Effect of varying thickness and artificial aging on color and translucency of cubic zirconia and lithium disilicate ceramics / Efeito da variação da espessura e do envelhecimento artificial na cor e translucidez de cerâmicas de zircônia cúbica e dissilicato de lítio

Objective: The aim of this study is to evaluate the effect of varying thickness and artificial aging on the color and translucency of cubic zirconia and lithium disilicate ceramics. Material and Methods: A total of 30 square shaped disks (12 mm x 12 mm) were fabricated from the cubic zirconia (Bruxzir Anterior) blank and lithium disilicate blocks (E.max CAD), used in three thicknesses (0.5mm, 0.8mm and 1mm). Portable spectrophotometer Vita Easyshade Advance was used to obtain color coordinates, which were substituted in formulas and used to calculate color change and translucency parameter values before and after aging (thermocycling for lithium disilicate and hydrothermal aging for cubic zirconia). Repeated measures Analysis of Variance (ANOVA) was used to study the effect of ceramic type, thickness, aging and their interaction on mean translucency parameter. Two-way (ANOVA) was used to study the effect of ceramic type, thickness and their interaction on mean color change (ΔE). Results: Statistical analysis showed that E.max CAD HT is more translucent than Bruxzir Anterior. Translucency decreased as thickness increased. There was a statistically significant decrease in TP after aging for both materials. Lithium disilicate showed statistically significant greater ΔE when subjected to aging than cubic zirconia, with both ΔE values being clinically imperceptible. As thickness increased, ΔE decreased. Conclusions: Thickness highly affected translucency and color of ceramics. As thickness increases, translucency parameter decreases and color change becomes less evident. Aging also causes a significant decrease in translucency parameter and induces color change however color changes are imperceptible. (AU)

Objetivo: O objetivo deste estudo é avaliar o efeito de diferentes espessuras e do envelhecimento artificial na cor e translucidez de cerâmicas de zircônia cúbica e dissilicato de lítio. Material e Métodos: Um total de 30 discos (12 mm x 12 mm) foram fabricados a partir de um bloco branco de zircônia cúbica (Bruxzir Anterior) e blocos de dissilicato de lítio (E.max CAD) em três diferentes espessuras (0,5mm, 0,8mm e 1mm). Um espectrofotômetro portátil Vita Easyshade Advance foi utilizado para obter as coordenadas de cores, que foram substituídas nas fórmulas e usadas para calcular os valores dos parâmetros de mudança de cor e translucidez antes e depois do processo de envelhecimento (termo ciclagem para dissilicato de lítio e envelhecimento hidrotérmico para zircônia cúbica). A análise de variância de medidas repetidas (ANOVA) foi usada para estudar o efeito do tipo de cerâmica, a espessura, o envelhecimento e a sua interação no parâmetro de translucidez média. Two-way (ANOVA) foi usado para estudar o efeito do tipo da cerâmica, espessura e sua interação na alteração de cor média (ΔE). Resultados: a análise estatística mostrou que a cerâmica E.max CAD HT é mais translúcida que Bruxzir Anterior. A translucidez diminuiu com o aumento da espessura. Houve uma diminuição estatisticamente relevante no TP após o envelhecimento para ambos os materiais. O dissilicato de lítio apresentou maior ΔE estatisticamente relevante quando submetido ao envelhecimento quando comparado com a zircônia cúbica, sendo ambos os valores de ΔE clinicamente imperceptíveis. Conforme a espessura aumentou, o ΔE diminuiu. Conclusão: a espessura afetou expressivamente na translucidez e cor das cerâmicas. À medida que a espessura aumentou, os parâmetros de translucidez diminuíram e a mudança de coloração se tornou menos evidente. O envelhecimento também causou uma diminuição significativa no parâmetro de translucidez das cerâmicas de zircônia cúbica e dissilicato de lítio. (AU)

Effect of Surface Treatment of Two Ceramic Materials by Er, Cr:YSGG Laser Irradiation on The Shear Bond Strength to Resin Cement: "a Comparative in-Vitro Study" / Efeito do tratamento de superfície de dois materiais cerâmicos por Irradiação de laser Er, Cr:YSGG na resistência ao cisalhamento a cimento Resinoso: "um estudo comparativo in-Vitro"

Objective: The aim of this study is to assess the effect of Er,Cr:YSGG laser on the shear bond strength (SBS) and surface topography of two CAD/CAM ceramic materials bonded with self adhesive resin cement. Material and methods: sixty ceramic CAD/CAM discs were obtained, 30 lithium disilicate (IPS Emax) (Group LD), and 30 hybrid resin ceramic (Vita Enamic) (Group RC). The Slices were allocated into six groups (n=10) according to ceramic material and surface treatment; Group (LD-C): IPS Emax treated with 9% hydrofluoric acid (HF), Groups (LD-L1) and (LD-L2): IPS Emax treated with Er,Cr:YSGG, Group (RC-C): Vita Enamic treated with 9% hydrofluoric acid (HF), Groups (RC-L1) and (RC-L2): Vita Enamic treated with Er,Cr:YSGG laser. The laser parameters and irradiation protocol was 1.5 W (L1) and 2.5 W (L2). All samples were cemented with self-adhesive resin cement and thermocycled for 5000 cycles. The SBS was measured using a universal testing machine and the mean values (MPa) were analyzed using Two-way (ANOVA) (P ≤ 0.05) and Bonferroni's post-hoc test. Results: RC-C (16.55) showed highest SBS followed by LD-C (13.79), which revealed no statistically significant difference with RCP1 (12.33) and RC-P2 (11.2). The lowest SBS values were found with LD-P1 (2.7) and LDP2 (2.1). SEM analysis revealed Vita Enamic to have the highest surface roughness. Fracture pattern analysis showed adhesive failure with IPS Emax groups and mixed failure with Vita Enamic groups. Conclusion: Er,Cr:YSGG laser irradiation with the parameters used did not increase SBS of IPS Emax and Vita Enamic with composite resin compared to HF acid etching (AU)

