Effect of cementation delay on bonding of self-adhesive resin cement to yttria-stabilized tetragonal zirconia polycrystal ceramic treated with nonthermal argon plasma.

STATEMENT OF PROBLEM: Nonthermal argon plasma (NTAP) has been reported to improve the bond strength of resin cements to yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramics. However, the effect of the inevitable delay before cementation and after treating Y-TZP ceramics with NTAP is unclear. PURPOSE: The purpose of this in vitro study was to investigate whether delays of 8, 12, and 24 hours between the Y-TZP ceramic treatment with NTAP and the cementation would affect the surface energy and the bond strength of a self-adhesive resin cement to Y-TZP ceramic. MATERIAL AND METHODS: Sixty plates and 50 blocks of 3Y-TZP ceramic were divided into 2 groups (n=30 and n=25): as-sintered (AS) and airborne-particle abraded with 50-µm Al2O3 (APA). These groups were further divided into 5 subgroups (n=6 and n=5) according to the delay between the NTAP treatment and the measurement of surface energy and microtensile bond strength (µTBS) evaluation: (0, 8, 12, and 24 hours). For both 3Y-TZP surface conditions (AS and APA), a control group without NTAP treatment was used (ASC and APAC). The surface energy (SE) was evaluated with a goniometer and the 3Y-TZP elemental composition with X-ray photoelectron spectroscopy (XPS). For the µTBS test, the 3Y-TZP ceramic blocks were cemented to composite resin blocks with a self-adhesive resin cement. After storage in distilled water at 37 °C for 24 hours, the 3Y-TZP-composite resin blocks were sectioned into beams and submitted to a µTBS test. Data were submitted to 2-way ANOVA and the Tukey HSD test (α=.05). RESULTS: For the AS group, NTAP increased the SE irrespective of the delay before measurement: ASC<0 hour=8 hours=12 hours=24 hours (P<.05). For the APA group, except after 12 hours, NTAP also increased the surface energy (P<.05). XPS analysis showed an increase in the oxygen/carbon ratio after NTAP treatment for both groups. For the AS group, NTAP increased the µTBS after 0, 8, and 12 hours (P<.05), whereas for the APA group this occurred only after 8 hours (P<.05). For the AS and APA groups, the highest µTBS was reached after 8 hours (P<.05). CONCLUSIONS: Treatment of 3Y-TZP ceramic with NTAP improved the SE and increased the µTBS of self-adhesive resin cement to 3Y-TZP ceramic. These effects were time dependent, with better results at 8 hours after NTAP treatment.