Characterization of sound enamel and natural white spot lesions / Caracterização de esmalte hígido e lesões de mancha branca naturais

Objective: To compare optical, morphological, chemical, and physical aspects of the sound enamel and white spot lesions (WSL) classified as ICDAS 2. Material and Methods: Seventeen human molars with one surface presenting WSL and a sound surface (2 x 2 mm window) were characterized by Quantitative light-induced fluorescence (QLF ®), Optical coherence tomography (OCT), microhardness, and Raman spectroscopy. The ANOVA and Tukey's test were used at 5% significance level. Results: The QLF comparison between distinct substrates yielded decreased ∆Q (integrated fluorescence loss) of -15,37%mm2 and -11,68% ∆F (fluorescence loss) for WSL. The OCT detected mean lesion depth of 174,43 µm. ANOVA could not detect differences in the optical attenuation coefficient between the substrates (p>0.05). Lower microhardness measures were observed in WSL than on sound enamel (p<0.05). The Raman spectra showed four vibrational phosphate bands (v1, v2, v3, v4), where the highest peak was at 960.3 cm-1(v1) for both substrates. However, a 40% decrease in phosphate (v1) was detected in WSL. The peak at 1071 cm-1 was higher for sound enamel, indicating the presence of a phosphate band instead of the B-type carbonate. The spectra showed higher intensity of the organic composition at 1295 cm-1 and 1450 cm -1 for WSL. Conclusion: Non-invasive QLF, OCT and Raman spectroscopy were able to distinguish differences in fluorescence, optical properties, and organic/inorganic components, respectively, between sound enamel and WSL, validated by the destructive microhardness analysis. (AU)

Objetivo: Comparar os aspectos ópticos, morfológicos, químicos e físicos do esmalte sadio e das lesões de mancha branca naturais, classificada como ICDAS 2. Material e métodos: Dezessete molares humanos com uma face apresentando uma lesão de mancha branca natural e outra face o esmalte hígido (2 x 2 mm) foram caracterizados utilizando a Fluorescência quantitativa induzida pela luz (QLF ®), Tomografia de coerência óptica (OCT), Microdureza e Espectroscopia Raman. A ANOVA e o teste de Tukey foram utilizados ao nível de significância de 5%. Resultados: A comparação entre os substratos distintos, utilizando o QLF ® demonstrou uma diminuição no ∆Q (perda de fluorescência integrada) de -15,37%mm2 e -11,68% de ∆F (Perda de fluorescência) para a lesão de mancha branca. O OCT detectou uma profundidade média de lesão de 174,43µm. A ANOVA não detectou diferenças no coeficiente de atenuação óptica entre os substratos (>0,05). Microdureza significantemente menor foi detectada nas lesões de mancha branca do que no esmalte sadio (p<0,05). Os espectros Raman mostraram quatro bandas vibracionais do fosfato (v1,v2,v3,v4), onde o maior pico foi em 960,3cm-1para ambos os substratos. No entanto, uma diminuição de 40% no fosfato (v1) foi detectada na lesão. O pico em 1071cm-1foi maior para o esmalte hígido, demonstrando tratar-se da banda do fosfato, ao invés do carbonato tipo B. Os espectros apresentaram maior intensidade da composição orgânica em 1295cm-1e 1450 cm-1para a lesão de mancha branca. Conclusão:Os métodos não invasivos QLF, OCT e espectroscopia Raman foram capazes dediferenciar a fluorescência, propriedades ópticas e conteúdo orgânico/inorgânico do esmalte sadio comparado com esmalte com lesões de mancha branca, sendo validado pela análise de microdureza. (AU)

Non-thermal plasma increase bond strength of zirconia to a resin cement / Plasma não-térmico aumenta a resistência de união da zircônia a um cimento resinoso

Objective: This study investigated the influence of different surface treatments on zirconia surface energy, roughness and microshear bond strength. Material and Methods: Forty eight slices of Yttriastabilized tetragonal zirconia polycrystal (Y-TZPVITA In-Ceram® YZ for inLab®) (6.4 x 3.2 x 1.6 mm) were divided into 3 groups according to the surface treatment (n = 16): YTZP_control -untreated; YTZP_plasma -surface treatment with non-thermal oxygen plasma; YTZP_primer - coating with ceramic primer. Surface energy (n = 6) was measured with a goniometer; and surface roughness (n = 10) was analyzed with a 3D profilometer were performed over zirconia surface. On the same specimens of surface roughness, on the treated zirconia's surface, resin cement (PANAVIA V5 - Kuraray Noritake Dental) was built up by inserting the resin cement into Tygon tubes (1 mm of internal diameter X 1 mm length). After 24h storage, microshear test was assessed. Data were analyzed by one-way ANOVA and Tukey posthoc test (p < 0.05). Results: Nonthermal oxygen plasma treated specimens exhibited higher statistically significant surface energy (p = 0.00) and bond strength (p = 0.00) when compared to control and primer groups. Roughness test (p = 0.897) could not detect statistical difference among the tested groups. Conclusion: Non-thermal oxygen plasma should be a suitable alternative for zirconia surface treatment prior to luting hence it improved microshear bond strength and provided higher surface energy without affecting surface roughness. (AU)

