Your browser doesn't support javascript.
loading
Show: 20 | 50 | 100
Results 1 - 20 de 83
Filter
1.
Article in English | IMSEAR | ID: sea-154497

ABSTRACT

Aim: The aim of this study was to evaluate the influence of accelerated artificial aging (AAA) on the color change of composite resins used in dentistry. Materials and Methods: Three composite resins were evaluated: Two microhybrids and one hybrid of higher viscosity, with different amounts and sizes of filler particles, shades C2 and B2. A total of 54 specimens were obtained (18 for each composite resin), made of a Teflon matrix (15 mm in diameter and 2 mm in height). The color measurements were obtained with a Spectrophotometer, (PCB 6807 BYK Gardner) before and after AAA. Data were submitted to the Kolmogorov-Smirnov test (α >0.05), ANOVA and Tukey test (α <0.05). After statistical analysis, the color difference among composite resins with the same shades was analyzed. Results: All composite resins showed unacceptable color changes after AAA (ΔE > 3). Considering the variable ∆E, it was observed that the color tone C2 was already statistically different for the microhybrid composite resin prior to AAA (P < 0.05) and in shade B2 for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.01). After this process, a statistically significant difference was observed only for shade B2 between microhybrid composite resins (P < 0.01) and for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.05). Regarding the color difference within a same composite resin group, before aging the composite resin hybrid of higher viscosity B2 showed the highest color variation rate and microhybrid with zirconium/silica C2 showed the lowest. Conclusions: All composite resins presented unacceptable color changes after 382 h of aging and different composite resins with same hue, presented different colors before being subjected to the aging process (B2 and C2) and after (B2). It was also observed color difference within a group of the same composite resin and same hue.

2.
Braz. oral res ; 24(4): 381-387, Oct.-Dec. 2010. ilus, tab
Article in English | LILACS | ID: lil-569231

ABSTRACT

Dentin hypersensitivity (DH) is a painful response to stimulus applied to the open dentinal tubules of a vital tooth. It's a common oral condition, however, without an ideal treatment available yet. This work evaluated in vitro the effect of micron-sized particles from a novel bioactive glass-ceramic (Biosilicate) in occluding open dentinal tubules. A dentin disc model was employed to observe comparatively, using scanning electron microscopy (SEM), dentinal tubule occlusion by different products and deposition of hydroxyl carbonate apatite (HCA) on dentin surface by Biosilicate, after a single application: G1 - Dentifrice with potassium nitrate and fluoride; G2 - Two-step calcium phosphate precipitation treatment; G3 - Water-free gel containing Biosilicate particles (1 percent); G4 - Biosilicate particles mixed with distilled water in a 1:10 ratio; all of them after 1, 12 and 24 hours of immersion in artificial saliva. Fourier transform infrared spectroscopy (FTIR) was performed to detect HCA formation on dentin discs filled with Biosilicate after 2 minutes, 30 minutes and 12 hours of immersion in artificial saliva. SEM showed a layer of HCA formed on dentin surface after 24 hours by G4. G1, G2 and G3 promoted not total occlusion of open dentinal tubules after 24 hours. FTIR showed HCA precipitation on the dentin surface induced by Biosilicate after 30 minutes. The micron-sized particles from the bioactive glass-ceramic thus were able to induce HCA deposition in open dentinal tubules in vitro. This finding suggests that Biosilicate may provide a new option for treating DH.


Subject(s)
Ceramics/pharmacology , Dentin Desensitizing Agents/pharmacology , Dentin Sensitivity/drug therapy , Dentin/drug effects , Dentin Desensitizing Agents/therapeutic use , Dentin/chemistry , Dentin/ultrastructure , Microscopy, Electron, Scanning , Saliva, Artificial , Spectroscopy, Fourier Transform Infrared , Surface Properties , Time Factors
3.
Int. j. morphol ; 27(3): 801-803, sept. 2009. ilus
Article in English | LILACS | ID: lil-598939

ABSTRACT

The intra-buccal polymeric bioadhesive systems that can stay adhered to the oral soft tissues for drug programmed release, with the preventive and/or therapeutic purpose has been employed for large clinical situations. A system based on hydroxypropyl methyl cellulose/Carbopol 934'/magnesium stearate (HPMC/Cp/StMg) was developed having the sodium fluoride as active principle. This kind of system was evaluated according to its resistance to the removal by means of physical test of tensile strength. Swine buccal mucosa extracted immediately after animals' sacrifice was employed as substrate for the physical trials, to obtain 16 test bodies. Artificial saliva with or without mucin was used to involve the substrate/bioadhesive system sets during the trials. Artificial salivas viscosity was determined by means of Brookfield viscometer, showing the artificial saliva with mucin 10.0 cP, and the artificial saliva without mucin 7.5 cP. The tensile strength assays showed the following averages: for the group "artificial saliva with mucin" - 12.89 Pa, and for the group "without mucin" - 12.35 Pa. Statistical analysis showed no significant difference between the assays for both artificial salivas, and it was possible to conclude that the variable mucin did not interfered with the bioadhesion process for the polymeric devices. The device was able to release fluoride in a safe, efficient and constant way up to 8 hours.


