Biocompatibility and security of calcium sulfate bone substitutes / 中国组织工程研究
Chinese Journal of Tissue Engineering Research
; (53): 2317-2323, 2016.
Artigo
em Chinês
| WPRIM (Pacífico Ocidental)
| ID: wpr-492148
Biblioteca responsável:
WPRO
ABSTRACT
BACKGROUND:
It is a great potential study that calcium sulfate product loaded with antibiotics is developed, but this product is not systematicaly studied and its biocompatibility and security need to be further studied.OBJECTIVE:
To evaluate the biocompatibility and safety of vancomycin- or gentamicin-loaded calcium sulfate bone.METHODS:
(1) Hemolysis test vancomycin-loaded, gentamicin-loaded calcium sulfate extracts, double distiled water and saline were added into rabbit anticoagulant blood samples. (2) Micronucleus test vancomycin-loaded and gentamicin-loaded calcium sulfate extracts, cyclophosphamide and normal saline solution were intraperitonealy injected to mice, respectively. (3) Acute toxicity test vancomycin-loaded and gentamicin-loaded calcium sulfate extracts, and normal saline solution were intraperitonealy injected to mice, respectively. (4) Pyrogen test the mice were injected vancomycin-loaded and gentamicin-loaded calcium sulfate extractsvia the ear vein. (5) Intradermal stimulation test vancomycin-loaded and gentamicin-loaded calcium sulfate extracts were respectively injected into the unilateral spine of rabbits, respectively. (6) Intramuscular implantation test vancomycin-loaded and gentamicin-loaded calcium sulfate extracts were respectively injected to the dorsal muscle of rabbits. (7) Intraosseous implantation test vancomycin-loaded and gentamicin-loaded calcium sulfate were implanted into the necrotic femoral bone of rabbits. RESULTS ANDCONCLUSION:
Both vancomycin-loaded and gentamicin-loaded calcium sulfate products, which have no hemolytic reaction, genetic toxicity, acute toxicity, pyrogen reaction and skin irritation, are considered to have good biocompatibility and safety.
Texto completo:
Disponível
Base de dados:
WPRIM (Pacífico Ocidental)
Idioma:
Chinês
Revista:
Chinese Journal of Tissue Engineering Research
Ano de publicação:
2016
Tipo de documento:
Artigo