Objetivo: Este estudo investigou a influência de diferentes tratamentos de superfície na energia de superfície, rugosidade e resistência de união da zircônia. Material e Métodos: Quarenta e oito fatias de zircônia tetragonal policristalina estabilizada por ítria (Y-TZP - VITA InCeram® YZ for inLab®) (6,4 x 3,2 x 1,6 mm) foram divididas em 3 grupos de acordo com o tratamento de superfície (n = 16): YTZP_controle sem tratamento; YTZP_plasma - tratamento de superfície com plasma de oxigênio não térmico; YTZP_primer - aplicação de um primer cerâmico. A energia da superfície (n = 6) foi medida com o auxilio de um goniômetro; e a rugosidade superficial (n = 10) foi analisada com um perfilômetro 3D. Nos mesmos espécimes da rugosidade, prolongamentos de cimento resinoso (PANAVIA V5 - Kuraray Noritake Dental) foram construídos inserindo o cimento em micro túbulos de silicone (1mm de diâmetro interno de X 1 mm de comprimento). O teste de microcisalhamento foi realizado após 24h. Os dados foram analisados estatisticamente ANOVA um fator e teste auxiliar de Tukey (p < 0,05). Resultados: Os espécimes tratados com plasma de oxigênio apresentaram maiores valores de energia de superficie (p = 0,00) e resistência de união estatisticamente significante (p = 0,00) quando comparados aos grupos controle e do primer. A análise de rugosidade (p = 0,897) não detectou diferença estatística entre os grupos testados. Conclusão: O plasma não térmico pode ser uma alternativa para o tratamento de superfície de zircônia antes da cimentação, pois aumentou a resistência de união ao microcilsalhamento e proporcionou maior energia superficial sem afetar a rugosidade da superfície. (AU)

Bonding efficiency and durability: current possibilities

Abstract Bonding plays a major role in dentistry nowadays. Dental adhesives are used in association with composites to solve many restorative issues. However, the wide variety of bonding agents currently available makes it difficult for clinicians to choose the best alternative in terms of material and technique, especially when different clinical situations are considered. Moreover, although bonding agents allow for a more conservative restorative approach, achieving a durable adhesive interface remains a matter of concern, and this mainly due to degradation of the bonding complex in the challenging oral environment. This review aims to present strategies that are being used or those still in development which may help to prevent degradation. It is fundamental that professionals are aware of these strategies to counteract degradation as much as possible. None of them are efficient to completely solve this problem, but they certainly represent reasonable alternatives to increase the lifetime of adhesive restorations.

Adhesion of a self-etching adhesive to caries-affected dentin treated with different methods for caries removal: a preliminary study / Avaliação de um sistema adesivo autocondicionante em dentina afetada por cárie tratada por diferentes mecanismos de remoção: estudo preliminar

Objetivo: O objetivo deste estudo foi avaliar a adesão (RU) de sistemas autocondicionantes à dentina afetada por cárie (CAD) e dentina normal (ND), após diferentes técnicas de remoção de tecido cariado. Materiais e Métodos: Foram utilizados vinte e quatro molares humanos extraídos, com lesão de cárie oclusal. A amostra foi aleatoriamente dividida em 5 grupos, de acordo com o método de remoção do tecido cariado: G1 - controle negativo (sem remoção); G2 - disco abrasivo; G3 – broca de aço de baixa velocidade; G4 - laser Nd:YAG (21,2 J/cm2 ); G5 - laser Er:YAG (80,24 J/cm2 ). Dentinas normais e afetados / infectados foram tratadas com o sistema adesivo (Clearfil SE Bond) e coroas de resina foram construídas. Resultados: ANOVA um fator mostrou diferença estatisticamente significante entre os grupos experimentais (p < 0,001), com um valor menor para a dentina infectada (G1), quando comparado com todos os grupos experimentais. Maior RU foi observada para ND irradiada com laser Er:YAG, quando comparado a CAD. Para os espécimes tratados com broca e laser Nd:YAG, a RU em ND e CAD foi semelhante. Conclusão: a dentina infectada não é um substrato adequado para a adesão; laser de Nd:YAG e brocas de aço mostraram-se adequados como ferramenta de tratamento das dentinas normal e afetada prévio à instalação de restaurações adesivas. Contudo, ambas as dentinas tratadas pelos laser de Er:YAG, não interagiram adequadamente com o sistema auto-condicionante resultando em fraca adesão

Objective: The aim of this study was to evaluate the adhesion of a self-etching system to cariesaffected dentin (CAD) and sound dentin (SD) after different caries removal techniques by using microtensile bond strength test (μTBS). Materials and Methods: Twenty-four extracted human molars with coronal carious lesions were used. The samples were randomly divided into 5 groups, according to caries removal method: G1 - negative control (no removal); G2 abrasive disc; G3 – slow speed steel bur; G4 - Nd:YAG laser (energy density 21.2 J/cm2 ); G5 - Er:YAG laser (energy density 80.24J/cm2 ). SD and CAD/ infected dentin substrates were tested. Self-etch system (Clearfil SE Bond) was applied and resin crowns were built up. Results: One-way ANOVA showed statistically significant difference between experimental groups (p < 0.001), with significantly lower results for infected dentin (G1), when compared to all other experimental groups. A statistically significant higher bond strength value was observed for SD irradiated with Er:YAG laser when compared to CAD. For bur and Nd:YAG laser specimens, SD and CAD showed the same bonding performance. Conclusion: infected dentin is not an adequate substrate for bonding; Nd:YAG laser and steel burs showed the same bonding performance for both SD and CAD; while both dentins, when irradiated by Er:YAG laser, did not adequately interact with self-etching system resulting in poor adhesion

