Knowledge about composite restorations repair vs replacement- a survey among a subpopulation of saudi dental students / Conhecimento sobre reparo e substituição de restaurações de resina - uma pesquisa entre uma subpopulação de estudantes sauditas de odontologia

Objective: The purpose of this study was to evaluate the knowledge among dental students at King Khalid University, Jazan University, and Najran University in the kingdom of Saudi Arabia about when to repair or replace defective direct composite restoration. Materials and Methods: A questionnaire-based survey was formulated, pursuing the information about management (repair/replacement) of defective composite restorations and distributed among 200 dental students of three universities in the southern region of the kingdom of Saudi Arabia. The data were collected with the help of an online questionnaire. Data entry and the analysis were done using the statistical software package SPSS version 20.0. It was presented using descriptive statistics in the form of frequencies and percentages for qualitative variables, and range means and standard deviations for age, quantitative variable. Analytic statistics were done using Chi-Square tests (χ2) to test the significant difference between categorical variables. The level of significance, the p-value was 0.01(p<0.01). Results: The decision to choose between composite repair or replacement was influenced by whether this topic was taught to them at various undergraduate levels during Bachelor of Dental Surgery. The reason associated with the decision to repair defective composite restorations, 76% reported as cost-effective followed by Increased longevity (71%), the permanent filling (70%), patient's preference for repair (65%), and least time consuming (50%). 67% participants preferred significantly (p<0.001) repair due to secondary caries in the previously restored tooth with composite, followed by the small surface defect in a composite restoration (65%), risk of pulpal damage significantly (p<0.001) in a defective composite restoration (62.5%) and more invasive and destructive treatment option (35%). More than half of respondents 123 (61.5%) reported that they were not taught about composite repair during the Bachelor of Dental Surgery. Conclusion: It is suggested with the help of our study that didactic and clinical training components regarding composite repair should be seriously included in the teaching curriculum of dental institutions as it is in the best interest of the patient. Dental students should be provided with clinical training on this topic so that they can follow proper decision-making protocols available during repair or replacement of defective resin composite restorations. Other researches in the future can be carried out for refining the guidelines and techniques utilized for composite repair. (AU)

Objetivo: O objetivo deste estudo foi avaliar o conhecimento entre estudantes de odontologia da King Khalid University, Jazan University e Najran University, no reino da Arábia Saudita, sobre quando reparar ou substituir restaurações de resina composta direta defeituosas. Material e Métodos: Foi formulada uma pesquisa baseada em questionário, buscando informações sobre o manejo (reparo / substituição) de restaurações de resina composta e distribuída entre 200 estudantes de odontologia de três universidades da região sul do reino da Arábia Saudita. Os dados foram coletados com o auxílio de um questionário online. A entrada e análise dos dados foram feitas com o software estatístico SPSS versão 20.0. Foi apresentado por meio de estatística descritiva na forma de frequências e percentuais para as variáveis qualitativas, e amplitude de médias e desvios-padrão para a idade, variável quantitativa. A estatística analítica foi feita usando testes de qui-quadrado (χ2) para testar a diferença significativa entre as variáveis categóricas. Ao nível de significância, o valor de p foi de 0,01 (p <0,01). Resultados: A decisão de escolher entre o reparo ou substituição do compósito foi influenciada pelo fato de este tópico ter sido ensinado a eles em vários níveis de graduação durante o Bacharelado em Odontologia. O motivo associado à decisão de reparar restaurações de resina composta defeituosas, 76% relataram como custo-benefício seguido por maior longevidade (71%), restauração definitva (70%), preferência do paciente para reparo (65%) e menos demorado ( 50%). Sessenta e sete por cento dos participantes preferiram o reparo significativamente (p <0,001) devido a cárie secundária no dente previamente restaurado com resina composta, seguido pelo pequeno defeito de superfície em uma restauração composta (65%), risco de dano pulpar significativamente (p <0,001) em um restauração de resina composta com defeito (62,5%) e opção de tratamento mais invasiva e destrutiva (35%). Mais da metade dos entrevistados, 123 (61,5%) relataram que não foram ensinados sobre reparo de resina composta durante o Bacharelado em Odonotlogia. Conclusão: É sugerido com a ajuda de nosso estudo que os componentes do treinamento didático e clínico sobre reparo de resina composta devem ser seriamente incluídos no currículo de ensino de instituições odontológicas, pois é do interesse do paciente. Os estudantes de odontologia devem receber treinamento clínico sobre este tópico para que possam seguir os protocolos de tomada de decisão adequados disponíveis durante o reparo ou substituição de restaurações de resina composta com defeito. Outras pesquisas no futuro podem ser realizadas para refinar as diretrizes e técnicas utilizadas para reparo de resina (AU)

