ABSTRACT
Objective@#To investigate the clinical effect of lithium disilicate glass ceramic cantilever resin-bonded fixed partial dentures (CRBFPDs) on single anterior tooth loss to provide a reference for the selection of restoration methods for single anterior tooth loss.@*Methods@#This study was reviewed and approved by the Ethics Committee, and informed consent was obtained from the patients. Forty-two patients with less than two anterior teeth with monomaxillary loss were included in this study. After 6 months, 1 year, 2 years, and 3 years, the aesthetic and functional effects of the restorations and the periodontal health status were evaluated, and the visual analog scale (VAS) was used to assess patient satisfaction.@*Results@#During the observation period, the connector fractured in one case within 3 months. One case had debonded within 2 years. The aesthetic restoration effect of all lithium disilicate glass ceramic CRBFPDs was categorized as Class A. The periodontal health was good, there was no clinical absorption in the soft and hard tissues of the abutment or subbridge, periodontal status according to the evaluation indices was classified as class A, and the total satisfaction rate of the patient was 100%.@*Conclusion@#For single anterior tooth loss patients, lithium disilicate glass ceramic cantilever resin-bonded fixed partial denture can achieve the restoration effect of less invasion, better adhesion, aesthetics, comfort and good biocompatibility. With high patient satisfaction, it can be considered an ideal restoration method for replacing a single anterior tooth.
ABSTRACT
Objective: The aim of this study was to evaluate the marginal gap of frameworks produced using the CAD-CAM system, from zirconia and lithium disilicate blocks, adapted to a tooth preparation and a gypsum die. Material and Methods: For this study, a human first molar tooth was used as a master model with a full crown preparation. It was molded 20 times to obtain the gypsum die and randomly divided into 2 groups (n=10) for the fabrication of zirconia and lithium disilicate frameworks. The frameworks were made using pre-sintered zirconia blocks and lithium disilicate blocks, both CAD-CAM systems. The marginal gap was measured in µm at four points (buccal, palatal, mesial, and distal) using a comparator microscope with 30x magnification, with the framework seated on the master model (tooth), and on the gypsum die. Marginal gap data (µm) were evaluated using two-way analysis of variance and Tukey's test with a significance level of 5%. Results: The results showed that there was no statistically significant interaction between the factors studied (p=0.223) or isolated factors (ceramic factor p=0.886 and die factor p=0.786). Conclusion: Both ceramics produced using the CAD-CAM technique did not exhibit statistical differences in marginal adaptation on the two types of substrates, both on tooth preparation and on the gypsum die (AU)
Objetivo: O objetivo deste estudo foi avaliar o espaço marginal de estruturas produzidas usando o sistema CAD-CAM, a partir de blocos de zircônia e dissilicato de lítio, adaptadas a um preparo sobre dente e a um troquel de gesso. Material e Métodos: Para este estudo, um dente molar humano foi utilizado como modelo mestre com preparo para coroa total. Este foi moldado 20 vezes para obter o troquel de gesso e dividido aleatoriamente em 2 grupos (n=10) para a fabricação de estruturas de zircônia e dissilicato de lítio. As estruturas foram feitas usando blocos de zircônia pré-sinterizados e blocos de dissilicato de lítio, ambos sistemas para CAD-CAM. O espaço marginal foi medido em µm, em quatro pontos (bucal, palatal, mesial e distal), utilizando um microscópio comparador com ×30 de ampliação e com a estrutura assentada no modelo mestre (dente) e no troquel de gesso. Os dados de espaço marginal (µm) foram avaliados usando análise de variância bidirecional e teste de Tukey com um nível de significância de 5%. Resultados: Os resultados mostraram que não houve interação estatisticamente significativa entre os fatores estudados (p=0,223) ou isoladamente (fator cerâmica p=0,886 e fator troquel p=0,786). Conclusão: Ambas as cerâmicas produzidas usando a técnica CAD-CAM não apresentaram diferenças estatísticas em relação à adaptação marginal nos dois tipos de substratos, tanto na preparação dentária quanto no troquel de gesso(AU)
Subject(s)
Dental Prosthesis , Computer-Aided Design , Dental Marginal Adaptation , Dental PorcelainABSTRACT
Abstract This study evaluated the effect of different firing protocols on the surface roughness and flexural strength of CAD/CAM lithium disilicate glass-ceramic (LD) after aging methods. Forty-two LD bars of 16 x 4 x 2 mm (IPS e-max CAD, Ivoclar) were randomly separated into two groups according to firing protocols: Single firing-Staining, glazing, and crystallization in a single step; Multiple firings-Crystallization+First staining+Firing+Second staining+Firing+Glazing+Firing. After protocols, initial surface roughness readings were taken (Surfcorder SE1700, Kosakalab). Samples were then randomly separated into three groups (n=7) according to the aging methods they were submitted: Thermomechanical cycling (TMC, ER System, Erios, 1,200,000 cycles, 0.3 MPa, 2 Hz and 5°C/37°C/55°C, 30 s swell time); Simulated toothbrushing (STB, Pepsodent, MAVTEC, 73,000 cycles), and Control (no aging). Final surface roughness readings were done, and samples were submitted to a three-point bending test (OM100, Odeme Dental Research) and fractographic analysis by scanning electron microscopy (EVO-MA10, ZEISS). Data were analyzed (2-way ANOVA, (α=.05). There was no difference (p>.05) in the flexural strength between the firing protocols, regardless of the aging method. STB decreased the flexural strength of samples submitted to multiple firings, different from control (p<.05). Without aging (Control), before TMC, and after STB, LD had lower surface roughness when submitted to multiple firings than to single firing (p<.05). The firing protocols did not affect the flexural strength or the surface roughness of the lithium disilicate glass-ceramic, even after aging. However, toothbrushing negatively affected the flexural strength and smoothed the surface of the ceramic submitted to multiple firings.
Resumo Este estudo avaliou o efeito de diferentes protocolos de queima na rugosidade de superfície e resistência à flexão de uma cerâmica vítrea de dissilicato de lítio (DL) para CAD/CAM, após métodos de envelhecimento. Quarenta e dois barras de DL (IPS e-max CAD, Ivoclar) de 16 x 4 x 2 mm foram separadas aleatoriamente em dois grupos de acordo com os protocolos de queima: Single firing-Pigmentação, glazeamento e cristalização em única etapa. Multiple firings-Cristalização+Primeira camada do pigmento+Queima+Segunda camada do pigmento+Queima+Glazeamento+Queima. Após os protocolos, foram realizadas leituras iniciais de rugosidade de superfície (Surfcorder SE1700, Kosakalab). As amostras foram então separadas aleatoriamente em três grupos (n=7) segundo o método de envelhecimento a que foram submetidas: Ciclagem termomecânica (CTM, Sistema ER, Erios, 1.200.000 ciclos, 0.3 MPa, 2 Hz e 5°C/37°C/55°C, 30 s de imersão), Escovação simulada (ES, Pepsodent, MAVTEC, 73.000 ciclos) e Controle (sem envelhecimento). Leituras finais de rugosidade foram realizadas, e as amostras foram submetidas ao ensaio de resistência à flexão em três pontos (OM100, Odeme Dental Research) e à análise fractográfica por microscopia eletrônica de varredura (EVO-MA10, ZEISS). Os dados foram analisados (ANOVA de dois fatores, (α=.05). Não houve diferença (p>.05) na resistência à flexão entre os protocolos de queima, independente do envelhecimento. ES diminuiu a resistência à flexão das amostras submetidas a multiple firings, diferente do controle (p<.05). Sem envelhecimento (Controle), antes da CTM e após ES, LD apresentou menor rugosidade de superfície quando submetido a multiple firings do que a single firing (p<.05). Os protocolos de queima não afetaram a resistência à flexão nem a rugosidade de superfície da cerâmica vítrea de dissilicato de lítio, mesmo após envelhecimento. No entanto, a escovação afetou negativamente a resistência à flexão e poliu a superfície da cerâmica submetida a multiple firings.
