Avaliação da influência dos diferentes tempos e meios de armazenamento de sistemas autocondicionantes na adesão de bráquetes ortodônticos / Evaluation of the influence of different times and storage media of self-etching systems on the adhesion of orthodontic brackets

RESUMO

O objetivo dos autores deste trabalho foi avaliar o grau de adesão do sistema autocondicionante (TPSEP) quanto à variação do tempo e meios de armazenamento. Foram avaliados a resistência ao cisalhamento e o Índice de Remanescente Adesivo. 120 incisivos bovinos foram divididos em 12 grupos sendo 2 controles e 10 grupos de trabalho, foram avaliados os tempos e o tipo de armazenamento do TPSEP aberto. Após quatorze dias da colagem de cada grupo, realizou-se o teste de resistência ao cisalhamento na máquina de ensaios universais EMIC DL 2000 (São José dos Pinhais, Brasil). Encontraram-se diferenças estatisticamente significantes entre os grupos Transbond Controle (11,93 ±3,53 MPa), Concise Controle (14,38 ± 7,81 MPa), Transbond Imediato (14,42 ± 5,16 MPa) e Transbond aberto por duas semanas e armazenado em geladeira (13,33 ±3,80 MPa) com os demais grupos (P<0.05). O grupo Concise aberto por duas semanas e armazenado em geladeira (2,19 ± 2,17 MPa), apresentou menor valor e o grupo Transbond Imediato (14,42 ± 5,16 MPa) o maior. Os grupos que apresentaram maior e menor quantidade de remanescente adesivo respectivamente foram o grupo Transbond aberto por quatro semanas e armazenado em temperatura ambiente (36,66 ± 29,53 mm²) e o grupo Concise Controle (1,42 ± 2,60 mm²). O armazenamento do TPSEP, à temperatura de 4ºC depois de ativado por até duas semanas, associado ao compósito Transbond XT (grupo T2G), parece não afetar os resultados na resistência ao cisalhamento, podendo ser usado com segurança. A associação do TPSEP, imediatamente após ativação, ao Transbond XT® apresentou excelentes valores de resistência ao cisalhamento (grupo TI, com 14,42 ± 5,16MPa), ocorrendo o oposto quando associado ao ConciseMR (grupo CI, com 4,76 ± 2,57MPa).Nos grupos onde o sistema autocondicionante estava aberto com duas semanas e associado com ConciseMR, bem como naqueles onde o tempo foi por quatro semanas, tanto associado com Transbond ou ConciseMR, os valores de resistência ao cisalhamento foram menores que o mínimo necessário, 6MPa (AU)

ABSTRACT

The goal of the authors of this study was to evaluate the degree of adhesion of the self-etching system (TPSEP) as the variation in the time and storage. They evaluated the shear bond strength and the Adhesive Remnant Index. 120 bovine incisors were divided into 12 groups with 2 controls and 10 working groups, were evaluated times and the kind of storage of the opened TPSEP. After 14 days each group, was subject to a shear bond strength test on universal testing machine EMIC DL 2000 (São José dos Pinhais, Brazil). Normality verification was performed using the Kolmogorov-Smirnov test, at a significance level of 0.05. Checked the normal distribution, the data were subjected to analysis of variance (ANOVA) and Tukey post hoc at the 0.05 significance level. The Pearson correlation test was applied to the variables. The intra class corroboration coefficient was used to evaluate the reliability of the IRA measures, (ICC = 0.92). Statistically significant differences were found between the groups Transbond Control (11.93 ± 3.53 MPa), Concise Control (14.38 ± 7.81 MPa), Transbond Immediate (14.42 ± 5.16 MPa) and Transbond activated for two weeks and storage in the refrigerator (13.33 ± 3.80 MPa) with the other groups (P < 0.05). The Group Concise activated for two weeks and storage in the refrigerator (2.19 ± 2.17 MPa), showed lowest value and the group Transbond Immediate (14.42 ± 5.16 MPa) the highest. The group that showed the highest and least amount of adhesive remnant respectively were Transbond activated for four weeks storage in ambience temperature (36.66 ± 29.53 mm), and the Group Concise Control (1.42 ± 2.60 mm). TPSEP storage at 4° C, after activated for up to 2 weeks, associated with the Transbond composite XT (T2G) doesn't seem to affect the results on shear bond strength, and can be used safely.The Association of TPSEP immediately after the Transbond XT® chemical mixture presented excellent shear bond strength values (TI Group) (14.42 ± 5, 16MPa), the opposite when associated with the Concise ® (IC Group) (4.76 ± 2, 57MPa). In open groups with two weeks associated to Concise® and in groups with four weeks, the shear bond strength values were lower than the minimum considered necessary for the literature, 6MPa (AU)