The influence of ultraviolet irradiation on sandblasted and acid-etching surface adsorbing human fibronectin / 中华口腔医学杂志
Chinese Journal of Stomatology
; (12): 234-238, 2014.
Artigo
em Chinês
| WPRIM (Pacífico Ocidental)
| ID: wpr-260848
Biblioteca responsável:
WPRO
ABSTRACT
<p><b>OBJECTIVE</b>To study the influence of ultraviolet (UV) irradiation on physical and chemical properties of sandblasted and acid-etched (SA) titanium surface and their ability to adsorb human fibronectin (HFn).</p><p><b>METHODS</b>SA and UV-SA surfaces were separately prepared. Surface morphology, roughness, elemental composition, wettability and HFn adsorption assay were performed for comparative analysis of these two surfaces.</p><p><b>RESULTS</b>SA and UV-SA surface had a similar morphology with multi-holes, and average roughness. UV-SA surface had a lower C content (22.83%) and higher O content (51.20%) and presented hydrophilicity, while SA surface showed hydrophobicity. But the quantity of adsorbed HFn on SA surface at 10 min assay point [(0.41 ± 0.07) µg] was statistically higher than that on UV-SA surface [(0.26 ± 0.08) µg](P = 0.007).</p><p><b>CONCLUSIONS</b>UV irradiation would not change the morphology and roughness of SA surface. However, it could reduce the hydrocarbon and increase the hydroxyl groups, and the absorption of HFn on UV-SA surface at 10 min assay point was statistically lower than that on SA surface. Therefore, the in-vitro bioactivity of UV-SA surface was not as good as that of SA surface.</p>
Texto completo:
Disponível
Base de dados:
WPRIM (Pacífico Ocidental)
Assunto principal:
Propriedades de Superfície
/
Titânio
/
Raios Ultravioleta
/
Microscopia Eletrônica de Varredura
/
Química
/
Fibronectinas
/
Molhabilidade
/
Adsorção
Limite:
Humanos
Idioma:
Chinês
Revista:
Chinese Journal of Stomatology
Ano de publicação:
2014
Tipo de documento:
Artigo