ABSTRACT
Mediante este caso se describen los criterios de selección del color en restauraciones indirectas con disilicato de litio en el sector anterior. Mujer de 34 años, atendida en la Facultad de Odontología de la Universidad Nacional de Concepción (FOUNC), Paraguay, por una preocupación estética del sector anterior, en especial la diferencia de color de las piezas dentarias. La rehabilitación consistió en la confección de coronas de disilicato de litio de las piezas 11, 12, 13, 14, 21, 22, 24, 25 y laminado para carillas de la pieza 23. Fueron aplicadas técnicas de selección de color individualizadas, pruebas de color y cementación antes del cementado final para obtener resultados altamente estéticos. Gracias a los resultados fue posible observar la conjunción de factores como la correcta selección del color del sustrato dentario, el cemento resinoso, el material de restauración y la comunicación eficiente con el laboratorio, fundamental para el éxito del tratamiento.
This case describes the color selection criteria for indirect lithium disilicate restorations in the anterior sector. A 34-year-old woman treated at the Faculty of Dentistry of the National University of Concepción (FOUNC), Paraguay, due to an aesthetic concern in the anterior sector, especially the difference in color of the teeth. The rehabilitation consisted of making lithium disilicate crowns for teeth 11, 12, 13, 14, 21, 22, 24, 25 and laminate for veneers for tooth 23. Individualized color selection techniques, color and cementation prior to final cementation for highly esthetic results. Thanks to the results, it was possible to observe the conjunction of factors such as the correct selection of the color of the dental substrate, the resinous cement, the restorative material, and efficient communication with the laboratory, essential for the success of the treatment.
Subject(s)
Humans , Female , Adult , Rehabilitation , Tooth , Dental Veneers , DentistryABSTRACT
Objective: To evaluate the biaxial flexural strength (BFS) of lithium disilicate (L), cemented on different substrates (epoxy resin - E and metal - M) with dual-cure resin cement (Rc) and zinc phosphate cement (Zc), not aged, thermally aged (TC) or thermo-mechanical aged (TC/MC). Material and Methods: Disks of L, E, and M were fabricated, and the cementation was performed according to the following groups: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Ten samples from each described group were tested in BFS, ten more samples were subjected to TC (1×104 cycles between 5 ºC and 55 ºC water), and the last 10 samples were subjected to TC/MC (MC: 1.2×106 cycles, 50 N, 3.8 Hz). The BFS test was performed and scanning electron microscopy (SEM) was performed to evaluate the failure mode. The effect of the cementation strategy (cement/substrate) was compared in each aging method and the effect of the aging method was evaluated for each cementation strategy by one-way ANOVA and Tukey post-hoc test (α=0.05). Results: The strength values were highest to M (237.8 ~ 463.9 MPa), in comparison to the E (41.03 ~ 66.76 MPa), despite aging and luting agent. Flexural strength data decreased after TC and TC/MC in groups cemented with Zc, but was stable when cemented with Rc. SEM analysis indicated that failure origins were located at the tensile surface of the L. Conclusion: Lithium disilicate discs cemented to the metallic substrate presented the highest biaxial flexural strength. The cementation with dual-cure resin cement did not decrease BFS after aging (AU)
Objetivo: Avaliar a resistência à flexão biaxial (BFS) do dissilicato de lítio (L), cimentado sobre diferentes substratos (resina epóxi - E e metal - M) com cimento resinoso dual (Rc) e cimento de fosfato de zinco (Zc), não envelhecido, submetido ao envelhecido térmico (TC) ou ao envelhecido térmico-mecânico (TC/MC). Material e Métodos: Foram confeccionados discos de L, E e M, e a cimentação foi realizada de acordo com os seguintes grupos: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Dez amostras de cada grupo descrito foram testadas em BFS, mais dez amostras foram submetidas à TC (1×104 ciclos de imersão em água entre 5 ºC e 55 ºC), e as últimas 10 amostras foram submetidas à TC/MC (MC: 1.2 ×106 ciclos, 50 N, 3.8 Hz). Foram realizados os testes de BFS e a microscopia eletrônica de varredura (MEV) para avaliar o modo de falha. O efeito da estratégia de cimentação (cimento/substrato) foi comparado em cada método de envelhecimento e o efeito do método de envelhecimento foi avaliado para cada estratégia de cimentação por ANOVA a um fator e teste post-hoc de Tukey (α=0,05). Resultados: Os valores de resistência foram maiores para M (237.8 ~ 463.9 MPa), em comparação com E (41.03 ~ 66.76 MPa), independentemente do envelhecimento e do agente cimentante utilizado. Os dados de resistência à flexão diminuíram após TC e TC/MC nos grupos cimentados com Zc, mas se mantiveram estáveis quando cimentados com Rc. A análise MEV indicou que a origem das falhas estava localizada na superfície de tração do L. Conclusão: Os discos de dissilicato de lítio cimentados ao substrato metálico apresentaram maior resistência à flexão biaxial. A cimentação com cimento resinoso dual não diminuiu o BFS após o envelhecimento (AU)
Subject(s)
Aging , Cementation , Flexural StrengthABSTRACT
Objective: The present study aims to evaluate the color stability and degree of conversion of amine-free dual cured resin cement compared to light cured and amine-containing dual cured resin cements used with two different translucencies of thin esthetic restorations. Material and Methods: A total of 120 specimens were prepared for color stability testing (n=60). The specimens were divided into three main groups according to the resin cement type. Group 1: amine-free dual cured, Group 2: light cured, Group 3: amine-containing dual cured. Each group was further subdivided according to the ceramic translucency into two subgroups: high and low translucency. Color stability was assessed by a spectrophotometer before and after thermal aging. For the degree of conversion assessment (n=60), Fourier transform infrared spectroscopy was used at three different time intervals. Statistical analysis was performed using multi-factorial ANOVA, followed by one-way ANOVA with Bonferroni correction. Results: Amine-containing resin cement showed significantly higher ΔEab and ΔE00in both translucencies (4.5±0.3, 3.5±0.3 respectively for high translucency ceramic and 3.8±0.4, 3.0±0.3 respectively for low translucency) than the other tested cements (p<0.001). The highest degree of conversion (DC) was shown after 2 weeks by the amine-free dual cured resin cement (86.27±0.74). Conclusion: Amine-free dual cured resin cement can be an alternative to light cured one for cementation of thin veneers since it showed comparable color stability and high degree of conversion (AU)
Objetivo: O presente estudo tem como objetivo avaliar a estabilidade de cor e o grau de conversão do cimento resinoso dual sem amina em comparação com cimentos resinosos fotopolimerizáveis contendo amina usados com duas translucidezes diferentes em restaurações estéticas definitivas. Material e Métodos: Um total de 120 espécimes foram preparados para teste de estabilidade de cor (n=60). Os espécimes foram divididos em três grupos principais de acordo com o tipo de cimento resinoso. Grupo 1: polimerização dupla sem amina, Grupo 2: fotopolimerização, Grupo 3: polimerização dupla contendo amina. Cada grupo foi ainda subdividido de acordo com a translucidez da cerâmica em dois subgrupos: alta e baixa translucidez. A estabilidade da cor foi avaliada por um espectrofotômetro antes e após o envelhecimento térmico. Para a avaliação do grau de conversão (n=60), a espectroscopia de infravermelho com transformada de Fourier foi usada em três intervalos de tempo diferentes. A análise estatística foi realizada usando ANOVA multifatorial, seguida de ANOVA um faot com correção de Bonferroni. Resultados: O cimento resinoso contendo amina apresentou ΔEab e ΔE00 significativamente maiores em ambas as translucidezes (4,5±0,3, 3,5±0,3 respectivamente para cerâmica de alta translucidez e 3,8±0,4, 3,0±0,3 respectivamente para baixa translucidez) do que os outros cimentos testados (p< 0,001). O maior grau de conversão (DC) foi mostrado após 2 semanas pelo cimento resinoso dual sem amina (86,27±0,74). Conclusão: O cimento resinoso dual sem amina pode ser uma alternativa ao cimento polimerizável na restauração de facetas finas, uma vez que apresentou estabilidade de cor comparável e alto grau de conversão. (AU).
