Estudo de deflexão de carga de fios ortodônticos de níqueltitânio: abordando a pseudoelasticidade e a influência do desvio padrão / Orthodontic Nickel-Titanium wires load deflection study: addressing pseudoelasticity and influence of the standard deviation
Ortho Sci., Orthod. sci. pract
; 13(49): 86-95, 2020. tab
Article
en Pt
| BBO
| ID: biblio-1100133
Biblioteca responsable:
BR243.1
RESUMO
Resumo Proposição O objetivo deste estudo é verificar os fenômenos de pseudoelasticidade em fios ortodônticos de níquel-titânio utilizados no tratamento do apinhamento dentário. Métodos:
Onze grupos de fios ortodônticos de níquel-titânio, calibre 0,36mm (0.014") de 6 marcas diferentes (Abzil convencional e termoativado; GAC convencional e termo ativado; Morelli convencional e termoativado; Ormco CuNiTi; Orthometric convencional e termoativado e Orthosource convencional e termoativado) foram testados pelo teste de descarga, em deflexões de 0,5mm, 1mm, 2mm e 3mm. Foi utilizada uma máquina de teste universal INSTRON 3342 com uma célula de carga 10N e, para padronizar os testes, seguiu-se o regulamento ISO 15.841. A análise estatística foi realizada usando os testes subsequentes Kolmogorov-Smirnov para verificar a normalidade e ANOVA, seguido do teste de Tukey para comparações intergrupos.Resultados:
Todos os grupos foram classificados como pseudoelásticos, dentro de uma faixa de força de 40cN, no máximo.Conclusões:
Dentre esses grupos, os que apresentaram pseudoelasticidade e excelente homogeneidade foram Morelli termoativado e Ormco CuNiTi. (AU)ABSTRACT
Abstract Proposition The purpose of this study is to check the pseudoelasticity phenomena on nickel-titanium orthodontic wires, used to treat dental crowding. Methods:
Eleven groups of nickel-titanium orthodontic wires, caliber 0.36mm (0.014") of 6 different brands (Abzil conventional and heat-activated; GAC conventional and heat-activated; Morelli conventional and heat-activated; Ormco CuNiTi; Orthometric conventional and heat-activated and Orthosource conventional and heat-activated) were tested by bend testing, at deflections of 0.5mm, 1mm, 2mm and 3 mm. A universal testing machine INSTRON 3342 with a 10N load cell was used and, in order to standardize the tests, the ISO 15.841 regulation was followed. Statistical analysis was performed using the subsequent tests Kolmogorov-Smirnov to verify normality and ANOVA followed by Tukey test for intergroup comparisons.Results:
All groups were classified as pseudoelastic, within a range of maximum. force of 40cN.Conclusions:
Among these groups those that presented pseudoelasticity and excellent homogeneity were Morelli heat-activated and Ormco CuNiTi. (AU)Palabras clave
Buscar en Google
Colección:
06-national
Base de datos:
BBO
Asunto principal:
Alambres para Ortodoncia
/
Ortodoncia
/
Ortodoncia Correctiva
Idioma:
Pt
Revista:
Ortho Sci., Orthod. sci. pract
Año:
2020
Tipo del documento:
Article