Los sistemas bioadhesivos poliméricos intra-bucales pueden permanecer adheridos a los tejidos blandos orales para una liberación programada de fármacos, con finalidad preventiva y/o propósito terapéutico han sido empleados en diversas situaciones clínicas. Un sistema basado en Hidroxipropilmetilcelulosa/Carbopol934Ô/ estearato de magnesio (HPMC/Cp/StMg) fue desarrollado con fluorato de sodio como principio activo. Este tipo de sistema fue evaluado de acuerdo a su resistencia a la eliminación física por medio de pruebas de resistencia a la tracción. Mucosas bucales de cerdos fueron tomadas inmediatamente después del sacrificio de los animales y se utilizaron como sustrato para las pruebas físicas, obteniendo 16 cuerpos de prueba. Saliva artificial con o sin mucina fue utilizada para participar como parte del sistema sustrato/bioadesivo durante los ensayos. La viscosidad de la saliva artificial, se determinó mediante un viscosímetro Brookfield, mostrando la saliva artificial con mucina 10,0 cP y saliva artificial sin mucina 7,5 cP. Las pruebas de resistencia a la tracción mostraron los siguientes promedios: para la "saliva artificial con mucina" - 12,89 Pa, y para el grupo "sin mucina" - 12,35 Pa. El análisis estadístico no mostró diferencias significativas entre las pruebas de saliva artificial, y es posible concluir que la variable de mucina no interfiere con el proceso de bioadhesión del dispositivo polimérico. El dispositivo fue capaz de liberar fluor de forma segura, eficiente y constante durante un máximo de hasta 8 horas.


Subject(s)
Animals , Male , Adult , Fluorine/analysis , Mouth Mucosa/anatomy & histology , Mouth Mucosa , Swine/anatomy & histology , Swine/classification , Swine/physiology , Tissue Conditioning, Dental/methods , Mucins/administration & dosage , Drug Delivery Systems/methods
4.
Braz. dent. sci ; 12(3): 20-25, jul.-set. 2009. ilus, tab
Article in English | LILACS, BBO | ID: lil-587924

ABSTRACT

This crossover study aimed to compare plaque removal efficiency of two manual toothbrushes with identical design, the exception being the pattern of bristle arrangement. Twenty-six subjects were selected following inclusion and exclusion criteria. Dental plaque was scored before and after seven days of use of each toothbrush (Sanifill Smooth® – T1 andSanifill Active Smooth® – T2) employing the Turesky Plaque Index. Plaque Index values were handled with parametrical statistics employing Analysis of Variance (p<0.05) and, later, the Tukey Test. At the end of the trial, each subject was asked which toothbrush they preferred. Results: plaque scores for toothbrush T1 were not statistically different from those for toothbrush T2. Subjects showed a distinct preference for toothbrush T1. Conclusion: there was no differencein terms of plaque removal when toothbrushes T1 and T2 were compared, although patients showed a higher preference for toothbrush T1. Thus the different toothbrushes bristles arrangements did not influence the dental plaque removal.


Este estudo cruzado se propôs a comparar a eficiência de remoção de placa dental de duas escovas manuais com modelos idênticos, exceto para o padrão da disposição das cerdas. Vinte e seis sujeitos foram selecionados de acordo com critérios de inclusão e exclusão. Placa dental foi mensurada antes e após sete dias de uso com cada uma das escovas (Sanifill Smooth® – T1 and Sanifill Active Smooth® – T2) utilizando-se o Índice de Placa de Turesky. No final do estudo, cada paciente foi questionado sobre qual a escova preferida. Os valores do Índice de Placa para T1 não foram estatisticamente diferentes para os da escova T2. Não houve diferença em termos de remoção de placa quando as escovas T1 e T2 foram comparadas, embora os pacientes tenham demonstrado grande preferência pela escova T1. Assim, as diferenças nas disposições das cerdas das escovas dentais manuais não influenciaram na remoção de placa dental.


Subject(s)
Humans , Male , Female , Dental Devices, Home Care , Toothbrushing , Oral Hygiene , Dental Plaque
5.
J. appl. oral sci ; 16(4): 271-274, July-Aug. 2008. tab
Article in English | LILACS | ID: lil-486495

ABSTRACT

For centuries, specific instruments or regular toothbrushes have routinely been used to remove tongue biofilm and improve breath odor. Toothbrushes with a tongue scraper on the back of their head have recently been introduced to the market. The present study compared the effectiveness of a manual toothbrush with this new design, i.e., possessing a tongue scraper, and a commercial tongue scraper in improving breath odor and reducing the aerobic and anaerobic microbiota of tongue surface. The evaluations occurred at 4 moments, when the participants (n=30) had their halitosis quantified with a halimeter and scored according to a 4-point scoring system corresponding to different levels of intensity. Saliva was collected for counts of aerobic and anaerobic microorganisms. Data were analyzed statistically by Friedman's test (p<0.05). When differences were detected, the Wilcoxon test adjusted for Bonferroni correction was used for multiple comparisons (group to group). The results confirmed the importance of mechanical cleaning of the tongue, since this procedure provided an improvement in halitosis and reduction of aerobe and anaerobe counts. Regarding the evaluated methods, the toothbrush's tongue scraper and conventional tongue scraper had a similar performance in terms of breath improvement and reduction of tongue microbiota, and may be indicated as effective methods for tongue cleaning.


Subject(s)
Adolescent , Adult , Female , Humans , Male , Middle Aged , Young Adult , Dental Devices, Home Care , Halitosis/therapy , Tongue/microbiology , Toothbrushing/instrumentation , Breath Tests , Bacteria, Aerobic/isolation & purification , Bacteria, Anaerobic/isolation & purification , Cross-Over Studies , Equipment Design , Saliva/microbiology , Young Adult
6.
Braz. oral res ; 22(1): 11-17, Jan.-Mar. 2008. ilus, tab
Article in English | LILACS | ID: lil-480577