Subject(s)
Color , Resin Cements , Polymerization , LithiumABSTRACT
Objective: the aim of this study was to compare the mechanical behavior of different ceramics when used in thin vertical preparations versus traditional horizontal preparation. Material and Methods: two stainless-steel dies were milled to simulate a minimally invasive vertical preparation (VP) and a traditional horizontal preparation (HP) for an all-ceramic crown of a maxillary first premolar. The stainless-steel dies were duplicated using epoxy resin. Eighty monolithic crowns were milled and divided into 2 groups according to preparation design. Each design group was subdivided into 4 sub-groups according to material (n=10): IPS e.max CAD (lithium disilicate), Bruxzir shaded zirconia (full contour zirconia), CeraSmart (resin nanoceramic) and CEREC Tessera (advanced lithium disilicate). The crowns were cemented on their relevant epoxy resin dies using self-adhesive resin cement. All specimens were subjected to 15,000 thermocycles and then loaded to fracture in a universal testing machine. Data were analyzed using two-way ANOVA and Tukey pair wise comparison test. Results: the fracture resistance mean values of the VP (1344 + 118 N) was significantly lower than the HP design (1646 + 191 N). Ceramic crowns made of full contour zirconia had higher fracture resistance mean values (2842 + 380 N) than advanced lithium disilicate (1272 + 125 N) followed by lithium disilicate crowns (983 + 52 N) and resin nanoceramic (882 + 61 N). Conclusion: both vertical and horizontal preparations, regardless the different ceramic materials, showed clinically acceptable fracture resistance values. (AU)
Objetivo: o objetivo deste estudo foi comparar o comportamento mecânico de diferentes cerâmicas quando utilizadas em preparos verticais finos ou preparos horizontais tradicionais. Material e Métodos: dois modelos de aço inoxidável foram fresados para simular um preparo vertical minimamente invasivo (PV) e um preparo horizontal tradicional (PH) para uma coroa totalmente em cerâmica de um primeiro pré-molar superior. As matrizes de aço inoxidável foram duplicadas usando resina epóxi. Oitenta coroas monolíticas foram fresadas e divididas em 2 grupos de acordo com o desenho do preparo. Cada grupo foi subdividido em 4 subgrupos de acordo com o material (n=10): IPS e.max CAD (dissilicato de lítio), zircônia Bruxzir (zircônia de contorno total), CeraSmart (resina nanocerâmica) e CEREC Tessera (dissilicato de lítio avançado). As coroas foram cimentadas em suas respectivas matrizes de resina epóxi usando cimento resinoso autoadesivo. Todos os espécimes foram submetidos a 15.000 ciclos térmicos e então carregados até a fratura em uma máquina de teste universal. Os dados foram analisados usando ANOVA com dois fatores e teste de comparação por pares de Tukey. Resultados: os valores médios de resistência à fratura do PV (1344 + 118 N) foram significativamente menores do que PH (1646 + 191 N). As coroas de cerâmica feitas de zircônia de contorno total apresentaram maiores valores médios de resistência à fratura (2842 + 380 N) do que dissilicato de lítio avançado (1272 + 125 N), seguido por coroas de dissilicato de lítio (983 + 52 N) e resina nanocerâmica (882 + 61 N). Conclusão: preparos verticais e horizontais, independentemente dos diferentes materiais cerâmicos, apresentaram valores de resistência à fratura clinicamente aceitáveis. (AU)
Subject(s)
Bicuspid , Dental Prosthesis , Tooth Crown , Resin Cements , Epoxy Resins , Fractures, BoneABSTRACT
Resumo Este estudo teve como objetivo avaliar a resistência à fractura do silicato de lítio reforçado com zircônio todo o material cerâmico "Celtra Press" em comparação com um "IPS e-max Press" em condições orais simuladas. Quatorze coroas cerâmicas foram fabricadas em moldes epóxi que foram duplicados a partir de moldes principais de aço inoxidável e divididos em dois grupos iguais (n=7) de acordo com o material de construção; Grupo A: Coroas fabricadas com material IPS e-max Press e Grupo B: Coroas fabricadas com material Celtra Press. As coroas foram então cimentadas nos seus moldes correspondentes com um cimento de resina auto-adesivo e submetidas a ciclos térmicos e cargas cíclicas. Em seguida, foram carregadas para fraturar numa máquina universal de ensaios. Os resultados foram tabulados e analisados estatisticamente utilizando os testes Kolmogorov-Smirnov e Shapiro-Wilk. O teste t de Student usado para comparar os valores médios. O nível de significância foi fixado em P ≤ 0,05 e intervalo de confiança de 95%. A análise estatística foi realizada utilizando o software Graph Pad Instat (Graph Pad, Inc.) para Windows. Os valores médios ± SD da resistência à fractura foram registados para o grupo Disilicate de lítio (1706,01 ±154,32 N) enquanto que os valores médios ± SD registados com o grupo celtra foram (1550,67±196,71 N). As coroas cerâmicas de silicato de lítio reforçado com zircónio produziram valores de resistência à fractura comparáveis aos das coroas cerâmicas de dissilicato de lítio e ambos os materiais testados estão dentro dos valores clinicamente aceitáveis na área posterior.
Abstract The aim of this study was conducted to assess the fracture resistance of zirconia reinforced lithium silicate all ceramic material "Celtra Press" compared to lithium disilicate one "IPS e-max Press" under simulated oral conditions. Fourteen ceramic crowns were fabricated on epoxy dies which were duplicated from stainless steel master die and divided into two equal groups (n=7) according to the material of construction; Group A: Crowns fabricated with IPS e-max Press material and Group B: Crowns fabricated with Celtra Press material. The crowns were then cemented onto their corresponding dies with a self-adhesive resin cement and subjected to thermocycling and cyclic loading. Then they were loaded to fractur in a universal testing machine. The results were tabulated and statistically analyzed using Kolmogorov-Smirnov and Shapiro-Wilk tests. Student t-test used to compare mean values. The significance level was set at P ≤ 0.05 and 95% Confidence interval. Statistical analysis was performed using Graph Pad Instat (Graph Pad, Inc.) software for windows. The mean ± SD values of fracture resistance were recorded for lithium Disilicate group (1706.01 ±154.32 N) meanwhile the mean ± SD value recorded with celtra group were (1550.67±196.71 N). Zirconia reinforced lithium silicate ceramic crowns produced comparable fracture resistance values to lithium disilicate ceramic crowns and both tested materials are within the clinically acceptable values in the posterior area.
