In vitro comparisons of casting retention on implant abutments among commercially available and experimental castor oil-containing dental luting agents.

STATEMENT OF PROBLEM: Although cement-retained implant prostheses are widely used, the quantification of optimal retention remains controversial, and new dental luting agents should be evaluated. PURPOSE: The purpose of this study was to compare, in vitro, the casting retention on implant abutments after cementation with 3 commercially available luting agents and an experimental luting agent (castor oil polyurethane, COP) with variable weight percentages (wt%) of calcium carbonate (CaCO3). MATERIAL AND METHODS: Seventy-two palladium-silver cast copings were fabricated and divided into 6 groups: Temp Bond interim cement (TB); zinc phosphate cement (ZP); Rely X ARC resin cement (RX); pure COP (COP); COP + 10% wt% CaCO3 filler (COP 10); and COP + 50% wt% CaCO3 filler (COP 50). After cementation, the specimens were stored in distilled water at 37°C for 24 hours and subjected to removal force tests in a universal testing machine (5 kN; 0.5 mm/min). Statistical analyses were performed with the Kruskal-Wallis and Student-Newman-Keuls tests (α=.05). RESULTS: The median values of casting retention (N) were as follows: TB=57.20 ±10.4; ZP=343.56 ±50.3; RX=40.07 ±9.7; COP=258.98 ±41.4; COP 10=466.57 ±79.3; and COP 50=209.63 ±31.4. The Kruskal-Wallis test showed significant differences among the groups (P<.01). TB and RX had the lowest mean retention values; COP, COP 10, and COP 50 were equal to ZP, and COP 10 had the highest retention. CONCLUSIONS: The casting retention on implant-abutments provided by COP was similar to that of copings cemented with zinc phosphate and may be influenced by the addition of calcium carbonate.