Influence of cleansing agents on enamel and dentin bond strength to a one-step self-etching adhesive system / Influência de agentes de limpeza em esmalte e dentina na resistência de união de um sistema adesivo auto-condicionante de passo único

Objective: The aim of this study was to detect the influence of application mode of cleansing agents, on enamel and dentin during the adhesion process of a one-step self-etching adhesive system. Materials & Methods: 24 human molars were sectioned into halves along the long axis for enamel and dentin tests. The cleansing agents used were 3% hydrogen peroxide (group HP), anionic detergent (group AD), and antiseptic solution (group AS). In the experiment, these agents were applied with (active) and without friction (passive) on enamel and dentin surfaces. A one-step self-etching adhesive system (Clearfil S3 Bond) was applied on dental surface and composite resin cylinders were built using Tygon tubing molds. After 24 h, μSBS (microshear) test (1 mm/ min) and fracture analysis were performed. Results: There was no statistically significant difference in bond strength values regarding the application mode of cleansing agents for enamel and dentin (p ≥ 0.05). The use of antiseptic solution on enamel resulted in bond strength results significantly higher when compared with HP and AD (p = 0.014). Conclusions: Regarding bond strength to enamel and dentin using one-step self-etching adhesive system, application mode of the cleansing agents used in this study presented the same behavior. Antiseptic solution applied on enamel before the application of a one-step adhesive system increased bond strength performance

Objetivo: O objetivo deste estudo foi detectar a influência do modo de aplicação de agentes de limpeza, em esmalte e dentina durante o processo de adesão de um sistema adesivo auto-condicionante de passo único. Materiais e Métodos: 24 molares humanos foram seccionados em duas metades ao longo do eixo para testes de esmalte e dentina. Os agentes de limpeza utilizados foram: peróxido de hidrogênio 3% (grupo HP), detergente aniônico (grupo AD) e solução anti-séptica (grupo AS). No experimento, esses agentes foram aplicados com fricção (ativa) e sem fricção (passiva) em superfícies de esmalte e dentina. O sistema adesivo autocondicionante de um passo (Clearfil S3 Bond) foi aplicado na superfície dental e cilindros de resina composta foram construídas usando moldes (Tubos Tygon). Após 24 h, o teste de microcisalhamento (1 mm / min) e análise de fratura foram executados. Resultados: Não houve diferença estatisticamente significante nos valores de resistência de união em relação ao modo de aplicação de agentes de limpeza para esmalte e dentina (p ≥ 0,05). O uso de solução anti-séptica no esmalte resultou em resultados de resistência de união significativamente maior quando comparada com HP e AD (p = 0,014). Conclusões: Em relação à resistência de união ao esmalte e dentina utilizando sistema adesivo autocondicionante de passo único, o modo de aplicação dos agentes de limpeza utilizados neste estudo apresentaram o mesmo comportamento. A aplicação da solução anti-séptica aplicada sobre o esmalte antes da aplicação de um sistema adesivo de passo único apresentou melhor desempenho de resistência de união.

A comparative leakage study on Er, Cr: YSGG laser- and bur- prepared Class V cavities restored with a low-shrinkage composite using different filling techniques

Aim: To evaluate the leakage on Er,Cr:YSGG laser- and bur- prepared Class V cavities restoredwith a silorane-based composite resin using different insertion techniques Methods: 40 cavitieswere outlined according to: the type of instrument [Er,Cr:YSGG laser (3.0 W power, energy perpulse of 150 mJ, fluence of 53.57J/cm2, pulse duration of 140-200 μs, 20 Hz repetition rate and55/65% air/water spray) or diamond bur]; and the type of filling technique (bulk increment orincremental). Four experimental groups were obtained (n=10): G1- diamond bur (DB) andincremental (I); G2- DB and bulk increment (BI); G3- Er,Cr:YSGG and I; and G4- Er,Cr:YSGGand BI. Specimens were restored with a silorane-based composite resin (Filtek P90, 3M/ESPE),subjected to 500 thermal cycles, sealed, infiltrated with 2% (w/v) methylene blue and sectioned inhalves. Specimen analysis was scored based on a scale. Statistical analyses were done usingthe Kruskal-Wallis and Student Newman-Keuls tests (α=0.05). Results: Statistically significantdifferences were observed between G2 and G4 (p=0.003) and between G1 and G2 (p=0.028).The filling technique did not influence the pattern of dye leakage in the cavity walls (p=0.151).Conclusions: Less leakage was observed when Er,Cr:YSGG cavities were restored withsilorane-based composite resin, using the bulk increment technique. Nevertheless, cavities doneusing diamond bur have less leakage only when incrementally restored.