ABSTRACT

Noncarious cervical lesions (NCCLs) are considered to be of multifactorial origin, normally associated with inadequate brushing. This study assessed the influence in vitro of simulated brushing on NCCL formation. Fifteen human premolars were submitted to brushing in the cementoenamel junction region, using hard-, medium- and soft-bristled brushes associated with a toothpaste of medium abrasiveness under a 200 g load, at a speed of 356 rpm for 100 minutes. The surface topography of the region was analyzed before and after brushing, by means of a laser interferometer, using "cut-off" values of 0.25 and considering roughness values in mm. The initial roughness (mm) results for dentin (D / bristle consistency: 1 - soft, 2 - medium and 3 - hard) were as follows: (D1) 1.25 ± 0.45; (D2) 1.12 ± 0.44; (D3) 1.05 ± 0.41. For enamel (E / bristle consistency: 1 - soft, 2 - medium and 3 - hard), the initial results were: (E1) 1.18 ± 0.35; (E2) 1.32 ± 0.25; (E3) 1.50 ± 0.38. After brushing, the following were the values for dentin: (D1) 2.32 ± 1.99; (D2) 3.30 ± 0.96; (D3) Over 500. For enamel, the values after brushing were: (E1) 1.37 ± 0.31; (E2) 2.15 ± 0.90; (E3) 1.22 ± 0.47. Based on the results of the ANOVA and Tukey statistical analyses (a = .05) it was concluded that soft, medium and hard brushes are not capable of abrading enamel, whereas dentin showed changes in surface roughness by the action of medium- and hard-bristled brushes.


Subject(s)
Humans , Dental Enamel , Dentin , Dentifrices/adverse effects , Tooth Abrasion/etiology , Toothbrushing/adverse effects , Analysis of Variance , Dental Devices, Home Care , Dentin/pathology , Hardness , Tooth Cervix/drug effects , Tooth Cervix/pathology , Toothpastes/adverse effects
7.
Arq. odontol ; 43(4): 137-143, out.-dez. 2007. tab
Article in Portuguese | LILACS, BBO | ID: lil-533413

ABSTRACT

Este estudo objetivou avaliar a capacidade de reprodução de detalhes presentes no molde por materiais de modelagem à base de gipsita Gesso pedra tipo IV, Durone, (Dentsply); Gesso pedra tipo IV, Fuji Rock EP,(GC); Gesso pedra tipo IV, Resinado Rock Plus, (Polidental); Gesso pedra tipo V, Durone, (Dentsply) epolímeros: resinas epóxicas Epoxiglass 1504, (Epoxiglass), resina epóxica Epoxiglass 1504 modificada com diatomita pura e silanizada. A resina e seu endurecedor foram carregados com diatomita numa relação de30%. A diatomita foi tratada com Silano Silquest A 187, (Crompton S/A). A resina modificada foi manipuladaem uma relação de 35%. Empregando-se silicona de adição Presidente (Kit de silicona leve e pesada, Coltène) realizaram-se três moldagens de uma matriz metálica com quatro hastes contendo sulcos dimensionados. Os corpos de prova foram analisados em microscópio óptico com aumento de 40 vezes (Measurescope Nikon, procedência Nippon Kogaru K. K.). Os resultados expressos por gessos e resinas foram analisados com o teste Variância e Tukey (p<0,05). Verificou-se que não há diferenças estatisticamente significantes entre os gessos e resinas analisadas. Concluiu-se que o carregamento da resina epóxica com diatomita ou com diatomita silanizada não reduz a sua capacidade em reproduzir detalhes presentes no molde. Com a metodologia empregada, não houve diferença entre gessos tipo IV e V e resina epóxica pura ou modificada com diatomita na capacidadede reprodução de detalhes presentes no molde.


Subject(s)
Dental Impression Materials/analysis , Epoxy Resins/analysis , Calcium Sulfate/analysis , Analysis of Variance , Data Interpretation, Statistical
8.
J. appl. oral sci ; 15(2): 120-126, Mar.-Apr. 2007. tab, ilus
Article in English | LILACS | ID: lil-452768

ABSTRACT

OBJECTIVE: The aim of this study was to assess the bond strength of indirect composite restorations cemented with a resin-based cement associated with etch-and-rinse and self-etching primer adhesive systems to dentin treated or not with a bioactive material. MATERIALS AND METHOD: Twenty bovine incisor crowns had the buccal enamel removed and the dentin ground flat. The teeth were assigned to 4 groups (n=5): Group I: acid etching + Prime & Bond NT (Dentsply); Group II: application of a bioactive glass (Biosilicato®)+ acid etching + Prime & Bond NT; Group III: One-up Bond F (J Morita); Group IV: Biosilicato® + One-up Bond F. Indirect composite resin (Artglass, Kulzer) cylinders (6x10mm) were fabricated and cemented to the teeth with a dual-cure resin-based cement (Enforce, Dentsply). After cementation, the specimens were stored in artificial saliva at 37°C for 30 days and thereafter tested in tensile strength in a universal testing machine (EMIC) with 50 kgf load cell at a crosshead speed of 1 mm/min. Failure modes were assessed under scanning electron microscopy. Data were analyzed statistically by ANOVA and Tukey's test (95 percent level of confidence). RESULTS: Groups I, II and III had statistically similar results (p>0.05). Group IV had statistically significant higher bond strength means (p<0.05) than the other groups. The analysis of the debonded surfaces showed a predominance of adhesive failure mode for Group III and mixed failure mode for the other groups. CONCLUSION: The use of desensitizing agent did not affect negatively the bonding of the indirect composite restorations to dentin, independently of the tested adhesive systems.

