Evaluation of Microleakage at the Junction Between Combined Amalgam/Composite Resin Restorations Using Different Bonding Systems in Class II Cavities
Pesqui. bras. odontopediatria clín. integr
; 22: e210148, 2022. tab
Artigo
em Inglês
| LILACS, BBO - Odontologia
| ID: biblio-1422278
Biblioteca responsável:
BR1264.1
ABSTRACT
Abstract Objective:
To evaluate the microleakage at the junction between amalgam-composite resin restorations using different bonding systems. Material andMethods:
In this in-vitro study, standard class II cavities were prepared on 40 human maxillary premolars. The axial and gingival floor depths of the cavities were 2 mm and 1 mm below (cementoenamel junction), respectively. The samples were divided into 4 groups (n = 10). In all groups, a layer of 1-mm thick amalgam was used as a coating for the initial part of the gingival floor. In group 1, no bonding system was used for amalgam restoration. In group 2, G-Premio Bond was applied. G-Premio bond + alloy primer and single bond + alloy primer were used in group 3 and group 4, respectively. The rest of the cavities in all groups were then repaired using FiltekZ250 composite. The samples were thermocycled at 500 rpm and immersed in 1% methylene blue solution for 24 hours to allow dye penetration. Once cut, the samples were placed under a stereomicroscope (40X) to determine the microleakage rate. Data analysis was carried out using post-hoc and Chi-square tests (p<0.05).Results:
The highest and lowest microleakage rate was related to groups 1 and 3, respectively. There was a significant difference between groups (1,2) and (1,3), and (1,4), and groups (2,3) (p<0.05).Conclusion:
The use of alloy primer and bonding could reduce the microleakage between the two restorations (AU).
Texto completo:
Disponível
Coleções:
Bases de dados internacionais
Base de dados:
BBO - Odontologia
/
LILACS
Assunto principal:
Adesivos Dentinários
/
Resinas Compostas
/
Infiltração Dentária
/
Restauração Dentária Permanente
Limite:
Humanos
Idioma:
Inglês
Revista:
Pesqui. bras. odontopediatria clín. integr
Assunto da revista:
Odontologia
Ano de publicação:
2022
Tipo de documento:
Artigo
País de afiliação:
Irã
Instituição/País de afiliação:
Zanjan University of Medical Sciences/IR