Ensaio de resistência adesiva por microtração: revisão de literatura / Microtensile bond strengh test: a literature review

Atualmente, a fim de se avaliar a resistência de união entre substrato e material restaurador, o teste mais utilizado é o ensaio por microtração. Todavia, na literatura encontram-se diversas maneiras de se realizar esse teste, desde a seleção da amostra até a análise dos resultados obtidos. Nesta revisão de literatura serão apresentados os principais métodos para realização do teste de microtração, bem como os fatores que podem afetar nos resultados obtidos por este ensaio

Currently, in order to evaluate the bond strength between the dental substrate and the restorative material, microtensile bond strength is the most used test. The purpose of this review is to describe all of the various modifications of the microtensile bond test in one paper. In the literature there are several ways to perform this test, since the selection of the sample to the analysis of the results. In this literature review will be presented the main methods for microtensile testing, as well as factors that may affect the results obtained by this test. The microtensile test methods offer versatility that cannot be achieved by conventional methods, It is up to the researcher to choose the test characteristics that best suits your needs

Estudo da adesão de sistema autocondicionante utilizado em dentina hígida e afetada por cárie / Study of self-etching adhesive applied to soud and artificially caries-affected dentin

O substrato mais conveniente para testar o desempenho de união de sistemas adesivos em estudos de laboratório é a dentina hígida. No entanto, a dentina de padrão laboratorial difere da dentina que permanece clinicamente depois que o tecido cariado foi removido. Este estudo teve como objetivo avaliar a adesão de um sistema autocondicionante utilizado em diferentes substratos, dentina hígida e dentina afetada por cárie produzida artificialmente pelo método microbiológico. Foram utilizados 10 molares hígidos que foram submetidos à indução de cárie artificialmente pelo método microbiológico em metade da superfície oclusal em dentina. Após a indução de cárie o sistema adesivo autocondicionante Clearfil SE Bond foi aplicado na porção de dentina hígida e de dentina afetada e foram confeccionados dois cilindros de resina microparticulada em cada porção relativa aos dois substratos avaliados. O teste mecânico de microcisalhamento foi realizado e os valores obtidos em MPa foram avaliados pelo teste T para amostras pareadas (a=50f0) que mostrou não haver diferença estatisticamente significante entre os dois grupos experimentais analisados (p=0,0706). Pode-se concluir que a adesão do sistema adesivo autocondicionante utilizado foi igualmente efetiva quando utilizado em dentina hígida e afetada por cárie

The most convenient substrate to test the bonding performance of dental adhesives in laboratory studies is sound dentine. However, this standard laboratory dentine differs from the kind of dentine that clinically remains after carious tissue was removed. This study aimed to evaluate the adhesion of self-etching system used on sound dentin and caries-affected dentin artificially produced by microbiological method. Ten non-carious molars were submitted to caries induction by artificially microbiological method on half of occl usa I dentin surface. After caries induction the adhesive system Clearfil SE Bond was applied to sound and caries-affected dentin portions. Two cylinders of microfill composite were made in each portion on the two evaluated substrates. The microshear mechanical test was performed and the values in MPa were evaluated by t test for paired samples (a=5%). No statistically significant difference was demonstrated between the two experimental groups analyzed (p = 0.0706).lt can be concluded that the self-etching adhesive system used performed equally effective when used in sound and caries-affected dents

A ausência de radiopacidade em algunscimentos de ionômero de vidro / The absence of radiopacity of some glass ionomer cements

A radiopacidade é um pré-requisito imprescindível para materiais utilizados como base eforramento de restaurações. Possibilita que o profissional identifique a presença do material,permitindo a diferenciação com a estrutura dental adjacente. Objetivo: O objetivo desse estudofoi avaliar a radiopacidade de materiais de base e forramento disponíveis para uso clínico ecomparar com a radiopacidade do esmalte e dentina. Materiais e Métodos: Foram analisados:13 marcas comerciais de cimento de ionômero de vidro, 1 amálgama e 1 resina composta. Foramconfeccionados três corpos de prova com espessura de 1 mm para cada cimento de ionômerode vidro e para cada material restaurador. Obteve-se 1 espécime, com 1 mm de espessura, deesmalte/dentina através de um corte transversal da coroa dental. As tomadas radiográficas foramfeitas com o sistema digital ~VG 5000 Kodak e tempo de exposição de 0,32 segundos. Asimagens obtidas foram trabalhadas no programa Image Tool® obtendo-se os valores médiosde cinza. A análise estatística ANOVA, seguida pelo teste de Tukey (p 0,05) detectou diferençasconsideráveis. Resultados: Alguns cimentos de ionômero de vidro apresentaram radiopacidadeinferior à da dentina e inadequada segundo as normas ISO9917, sendo considerada insuficientepara um correto diagnóstico radiográfico. Conclusão: Conclui-se que existem cimentos de ionômerode vidro indicados como base e forramento de restaurações disponíveis para aquisiçãocom radiopacidade imprópria para serem detectados radiograficamente.

The radiopacity is an essential prerequisite for materiais used as a base liner and restorationsand allows the professional to identify the presence of the material allowing the differentiationfrom the adjacent tooth structure. Objectives: The aim of this study was to evaluate the radiopacityof base and liner materiais available for clinical use and compare to the radiopacity ofenamel and dentin. Materiais and methods: 13 glass ionomer cements, one resin composite andone amalgam were evaluated. Three specimens with 1 mm thickeness for each glass ionomercement and restorative material were prepared. Cross section was made from a third molardental crown to obtain enamel and dentin specimen with thickness of 1 mm. Radiographswere taken with digital system Kodak RVG5000 and exposure time of 0.32 seconds. The imageswere analysed through the programe Image Tool" to obtain the mean grey values. Statisticaltest ANOVA followed by Tukey test (p<0.05) detected considerable differences. Results: Someglass ionomer cements presented radiopacity lower than dentin, considered insufficient for acorrect radiographic diagnosis, according to ISO 9917. Conclusion: It was concluded that somebase and liner materiais available for purchase have an inadequaderadiopacity to be detectedradiographically.