9.
Rev. odontol. UNESP ; 36(1): 1-8, jan.-mar. 2007. tab
Article in Portuguese | LILACS, BBO | ID: lil-529245

ABSTRACT

Este estudo avaliou a rugosidade superficial dos gessos Tipo IV e V e de uma resina epóxica pura e uma carregada com zirconita. Para a análise da rugosidade, os polímeros e os gessos foram vertidos em matrizes hexagonais apoiadas em lâmina de vidro, permitindo, após endurecimento dos materiais, três leituras em cada corpo-de-prova. Este estudo também avaliou a compatibilidade do polímero puro e da resina carregada com zirconita quando em contato com materiais elastoméricos utilizando dois critérios: aderência do molde e alteração na coloração do modelo. Para a análise da compatibilidade, os polímeros foram colocados em contato com quatro diferentes elastômeros e, após endurecimento dos materiais, realizou-se a inspeção com lupa de quatro aumentos. A resina foi 100% compatível com os materiais de moldagem. Com análise de variância e teste Tukey com significância 5%, verificou-se que não há diferença entre o gesso IV e o gesso V e que não há diferença entre a resina epóxica pura e a modificada com zirconita. Na comparação entre gessos e resinas, verificou-se que há diferença estatisticamente significante. Concluiu-se que: a adição de zirconita na proporção de 1/1 em peso na resina epóxica Epoxiglass 1504 e no endurecedor Epoxiglass 1603 proporcionou um material resinoso para obtenção de modelos compatível com os elastômeros mercaptana, poliéter, silicona de condensação e de adição; quando comparada aos gessos tipos IV e V, a resina epóxica Epoxiglass 1504 possibilitou obtenção de modelos com superior lisura superficial; a adição de zirconita na proporção de 1/1 na resina epóxica não comprometeu sua lisura superficial.


This study evaluated the surface roughness of Type IV and V dental plasters and epoxy resin with and without zirconite filler. To analyze the roughness, the polymers and plasters were poured into hexagonal dies supported on a sheet of glass, allowing, after hardening of the materials, for three readings of each test specimen. An evaluation was also made of the compatibility of this polymer, with and without zirconite filler, when in contact with elastomeric materials, based on two criteria: adherence of the die and alteration in the color of the model. To analyze the compatibility, the polymers were put into contact with four different elastomers and, after the materials hardened, they were examined with a magnifying glass with four times magnification. The resin was found to be 100% compatible with the molding materials. A variance analysis and Tukey’s test with 5% significance indicated that there was no difference between the IV and the V plasters, and that there was no difference between the pure epoxy resin and resin modified with zirconite. A comparison between plasters and resins revealed a statistically significant difference. It was concluded that the addition of zirconite in a 1:1 wt ratio to Epoxyglass 1504 resin and to Epoxyglass 1603 hardener produced a resinous material suitable for producing models compatible with the elastomers mercaptan, polyether, condensation silicone and silicone additive. When compared with the IV and V type plasters, the resinous epoxy Epoxyglass 1504 produced models with superior surface smoothness. The addition of zirconite in a proportion of 1:1 to epoxy resin did not affect the surface smoothness.


Subject(s)
Elastomers , Models, Dental , Epoxy Resins , Calcium Sulfate
10.
Rev. ABO nac ; 14(6): 364-367, dez. 2006-jan. 2007.
Article in Portuguese | LILACS, BBO | ID: lil-544424

ABSTRACT

A ampla ação que os dentifrícios têm na promoção de saúde bucal de crianças, jovens, adultos e idosos é reflexo de sua formulação básica e dos agentes terapêuticos e cosméticos veiculados. Juntamente com a escova dental é o dispositivo mais usado mundialmente nos procedimentos de higiene bucal. Assim, os dentifrícios despertam interesse no mercado, pacientes e profissionais de saúde. O bom entendimento da formulação básica dos dentifrícios e das opções terapêuticas e cosméticas é essencial para o cirurgião-dentista envolvido com a orientação sobre saúde bucal dos seus pacientes.


Dentifrices have a broad action on the oral health of children, adolescents, adults and elderly due to their basic formulation and the incorporation of therapeutics and cosmetics agents. Together, dentifrices and toothbrushes, are the most common devices used in oral hygiene. For this reason, they are interesting for the manufacturers, patients and dentists. The knowledge about basic dentifrices formulation as well as their therapeutic choices is essential to dentistry involved with oral health education.


Subject(s)
Dentifrices/analysis , Dentifrices/chemical synthesis , Oral Health , Oral Hygiene
11.
Braz. oral res ; 21(4): 323-329, 2007. tab
Article in English | LILACS | ID: lil-467977

ABSTRACT

This study evaluated in vitro the antimicrobial activity of irreversible hydrocolloids (one containing an antimicrobial agent) prepared with water or with a 0.2 percent chlorhexidine digluconate solution against 12 strains of the oral microbiota. Twenty specimens (0.5 x 1.0 cm) for each group (1. Jeltrate mixed with water; 2. Jeltrate mixed with 0.2 percent chlorhexidine digluconate solution; 3. Greengel mixed with water; 4. Greengel mixed with 0.2 percent chlorhexidine digluconate solution) were prepared under sterile conditions and placed in culture media inoculated with the indicator strains. After incubation in aerobiosis or microaerophilia, inhibition of the microbial growth was measured and the results were interpreted. The normal adherence curve revealed a non-normal distribution of the data, so the non-parametric Friedman Test was performed (p < 0.05). The antimicrobial activity of the groups was classified in the following order: 1, 3, 4, and 2. The results suggest that the method of preparing irreversible hydrocolloids with a 0.2 percent digluconate chlorhexidine solution is more effective than the incorporation of an antimicrobial agent in the powder to reduce cross-contamination caused by impressions.