Effect of the photoinitiator system on the properties of a dental material based on a hybrid polymer / Efeito do sistema fotoiniciador sobre as propriedades de um material dentário baseado em um polímero híbrido

Objetivo: Nesse estudo, foram avaliados os efeitos de dois diferentes protocolos de cura sobre as propriedades de um compósito usando um polímero híbrido como resina dentária. Material e Métodos: Dois compósitos diferentes foram preparados, um contendo uma mistura de TEGDMA/Bis-GMA (50:50) e, outro contendo uma mistura de TEGDMA/p-MEMO (50:50), [p-MEMO: precursor oligomérico inorgânico]. Ambos compósitos foram reticulados com lucirin e canforoquinona. Os compósitos foram preparados com 70% em massa de carga inorgânica. Resistência flexural foi avaliada com uma máquina de testes universal e o grau de conversão calculado por espectroscopia na região do infravermelho. Um picnômetro a gás hélio foi usado para obter os dados de contração de polimerização. Testes de sorção foram feitos e microscopia eletrônica de varredura foi usada para avaliar efeitos deletérios sobre as superfícies das resinas. Resultados: A amostra constituída com TEGDMA/p-MEMO reticulada com lucirin (L-T/p) apresentou os melhores valores das propriedades monitoradas. Conclusão: Lucirin é o sistema fotoiniciador mais adequado para compostos dentários contendo polímeros híbridos.

Objective: In this study, the effects of two different cure protocols upon the properties of composites using a hybrid-polymer as dental resin were evaluated. Material and Methods: Two distinct dental composites were prepared, one containing a mixture of TEGDMA/bis-GMA (50:50) and, another containing a mixture of TEGDMA/p MEMO (50:50), [p-MEMO: oligomeric inorganic precursor]. Both composites were polymerized with lucirin and canphorquinone as photoinitiators. The composites were made with a 70 % wt of inorganic filler. Flexural strength was evaluated with a universal test machine and the degree of conversion was measured by infrared spectroscopy. A helium pycnometer was used to obtain polymer shrinkage data. Sorption tests were performed and SEM microscopy was used to show deleterious effects upon the resins’ surfaces. Results: The sample based on TEGDMA/p-MEMO polymerized with lucirin (L-T/p) showed the best values of the monitored properties. Conclusion: Lucirin is the most suitable photoinitiator for dental composites containing hybrid polymers.

Síntese e análise de compósitos experimentais para uso odontológico reforçados com nanoargila / Synthesis and analysis of experimental composites for dentistry use reinforced with nanoclay

O objetivo do presente estudo foi de avaliar os efeitos de diferentes frações de partículas de nanoargila modificadas do tipo montmorilonita Cloisite® 20A em propriedades físicas, mecânicas e biológicas de resinas experimentais do tipo nanohíbrida. Compósitos dentais foram preparados através da mistura de 30% de matriz resinosa (BisGMA/TEGDMA) em 70% de partículas de carga (vidro de bário silicato silanizado ­VB, dióxido de silício ­ SD, partículas de nanoargila MMT). Quatro grupos de compósitos experimentais foram formados, variando o percentual de nanoargila empregada (0%, 5%, 7,5%, 10%). O processamento foi realizado em uma máquina de dupla mistura (SpeedMixer DAC, Germany, 3500 rpm). A citotoxicidade in vitro do material foi avaliada baseada nas normas ISO 10993- 5-2009 e comparado com compósito comercial. Ensaios mecânicos para cálculo de Resistência à Flexão e Módulo de Elasticidade foram realizados em máquina de ensaios universal EMIC. O aparelho Acuvol® foi utilizado para o ensaio de contração de polimerização. A sorção e solubilidade dos compósitos foram calculadas baseadas nas normas ISO 4049. Os dados foram analisados estatisticamente, utilizando-se a tabela ANOVA e o Teste de Tukey para comparação dos grupos de dois em dois. O nível de significância utilizado foi de 95% (p< 0,05). Por meio do exame dos resultados, concluiu-se que foi possível esfoliar 5 e 7,5% de partículas de MMT satisfatoriamente na matriz BisGMA/TEGDMA, porém, o inserção de 10% de MMT na matriz orgânica não trouxe vantagens ao compósito, certamente por não permitir a total exfoliação de suas partículas. A inserção de 5 e 7,5% de nanoargila ao compósito dental experimental possibilitou uma diminuição da contração de polimerização do material em 22,13 e 17,4%, respectivamente. Além disso, esses dois grupos permaneceram com suas propriedades mecânicas e de absorção e solubilidade satisfatórias, além de apresentar ausência de citotoxicidade para as células fibroblasticas L929 testadas