Evaluation of caries-affected dentin with optical coherence tomography

The purpose of this study was to evaluate the degree of demineralization of artificially induced caries-affected human dentin by an in vitro microbiological method. The occlusal surfaces of 6 human molar teeth were abraded until a flat surface was obtained, and the enamel was removed to expose the occlusal dentin surface. These teeth were sectioned in 12 halves in the vestibular-lingual direction and divided into 3 groups according to the period length of the microbiological essay (n = 4): G1, 7 days; G2, 14 days; and G3, 21 days. The surfaces of all specimens were protected by an acid-resistant nail varnish, except for a window where the caries lesion was induced by a Streptoccocus mutans biofilm in a batch-culture model supplemented with 5 percent sucrose. The specimens were then analyzed by optical coherence tomography (OCT) with a super-luminescent light diode (Λ = 930 nm) with 6.0-µm lateral and longitudinal resolution (in the air). Qualitative and quantitative results (images and average dentin demineralization, respectively) were obtained. The mean demineralization depths were (µm) 235 ± 31.4, 279 ± 14, and 271 ± 8.3 in groups 1, 2, and 3, respectively. In addition, no significant change was observed in the lesion mean depth from 7 days of cariogenic challenge on. In conclusion, OCT was shown to be an efficient and non-invasive method to detect the depths of lesions caused by demineralization. Further, a seven-day demineralization time was considered sufficient for caries-affected dentin to be obtained.

Avaliação da influência da contaminação salivar na resistência de sistema adesivo autocondicionate de dois passos / Influence of Saliva contamination on the bonding resistance of a two-step self-etching

Este estudo teve o objetivo de avaliar a influência da contaminação salivar sobre a resistência de união (RU) em dentina de um sistema adesivo autocondicionante de dois passos. Sessenta dentes bovinos foram incluídos e lixados para exposição de dentina superficial, onde foi preparado smear layer padronizado. Seis grupos (n=10) foram divididos de acordo com os fatorers de variação: momento da contaminação [antes do sistema adesivo (G2 e G3); após aplicação do primer (G4); e após a aplicação do bond (G5 e G6)] e tratamento do contaminante [secagem (G2, G4 e G5) ou lavagem (G3 e G6)]. No grupo controle (G1), não houve contaminação. O sistema adesivo Clearfil SE Bond (SE) foi utilizado de acordo com as recomendações do fabricante. A contaminação foi efetuada com saliva aplicada sobre a área de dentina exposta, sendo o contaminante lavado por 10 segundos com jato de água ou secado por 10 segundos com jato de ar. A resina composta (Filtek Z-250, 3M ESPE) foi utilizada para montar os corpos-de-prova, que foram tracionados após 24 horas de estocagem em água a 37ºC. Os resultados obtidos (em MPa) foram avaliados por meio do teste ANOVA e comparados através do intervalo de confiança. Os resultados obtidos [G1-24,27(±2,82); G2-18,71(±5,51); G3-19,90(±4,56); G4-17,54(±6,24); G5-5,95 (±4,58); G6-6,91(±0,03)] demonstraram que a saliva influencia significativamente na RU, mas não os tratamentos do contaminante, e há influência estatisticamente significativa quanto ao momento em que ocorreu a contaminação.

Concluiu-se que a presença do contaminante reduz a resistência de união do sistema autocondicionate em dentina, sendo que o momento mais crítico para ocorrer a contaminação é após a aplicação do bond. Nenhum dos tratamentos da saliva realizados foi capaz de recuperar a resistência de união

Análise do selamento marginal de restaurações realizadas após preparo cavitário com Laser de Er; Cr: YSGG utilizando diferentes parâmetros em dentina hígida / Analysis of the marginal sealing of restorations after cavity preparation performed with laser Er, Cr: YSGG using different parameters in sound dentin

O objetivo deste trabalho foi avaliar a microinfiltração de restaurações classe V em preparos de cavidades obtidos com diferentes potências do laser Er; Cr: YSGG e as cavidades preparadas convencionalmente (ponta diamantada em alta rotação). Sessenta amostras de dentina foram divididas em seis grupos (n = 10). O primeiro grupo serviu como um controle padronizado com preparo de ponta diamantada (G1) e os demais grupos foram irradiados com laser de Er; Cr:YSGG com diferentes parâmetros: G2 - 2,0W; G3- 2,25W; G4- 2,5W; G5- 2,75W; G6- 3,0W. Este laser emite comprimento de onda de 2,78 µm e tem largura de pulso de 140 µm e taxa de repetição fixa de 20Hz. A energia do laser foi entregue através de um sistema de fibra óptica para um terminal de ponta de safira de 6 mm de comprimento e 600 µm de diâmetro, utilizando modo não-contato. O sistema adesivo autocondicionante (Clearfil SE Bond) e a resina composta micro-híbrida (Z-250) foram utilizados para compor os corpos de prova. Após as restaurações, os espécimes foram submetidos a teste de microinfiltração com solução de azul de metileno a 2% em pH 7,0 durante 4 horas, a 37ºC. Os resultados mostraram não haver diferença estatística (p = 0,203) entre grupos experimentais em que os preparos das cavidades foram realizados com ponta diamantada ou com diferentes parâmetros de energia do laser de Er; Cr: YSGG. A partir do presente estudo, pode-se concluir que a microinfiltração foi semelhante em todos os grupos experimentais independentemente do método de preparo cavitário de Classe V usado - laser Er; Cr:YSGG ou ponta diamantada

