Comparative study of synthesised hyroxyapatite from pure chemicals and Malaysian natural limestone precursors.

Hydroxyapatite, (HA; Ca1O(PO4)6(OH)2) has been successfully applied in medical and dental applications for several years due to its excellent biocompatibility. The usage of HA in Malaysia, however, is limited due to the lack of availability. Therefore the aim of this work is to produce HA materials from both pure chemicals and from Malaysian natural limestone precursors, and to compare their bulk properties. However, parts of Malaysian natural limestone deposits actually consist of a combination of Ca(OH)2 and CaCO3. In order to utilise the limestone to produce HA material, the combination of these commercially pure chemicals as HA precursors should still work. In order to test this hypothesis, two HAs were produced by wet synthesis technique utilising (a) combination of Ca(OH)2 + CaCO3 from pure commercial chemicals [WCC] and (b) a local natural limestone [WL] precursors. The HAs produced; WCC and WL, were compacted into discs and sintered at 1250 degrees C. The characterisations and evaluations conducted were XRD, SEM-EDX, FTIR and shrinkage factor. The results indicate that WL gives slightly better bulk properties compared to WCC.

Resposta do tecido conjuntivo pulpar frente ao hidróxido de cálcio P.A. associado à água destilada e ao hidróxido de cálcio P.A. associado a soro fisiológico / Response of pulp connective tissue to calcium hidroxide associated to distilled water and calcium hydroxide associated to seline solution

Este estudo verificou, através da histopatologia e da Microscopia Eletrônica de Varredura (M.E.V.), a reaçäo pulpar de dentes de ratos submetidos à exposiçäo pulpar, sob a açäo do hidróxido de cálcio P.A. misturado a soro fisiológico e sob a açäo do hidróxido de cálcio P.A. associado a água destilada. Foram selecionados 24 ratos de linhagem Wistar, divididos em 6 grupos experimentais numericamente iguais para cada período de 7, 14, 21, 28, 45, e 60 dias, para o estudo histopatológico, e dois grupos, nos tempos de 14 e 60 dias, para observaçäo em M. E. V. A análise histológica das polpas dentais tratadas revelou que ambas as soluçöes de hidróxido de cálcio levaram a alteraçöes semelhantes no tecido. Em todos os casos, havia presença de infiltrado inflamatório e algum grau de necrose tecidual. No grupo de 7 dias, a área de necrose era localizada à superfície da polpa coronária. Gradual aumento do processo de necrose foi observado nos grupos experimentais subseqüentes, terminando com o envolvimento de todo o tecido pulpar (grupo de 60 dias). Formaçäo incompleta de ponte de dentina foi observada em todos os espécimes após 14 dias de experimento. Na microscopia eletrônica de varredura, observamos uma formaçäo sugestiva de tecido mineralizado, que se apresentava de forma amorfa e irregular