Este trabalho avaliou in vitro a atividade antimicrobiana de alginatos (um deles contendo agente antimicrobiano) manipulados com água ou solução de digluconato de clorexidina a 0,2 por cento contra 12 cepas da microbiota oral. Vinte espécimes (0,5 x 1,0 cm) para cada grupo (1. Jeltrate manipulado com água, 2. Jeltrate manipulado com solução de digluconato de clorexidina a 0,2 por cento; 3. Greengel manipulado com água; 4. Greengel manipulado com solução de digluconato de clorexidina a 0,2 por cento) foram confeccionados sob condições estéreis e semeados em meios de cultura inoculados com as cepas indicadoras. Após incubação em aerobiose ou microaerofilia, a inibição do crescimento microbiano foi medida e os resultados foram interpretados. A curva normal de aderência revelou uma distribuição não-normal dos dados, então o teste não paramétrico de Friedman (p < 0,05) foi realizado. A atividade antimicrobiana dos grupos foi classificada na seguinte ordem crescente: 1, 3, 4 e 2. Os resultados sugerem que a manipulação de alginatos com solução de digluconato de clorexidina a 0,2 por cento é um método efetivo para reduzir a contaminação-cruzada causada pelos moldes, mais que a incorporação do agente antimicrobiano no pó.


Subject(s)
Alginates/pharmacology , Anti-Infective Agents, Local/pharmacology , Bacteria/drug effects , Chlorhexidine/pharmacology , Dental Impression Materials/pharmacology , Disinfectants/pharmacology , Colloids , Drug Evaluation, Preclinical , Dental Casting Technique/standards , Statistics, Nonparametric
12.
Acta odontol. venez ; 45(2): 255-258, 2007. ilus, tab
Article in Spanish | LILACS | ID: lil-499556

ABSTRACT

Este estudio pretendió evaluar el comportamiento de resistencia a la tensión de modelos odontológicos obtenidos a partir de una resina epóxica de uso industrial modificada con circonita. A la resina Epoxiglass 1504 y el endurecedor Epoxiglass 1603 les fue adicionada circonita en una proporción de 1 para 1 en peso; modificada de esta manera fue manipulada siguiendo las instrucciones del fabricante, el cual establece una proporción de 35 por ciento en peso entre la resina y el endurecedor. Fueron realizadas 15 impresiones de un modelo matriz, utilizando silicona de adición, siendo vaciados con Epoxiglass 1504, Epoxiglass 1504 modificada y Yeso Piedra tipo IV, obteniéndose 60 cuerpos de prueba en total. Las características de los mismos fueron: 12 mm. de altura y 6.0 mm. de diámetro. Los cuerpos de prueba fueron divididos en dos grupos de 30 cada uno, de estos uno de ellos fue sometido al ensayo mecánico de compresión y el otro al de tracción por compresión diametral, utilizando una máquina universal de ensayos DL2000 EMIC, con una célula de carga de 2000kgf y velocidad de 0,5mm/min. Los resultados fueron analizados con el análisis estadístico ANOVA y comprobación con el test de Tuckey con grado de exactitud de 5 por ciento verificando que: los modelos de resina epóxica Epoxiglass 1504 mostraron resistencia a compresión y resistencia a tracción por compresión diametral superior a los modelos de yeso tipo IV; la circonita aumenta la resistencia a tracción por compresión diametral de la resina Epoxiglass 1504. Frente a estos resultados, se puede concluir que la resina epoxica Epoxiglass 1504 se presenta como un material viable para la obtención de modelos odontológicos, así como también, que la circonita mejoró comportamiento mecánico del material en relación a las propiedades mecánicas estudiadas.


This study evaluated the tensil behavior of dental models obtained using an industrial epoxic resin modified with zirconita. The Epoxiglass resin 1504 and the hardener Epoxiglass 1603 were added with zirconita in a ratio of 1/1 in weight. The modified resin was manipulated in accordance with the manufacturer's specifications, which establishes a relation of 35% in weight between the resin and the hardener. Fifteen moldings of a matrix were conducted using addition silicone. Then, they were filled with epoxic resin Epoxiglass 1504, resin Epoxiglass 1504 modified or type IV Durone plaster, which provided 60 test specimens with 12mm of height and 6mm of diameter. Thirty specimens were submitted to the compression assay and thirty to the traction assay by diametrical compression, using the universal machine DL2000 (EMIC), with a load cell of 2000 Kgf and 0,5mm/mim speed. The results were analyzed by Variance analysis followed by Tukey test with significance level set at 5%. It was verified that models made of Epoxiglass 1504 presented superior tensile strenght for diametrical compression and also superior compressive strength than models made of plaster type IV. The zirconita increased the tensile strenght for diametrical compression of the epoxic resin Epoxiglass 1504. In accordance to the present results, it was verified that the epoxic resin Epoxiglass 1504 is a viable material for dental modeling and that the zirconita provides mechanical benefit for the epoxic resin.


Esse estudo avaliou o comportamento tensil de modelos odontológicos obtidos a partir de uma resina epóxica de uso industrial modificada com zirconita. A resina Epoxiglass 1504 e o endurecedor Epoxiglass 1603 foram carregados com zirconita numa proporção de 1/1 em peso. A resina modificada foi manipulada de acordo com as especificações do fabricante, que estabelece uma relação de 35% em peso entre a resina e o endurecedor. Foram realizadas quinze moldagens de uma matriz, os moldes foram obtidos com silicone de adição e preenchidos com resina epóxica Epoxiglass 1504, resina Epoxiglass 1504 modificada e gesso tipo IV Durone, o que proporcionou 60 corpos de prova com 12mm de altura e 6mm de diâmetro. Trinta corpos de prova foram submetidos ao ensaio de compressão e trinta ao ensaio de tração por compressão diametral, empregando-se a máquina universal de ensaios DL2000 da EMIC, com célula de carga de 2000Kgf e velocidade de 0,5mm/mim. Os resultados foram analisados com Teste de Variância e Tukey com significância de 5%, e verificou-se que: Modelos obtidos em resina epóxica Epoxiglass 1504 apresentam superior resistência à tração por compressão diametral que modelos obtidos em gesso tipo IV; Modelos obtidos em resina epóxica Epoxiglass 1504 apresentam superior resistência à compressão que modelos obtidos em gesso tipo IV; A zirconita aumenta a resistência à tração por compressão diametral da resina epóxica Epoxiglass 1504. Diante dos resultados encontrados, verificou-se que a resina epóxica Epoxiglass 1504 apresenta-se como material viável para a modelagem odontológica e que a zirconita proporciona ganho mecânico para a resina epóxica.


