Cytotoxicity Comparison of a Calcium Silicate-Based Resin Cement versus Conventional Self-Adhesive Resin Cement and a Resin-Modified Glass Ionomer: Cell Viability Analysis

Abstract Objective: To compare the cytotoxicity level of a new calcium silicate-based resin cement (TheraCem) with two commonly used cements, including a conventional self-adhesive resin cement (Panavia SA) and a resinmodified glass ionomer cement (FujiCem2), on the human gingival fibroblast cells after 24 and 48 hours. Material and Methods: Twelve discs of each cement type were fabricated. The extract of cement disks was made by incubating them in the cell medium. Human gingival fibroblast cells were cultured and exposed to cement extracts for 24 h and 48 h. MTT assay was performed on extracts and optical density and cell viability rates were calculated by the spectrophotometer device at 570 nm. Data were analyzed using ANOVA and Tukey HSD tests. Results: The cell viability rates after 24 hours and 48 hours were as follows: TheraCem: 89.24% and 85.46%, Panavia SA: 49.51% and 46.57% and FujiCem2: 50.63% and 47.36%. TheraCem represented the highest cell viability rate. However, no significant difference was noted between Panavia SA and FujiCem2. Time had no significant effect on cell viability. Conclusion: TheraCem exhibited the best results among three tested cements and was considered non-toxic. Panavia SA and FujiCem2 were not significantly different regarding the cell viability rate. Time had no significant effect on the cytotoxicity level of cements (AU).

Degree of conversion and water sorption of self-adhesive and conventional flowable composites: an in vitro study

Aim: Self-adhesive flowable composite resins have been recently introduced to the market. Degree of conversion (DC) and water sorption (WS) are two important parameters affecting the properties of restorative materials. This study aimed to assess the DC and WS of a self-adhesive flowable composite resin in comparison with two conventional flowable composite resins. Methods: Vertise Flow (VF) self-adhesive and Tetric-N Flow (TF) and Grandio Flow (GF) conventional flowable composites were evaluated in this in vitro, experimental study. The DC (n=3) was determined by attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR). The WS (n=7) was measured after 7 days of immersion in artificial saliva accordingto ISO 4049specifications. Data were analyzed by one-way ANOVA and a post-hoc test (p<0.05). Results: VF showed the highest DC percentage (84.3%) followed by GF (72.79%) and TF (68.7%). The latter two had no significant difference (p=0.8). WS was the highest in VF (55.2 µg/mm3), and the two conventional flowable composites had a significant difference in WS (19.5 µg/mm3 in TF and 11 µg/mm3 in GF; p<0.001). Conclusions: Flowable composite resins had significant differences in DC and WS, and VF demonstrated the highest DC and WS