Shear bond strength of ceramic brackets after different pre-treatments in porcelain surface
Braz. j. oral sci
; 14(1): 31-35, Jan-Mar/2015. tab, graf
Artículo
en Inglés
| LILACS
| ID: lil-745779
Biblioteca responsable:
BR218.1
ABSTRACT
To evaluate the bond strength of brackets bonded after different surface treatments on two dental ceramics. METHODS:
One hundred and twenty discs 5 mm thick and 7 mm diameter of two ceramic types were made and randomly divided in 8 groups. Groups 1, 3, 5, and 7 used Eris ceramic and groups 2, 4, 6, and 8 used d.Sign ceramic. The ceramic surfaces were treated with 10% hydrofluoric acid G1 and G2, 10% hydrofluoric acid + silane G3 and G4, aluminum oxide blasting + 35% phosphoric acid + silane G5 and G6, CoJet blasting + 35% phosphoric acid + silane G7 and G8. Metallic brackets were cemented with Concise cement. Mechanical test was performed in a universal testing machine until failure.RESULTS:
The average values MPa obtained G1 - 7.30; G2 - 6.12; G3 - 17.49; G4 - 19.54; G5 - 18.80; G6 - 21.93; G7 - 6.81 e G8 - 9.77 were submitted to ANOVA and Tukey test p<0.05. The fracture patterns were analyzed in stereoscopic microscope 25´X and representative samples of each group were analyzed in SEM.CONCLUSIONS:
It was possible to conclude that use of silane after hydrofluoric acid increased the bond strength values...
Texto completo:
Disponible
Colección:
Bases de datos internacionales
Base de datos:
LILACS
Asunto principal:
Adhesivos
/
Recubrimiento Dental Adhesivo
/
Soportes Ortodóncicos
/
Resistencia al Corte
/
Porcelana Dental
Límite:
Humanos
Idioma:
Inglés
Revista:
Braz. j. oral sci
Asunto de la revista:
Odontología
Año:
2015
Tipo del documento:
Artículo
País de afiliación:
Brasil
Institución/País de afiliación:
Universidade do Sul de Santa Catarina/BR