Subject(s)
Compressive Strength , Models, Dental , Polymers/chemistry , Epoxy Resins/chemistry , Tensile Strength , Analysis of Variance , Zirconium/chemistry , Materials Testing , Data Interpretation, Statistical , Calcium Sulfate/chemistry
13.
Braz. oral res ; 21(2): 106-111, 2007. tab
Article in English | LILACS | ID: lil-453188

ABSTRACT

This study assessed the level of contamination of six commercially available irreversible hydrocolloids (two containing chlorhexidine) and identified the contamination present in the materials. Petri dishes containing selective and enriched culture media were inoculated with alginate powder (0.06 g), in triplicate. After incubation (37°C/7 days), the colony-forming units (CFU) were counted and Gram stained. Biochemical identification of the different morphotypes was also performed. The contamination levels for the materials were: Jeltrate - 389 CFU/g; Jeltrate Plus - 516 CFU/g; Jeltrate Chromatic - 135 CFU/g; Hydrogum - 1,455 CFU/g; Kromopan - 840 CFU/g; and Greengel - 59 CFU/g. Gram staining revealed the presence of Gram-positive bacillus and Gram-positive cocci. The bacteria Staphylococcus epidermidis, Bacillus subtilis, Bacillus sp., Bacillus coagulans, Bacillus licheniformis, Bacillus cereus, Micrococcus luteus, and Nocardia sp.; the filamentous fungi Aspergillus niger, Aspergillus flavus, Rhizopus sp., Neurospora sp.; and the yeast Candida sp. were isolated. The contamination detected in the impression materials points out the need for adopting measures to improve the microbiological quality of these materials. The use of contaminated materials in the oral cavity goes against the basic principles for controlling cross-contamination and may represent a risk for debilitated or immunocompromised patients.


Este estudo avaliou o nível de contaminação de seis marcas comerciais de alginato (duas contendo clorexidina) e identificou a contaminação presente nesses materiais. Alíquotas de alginato (0,06 g) foram semeadas em meios de cultura seletivos e enriquecidos, em triplicata. Após incubação (37°C/7 dias), as unidades formadoras de colônia (UFC) foram contadas e foram realizadas as identificações morfotintorial (Gram) e bioquímica. Os níveis de contaminação dos materiais foram: Jeltrate - 389 UFC/g; Jeltrate Plus - 516 UFC/g; Jeltrate Chromatic - 135 UFC/g; Hydrogum - 1.455 UFC/g; Kromopan - 840 UFC/g; e Greengel - 59 UFC/g. A coloração de Gram revelou a presença de bacilos Gram-positivos e cocos Gram-positivos. As bactérias Staphylococcus epidermidis, Bacillus subtilis, Bacillus sp., Bacillus coagulans, Bacillus licheniformis, Bacillus cereus, Micrococcus luteus e Nocardia sp.; os fungos filamentosos Aspergillus niger, Aspergillus flavus, Rhizopus sp., Neurospora sp.; e a levedura Candida sp. foram isolados. A contaminação detectada nos materiais aponta a necessidade de adoção de medidas para melhorar seu controle de qualidade microbiológica. O uso de materiais contaminados na boca contradiz os princípios básicos de controle de infecção-cruzada e pode representar um risco para pacientes debilitados ou imunocomprometidos.


Subject(s)
Colloids , Dental Impression Materials , Drug Contamination , Fungi/isolation & purification , Gram-Positive Bacteria/isolation & purification , Yeasts/isolation & purification , Cross Infection/prevention & control , Dental Equipment/microbiology , Gram-Positive Cocci/isolation & purification , Microbiological Techniques
14.
Rev. odonto ciênc ; 21(53): 207-211, jul.-set. 2006. ilus, tab
Article in Portuguese | LILACS, BBO | ID: lil-457359

ABSTRACT

Este trabalho comparou os tempos de presa inicial e final e as resistências à tração diametral e compressão de gessos utilizados em odontologia (natural, sintético e reforçado com resina). Os ensaios mecânicos foram realizados nos tempos de 1h e 24h após a manipulação, sendo os resultados submetidos à análise estatística (Anova two way. Thckey P < 0.05). As partículas foram analisadas em microscópio eletrônico de varredura, procurando-se estabelecer correlações com as propriedades avaliadas. Observou-se que o gesso natural possui propriedades mecânicas superiores e maior tempo de presa que os demais. As partículas do mesmo material se apresentaram maiores que as dos outros gessos, sendo as do gesso reforçado com resina as menores de todas. Conclui-se que há relação direta entre o tamanho das partículas e as propriedades avaliadas, como pode ser observado, por exemplo, para o gesso natural (maiores partículas e maiores valores nos testes realizados).


