Tensile bond strength and SEM analysis of enamel etched with Er:YAG laser and phosphoric acid: a comparative study In vitro

Er:YAG laser has been studied as a potential tool for restorative dentistry due to its ability to selectively remove oral hard tissue with minimal or no thermal damage to the surrounding tissues. The purpose of this study was to evaluate in vitro the tensile bond strength (TBS) of an adhesive/composite resin system to human enamel surfaces treated with 37 percent phosphoric acid, Er:YAG laser (lambda=2.94 mum) with a total energy of 16 J (80 mJ/pulse, 2Hz, 200 pulses, 250 ms pulse width), and Er:YAG laser followed by phosphoric acid etching. Analysis of the treated surfaces was performed by scanning electron microscopy (SEM) to assess morphological differences among the groups. TBS means (in MPa) were as follows: Er:YAG laser + acid (11.7 MPa) > acid (8.2 MPa) > Er:YAG laser (6.1 MPa), with the group treated with laser+acid being significantly from the other groups (p=0.0006 and p= 0.00019, respectively). The groups treated with acid alone and laser alone were significantly different from each other (p=0.0003). The SEM analysis revealed morphological changes that corroborate the TBS results, suggesting that the differences in TBS means among the groups are related to the different etching patterns produced by each type of surface treatment. The findings of this study indicate that the association between Er:YAG laser and phosphoric acid can be used as a valuable resource to increase bond strength to laser-prepared enamel.

A tecnologia a laser tem sido estudada como uma ferramenta potencial para uso em odontologia devido à sua habilidade em remover tecido ósseo com um mínimo ou nenhum dano aos tecidos vizinhos. O objetivo deste estudo é comparar in vitro a resistência à tração do sistema adesivo em esmalte tratado com ácido fosfórico a 37 por cento, laser Er:YAG (lambda=2,94 mim) com energia total de 16 J (80 mJ/pulso, 2 Hz, 200 pulsos e largura de pulso de 250 ms) e com a combinação laser Er:YAG seguido por ácido fosfórico. O teste de resistência à tração foi usado para comparar a resistência à tração em cada grupo. Foi também realizada microscopia eletrônica de varredura para permitir a análise das diferenças morfológicas entre os grupos. Foram obtidos os seguintes valores médios de resistência para os grupos tratados com: laser (6,1 MPa), ácido fosfórico (8,2 MPa) e laser mais ácido (11,7 Mpa). Amostras tratadas com laser e ácido apresentaram valores maiores de resistência do que amostras com laser ou ácido isoladamente. A análise da microscopia eletrônica revelou diferenças que corroboram os resultados, demonstrando que diferenças de resistência entre os grupos são devidas às diferenças entre os padrões superficiais resultantes. Nossos resultados sugerem que a combinação do laser Er:YAG com ácido fosfórico pode ser usada como um método para aumentar a resistência à tração do sistema esmalte resina.

The effect of additional enamel etching on microleakage of the adhesion of self-etching primer system / 대한치과보존학회지

The purpose of this study is to evaluate the effect of additional enamel etching with phosphoric acid on the microleakage of the adhesion of self-etching primer system. Class V cavity(4 mmx3 mmx1.5 mm) preparations with all margins in enamel were prepared on buccal surface of 42 extracted human upper central incisor teeth. Prepared teeth were randomly divided into 3 groups. Group 1 : no additional pretreatment with 37% phosphoric acid (NE). Group 2 : additional pretreatment with 37% phosphoric acid for 10 seconds (E10s). Group 3 : additional pretreatment with 37% phosphoric acid for 20 seconds (E20s). The adhesives(Clearfil SE Bond(R), Kuraray, Osaka, Japan) and composite resins(Clearfil AP-X(R), Osaka, Kuraray, Japan) were applied following the manufacturer's instructions. All the specimens were finished with the polishing disc(3M dental product, St Paul, MN, USA), thermocycled for 500 cycles between 5degrees C and 55degrees C and resected apical 3-mm root. 0.028 stainless steel wire was inserted apically into the pulp chamber of each tooth and sealed into position with sticky wax. Surrounding tooth surface was covered with a nail varnish 2 times except areas 1 mm far from all the margins. After drying for one day, soaked the samples in the distilled water. Microleakage was assessed by electrochemical method(System 6514, Electrometer(R), Keithley, USA) in the distilled water. In this study, the microleakage was the lowest in group 1(NE) and the highest in group 3(E20s)(NE