Objetivo: O objetivo deste estudo é avaliar o efeito do laser Er,Cr:YSGG na resistência ao cisalhamento (SBS) e na topografia superficial de dois materiais cerâmicos CAD/CAM cimentados com cimento resinoso autoadesivo. Material e métodos: foram obtidos sessenta discos cerâmicos CAD/CAM, 30 de dissilicato de lítio (IPS Emax) (Grupo LD) e 30 de resina híbrida (Vita Enamic)(Grupo RC). Os discos foram alocados em seis grupos (n = 10), de acordo como material cerâmico e o tratamento de superfície; Grupo (LD-C): IPS Emaxtratado com ácido fluorídrico (HF) a 9%, Grupos (LD-L1) e (LD-L2): IPS Emaxtratado com Er,Cr:YSGG, Grupo (RC-C): Vita Enamic tratada com ácido fluorídrico (HF) a 9%, Grupos (RC-L1) e (RC-L2): Vita Enamic tratada com laser Er,Cr:YSGG. Os parâmetros do laser e o protocolo de irradiação foram de 1,5 W (L1) e 2,5 W (L2). Todas as amostras foram cimentadas com cimento resinoso autoadesivo e termocicladas por 5000 ciclos. A SBS foi medida usando uma máquina de ensaios universais e os valores médios (MPa) foram analisados usando (ANOVA) a dois fatores (P ≤ 0,05) e teste post-hoc de Bonferroni. Resultados: RC-C (16,55) apresentou maior SBS seguido por LD-C (13,79), que não revelou diferença estatisticamente significante com RCP1(12,33) e RC-P2 (11,2). Os menores valores de SBS foram encontrados comLD-P1 (2,7) e LD-P2 (2,1). A análise por MEV revelou que a Vita Enamic possui maior rugosidade de superfície. A análise do padrão de fratura mostrou falha adesiva nos grupos IPS Emax e falha mista nos grupos Vita Enamic. Conclusão: A irradiação com laser Er,Cr:YSGG com os parâmetros utilizados não aumentou a SBS de IPS Emax e Vita Enamic ao cimento resinoso em comparação com o condicionamento ácido com HF.(AU)

Clinical Evaluation of Wear Behavior of Human Enamel and Chipping of Veneered Zirconia against Monolithic Zirconia (Randomized Controlled Clinical Trial) / Avaliação clínica do comportamento de desgaste do esmalte humano e lascamento da zircônia estratificada contra a zircônia monolítica (ensaio clínico controlado randomizado)

Objective: To evaluate the wear behavior of human enamel and chipping of veneered and monolithic zirconia for posterior full coverage restorations. Material and methods: Thirty-four zirconia full coverage restorations (seventeen in each group) were fabricated. The patients were divided into two groups according to the type of zirconia used; group 1 (comparator group) veneered zirconia crowns and group 2 (intervention group) monolithic zirconia single crowns. All crowns were lab fabricated and polished. For opposing teeth wear measurements 3D non-contact profilometer was used where epoxy resin replicas were constructed for opposing arch immediately after crowns cementation, three, six and twelve months. Restoration chipping was measured using modified United States Public Health Services (USPHS) criteria. Results: All restorations were reported as alpha with no chipping. There was no statistically significant difference between (Group 1) and (Group 2) for wear test. Conclusion: Both monolithic and veneered restorations revealed satisfactory mechanical properties with no chipping after one year of clinical use. Wear of opposing enamel was clinically acceptable for both materials. (AU)

Objetivo: Avaliar o comportamento ao desgaste do esmalte humano e lascamento de zircônia estratificada e monolítica para coroas totais posteriores. Material e métodos: Trinta e quatro coroas totais de zircônia (dezessete em cada grupo) foram fabricadas. Os pacientes foram divididos em dois grupos de acordo com o tipo de zircônia utilizada; grupo 1 (grupo controle) coroas de zircônia estratificada e grupo 2 (grupo de intervenção) coroas de zircônia monolítica. Todas as coroas foram fabricadas e polidas em laboratório. Para medidas de desgaste de dentes opostos, foi utilizado um perfilômetro 3D sem contato, onde réplicas de resina epóxi foram construídas para o arco oposto imediatamente após a cimentação das coroas, três, seis e doze meses após. O lascamento da restauração foi medido usando critérios modificados dos Serviços de Saúde Pública dos Estados Unidos (USPHS). Resultados: Todas as restaurações foram relatadas como alfa sem lascamento. Não houve diferença estatisticamente significativa entre (Grupo 1) e (Grupo 2) para o teste de desgaste. Conclusão: Ambas as coroas monolíticas e estratificadas revelaram propriedades mecânicas satisfatórias sem lascamento após um ano de uso clínico. O desgaste do esmalte oposto foi clinicamente aceitável para ambos os materiais. (AU)