The influence of different chemical treatments on the surface modification and biological behavior of PEEK / 实用口腔医学杂志
Journal of Practical Stomatology
; (6): 32-36, 2019.
Artigo
em Chinês
| WPRIM (Pacífico Ocidental)
| ID: wpr-743702
Biblioteca responsável:
WPRO
ABSTRACT
Objective:
To improve the bioactivity of PEEK by chemical methods.Methods:
PEEK samples were treated by polish only (group (1)) ; concentrated sulfuric acid for 5 min (group (2)) ; concentrated sulfuric acid for 10 min (group (3)) ; concentrated sulfuric acid for 5 min, followed by treatment of hydrogen nitrate for 5 min (group (4)) and mineral chameleon and ortho-phosphoric acid (group (5)) respectively (n = 9) . Then, all samples were treated by water at 100 ℃ for 4 h. The sample surface was observed by FE-SEM, the chemical comporent of the samples was analyzed by XPS. BMSCs were cultured on the sample surface for 4 h and observed by SEM.Results:
The sample sureface in group (1) was smooth, in group (2), (3) and (4) was with 3 D ethmoidal foramen structure, in group (5) with petal-like from. The sulfur content (Wt%) of the samples of group (1), (2), (3), (4) and (5) was 0, 2. 45 ± 0. 22, 3. 48 ± 0. 16 (vs (1), P= 0. 000), 1. 79 ± 0. 05 (vs (1) P = 0. 002) and 0 respectively. BMSCs cultured on the sample surface of group (2), (3), (4) and (5) were more and with more pseudopod.Conclusion:
The bioactivity of PEEK can be enhanced after acid pickling. Water bath and nitric acid treatment can remove the residual acid and further enhance the bioactivity of PEEK.
Texto completo:
Disponível
Base de dados:
WPRIM (Pacífico Ocidental)
Idioma:
Chinês
Revista:
Journal of Practical Stomatology
Ano de publicação:
2019
Tipo de documento:
Artigo