Urchin-like NiCo-based bimetallic hydroxide decorated with DOPO as highly hydrophobic flame retardant for remarkably reducing fire hazard of poly (L-lactic acid).

ABSTRACT

Designing high-performance flame retardants for poly (L-lactic acid) (PLA) materials and exploring a simple and scalable strategy have been hot topics in research. In this work, a novel and highly efficient flame retardant, that is, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) decorated urchin-like NiCo-based bimetallic hydroxide (NiCo-BH@DOPO), was synthesized and incorporated into PLA to prepare PLA and NiCo-BH@DOPO (PLA/NiCo-BH@DOPO) composite. Benefiting from the DOPO organic modification, NiCo-BH@DOPO had superb hydrophobicity and presented excellent dispersion in the PLA matrix. When 20 wt% NiCo-BH@DOPO was added, the LOI value of PLA/NiCo-BH@DOPO composites reached 33.2 %, passed the V-0 level of UL-94 grade, and its maximum peak heat release rate (PHRR) and total heat release (THR) were reduced by 13.2 % and 17.3 %, respectively, compared with PLA/NiCo-BH composites. Furthermore, the residue of PLA/NiCo-BH@DOPO at 800 °C reached 19.8 wt% and the T10% (temperature at 10 % weight loss) increased by 33 °C. More importantly, the residual PLA/NiCo-BH@DOPO char exhibits a significantly reduced presence of large cracks compared to PLA/NiCo-BH, indicating a more compact formation of residual char. NiCo-BH@DOPO endowed PLA with outstanding flame retardancy, thermal stability and carbonization properties, which were owing to the multi-coordinating effect transition metal (NiCo-BH) catalyzed the char formation to form a char layer barrier and DOPO free radicals captured to inhibit the combustion reaction chain. This investigation provided a facile strategy for the novel multi-function NiCo-based bimetallic hydroxide flame retardant, expanding NiCo-BH potential applications in PLA.