ABSTRACT
Abstract To evaluate stress distribution when applying vertical and tangential forces to 1mm thick occlusal veneers with different finish lines preparations, using the finite element method. One extracted third molar was prepared for occlusal veneers, firstly without any bevel. It was scanned in order to design two groups of lithium disilicate (G1A, G2A) and composite resin (G1B, G2B) occlusal veneers. Then, the third molar preparation was modified, beveling the finish line and it was subsequently scanned again to design the occlusal veneer groups with bevel (LD: G3A, G4A and CR: G3B, G4B). The four groups were subjected to different forces (400 N vertical and 900 N tangential). At 400 N, the non-beveled veneers showed slightly higher Von Mises stress values (G1A: 783 MPa and G1B 736.5 MPa) than the beveled veneers (G3A: 685.7 MPa and G3B: 675.8 MPa). However, when 900 N tangential forces were applied, the beveled occlusal veneers showed higher Von Mises stress values (G4A: 4297 MPa and G4B: 4133 MPa) than the non-beveled occlusal veneers (G2A: 2581.1 MPa and G2B: 3519.1 MPa). Furthermore, it was observed that the tissue under the occlusal veneers with bevel showed higher Von Mises stress values than the models without any bevel. Beveled and non-beveled occlusal veneers of lithium disilicate and composite resin presented similar stress distribution values when vertical forces of 400 N were applied; whereas with tangential forces of 900 N applied near to the finish line, the beveled groups presented notably higher stress values than the non-beveled groups. However, both finish line preparations presented adequate values for possible clinical performance.
Resumen Evaluar la distribución de estrés al aplicar fuerzas verticales y tangenciales en carillas oclusales de 1mm de espesor con diferentes líneas de terminación marginal por el método de elementos finitos. Se preparó un tercer molar extraído para carilla oclusal, primero sin bisel. Se escaneó para diseñar dos grupos de carillas oclusales de disilicato de litio (G1A, G2A) y resina compuesta (G1B, G2B). Después, esta preparación molar fue modificada, biselando la línea de terminación y escaneándola nuevamente para diseñar los grupos de carillas oclusales con bisel (DL: G3A, G4A and RC: G3B, G4B). Los 4 grupos fueron sometidos a fuerzas diferentes (400 N vertical y 900 N tangencial). Con 400 N, las carillas sin bisel presentaron ligera mayor tensión de Von Mises (G1A: 783 MPa y G1B 736.5 MPa) que las carillas con bisel (G3A: 685.7 MPa y G3B: 675.8 MPa). De distinta forma, al aplicar fuerzas tangenciales de 900 N, las carillas oclusales con bisel presentaron mayor tensión de Von Mises (G4A: 4297 MPa y G4B: 4133 MPa) que las carillas oclusales sin bisel (G2A: 2581.1 MPa y G2B: 3519.1 MPa). Además, se observó que los tejidos subyacentes a las carillas oclusales con bisel, presentaron mayor tensión de Von Mises, frente a los modelos sin bisel. Las carillas oclusales con y sin bisel de disilicato de litio y resina compuesta presentaron una distribución de estrés similar con fuerzas verticales de 400 N, por otro lado, con fuerzas tangenciales de 900 N, los grupos con bisel presentaron notablemente mayor tensión que los grupos sin bisel. Sin embargo, ambos diseños de terminación marginal presentaron valores adecuados para un posible desempeño clínico.
Subject(s)
Humans , Bite Force , Composite Resins , Dental VeneersABSTRACT
ABSTRACT: Nowadays, maxillary midline diastema (MMD) can be treated with different multidisciplinary approaches. When restorative dentistry is needed, glass-matrix ceramic materials is one of the best choices, since they present good optical behavior and high survival rates in the anterior dentition. To obtain an adequate interphase, and color integration are one of the main restorative goals, and for that purpose, specific finishing and polishing procedures must be employed to avoid staining and ensure the restoration's color stability. In the case report presented in this article, a single lithium disilicate ceramic fragment was performed to close a MMD produced by the shape alteration of one of the maxillary central incisors. Also, the finishing and polishing procedure is discussed.
ABSTRACT
ABSTRACT The aim of this study was to evaluate the amount of radiating energy transmitted through lithium disilicate discs of different thicknesses and opacities with different curing units (CU). Discshaped specimens 8 mm in diameter and 1.5 mm or 0.7 mm thick were designed with Zbrush® and Cura 3D® software, milled from HT and MO IPS e-maxCAD blocks (Ivoclar Vivadent) with Ceramill Mikro 4 (Amann Girrbach, Austria) and processed according to manufacturer instructions. Thickness was checked with a Mitutoyo (México) caliper. Four groups (n=4) were formed: G1(HT/1.5 mm), G2(MO/1.5 mm), G3(HT/0.7 mm) y G4(MO/0.7 mm), and the effect of three CUs: Coltolux (Coltene- Whaledent), LED.C, (Woodpecker Medical Instrument Co.Ltd) and Deepcure L(3M-ESPE) was tested Measurements were taken with a halogen and LED radiometer (Woodpecker® LM-1-Guilin Woodpecker Medical Instrument Co.Ltd) after applying the guide of each CU directly on the reading window (d) and after interposing each of the specimens. The ratio of transmitted energy was determined in each case and data was analyzed with repeated measures ANOVA and Tukey test for multiple comparisons. LED.C: d:1600 mW/cm2, G1: 0.31(0.00), G2: 0.14(0.00) G3: 0.54(0.01), G4: 0.38(0.01); Deepcure L: d:1500 mW/cm2, G1: 0.34(0.01), G2: 0.20(0,00), G3: 0.56(0.01), G4: 0.41(0.02); Coltolux: d:1275 mW/cm2, G1: 0.44(0.01), G2: 0.24(0,00), G3: 0.65(0.01), G4: 0.47(0,00). Statistically significant differences were found among the curing units (P<0.001) and for the interaction CU-thickness (P<0.001) and CU-opacity (P=0.023). Within the conditions of this study, the ratio of light transmitted through lithium disilicate structures is related to their thickness and opacity, and to the curing unit employed.
RESUMEN Uno de los factores relacionados con éxito de las restauraciones y prótesis de cerámica de matriz vítrea es el logro de una fijación adhesiva para lo cual la correcta polimerización del medio de fijación es un requisito fundamental. El objetivo de este trabajo fue valorar la transmitancia de una cerámica a base de disilicato de litio de diferentes opacidades y espesores, con distintas unidades de curado. Probetas con forma de discos de 8mm de diámetro y dos diferentes espesores (1.5 mm y 0.7 mm) fueron diseñadas con Zbrush® y Cura 3D®, maquinadas a partir de bloques HT y MO de IPS e-maxCAD (Ivoclar Vivadent) con Ceramill Mikro 4 (Amann Girrbach, Austria) y procesadas según instrucciones del fabricante. Se obtuvieron cuatro grupos (n=4): G1(HT/1.5 mm), G2(MO/1.5 mm), G3(HT/0.7 mm) y G4(MO/0.7 mm),los espesores se controlaron con un calibre (Mitutoyo, México). A continuación, se registró la irradiancia con cada una de las unidades de curado (UC) Coltolux (Coltene- Whaledent) LED.C, (Woodpecker Medical Instrument Co.Ltd) y Deepcure L(3M-ESPE), aplicadas sobre la ventana de un radiómetro (Halogen and led radiometer Woodpecker® LM-1-Guilin Woodpecker Medical Instrument Co.Ltd) en forma directa (d), y luego de interponer los diferentes especímenes y se calculó la proporción de energía transmitida en cada caso. Los datos se analizaron con ANOVA de medidas repetidas y prueba de Tukey para las comparaciones múltiples. LED.C: d:1600 mw/ cm2, HT/0,7mm: 0,54(0,01), HT/1,5mm:0,31(0); MO/0,7mm: 0,38(0,01), MO/1,5mm: 0,14(0,00); Deepcure L: d:1500 mW/ cm2, HT/0,7 mm: 0,56(0,01), HT/1,5 mm: 0,34(0,01), MO/0,7 mm: 0,41(0,02), MO/1,5 mm: 0,20(0,00); Coltolux: d:1275 mw/ cm2, HT/0,7 mm:0,65 (0,01), HT/1,5 mm:0,44(0,01), MO/0,7 mm: 0,47(0,00), MO/1,5mm: 0,24(0,00). Se encontraron diferencias estadísticamente significativas entre las diferentes unidades de curado (P<0,001), y en la interacción unidades de curado-espesor (P<0,001) y unidades de curado-opacidad (P=0,023). La proporción de energía luminosa transmitida por una estructura de cerámica de disilicato de litio depende del espesor y opacidad de la restauración y de la unidad de curado utilizada.