Subject(s)
Dental Impression Materials , Calcium Sulfate , Microscopy, Electron, Scanning , Tensile Strength
15.
RBCF, Rev. bras. ciênc. farm. (Impr.) ; 42(1): 29-47, jan.-mar. 2006. tab
Article in Portuguese | LILACS | ID: lil-431421

ABSTRACT

A doença periodontal é morbidade com alta prevalência na população mundial. É causada pelo acúmulo de componentes microbianos do biofilme dental no interior das áreas subgengivais do periodonto, desencadeando processo inflamatório que afeta as estruturas de suporte dental, resultando em formação de bolsa periodontal e perda dos dentes, se não tratada. O tratamento convencional consiste de raspagem e alisamento radicular, associado ou não ao uso de antimicrobianos de ação sistêmica, o que implica altas doses, porém com eficácia reduzida, efeitos adversos e dificuldades de adesão ao tratamento por parte do paciente. Nas últimas décadas, o tratamento tem sido otimizado pelo uso de sistemas de liberação de fármaco intrabolsa periodontal, com a vantagem de liberar o fármaco no local de ação, possibilitando prolongar e/ou controlar sua concentração. A presente revisão aborda os principais sistemas de liberação de fármaco intrabolsa periodontal, o potencial de utilização, assim como os protocolos disponíveis para a avaliação da efetividade dos mesmos na terapia periodontal.


Subject(s)
Drug Delivery Systems , Periodontal Diseases/epidemiology , Oral Health , Periodontal Pocket
16.
Braz. dent. j ; 17(3): 191-194, 2006. tab
Article in English | LILACS | ID: lil-442365

ABSTRACT

During fabrication of bonded ceramic restorations, cervical adaptation, occlusal adjustment and final finishing/polishing are procedures to be performed at the dental office after adhesive cementation. Final adjustments may result in loss of ceramic glaze, which requires new polishing of the ceramic surface, with special attention for selection of adequate materials and instruments. The purpose of this study was to evaluate the efficiency of different vehicles associated with diamond pastes indicated for dental ceramic polishing. Two polishing pastes (Crystar Paste and Diamond Excell) associated with four vehicles (rubber cup, Robinson bristle brush, felt wheel and buff disc) were evaluated. Disc-shaped specimens were fabricated from Ceramco II dental ceramic. Surface roughness means (Ra) of the ceramic specimens were determined with a rugosimeter. Data were analyzed statistically by two-way ANOVA and Tukey's test at 5 percent significance level. There was no statistically significant difference (p>0.01) between the polishing pastes. However, there were statistically significant differences (p<0.01) among the tested vehicles. Vehicle-paste interaction showed statistically significant difference (p<0.05) as well. It may be concluded that: 1) Robinson bristle brush, felt wheel and buff disc were efficient vehicles to be used in association with a diamond polishing paste; 2) The use of rubber cup as a vehicle showed poor efficiency for mechanical polishing of the ceramic surfaces; 3) Both pastes provided similar and efficient polishing and may be recommended for use with an appropriated vehicle.


Durante a confecção de restaurações de cerâmica aderidas, a adaptação cervical, o ajuste oclusal e o polimento/acabamento final são procedimentos a serem executados no consultório odontológico após a cimentação adesiva. Os ajustes finais podem resultar na perda do "glaze" da cerâmica, o que requer novo polimento da superfície da restauração, necessitando de atenção especial em relação aos materiais e instrumentos adequados. O objetivo deste estudo foi avaliar a eficiência de diferentes veículos associados a pastas diamantadas indicadas para polimento de cerâmicas odontológicas. Duas pastas de polimento diamantadas (Crystar Paste and Diamond Excell) associadas a quatro veículos (taça de borracha, escova de Robinson, roda de feltro e disco de feltro) foram avaliadas. A cerâmica Ceramco II foi selecionada para a confecção dos espécimes. A rugosidade superficial (Ra) dos espécimes de cerâmica foi determinada por um rugosímetro. Os dados foram submetidos a análise de variância a dois critérios e ao teste de Tukey com nível de significância de 5 por cento. Não houve diferença estatisticamente significante (p>0,01) entre as pastas de polimento avaliadas. Contudo, houve diferença significante (p<0,01) entre os veículos. A interação veículo-pasta revelou diferença significante (p<0,05). Conlcuir que: 1) A escova de Robinson, a roda de feltro e o disco de feltro foram veículos efetivos para serem usados em associação com as pastas de diamante; 2) O uso da taça de borracha como veículo foi menos eficiente para o polimento mecânico das superfícies cerâmicas; 3) Ambas as pastas de polimento apresentaram comportamento similar e eficiente e podem ser indicadas para o polimento final de restaurações cerâmicas com um veículo apropriado.


Subject(s)
Humans , Dental Materials/chemistry , Dental Polishing/methods , Dental Porcelain/chemistry , Diamond/chemistry , Aluminum Silicates/chemistry , Dental Polishing/instrumentation , Equipment Design , Materials Testing , Potassium Compounds/chemistry , Surface Properties
17.
Braz. dent. j ; 17(1): 24-28, 2006. ilus, tab
Article in English | LILACS | ID: lil-430128