Análise morfológica e morfométrica da camada híbrida formada por adesivo autocondicionante na presença de sangue / Morphological and morphometrical analisys of a self-etching adhesive system hybrid layer formed in the presence of blood

Este estudo objetivou analisar, por meio de microscopia eletrônica de varredura (MEV), a interface adesiva de restaurações realizadas com sistema adesivo autocondicionante de dois passos (Clearfill SE Bond, Kuraray Co., Ltd., Osaka, Japão), contaminadas por sangue em dois momentos diferentes, recebendo essa contaminação dois tratamentos distintos. Quinze molares humanos foram divididos em cinco grupos experimentais (n = 3): G1 - controle (sem contaminação); G2 - contaminação antes do primer, com lavagem e secagem; G3 - contaminação antes do primer com secagem; G4 - contaminação após bond fotopolimerizado com lavagem e secagem; G5 - contaminação após bond fotopolimerizado com secagem. Os dentes tiveram sua superfície oclusal seccionada e lixada para obtenção de dentina plana. Os espécimes foram contaminados, de acordo com os grupos experimentais, e então foram restaurados e preparados para análise em MEV. Os resultados obtidos foram descritos de duas formas: análise morfológica, na qual foram observadas alterações na formação da camada híbrida (CH) em grupos com a presença do contaminante, e análise morfométrica, em que os dados foram analisados estatisticamente, e pode-se constatar uma relação entre a presença do contaminante e a diminuição do tamanho de tags, em µm, quando comparados ao grupo controle (p ≤ 0, 05). Adicionalmente, foi observado que o tratamento de lavagem com água não foi suficiente para restabelecer a formação de CH semelhante à observada em G1.

Longitudinal evaluation of the effect of saliva contamination during the bonding protocol with a self-etch adhesive system

Aim: To evaluate the influence of saliva contamination on the short- and long-term bond strength of a self-etch adhesive system. Methods: One hundred and twelve non-carious human molars were randomly divided according to: substrate (enamel/dentin); presence of saliva [none (control- C), before primer (BP), after primer (AP) and after bonding agent (AB)]; treatment of the contamination [none (1), rinsing + drying (2), drying (3) and primer re-application (4)] and specimen storage (24 h or 6 months). A self-etch adhesive system was applied to the dental surfaces followed by incremental insertions of composite resin. After storage in water at 37oC, the specimens were perpendicularly cut into beams for microtensile bond strength testing. Data in MPa were compared by A NOVA followed by Tukey’s test (p< 0.05). Micrographs were obtained by low vacuum scanning electron microscopy. Results: Control groups (G1 and G8) presented higher bond strength than all other groups. The factors presence of saliva, treatments of the contaminant and specimen storage showed no statistically significant results for the two dental substrates. Contaminants could be detected by LV-SEM. Six-month storage did not affect bond strength. Conclusions: The presence of saliva during the application of the self-etch system was deleterious to the bond to enamel and dentin, irrespective of the operative step in which the contamination occurred.

Effect of saliva contamination on the bond strength of an etch-and-rinse adhesive system to dentin / Efeito da contaminação salivar na resistência de união de um adesivo etch-and-rinse em dentina

Purpose: The aim of this study was to investigate the effect of saliva contamination on bond strength of an etch-and-rinse system to dentin. Methods: Fifty bovine incisors were embedded in acrylic resin and divided into 5 groups: G1 (control) - application of the adhesive system (Adper Single Bond 2 - 3M-ESPE); G2 - saliva contamination after acid etching of dentin, rinsing and drying; G3 - saliva contamination after acid etching of dentin and drying; G4 - saliva contamination after adhesive application, rinsing and drying; G5 - saliva contamination after adhesive application and drying. Contamination was performed by using 4 µL of simulated human saliva for 20 s. The adhesive system was applied according to the manufacturer's instructions; a composite resin was built as an inverted cone and was tested after 24 h at a cross-head speed of 0.5 mm/min. Results: When saliva contamination occurred after the adhesive photo-polymerization, bond strength was significantly reduced. The adhesive strength (MPa) mean values were: G1 = 18.1(±4.7) a; G2 = 20.5(±5.7) a; G3 = 17.3(±3.4) a; G4 = 12.6(±4.0) b; G5 = 9.8(±2.1) b (means followed by distinct letters are statistically different, P < 0.05). Conclusion: Saliva contamination negatively influenced bond strength of an etch-and-rinse adhesive, especially after the final polymerization of the adhesive system; in this condition, treatments were not efficient to recover adhesion.

