIVES: In-office and lab milled prostheses are the staple for indirect restorations. It is therefore critical to determine their long-term bonding durability. METHODS: CAD/ CAM blocks of two classes of restorative materials: 1) a nano-ceramic reinforced polymer matrix (NCPM) and, 2) a polymer-infiltrated ceramic network (PICN) were bonded using four different universal adhesives (UA) and silane systems. A lithium disilicate glassceramic (LDS) was used as a reference. The blocks were bisected and bonded with different UA/resin-cement pairs. Bonded blocks were then cut into 1.0x1.0x12.0 mm bar specimens for microtensile bond testing. Half the bars were subjected to bond strength testing immediately and the other half after aging by 50,000 thermal cycles between 5°C and 55°C. ANOVA and post-hoc tests were used to compare mean bond strength among groups. RESULTS: NCPM presented consistently high bond strength regardless of bonding techniques, while the bond strength of PICN and LDS were lower when bonded with UA relative to traditional silanes. The more hydrophilic UA produced higher bond strengths. DISCUSSION: Glass-ceramics exhibited lower bond strength with UA than the conventional etch-rinse-silane techniques. However, UAs preserved bonding interface in the long-term. SIGNIFICANCE: NCPM displayed superior bond strength relative to PICN and LDS regardless of the type of adhesives and bonding techniques.

Influence of Different Surface Treatments on the Bond Strength of Yttria-Stabilized Tetragonal Zirconia Ceramic.

Objective: This in vitro study evaluates the shear bond strength (SBS) of yttria-stabilized tetragonal zirconia (Y-TZP) and resin cement after different surface treatments. Materials and methods: Forty-eight ceramic cubes were divided into four groups (n = 12): G1 (control) sandblasting with Al2O3; G2-sandblasting with silica-coated Al2O3 (Rocatec); G3-Rocatec + CO2 laser; and G4-CO2 laser + Rocatec. A metallic primer was applied to the pretreated ceramic. A rubber ring was adapted on the central area, and then, the resin cement was inserted into the matrix and photoactivated. The samples were evaluated regarding surface roughness (Ra), SBS, failure type, and qualitatively with scanning electron microscopy (SEM). The data were analyzed by one-way analysis of variance followed by Tukey's test (p < 0.05). Results: The mean values of Ra (µm) were as follows: G1-4.52a, G2-4.24a,b, G3-4.10a,b, and G4-2.90b and the mean values of SBS (MPa) were as follows: G1-7.84a , G2-4.41b , G3-4.61b and G4-6.14a,b. SEM analyses showed superficial irregularities for all groups, being more prominent for G1. The presence of silica deposits was observed for G2, G3, and G4, but in the last two groups there were some linear areas, promoted by the fusion of silica, due to the thermomechanical action of the CO2 laser. Conclusions: The surface treatment with CO2 laser + Rocatec, using one MDP-based cement, can be an alternative protocol for the adhesion cementation of Y-TZP ceramic since it was as effective as the conventional pretreatment with aluminum oxide sandblasting.

Comparison of the Effect of Implant Abutment Surface Modifications on the Retention of Implant-Supported Restorations.

PURPOSE: To evaluate and compare the difference in retention between implant-supported restorations with and without surface modification of the implant abutments. MATERIALS AND METHODS: A total of 30 patients with singletooth implants were restored with cement-retained (Multilink N, Ivoclar) restorations using titanium base abutments (Variobase, Straumann) and randomly assigned surface modifications. Group 1 used nonmodified abutments, group 2 used sandblasted abutments, and group 3 used sandblasted abutments followed by an application of metal primer. All patients were recalled for a baseline examination 6 months after crown placement. The pull-out strength and intergroup distribution of mean pull-out strength were assessed. To assess differences between the three groups, intergroup statistical comparison of continuous variables was done using one-way ANOVA with Tukey correction for multiple group comparisons. RESULTS: The results of the intergroup mean pull-out strength distribution revealed that the distribution of mean ± SD pull-out strength in group 1, group 2, and group 3 were 220.79 ± 94.23, 488.64 ± 84.12, and 705.46 ± 112.75 Ncm, respectively. CONCLUSIONS: Sandblasting followed by the application of metal primer produced the highest retention of porcelain-fused-to-metal (PFM) crowns to titanium base abutments, followed by sandblasting alone, with the least retention being observed with no surface treatment.

Assessing push-out bond strength in re-irradiated teeth: Universal resin cement performance in self-etch and self-adhesive modes.

OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Comparative Evaluation of Luting Efficacy Between a Dual-Cure and Light-Cure Resin Cement on Its Application on Root Surface Indirect Restorations: An In Vitro Study.

Aim The aim is to evaluate the degree of dye penetration between a dual-cure and conventional resin cement on its application on the root surface indirect restorations to provide a reference for clinical choice. Materials and methods Ten freshly extracted human maxillary central anteriors were selected and randomly divided into two groups of five each. Teeth were prepared for veneer restoration, and veneers were luted using two groups of cements Calibra veneer cement and Fusion Ultra D/C cement. After they were immersed in methylene blue dye solution for 24 h, the specimens were then sectioned buccolingual into three halves in a parallel vertical plane and measured dye penetration using a stereomicroscope (Zeiss). The data collected was recorded by the dye penetration index (0-4) and statistically analyzed using the IBM SPSS Statistics for Windows, Version 24 (Released 2016; IBM Corp., Armonk, New York, United States). Results It is evident that group 1 (Calibra veneer cement) showed the lowest mean score of 0.43 mm and group 2 (Fusion Ultra D/C) showed a highest mean score of 0.72 mm. Overall, when the two groups were compared for microleakage using SPSS, there was a significant difference among the groups. Conclusion It was determined that both the resin cements evaluated in this study showed microleakage to some level given the limits of the investigation and the findings. To evaluate the dye penetration of microleakage, the Calibra veneer resin cement showed a better marginal adaptability for veneer restoration. Further investigations with broader methodology and more clinical simulation are needed to evaluate other resin cements available for root surface indirect restorations to be analyzed for prospective clinical outcomes.