ABSTRACT

A resistência da união metal/porcelana tem um importante papel na subistituição das ligas de ouro por ligas à base de níquel-cromo na Odontologia. Este estudo avaliou a resistência da união metal/porcelana de três sistemas cerâmicos (Vita VMK 88, Williams e Duceram) em combinação com três ligas metálicas à base de níquel-cromo (Durabond, Lite Cast B e Resistal P) e uma liga experimental à base de cobalto-cromo-titânio. Trinta corpos-de-prova cilíndricos (15 mm de altura; 6 mm de diâmetro) foram obtidos para cada liga, sendo 10 corpos-de-prova de cada liga testados com cada uma das porcelanas. A resistência de união foi calculada utilizando uma máquina EMIC aplicando uma força de cisalhamento paralela ao corpo-de-prova até a fratura. Os testes de Kruskal-Wallis e U de Mann-Whitney foram usados para a análise estatistica das interações metal/porcelana (p<0,05). A combinação Duceram/Resistal P apresentou resistência de união significantemente maior (44,38±9,12 MPa) (p<0,05) que as outras combinações, exceto a associaçãoVita VMK 88/liga experimental Co-Cr-Ti (38,41±12,64 MPa). A combinção da liga de Co-Cr-Ti com o sistema cerâmico Williams teve resistência ao cisalhamento significantemente maior que a combinação das outras ligas com a mesma porcelana (28,20±3,86 MPa) (p<0,05). Com base nestes resultados e dentro das limitações de um estudo in vitro, pode-se concluir que a resistência da união metal/porcelana dos três sistemas cerâmicos testados às ligas de Ni-Cr e Co-Cr-Ti variaram significativamente, mostrando que a compatibilidade metal/porcelana foi muito importante para esta união.


Subject(s)
Chromium Alloys/chemistry , Dental Alloys/chemistry , Dental Bonding/methods , Dental Porcelain/chemistry , Titanium/chemistry , Shear Strength , Statistics, Nonparametric
18.
JBC j. bras. clin. odontol. integr ; 9(50/51): 234-243, jul.-dez. 2005. ilus, tab, graf, CD-ROM
Article in Portuguese | LILACS, BBO | ID: biblio-851622

ABSTRACT

As ligas de metais são muito úteis na Odontologia e de grande importância na confecção de coroas metalocerâmicas, para as quais a resistência, adaptação e estética são fatores primordiais. Ligas de Ni-Cr possuem alta resistência a corrosão, assim, elas apresentam grande importância e indicação para esse tipo de restauração. Existem muitas possibilidades de se combinar ligas de Ni-Cr com outros diferentes metais. Consequentemente, são necessários estudos para se conhecer o seu comportamento diante de cada combinação e sua utilidade naquelas condições. No presente trabalho, avaliou-se a resistência da união de quatro sistemas cerâmicos em quatro ligas de Ni-Cr diferentes, duas delas incluindo titânio. Para experimento de resistência, utilizou-se o teste de Shell e Nielsen, modificado por Chiodi Netto. Os resultados mostraram que ligas de Ni-Cr com titânio podem ser indicadas para uso clínico, com relação à adesão metal/porcelana


Subject(s)
Chromium Alloys , Dental Porcelain , Metal Ceramic Alloys , Dental Alloys , Titanium
19.
Braz. dent. j ; 16(3): 202-206, set. -dez. 2005. ilus, tab
Article in English | LILACS | ID: lil-419843

ABSTRACT

Devido ao contínuo avanço tecnológico e crescente disponibilidade de novas ligas não-nobres e sistemas cerâmicos no mercado, e também à prática clínica diária, a constante avaliação da resistência de união das combinações metal/porcelana tornou-se necessária. Este estudo avaliou a resistência da união metal/porcelana de três sistemas cerâmicos (Duceram, Williams e Noritake) em combinação com três ligas à base de níquel-cromo (Ni-Cr) (Durabond, Verabond e Viron). Trinta cilindros fundidos (15 mm de altura; 6 mm de diâmetro) foram obtidos para cada liga e 10 espécimes de cada liga foram testados com cada porcelana. A resistência de união foi calculada utilizando uma máquina EMIC aplicando uma força de cisalhamento paralela ao corpo-de-prova até a fratura. A resistência ao cisalhamento foi calculada usando a força aplicada dividida pela área de superfícia da camada de opaco. O teste U de Mann-Whitney foi empregado para a análise estatistica das interações metal/porcelana (p<0,05). Viron/Noritake apresentou a maior média de resistência adesiva (32,93 MPa), enquanto Verabond/Duceram apresentou a menor média (16,31 MPa). Viron/Noritake diferiu estatisticamente das demais combinações (p<0,05). Viron/Duceram apresentou média estatisticamente maior que Verabond/Duceram, Verabond/Williams e Durabond/Noritake (p<0,05). Houve diferença significante (p<0.05) também entre Verabond/Noritake, Verabond/Duceram e Durabond/Noritake. Não houve diferença estatisticamente significante entre as demais combinações (p>0,05). Em conclusão, o sistema cerâmico Noritake utilizado em associação com a liga Viron apresentou a maior resistência às forças de cisalhamento, enquanto o sistema Duceram em combinação com a liga Verabond apresentou a menor média de resistência ao cisalhamento. Viron/Duceram e Verabond/Noritake promoveram resultados intermediários. As combinações entre o sistema cerâmico Williams e as ligas de Ni-Cr apresentaram médias de resistência ao cisalhamento semelhantes entre si.


Subject(s)
Dental Alloys , Metal Ceramic Alloys , Nickel , Chromium Alloys , Shear Strength , Data Interpretation, Statistical
20.
Rev. ABO nac ; 13(2): 86-91, abr.-maio 2005.
Article in Portuguese | LILACS, BBO | ID: biblio-872688

ABSTRACT

A própolis é uma resina produzida pelas abelhas melíferas a partir da coleta de exsudatos de várias fontes vegetais e que possui um amplo espectro de atividades biológicas. Vários grupos de pesquisadores têm estudado a utilização da própolis na Odontologia, e os artigos científicos relatam suas propriedades farmacológicas. Esse artigo revisa os resultados de estudos recentes da utilização de própolis na Periodontia. Também é discutido o desenvolvimento de formas farmacêuticas com própolis, para o uso na prevenção e tratamento de doenças periodontais...


Subject(s)
Periodontal Diseases/prevention & control , Propolis/therapeutic use
SELECTION OF CITATIONS
SEARCH DETAIL