Objetivo: Investigar o efeito da contaminação salivar na resistência de união de um adesivo condicione-e-lave em dentina. Metodologia: Cinquenta incisivos bovinos foram divididos em 5 grupos: G1 = (controle) aplicação do sistema adesivo (Adper Single Bond 2 - 3M-ESPE); G2 = contaminação com saliva após condicionamento ácido da dentina + lavagem e secagem; G3 = contaminação após o condicionamento ácido da dentina + secagem; G4 = contaminação com saliva após a aplicação do adesivo + lavagem e secagem; G5 = contaminação com saliva após a aplicação do adesivo + secagem. A contaminação foi realizada com 4 µL de saliva humana estimulada por 20 s. O sistema adesivo foi usado de acordo com as instruções do fabricante. A resina composta foi aplicada na forma de cone invertido, com o teste de tração realizado após24 h a 0,5 mm/min de velocidade. Resultados: As médias de resistência de união (em MPa): G1 = 18,1(±4,7) a; G2 = 20,5(±5,7) a; G3 = 17,3(±3,4) a; G4 = 12,6(±4,0) b; G5 = 9,8(±2,1) b, demonstrando que a resistência de união foi reduzida significativamente quando a contaminação salivar ocorreu após a fotopolimerização do adesivo. Conclusão: A contaminação influenciou negativamente a resistência de união do adesivo somente após a sua polimerização; nesta condição os tratamentos realizados não foram eficientes para recuperar a adesão.

Influência do uso da clorexidina na resistência de união de sistemas adesivos / Chlorhexidine influence on tensile bond strength of adhesive systems

O objetivo deste trabalho foi avaliar o efeito do modo de aplicação de uma substância inibidora da ação de metaloproteinases na resistência adesiva de dois sistemas adesivos (etch-and-rinse e self-etch) em dentina humana. Trinta e seis dentes humanos foram seccionados no sentido mésio-distal, perfazendo 72 espécimes (n=12) que foram incluídos e lixados até a exposição de dentina superficial e divididos em grupos:para o adesivo etch-and-rinse, realizou-se condicionamento com ácido fosfórico 35% por 15 segundos, seguido de lavagem, secagem e reumedecimento com água deionizada (G1); reumedecimento com solução aquosa de digluconato de clorexidina a 2% por 60 segundos (G2) ou por 30 segundos (G3). Quando se utilizou o sistema adesivo self-etch, o primer acídico foi aplicado por 20 segundos sobre dentina seca (G4). Adicionalmente, outros grupos experimentais foram realizados sob duas diferentes condições de reumedecimento da dentina com solução aquosa de digluconato de clorexidina a 2% por 60 segundos (G5) ou por 30 segundos (G6). Após o reumedecimento da dentina com a solução de clorexidina, a dentina foi seca e o primer e o bond, aplicados. Após a confecção, cones invertidos de resina composta microhíbrida foram imersos em água destilada (a 37ºC), realizando-se após 24 horas o ensaio mecânico de tração a uma velocidade de 0,5 mm/min. As fraturas foram avaliadas em lupa estereoscópica (40X). O resultado da análise de variância de dois fatores (Sistema Adesivo versus protocolo de reumedecimento), com comparações por meio do teste de Tukey, demonstrou haver diferença estatisticamente significativa (p<0,05), bem como para a interação entre esses fatores (p<0,05). Do exposto, pode-se concluir que o modo de aplicação da solução de clorexidina depende do tipo de sistema adesivo utilizado. Para o sistema etch-and-rinse, 60 segundos é o tempo de aplicação mais adequado, enquanto para o sistema self-etch a aplicação mais indicada é a de 30 segundos

Influência de duas técnicas de cimentação adesiva na retenção de pinos intra-radiculares de fibra de vidro / Influence of two adhesive cementation technique in retention force of fiber post system / Influence of two adhesive cementation technique in retention force of fiber post system

Introdução - Este estudo se propõe a comparar a força de retenção de núcleos diretos de fibra de vidro obtidos a partir das técnicas direta e direta-indireta, cujos preenchimentos radiculares foram realizados com diferentes materiais (cimento resinoso ou resina composta). Material e Métodos - Quarenta raízes de dentes bovinos com comprimento de 12 mm foram tratadas endodonticamente e divididas aleatoriamente em 4 grupos de acordo com a técnica de obtenção dos pinos e material utilizado para preenchimento (n=10): grupo 1 (técnica direta associada ao cimento resinoso); grupo 2 (técnica direta associada à resina composta); grupo 3 (técnica direta-indireta associada ao cimento resinoso); e grupo 4 (técnica direta-indireta associada à resina composta). A força de retenção foi determinada através do teste de tração usando Universal Testing Machine (Instron). Todos os dados foram analisados usando one-way analysis of variance (ANOVA) com a significância de p<0.05. Após o teste, as interfaces adesivas onde ocorreram as falhas foram examinadas e classificadas. Resultados - O grupo 4 (95,18N) apresentou força de retenção estatisticamente maior que os grupos 3 (57,94N), 2 (39,09N) e 1 (30,70N). A maior parte das fraturas ocorreu na interface dentina/resina. Conclusão - Com base nos resultados obtidos, conclui-se que a utilização da resina composta como material de preenchimento, utilizada com método direto-indireto proporcionou a melhor retenção dos pinos de fibra de vidro.

