Preparation of nanometer powders of dental alumina ceramics / 华西口腔医学杂志

ABSTRACT

<p><b>OBJECTIVE</b>The purpose of this study was to explore the preparation method of nanometer powders of dental alumina ceramics.</p><p><b>METHODS</b>The effects of concentration of inorganic precursors, pH value, calcination temperature and ageing time on the synthesizing process, phase composition and microstructure of the materials were studied. Aluminium nitrate with concentrations of 0.03 mol/L, 0.05 mol/L, 0.1 mol/L and 0.2 mol/L were used as inorganic precursors to prepare alumina powders via sol-gel method. Ammonia water was added into the solutions to adjust the pH values to 5, 9 and 11. The dried gel was then calcined under different temperatures, from 950 degrees C to 1200 degrees C. The prepared alumina powders were studied by using X-ray diffraction (XRD), and scanning electron microscope (SEM).</p><p><b>RESULTS</b>The alumina powder which was prepared with 0.1 mol/L aluminium nitrate, pH 9, and calcined at 1200 degrees C for 10 min showed good physical characteristics. The diameter of final powder was about 70 nm.</p><p><b>CONCLUSION</b>With the proper preparation condition, weakly agglomerated powders of alumina in nanometer particle size could be obtained.</p>