Diferentes padrões tubulares dentinários de molares decíduos interferem na força de união de adesivos baseados no condicionamento ácido total e autocondicionantes? / Do different dentin tubular patterns of primary molars affect the bond strength of total-etching and self-etching adhesive systems?

Avaliar a resistência de união, pelo ensaio de tração, de sistemas adesivos autocondicionantes e baseados no condicionamento ácido total em diferentes superfícies dentinárias de molares decíduos e analisar a interface de união adesiva. Metodologia: Neste estudo in vitro, amostras de dentina de 35 a 65% de distância pulpar (dentina intermediária) foram obtidas do terço médio das faces vestibular e lingual/palatina de primeiros e segundos molares decíduos. As superfícies dentinárias foram polidas com lixas de carboneto de silício de granulação 400 e 600. Três sistemas adesivos (Prime & Bond NT, AdheSE e Clearfil SE Bond) foram empregados nas amostras dos primeiros e segundos molares (n=15); corpos de prova foram confeccionados em resina composta com uma área de adesão de 2 mm de diâmetro. Após 24 horas de armazenagem em água destilada a 37ºC, fez-se o ensaio de tração. Para a análise da interface de união adesiva entre sistema adesivo e dentina usando microscopia eletrônica, as amostras foram preparadas com os mesmos três sistemas adesivos (n=5). Resultados: Não foram observadas diferenças estatisticamente significantes nos valores de adesão entre primeiros e segundos molares (ANOVA; p>0,05). Os seguintes valores médios de adesão em MPa foram obtidos: 15,65±3,70 (Prime & Bond NT), 19,47±7,09 (AdheSE) e 17,14±5,35 (Clearfil SE Bond). Não foram observadas diferenças estatisticamente significantes entre os adesivos autocondicionantes. A formação de camada híbrida e tags foi observada em todos os grupos. Conclusões: Os sistemas adesivos contemporâneos apresentaram comportamentos similares em ambos os tipos de superfícies tubulares dentinárias dos molares decíduos. Estudos de seguimento são necessários para o acompanhamento do desempenho clínico desses materiais...

Aims: To evaluate the tensile bond strength of self-etching and total-etching adhesive systems to the different dentin surfaces of primary molars and to analyze the resin-dentin interface. Methodology: In this in vitro study, dentin samples 35 to 65% distant from the pulp (intermediate dentin) were obtained from buccal and lingual surfaces at the middle third of the crown of first and second primary molars. Dentin surfaces were prepared with 400 and 600-grit silicon carbide paper. Three adhesive systems (Prime & Bond NT, AdheSE and Clearfil SE Bond) were tested on the first and second primary molar surfaces (n=15); inverted truncated cones of resin composite with a 2.0 mm bonding diameter were built. After 24 hour storage in distilled water at 37°C, the specimens were submitted to the tensile bond strength test. To analyze the resin-dentin interface under scanning electron microscopy, samples were prepared with the same three adhesive systems (n=5). Results: No differences between first and second primary molar dentin substrates could be observed in mean bond strength values (ANOVA; p>0.05). The following mean bond strength values (MPa) were obtained: 15.65±3.70 (Prime & Bond NT), 19.47±7.09 (AdheSE) and 17.14 ±5.35 (Clearfil SE Bond). There were no statistically significant differences between the self-etching adhesive systems. The presence of hybrid a layer and tags were observed in all groups. Conclusions: Contemporary adhesive systems showed similar behaviors on both dentin tubular surfaces of primary molars. Follow-up studies of the clinical performance of these materials are needed...

Anomalías dentarias de impacto estético en odontopediatría: características y tratamiento / Dental anomalies of esthetic impact in pediatric dentistry: characteristicsand treatment

El desarrollo dentario es un proceso que comienza en la vida intrauterina. Los disturbios de desarrollo en este proceso se presentan como anomalías y pueden afectar ambas denticiones, temporal y permanente, teniendo carácter sistémico, local y/o hereditario. Los profesionales que atienden niños deben reconocer y diferenciar características normales de eventuales anomalías de la cavidad bucal que necesitan ser tratadas. Este artículo ofrece a los profesionales del área odontológica una revisión sobre las principales anomalías dentarias directamente relacionadas con la estética del niño y su respectivo tratamiento, con el objetivo de promover una mejor calidad de vida en estos pacientes.

Tooth development is a process that begins in the intrauterine life. The developmental disorders in this process are presented as anomalies and can affect both dentitions, deciduous and permanent, having a systemic, local and/or hereditary character. Professionals who treat children must recognize and differentiate normal characteristics of possible abnormalities in the oral cavity that need to be treated This article provides to dental professionals a review of the major dental abnormalities directly related to the aesthetic of children and their respective treatment, with the aim to promote a better quality of life in these patients.