Use of glass transition temperature for stabilization of board's cracks of Eucalyptus grandis
An. acad. bras. ciênc
; 82(3): 791-797, Sept. 2010. ilus, graf, tab
Artigo
em Inglês
| LILACS
| ID: lil-556813
Biblioteca responsável:
BR1.1
ABSTRACT
The Eucalyptus grandis logs temperatures were determined and correlated with the board's cracks during steaming. Thermocouples were inserted in the logs center, registering their temperatures during steaming at 90"C. The logs were sawed and the board's cracks measured. It was concluded that (1) the logistic S-shaped curve explains the logs temperature variation; (2) the logs with diameter of 20 to <25, 25 to <30 and 30 to <35 cm presented, respectively, 84.2"C, 73.1"C and 45.8"C in the steaming; and (3) the cracks lengths significantly decreased in logs that reached the glass transition temperature.
RESUMO
As temperaturas em toras de Eucalyptus grandis, durante a vaporização, foram determinadas e correlacionadas com as rachaduras das tábuas. Nos centros das toras foram inseridos termopares e registradas suas temperaturas durante a vaporização à 90"C. As toras foram desdobradas e as rachaduras das tábuas mensuradas. Concluiu-se que (1) o modelo estatístico sigmoidal logístico explica a variação da temperatura nas toras; (2) as toras com 20 a <25, 25 a <30 e 30 a <35 cm de diâmetro apresentaram, respectivamente, 84,2"C, 73,1"C e 45,8"C ao final da vaporização; e (3) as rachaduras foramsignificativamente menores nas toras que atingiram a temperatura de transição vítrea.
Texto completo:
Disponível
Coleções:
Bases de dados internacionais
Base de dados:
LILACS
Assunto principal:
Madeira
/
Temperatura de Transição
/
Eucalyptus
Idioma:
Inglês
Revista:
An. acad. bras. ciênc
Assunto da revista:
Ciência
Ano de publicação:
2010
Tipo de documento:
Artigo
/
Documento de projeto
País de afiliação:
Brasil
Instituição/País de afiliação:
UNESP/BR