RESUMO
Grafts of biological tissues have been used since the 1960s as an alternative to the mechanical heart prostheses. Nowadays, the most consolidated treatment to bovine pericardial (BP) bioprostheses is the crosslinking with glutaraldehyde (GA), although GA may induce calcification in vivo. In previous work, our group demonstrated that electron beam irradiation applied to lyophilized BP in the absence of oxygen promoted crosslinks among collagen fibers of BP tissue. In this work, the incorporation of silk fibroin (SF) and chitosan (CHIT) in the BP not treated with GA was studied. The samples were irradiated and then analyzed for their cytotoxicity and the ability of adhesion and growth of endothelial cells. Initially, all samples showed cytotoxicity. However, after a few washing cycles, the cytotoxicity due to acetic acid and ethanol residues was removed from the biomaterial making it suitable for the biofunctional test. The samples modified with SF/CHIT and electron beam irradiated favored the adhesion and growth of endothelial cells throughout the tissue.
Assuntos
Bioprótese , Adesão Celular/efeitos dos fármacos , Quitosana/farmacologia , Reagentes de Ligações Cruzadas/farmacologia , Células Endoteliais/efeitos dos fármacos , Fibroínas/farmacologia , Liofilização , Implante de Prótese de Valva Cardíaca/instrumentação , Próteses Valvulares Cardíacas , Pericárdio/efeitos dos fármacos , Pericárdio/efeitos da radiação , Animais , Células CHO , Bovinos , Proliferação de Células/efeitos dos fármacos , Sobrevivência Celular/efeitos dos fármacos , Quitosana/toxicidade , Colágeno/efeitos dos fármacos , Colágeno/efeitos da radiação , Cricetinae , Cricetulus , Reagentes de Ligações Cruzadas/toxicidade , Fibroínas/toxicidade , Humanos , Teste de Materiais , Pericárdio/transplante , Técnicas de Cultura de TecidosRESUMO
OBJECTIVE: To evaluate the effect of gamma irradiation on glutaraldehyde-fixed bovine pericardium. METHOD: Glutaraldehyde-fixed bovine pericardium was exposed to gamma radiation (doses from 0 to 10000 Gy). Six samples from each of nine groups were evaluated by optic microscopy, and shrinking and mechanical tests and the denaturation temperature was determined. Additionally, they were subcutaneously implanted in rats and after four months they were explanted and Ca2+ levels measured by atomic absorption spectroscopy. RESULTS: The Ca2+ levels were (in microg/mg): control (0 Gy) - 194.45; 50 Gy - 154.64; 100 Gy - 169.37; 200 Gy - 163.64; 500 Gy - 199.89; 1000 Gy - 184.02; 2000 Gy - 198.95; 5000 Gy - 227.95; 10000 Gy - 362.62. Gamma irradiation caused a significant effect on the biomechanical properties of the tissue. CONCLUSION: e-fixed bovine pericardium.
Assuntos
Fosfatase Alcalina/efeitos da radiação , Calcinose/prevenção & controle , Fixadores/farmacologia , Raios gama/uso terapêutico , Glutaral/farmacologia , Pericárdio/efeitos da radiação , Fosfatase Alcalina/análise , Animais , Cálcio/análise , Bovinos , Colágeno , Modelos Animais de Doenças , Relação Dose-Resposta à Radiação , Feminino , Próteses e Implantes , Ratos , Estresse MecânicoRESUMO
OBJETIVO: Avaliar o comportamento mecânico e os efeitos no processo de calcificação pós-implante do pericárdio bovino tratado com glutaraldeído submetido a várias doses de radiação gama. MÉTODO: Pericárdios bovinos fixados com glutaraldeído foram submetidos a radiação gama, nas doses de 0 a 10000 Gy. Seis amostras de cada grupo foram avaliadas pela microscopia óptica, determinação da temperatura de desnaturação do colágeno e ensaio mecânico de tração e implantadas subcutaneamente em ratos. Após quatro meses do implante, as amostras foram explantadas e o conteúdo de Ca2+ determinado pela espectrometria de absorção atômica. RESULTADOS: Níveis de Ca2+ (em µg/mg): 0 Gy (controle) - 194,45; 50 Gy - 154,64; 100 Gy - 169,37; 200 Gy - 163,64; 500 Gy - 199,89; 1000 Gy - 184,02; 2000 Gy - 198,95; 5000 Gy - 227,95 e 10000 Gy - 362,62. Houve alteração significativa no comportamento mecânico do tecido irradiado, quando comparado ao grupo controle, mesmo com o emprego de baixas doses de radiação. CONCLUSÃO: O emprego da radiação gama no pericárdio bovino tratado com glutaraldeído não reduziu os níveis de Ca2+ em implantes subcutâneos em ratos por quatro meses e promoveu alteração significativa no comportamento mecânico do tecido, com redução na sua resistência, quando comparados ao grupo controle.
OBJECTIVE: To evaluate the effect of gamma irradiation on glutaraldehyde-fixed bovine pericardium. METHOD: Glutaraldehyde-fixed bovine pericardium was exposed to gamma radiation (doses from 0 to 10000 Gy). Six samples from each of nine groups were evaluated by optic microscopy, and shrinking and mechanical tests and the denaturation temperature was determined. Additionally, they were subcutaneously implanted in rats and after four months they were explanted and Ca2+ levels measured by atomic absorption spectroscopy. RESULTS: The Ca2+ levels were (in µg/mg): control (0 Gy) - 194.45; 50 Gy - 154.64; 100 Gy - 169.37; 200 Gy - 163.64; 500 Gy - 199.89; 1000 Gy - 184.02; 2000 Gy - 198.95; 5000 Gy - 227.95; 10000 Gy - 362.62. Gamma irradiation caused a significant effect on the biomechanical properties of the tissue. CONCLUSION: e-fixed bovine pericardium.