ABSTRACT
Objective@#To analyze the effects of different restorations and the thickness of the occlusal space on the stress distribution of endodontically treated molars with endocrowns.@*Methods @# The finite element model of the restoration of the first mandibular molar was created, and four different endocrown materials were used including two resin based ceramics (Lava Ultimate, Vita Enamic), one lithium disilicate ceramic (IPS e.max CAD) and one zirconia ceramics (Cercon), and four kinds of surface space thickness were designed: 1 mm, 2 mm, 3 mm and 4 mm. A total of 600 N was loaded to simulate the maximum bite force in the vertical and inclined directions, and the finite element software ANSYS 10.0 was used to analyze the stress distribution@*Results@#The vertical loading analysis showed that the crown stress of the 1 mm-Cercon group was the highest at 211.30 MPa, and that of the 4 mm-Lava Ultimate group was the lowest at 11.56 MPa; the highest dentin stress was 38.84 MPa in the 3 mm-Lava Ultimate group, and the lowest was 11.68 MPa in 1 mm-Cercon group. The stress in the periodontal ligament and alveolar bone had little change. The inclined loading analysis showed that the crown stress of the 1 mm-Cercon group was the highest at 78.73 MPa and that of the 1 mm-Lava Ultimate group was the lowest at 35.51 MPa; the highest dentin stress was 41.63 MPa in the 1 mm-Cercon cervical group, and the lowest was 10.81 MPa in the 4 mm-Cercon coronal group. The stress concentration of cement and cervical dentin under inclined loading was higher than that under vertical loading.@* Conclusion @# The results of finite element analysis show that the elastic modulus of the endocrown increases, the stress of the crown restoration shows an upward trend, and the stress in the tooth shows a downward trend. With increasing crown thickness, the stress of the crown prosthesis decreased.
ABSTRACT
Objective: The purpose of the present study was to synthesize and characterize lithium disilicate glass-ceramics through the Li2O-SiO2system for determining the most satisfactory sintering parameter by evaluating the crystalline composition, microstructure and mechanical properties. Material and methods: The glass-ceramics were prepared from a glass precursor by means of the melting/cooling technique with a composition of 33.33 Li2O and 66.67 SiO2 (mol.%). The specimens were compressed by the uniaxial pressing technique and three different thermal treatments were used for sintering: 850 °C (Group 1), 900 °C (Group 2), and 950 °C (Group 3), which were determined based on the differential scanning calorimetry (DSC) result. The glass-ceramics were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Archimedes method, microhardness and biaxial flexural strength analyses. Results: The results regarding XRD predominantly showed lithium disilicate phase for all the heat treatments performed. Moreover, grains with a needle form were more predominantly observed in the SEM images for Group 3, as well as a higher densification and consequently higher mechanical properties. In contrast, Group 1 presented the lowest mechanical properties and densification, as well as the highest porosity. Conclusion: The present study demonstrated how extremely important it is to follow the heat treatment recommended by the manufacturers of ceramics, including time and temperature, which possess direct effects in the crystalline phase formation, as well as in the material's microstructure and mechanical properties (AU)
Objetivo: O presente estudo teve como objetivo sintetizar e caracterizar uma vitrocerâmica de dissilicato de lítio através do sistema Li2O-SiO2para determinar o parâmetro de sinterização mais satisfatório através da avaliação da composição cristalina, microestrutura e propriedades mecânicas. Material e Métodos: As vitrocerâmicas foram preparadas a partir de um vidro precursor pelo método fusão/resfriamento utilizando a composição de 33.33 Li2O e 66.67 SiO2 (mol.%). As amostras foram prensadas utilizando uma técnica de prensagem uniaxial e três tratamentos térmicos diferentes foram utilizadas para sinterização: 850 °C (Grupo 1), 900 °C (Grupo 2), e 950 °C (Grupo 3), que foram determinados através do resultado da análise diferencial de calorimetria. As vitrocerâmicas foram caracterizadas através das análises de difração de raios X (DRX), microscopia eletrônica de varredura (MEV), métodos de Arquimedes, microdureza e ensaio de flexão biaxial. Resultados: Os resultados de DRX mostraram predominantemente a fase de dissilicato de lítio para todos os tratamentos realizados. Além disso, grãos com forma agulhada foram mais predominantemente observados por MEV no grupo 3, assim como uma densificação maior e consequentemente valores maiores das propriedades mecânicas. Em contraste, o grupo 1 apresentou os menores valores de propriedades mecânicas e densificação, e também a maior porosidade. Conclusão: O presente estudo demonstrou como é extremamente importante seguir o tratamento térmico recomendado pelos fabricantes de cerâmica, incluindo tempo e temperatura, que possuem efeitos diretos na formação da fase cristalina, assim como na microestrutura do material e propriedades mecânicas. (AU)
Subject(s)
X-Ray Diffraction , Microscopy, Electron, Scanning , CrystallizationABSTRACT
Background: To present the benefits of high power lasers (Er: YAG and Nd: YAG) over the use of the high speed turbine for the extraction of ceramics restorations, without damaging the surfaces of the teeth; being a relatively easier and faster procedure without the use of anesthetic agents, and the preparation of the ceramic restorations and cementing in the single session; with a follow-up of 1 year. Objective: The benefits of lasers over high-speed turbine mechanical instrumentation for crown removal encompass efficient restoration recovery without damage to tooth surfaces; and a relatively easier and faster procedure without the use of anesthetic agents. Methods: The Er: YAG laser (no contact; 3.2-4.0 W, 20 Hz) was used to extract the porcelain prosthesis, followed by a gingivectomy with the Nd: YAG laser on tooth 12 to improve the gingival contour. The dental surfaces where the ceramic prosthesis will be cemented were scanned. Then, CAD / CAM technology was used to make the ceramic veneers that were cemented in the same session. Results: The efficacy the Er:YAG laser energy was observed by the decreased of the time to remove all-ceramic materials through ablation of bonding cements, reducing working time by 75% compared to a high-speed turbine. Conclusions: An Er: YAG laser can safely remove lithium disilicate crowns with the settings used in this study. Laser-assisted removal of all ceramic PDFs is a promising treatment protocol. The use of the Nd: YAG (2.0 W power, short 20Hz, 320 µm optical fiber, in contact) laser allowed gingivoplasty to be performed, automatically cauterizing avoiding post-operative bleeding, and facilitating the preparation of ceramic restorations the same day. The use of high-power lasers and the use of accompanying CAD / CAM technology allowed this clinical case to be completed in a single visit without the use of temporary restorations, achieving absolute patient satisfaction. (AU)