The aim of the present study was to evaluate the effect of different weight fractions of modified montmorillonite nanoclay fillers Cloisite ® 20A on mechanical, physical and biological properties of nanohybrid experimental resins. Dental composites were prepared by mixing 30% of resin matrix (BisGMA / TEGDMA) to 70% of particulate fillers (Silanized barium silicate particles - BS, silicone dioxide - SD, montmorillonite nanoclay cloisite 20AMMT). Four groups of experimental composite were formed with various fractions of the nanoclay fillers (0%; 5%; 7,5%; 10% ). Processing was performed using a dual high speed mixing machine (SpeedMixer DAC, Germany, 3500 rpm). In vitro citotoxicity of the material was calculated based on standards ISO 10993-5-2009 and compared to a comercial composite. Tensile strenght and elastic modulus were performed using an universal test machine EMIC. The volumetric shrinkage was calculated by Acuvol® machine. Water sorption and solubility were measured based on International Standard ISO 4049. Data were statistically analyzed by ANOVA and Tukey Test for multiple comparisons. The significance level utilized was 95% (p < 0,05). By the results, it was concluded that it is possible to exfoliate nicely 5 and 7.5% of MMT particles inside Bis-GMA/TEGDMA matrix. However, insertion of 10% of MMT did not improve composite, certainly, because the total exfoliation of particles did not occured. Insertion of 5 and 7.5% of nanoclay in dental composite diminished polymerization shrinkage in 22,13% and 17,4% , respectively. Furthermore, these two groups maintained their mechanical properties, satisfactory sorption and solubility and also presented no citotoxicity for L929 fibroblastic cells

Influência da técnica de inserção de resina composta sobre o selamento marginal em restaurações estéticas oclusais / The influence of the insertion technique of composite resin on the microleaakage of occlusal esthetic restorations

Este trabalho objetiva avaliar a influência da técnica de inserção de resina composta sobre o selamento marginal de restaurações oclusais. Cavidades oclusais em 60 molares humanos foram restauradas de acordo com os grupos: 1 - Filtek Z350/3M ESPE; 2 - Ice®/SDI e 3 - Concept Advantage®/Vigodent, subdivididos em: A - Técnica de inserção incremental e B - Técnica de Inserção cruciforme. Os corpos de prova sofreram: estresse térmico (500 ciclos; 5ºC +/- 1 e 55ºC +/-1); exposição ao agente químico traçador (AQT); seccionamento e análise (lupa estereoscópica 25X) para atribuição de escores de 0 (sem penetração do AQT) a 2 (penetração máxima do AQT). Os resultados evidenciaram os maiores percentuais para o escore 0 para 3-B (80,0%), 2-A (75,0%), 2-B (75,0%), 1-A (70,0%). Houve diferenças estatisticamente significantes nos grupos 1 e 3, não ocorrendo no grupo 2 (testes de Mann-Whiteny e Kruskal-Wallis / nível de significância de 5%). Concluiu-se que nenhuma técnica de inserção foi capaz de impedir a microinfiltração e que a técnica cruciforme representa uma alternativa à técnica incremental, considerando o tipo de resina composta empregado.

The aim of this study was to evaluate the influence of the insertion technique of composite resin on the microleakage of occlusal restorations. Occlusal cavities in 60 human molars were restored according to the following groups: 1 - Filtek Z350?/3M ESPE; 2 - Ice?/ SDI and 3 - Concept Advantage ? / Vigodent; subdivided into: A - Technique of incremental insertion and B - cruciform Insertion Technique. The specimens were toexposed: heat stress (500 cycles, 5 ? C + / - 1 and 55 ? C + / -1); exposure to the chemical tracer (AQT); sectioning and examination (25X stereomicroscope) for assigning scores from 0 (no penetration of AQT) to 2 (maximum penetration of AQT). The results showed the highest percentages for the score 0 for 3-B (80.0%), 2-A (75.0%), 2-B (75.0%), 1-A (70.0%). There were statistically significant differences in groups 1 and 3, which did not occur in group 2 (Mann-Whiteny and Kruskal-Wallis / significance level of 5%). It was concluded that no technique of insertion was able to prevent microleakage and the cruciform technique represents an alternative to the incremental technique depending on the type of composite resin used.