Effect of micro-particles on cavitation erosion of Ti6Al4V alloy in sulfuric acid solution.

The influences of micro-particles on ultrasonic cavitation erosion of Ti6Al4V alloy in 0.1M H2SO4 solution were investigated using mass loss weight, scanning electron microscopy (SEM) and white light interferometer. Mass loss results revealed that the cavitation erosion damage obviously decreased with increasing particle size and mass concentration. Open circuit potential recorded during cavitation erosion shifted to positive direction with the decreased mass loss. Meanwhile, the mass loss sharply decreased with applying a positive potential during the entire ultrasonic cavitation erosion, and the relationship between the open circuit potential and the cavitation erosion resistance was discussed.