Antecedentes: Apresentar os benefícios dos lasers de alta potência (Er: YAG e Nd:YAG) sobre o uso da turbina de alta velocidade para a remoção de restaurações cerâmicas, sem danificar as superfícies dos dentes; sendo um procedimento relativamente mais fácil e rápido evitando o uso de agentes anestésicos, conseguindo fazer o preparo das restaurações de cerâmica e cimentação em uma única sessão; com seguimento de 1 ano. Objetivo: Os benefícios dos lasers sobre a instrumentação mecânica com turbina de alta velocidade para a remoção da coroa abrangem a recuperação eficiente da restauração sem danos às superfícies dos dentes; e um procedimento relativamente mais fácil e rápido sem o uso de agentes anestésicos. Métodos: O laser Er: YAG (sem contato; 3,2-4,0 W, 20 Hz) foi utilizado para remover a prótese de porcelana, seguido de gengivectomia com o laser Nd: YAG no dente 12 para melhorar o contorno gengival. As superfícies dentais onde a prótese de cerâmica será cimentada foram escaneadas. Em seguida, a tecnologia CAD / CAM foi utilizada para confeccionar as facetas de cerâmicas que foram cimentadas na mesma sessão. Resultados: A eficácia da energia do laser Er: YAG foi observada pela diminuição do tempo na remoção dos materiais cerâmicos por meio da ablação dos cimentos de ligação, reduzindo o tempo de trabalho em 75% em relação a uma turbina de alta velocidade. Conclusão: Um laser Er: YAG pode remover com segurança as coroas de dissilicato de lítio com as configurações usadas neste estudo. A remoção assistida por laser de todos os PDFs de cerâmica é um protocolo de tratamento promissor. O uso do laser Nd: YAG (2,0 W potência, curta 20Hz, 320 µm fibra ótica, em contato) permitiu a realização da gengivoplastia, cauterizando automaticamente evitando sangramento pós-operatório e facilitando o preparo das restaurações cerâmicas no mesmo dia. O uso de lasers de alta potência e o uso da tecnologia CAD / CAM que o acompanha permitiram que este caso clínico fosse concluído em uma única visita, sem o uso de restaurações temporárias, alcançando a satisfação absoluta do paciente (AU)
Subject(s)
Humans , Female , Middle Aged , Computer-Aided Design , Dental Materials , Lasers, Solid-StateABSTRACT
Objective: To evaluate the influence of background, substrates and thickness on the color and light behaviour of two ZLS glass ceramics. Material and Methods: Standardized disc-shape specimens (12 x 1.2 mm), color A1 HT, of Celtra Duo and Vita Suprinity (n=30), were tested over a white/black background, and divided in five groups (n=6) to be tested over five substrates (polished gold alloy, white zirconia and composite, dentine and enamel A1 colour). The L*, C*, h*, a*, b* and Δ E values, were recorded in two thicknesses (1.2 and 2.4 mm). Translucency parameter (TP), contrast ratio (CR) and opalescence parameter (OP) were calculated. Data was analysed with nonparametric tests: Mann Whitney between ceramic materials for thickness, Wilcoxon for thicknesses in substrates and ceramic material and KruskalWallis with Bonferroni corrections tests (p<0,01) for substrates. Results: For 2.4 mm, the Δ E values were always higher independently of ceramic material or substrates. Vita Suprinity registered lower values than Celtra Duo. Zirconia substrate registered the lower values. For 1.2 mm, dentine registered the lower values. Gold alloy and composite substrates registered the lower Δ E values for 1.2 mm Celtra Duo and 2.4 mm Vita Suprinity specimens. CT and OP higher values and TP lower values were registered for 2.4 mm Vita Suprinity. It was impossible to calculate for Celtra Duo specimens. Conclusions: Background, substrate and thickness had significant influence in light behaviour and final color of ZLS glass ceramics. Substrates Gold alloy and dentine exhibited clinical acceptable Δ E values for 1.2 mm Celtra Duo specimens. (AU)
Objetivo: Avaliar a influência do fundo, do substrato e da espessura no comportamento da luz e na cor de duas cerâmicas ZLS. Material e métodos: Discos de cerâmica (12 x 1.2 mm) de cor A1 HT, de Celtra Duo e Suprinity (n=30), foram testados sobre fundo branco/preto e cinco substratos (liga Ag-Au-Pt polida; zircónia branca; compósito, dentina e esmalte de cor A1). Os valores L*, C*, h*, a*, b* e Δ E foram registados em duas espessuras (1.2 mm e 2.4 mm). O parâmetro de translucidez (TP), o parâmetro de opalescência (OP) e o índice de contraste (CR) foram determinados. Foram realizados testes não paramétricos: Mann Whitney entre cerâmicas por espessura, Wilcoxon entre categoria de espessura por substrato e cerâmica; KruskalWallis com correção de Bonferroni para substratos (p <0,01). Resultados: Para 2,4 mm, o Δ E foi sempre superior independentemente do material ou substrato. Os valores de Suprinity foram inferiores aos de Celtra Duo. O substrato zirconia obteve o Δ E mais baixo. Para 1,2 mm, a dentina obteve o Δ E mais baixo. A liga dourada e o compósito obtiveram Δ E mais baixo para Celtra Duo 1,2 mm e Suprinity 2,4 mm. Para Suprinity, CT e OP foram maiores para 2,4 mm e menores para TP. Não foi possível calcular para Celtra Duo. Conclusão: O fundo, substrato e espessura tiveram influência significativa no comportamento da luz e cor das restaurações de cerâmica ZLS. Apenas os substratos metal e dentina apresentaram valores clinicamente aceitáveis, para Celtra Duo na espessura de 1.2 mm.(AU)
Subject(s)
Color , Composite Resins , Dental Enamel , Dental Materials , DentinABSTRACT
Objective: The aim of this study was to compare the bond strength of High-Translucency zirconia (HT) and lithium disilicate dental ceramics, under different surface treatments. Material And Methods: For this, ceramics were divided into groups: Control Group (C) (n = 5), lithium disilicate sheets, conditioned with 10% hydrofluoric acid, followed by application of 37% phosphoric acid, silane and universal adhesive application; Group HTAI (n = 5), HT zirconia sheets were blasted with silica oxide, followed by the application of universal adhesive; Group HTPAI (n = 5), HT zirconia sheets were blasted with silica oxide, followed by the application of non-thermal plasma and universal adhesive and the HTP Group (n = 5), HT zirconia received only the application of non-thermal argon plasma. Subsequently, the specimens of each group were subjected to a cementation process with resin cement, obtaining cylinders. After 24 h of storage, in distilled water, at 37°C, the specimens were subjected to a mechanical micro-shear test. The data obtained were submitted to ANOVA One-way followed by the Tukey test (5%). Results: The HTP Group was excluded from the statistical analysis, as adhesions failed within the storage period. In addition, it was not possible to verify a statistical difference between the control group C and the experimental groups HTAI and HTPAI. Conclusion: The results showed that the applicability of high translucency zirconia can potentially be compared to the lithium disilicate bond strength, when submitted to the same surface treatments, except for the plasma application, which alone was not effective (AU)