Introduction - The purpose of this study is to compare the retention force of direct-technique and direct-indirect technique using posts fulfilled with resin cement or resin. Material and Methods - Fourty bovine single root teeth with 12mm of length were used in this study. The roots were endodontically treated and randomly divided in four groups according to the fulfill material and technique used: group 1 (direct technique, resin cement), group 2 (direct technique, composite resin), group 3 (direct-indirect technique, resin cement), group 4 (direct-indirect technique, composite resin). The retention force was determined sing a Universal Testing Machine (Instron). All data were analyzed using one-way analysis of variance (ANOVA) and Scheffe's test. After the test, the failure was examined and classified according to the fracture place: post/ resin; resin/dentin; mix. Results - Group 4 (95,18N) showed statistically higher retention force than group 3 (57,94N), 2 (39,09N) and 1 (30,70N). Most of fracture occurred in interface between dentin/resin. Conclusion - Based on the obtained results, it was concluded that adhesive cementation technique influenced in the retention of glass fiber post with better retention force obtained when composite resin was used as a core build up material with direct-indirect technique.

Ensaio de microtração: uma revisão crítica da literatura / Microtensile bond test: a literature overview

O teste de microtração é uma importante ferramenta para o estudo da resistência adesiva, introduzida por Sano et al.24, em 1994. A nova proposta parecia solucionar as limitações dos ensaios tradicionais de cisalhamento e tração, tais como fraturas predominantemente coesivas nos substratos testados, além de permitir a localização das áreas de adesão e uma diminuição na dimensão dos espécimes. Entretanto, a confecção dos corpos-de-prova para execução do teste mostrou-se crítica, e suas particularidades se refletem nos resultados de resistência adesiva obtidos. Uma série de fatores devem ser considerados na análise dos resultados; o substrato envolvido, formato do corpo-de-prova, método de corte para sua obtenção, área de adesão e características das superfícies fraturadas são alguns dos itens que merecem ser analisados. Existem uma variedade de protocolos para execução do teste, o que dificulta a comparação entre os resultados obtidos. Cabe, portanto,realizar uma discussão crítica sobre os relatos encontrados na literatura

Influência da técnica restauradora na microinfiltração de restaurações Classe V de resina composta compactável / Restorative technique influence on microleakage of Class V restorations of packable composite resin

Introdução - O propósito deste estudo in vitro foi avaliar a microinfiltração em preparos Classe V restaurados com resina composta compactável (P60 - 3M) com diferentes técnicas restauradoras em associação ou não com resina composta de baixa viscosidade (Filtek Flow - 3M)como base. Material e Métodos - Foram confeccionados preparos Classe V em sessenta incisivos bovinos, condicionados com ácido fosfórico 37% e sistema adesivo (3M Single Bond) foi aplicado e fotopolimerado. As amostras foram divididas em seis grupos para serem restauradas com resina composta compactável com diferentes técnicas de inserção (incremental ou único), associando-se ou não a aplicação de resina de baixa viscosidade com espessuras variáveis como base das restaurações. Após acabamento, os dentes foram termociclados (5°-55°C; 700 ciclos) e a microinfiltração marginal foi avaliada através da imersão das amostras em solução de nitrato de prata (50%) por oito horas. A extensão da microinfiltração foi avaliada através de lupa estereoscópia e os dados foram analisados estatisticamente. Resultados - A aplicação da resina compactável pela técnica incremental aumentou a microinfiltração apenas quando se utilizou a resina fluida com 0,5 mm de espessura; quando se testou apenas a espessura da resina fluida independente da técnica restauradora empregada para a resina compactável os maiores escores de microinfiltração foram encontrados quando se utilizou maior espessura de resina fluida. Conclusões - Cavidades de Classe V de até 2 mm de profundidade podem ser restauradas com resina composta condensável utilizando técnica do incremento único. Quando da utilização de base de resina fluida associada a restauração com resina composta compactável, esta deverá ser utilizada em espessura de até 0,2 mm

Contaminação química superficial de implantes osseointegrados: estágio atual / Surface contamination of osseointegrated implants: current state of art

Atualmente, a implantodontia é um dos grandes recursos para a reabilitação oral. O êxito deste tipo de tratamento está diretamente relacionado à preservação da integridade dos dentes vizinhos e ao crescente avanço nos conhecimentos sobre biomateriais. O titânio, é hoje, o material de eleição para este tipo de procedimento, formando entre a sua superfície e o tecido ósseo a bioadesão. Diversos fatores podem contribuir para o inssucesso desta técnica, entre eles: a contaminação da superfície metálica, que pode ocorrer durante a produção, esterilização e manuseio dos implantes. Este estudo, baseado na revisão da literatura, procurou discutir a influência destas substâncias no sucesso clínico deste procedimento. Os implantes de titânio apresentam contaminação superficial, provenientes do processo de fabricação, limpeza, esterilização e embalagem, bem como durante a manipulação clínica do material; esta contaminação pode influir, negativamente, total ou parcialmente, no processo de osseointegração; dentre as substâncias que podem ser encontradas na superfície dos implantes destacam-se o carbono, cálcio, fósforo, sódio, flúor, silício, cloro, enxofre, alumínio, ferro e nitrogênio; são necessários estudos experimentais para se estabelecer os limites de contaminação e a influência desta no processo de osseointegração.