Objetivo: O objetivo deste estudo foi comparar a resistência adesiva das cerâmicas dentárias de zircônia de alta translucidez e dissilicato de lítio. Materiais e Métodos: Para isso, cerâmicas foram divididas em grupos: Grupo Controle (C) (n = 5), lâminas de dissilicato de lítio, condicionadas com ácido fluorídrico 10%, seguido de aplicação do ácido fosfórico 37%, aplicação de silano e aplicação do adesivo universal; Grupo HTAI (n = 5), lâminas de zircônia HT foram submetidas ao jateamento com óxido de sílica, seguido da aplicação do adesivo universal; Grupo HTPAI (n = 5), lâminas de zircônia HT foram submetidas ao jateamento com óxido de sílica, seguido da aplicação do plasma não térmico e do adesivo universal e o Grupo HTP (n = 5), lâminas de zircônia HT receberam apenas a aplicação do plasma não térmico de argônio. Posteriormente, os espécimes de cada grupo foram submetidos a um processo de cimentação com cimento resinoso, obtendo-se cilindros. Após 24h, de armazenamento em água destilada a 37°C, os espécimes foram submetidos a ensaio mecânico de microcisalhamento. Os dados obtidos foram submetidos à ANOVA 1-fator seguido pelo teste de Tukey (5%). Resultados: O Grupo HTP foi descartado da análise estatística, pois as adesões falharam dentro do período de armazenamento. Além disso, não foi possível verificar diferença estatística entre o grupo controle C e os experimentais HTAI e HTPAI. Conclusão: Os resultados mostraram que a aplicabilidade das zircônias de alta translucidez pode potencialmente ser comparada à resistência adesiva da cerâmica de dissilicato de lítio, quando submetidas aos mesmos tratamentos de superfície, com exceção da aplicação de plasma, que isoladamente não foi efetiva (AU)
Subject(s)
Metal Ceramic Alloys , Dentin-Bonding Agents , Resin Cements , Dental CementsABSTRACT
Objective: The present study aimed to evaluate the effect of repressing and different surface treatment protocols on the shear bond strength of lithium disilicate glass-ceramics. Material and Methods: A total of 52 lithium disilicate glass-ceramic discs (IPS emax Press, Ivoclar Vivadent) were fabricated using the heat-press technique. The discs were divided into two groups; group (P): discs fabricated from new e.max ingots (n=26), group (R): discs fabricated from reused e.max buttons (n=26). Each group was subdivided into subgroup (E): discs were etched with hydrofluoric acid (9.5%) (n=13), subgroup (S): discs were air-abraded with 110 µm alumina particles. All specimens were subjected to X-ray Diffraction analysis, Scanning Electron Microscope, Energy Dispersive X-Ray, Thermo-Cycling, and Shear Bond Strength Testing. Results: Repressed Etched subgroup (RE) recorded the statistically highest shear bond strength value, followed by the Pressed Etched subgroup (PE), while the statistically lowest shear bond strength value was recorded for the Pressed Air-Abraded subgroup (PS) and Repressed Air-Abraded subgroup (RS). Conclusion: Repressing the leftover buttons for the construction of new lithium disilicate glass-ceramic restorations has no adverse effect on the bond strength of the resin cement to the ceramic. Hydrofluoric acid surface treatment improves the shear bond strength and durability of resin cement bond to both pressed and repressed lithium disilicate glass-ceramic. Air-abrasion cannot be considered as a reliable surface treatment when bonding to lithium disilicate glass-ceramics. (AU)
Objetivo: O presente estudo teve como objetivo avaliar o efeito da reprensagem e de diferentes protocolos de tratamento de superfície na resistência ao cisalhamento de vitrocerâmica de dissilicato de lítio. Materiais e Métodos: Um total de 52 discos de vitrocerâmica de dissilicato de lítio (IPS emax Press, Ivoclar Vivadent) foram fabricadas usando a técnica de prensagem quente. Os discos foram divididos em dois grupos: grupo (P): discos fabricados a partir de novo lingotes de e-max (n=26), grupo (R): discos fabricados a partir de botões de emax reutilizados (n=26). Cada grupo foi subdividido em subgrupo (E): discos condicionados com ácido fluorídrico (9,5%) (n=13), subgrupo (S) discos foram abrasivos com partícula 110 µm de alumínio. Todos os espécimes foram submetidos a analise de difração de raio-x, microscópio eletrônico de varredura, raio-x de energia dispersiva, termociclagem e teste de resistência de cisalhamento. Resultados: O subgrupo Reprensado-condicionado (RE) registrou o valor estatisticamente mais alta em relação a resistência ao cisalhamento, seguido pelo subgrupo Prensado-condicionado (PE), enquanto o valor estatisticamente mais baixo de resistência ao cisalhamento foi o subgrupo Prensado-Jateado (OS) e o subgrupo Reprensado-Jateado (RS). Conclusão: A reprensagem dos botões restantes para a construção de novas restaurações vitrocarâmicas de dissilicato de lítio não apresentou efeitos adversos na resistência de unicãp do cimento resinoso à cerâmica. O tratamento de superfície com ácido fluorídrico melhora a resistência ao cisalhamento e a durabilidade do cimento resinoso para vitrocerâmica de dissilicato de lítio prensada e reprimida. A abrasão por ar não pode ser considerada um tratamento de superfície confiável quanto a colagem da vitrocerâmica de dissilicato de lítio (AU)
Subject(s)
X-Ray Diffraction , Resin Cements , Shear Strength , Microscopy, Electrochemical, ScanningABSTRACT
Objective: The aim of this study was to analyze mechanical and thermal stresses of hybrid ceramic and lithium disilicate based ceramic of CAD/CAM inlays using 3D Finite element analysis. Material and Methods:A three dimensions finite element model of permanent maxillary premolar designed according to standard anatomy with class II cavity preparation for inlay restored with two different ceramic materials: 1- Hybrid ceramic (Vita Enamic), 2- Lithium disilicate based ceramic (IPS e.max CAD). Totally six runs were performed on the model as: One loading case for each restorative material was tested in stress analysis; seven points of loading with 140N vertically applied at palatal cusp tip and cusp slop, marginal ridges and central fossa while the models base was fixed as a boundary condition in the two cases. Two thermal analysis cases were performed for each restoration material by applying 5ºC and 55ºC on the crown surface including the restoration surface. Results:The results of all structures were separated from the rest of the model to analyze the magnitude of stress in each component. For each group, maximum stresses on restorative materials, cement, enamel, and dentin were evaluated separately. Both ceramic materials generated similar stress distribution patterns for all groups when a total occlusal load of 140 N was applied. Conclusion: Thermal fluctuations of temperature have a great influence on the stresses induced on both restoration and tooth structure. IPS e.max CAD produced more favorable stresses on the tooth structure than Vita Enamic. (AU)
Objetivo: O objetivo deste estudo foi analisar o estresse mecânico e térmico de inlays de cerâmica hibrida e a base de dissilicato de lítio através da análise em 3D de elementos finitos. Material e Métodos: Foi realizado o design de um modelo de três dimensões em elementos finitos de um pré-molar superior de acordo com os padrões anatômicos de um preparo de cavidade classe II para restauração de inlay em dois tipos de cerâmicas diferentes: 1 Cerâmica hibrida (Vita Enamic), 2 Cerâmica a base de dissilicato de lítio (IPS e.max CAD). No total, seis execuções foram realizadas no modelo como: Uma carga para cada material restaurador foi testado para análise de tensão; sete pontos de carga com 140N foi aplicado verticalmente na ponta da cúspide palatina, saliência da cúspide, cristas marginais e fossa central enquanto a base do modelo foi fixada como uma condição de limite nos dois casos. Duas análises térmicas foram realizadas para cada material de restauração, aplicando 5ºC e 55ºC na superfície da coroa, incluindo a superfície da restauração. Resultados: Os resultados de todas as estruturas foram separados do resto do modelo para analisar a magnitude do estresse de cada componente. Para cada grupo, o máximo de estresse nos materiais restauradores, cemento, esmalte e dentina foram avaliados separadamente. Padrões similares de distribuição de estresse foram gerados em todos os grupos para ambos os materiais cerâmicos, quando a carga oclusal de 140 N foi aplicada. Conclusão: As variações térmicas de temperatura têm uma grande influência nas tensões induzidas na restauração e na estrutura dentária. IPS e.max CAD produziu tensões mais favoráveis na estrutura dentária do que o Vita Enamic (AU)
Subject(s)
Bicuspid , Finite Element Analysis , Dental Cavity Preparation , Dental Cementum , Dental Enamel , DentinABSTRACT
Objective: The recycling of heat pressed lithium disilicate glass-ceramic leftover material has been reported to be done by dental laboratories. The effect of this procedure on the fracture resistance of single crowns is unknown, especially when it is functioning inside the oral cavity with subsequent exposure to temperature changes and cycles of mastication. Material and Methods: A total of 28 lithium disilicate glass-ceramic crowns (IPS emax Press) were constructed and randomly assigned into two groups (n = 14); Group (P): Included crowns fabricated from new e.max ingots. Group (R): Included crowns fabricated from repressed e.max buttons. Specimens of each group were divided into two equal subgroups (n = 7) according to whether the aging of specimens will be performed or not before fracture resistance testing. Subgroup (N), samples were subjected to fracture resistance without thermo-mechanical aging, while subgroup (A), samples were subjected to thermo-cycling and cyclic loading before being subjected to fracture strength testing. Different methods; SEM, XRD, EDAX were used to characterize the properties of lithium disilicate glass-ceramics before and after repressing. Results: The highest statistically significant fracture resistance value was recorded for the subgroup (RN) repressed/non-aged, followed by the subgroup repressed/aged (RA), while the lowest statistically significant mean value was recorded for the subgroup pressed/aged (PA). There was no significant difference between pressed/non-aged (PN) and repressed/aged (RA) subgroups. Conclusion: Repressing of leftover buttons may increase the fracture resistance of IPS emax Press crowns. Thermo-mechanical aging may negatively affect the fracture resistance of IPS emax Press crowns, yet Repressing may decrease this effect. Clinical implications:This is a novel approach that targets a point of research that has not been investigated before. It elaborates how repressing may decrease the effect of aging and increase the fracture resistance of lithium disilicate crowns. Thus, recycling of lithium disilicate glass ceramics might decrease its failure and prolong their serviceability (AU)
Objetivo: A reutilização de material residual de vitrocerâmicas de dissilicato de lítio prensadas a quente tem sido realizada pelos laboratórios de prótese. O efeito deste procedimento na resistência à fratura de coroas unitárias é desconhecido, especialmente quando estão em função na cavidade oral com subsequente exposição às variações de temperatura e ciclos mastigatórios. Material e Métodos: Vinte e oito coroas de dissilicato de lítio (IPS e.max Press) foram confeccionadas e divididas aleatoriamente em dois grupos (n = 14); Grupo (P): Incluiu coroas fabricadas de pastilhas novas de e.max; Grupo (R): Incluiu coroas fabricadas de e.max reprensado. As amostras de cada grupo foram divididas em dois subgrupos iguais (n = 7) de acordo com a realização de envelhecimento dos espécimes antes do teste de resistência à fratura. As amostras do subgrupo (N) foram submetidas ao teste de resistência à fratura sem envelhecimento termomecânico, enquanto as amostras do subgrupo (A) foram submetidas ao envelhecimento termomecânico antes do teste de resistência à fratura. Diferentes métodos (MEV, DRX e EDS) foram usados para caracterizar as propriedades da cerâmica de dissilicato de lítio antes e depois da reprensagem. Resultados: O maior valor de resistência à fratura estatisticamente significativo foi do subgrupo (RN) reprensado/não envelhecido, seguido pelo subgrupo reprensado/envelhecido (RA), enquanto o menor valor médio estatisticamente significativo foi do subgrupo prensado/envelhecido (PA). Não houve diferença estatística entre os subgrupos prensado/não envelhecido (PN) e reprensado/envelhecido (RA). Conclusão: A reprensagem de material residual pode aumentar a resistência à fratura de coroas de IPS e.max Press. O envelhecimento termomecânico pode afetar negativamente na resistência à fratura deste material, enquanto a reprensagem pode diminuir este efeito. Relevância clínica: Esta é uma nova abordagem que busca estudar um tema que não havia sido investigado anteriormente. Este estudo demonstrou como a reprensagem pode diminuir o efeito do envelhecimento e aumentar a resistência à fratura de coroas de dissilicato de lítio. Assim, a reutilização de vitrocerâmicas de dissilicato de lítio pode diminuir o risco à falha e aumentar o tempo de vida útil (AU)
Subject(s)
Crowns , Recycling , Flexural Strength , MouthABSTRACT
Resumen Evaluar la influencia del tipo de terminación marginal; filo de cuchillo (F) y chamfer (C) sobre la resistencia flexural de coronas de disilicato de litio CAD/CAM en espesores de 0,8 mm y 0,5 mm. Materiales y métodos: 40 premolares superiores sanos, en 2 grupos de acuerdo con el tipo de terminación G1=F y G2=C; 2 subgrupos referentes al espesor del material Sg1=0,8mm y Sg2 0,5 mm (5 coronas por cada subgrupo), se sometieron a fuerzas de compresión vertical (v) y horizontal (h). Se observó el tipo de fractura más frecuente; cohesivas en porcelana (cp), adhesiva en porcelana (ap), mixta pequeña (mp) y mixta larga (ml). Resultados: En preparaciones a 0,8 mm y 0,5 mm, existió diferencia significativa en relación con la mejor terminación, esta fue el C; sus valores fueron, Sg1 (h=1347,2 N / v=1402,0. F; Sg1 (h=965,6 N/ v= 794,8 N). F a 0,5 mm mostró mejor desempeño ante fuerzas horizontales. C; Sg2 (h=924,8 N /v=813,4 N) y para F; Sg2 (h=1217,0 N /v= 576,0 N). Conclusiones: Tipo de fractura más frecuente es cp y ap. Terminación chamfer y filo de cuchillo pueden ser utilizados con seguridad, pues muestran valores aceptables de resistencia flexural, al reducirse el grosor de la restauración en chamfer reduce su resistencia, el filo de cuchillo la aumenta.
Abstract Objective: To evaluate the influence of the type of shoulder margins; Knife edge (F) and Chamfer (C) on the flexural strength of CAD / CAM lithium disilicate crowns in thicknesses of 0.8 mm and 0.5 mm. Materials and Methods: 40 healthy upper premolars, in 2 groups according to the type of termination G1 = F and G2 = C; 2 subgroups referring to the material thickness Sg1 = 0.8mm and Sg2 0.5mm (5 crowns for each subgroup), were subjected to vertical (v) and horizontal (h) compression forces. The most frequent type of fracture was observed; cohesive in porcelain (cp), adhesive in porcelain (ap), mixed small (mp) and mixed long (ml). Results: In preparations with 0.8 mm and 0.5 mm thicknesses, there was a significant difference in relation to the best termination, this was C; their values were Sg1 (h = 1347.2 N / v = 1402.0.F; Sg1 (h = 965.6 N / v = 794.8 N) .F at 0.5 mm showed better performance against horizontal forces C; Sg2 (h = 924.8 N / v = 813.4 N) and for F; Sg2 (h = 1217.0 N / v = 576.0 N) Conclusions: The most frequent type of fracture is cp and ap finishing chamfer and knife edge can be used safely show acceptable values of flexural strength, by reducing the thickness of the chamfer restoration reduces its strength, the knife edge increases it.