Evaluation of mechanical properties of fluoride-releasing dental materials after multiple fluoride recharge/discharge application / Avaliação das propriedades mecânicas de materiais dentários liberadores de flúor após aplicação múltipla de recarga/descarga de flúor

This study aimed to determine the mechanical properties of fluoride-releasing dental materials after an accelerated fluoride recharge/discharge procedure. Two fluoride-releasing glass ionomer types of cement (Ketac Molar Easymix and IonoStar Molar), a resin-modified glass ionomer (Photac Fil Quick Aplicap), and two compomers (Compoglass F and Glasiosite) were used in this study. A total of 30 rectangular specimens and 30 disk specimens of each material were prepared and placed in distilled/deionized water (n = 5). The amount of fluoride released was analyzed from the materials for 7-day discharge, 1st recharge, 7-day discharge, 2nd recharge, and 7-day discharge, and 3rd recharge. The de/pre- and post-recharge fluoride release were measured using an ion chromatography for 24 days. The flexural strength and microhardness of each group were evaluated. The microhardness of all restorative materials showed no significant change (p > 0.05) over the experimental period. The flexural strength properties of the restorative materials did not change within the time of the study. The study showed that the fluoride release/uptake causes no effect on the mechanical and physical properties of dental materials.

Este estudo teve como objetivo determinar as propriedades mecânicas de materiais dentários liberadores de flúor após um procedimento acelerado de recarga/descarga de flúor. Dois tipos de cimento de ionômero de vidro liberador de flúor (Ketac Molar Easymix e IonoStar Molar), um ionômero de vidro modificado por resina (Photac Fil Quick Aplicap) e dois compômeros (Compoglass F e Glasiosite) foram utilizados neste estudo. Um total de 30 amostras retangulares e 30 amostras de disco de cada material foram preparadas e colocadas em água destilada/deionizada (n = 5). A quantidade de fluoreto liberado foi analisada a partir dos materiais para descarga em 7 dias, 1ª recarga, descarga em 7 dias, 2ª recarga e descarga em 7 dias e 3ª recarga. A liberação de fluoreto pré e pós-recarga foi medida usando uma cromatografia de íons por 24 dias. A resistência à flexão e a microdureza de cada grupo foram avaliadas. A microdureza de todos os materiais restauradores não apresentou alteração significativa (p > 0,05) durante o período experimental. As propriedades de resistência à flexão dos materiais restauradores não mudaram no período do estudo. O estudo mostrou que a liberação/captação de flúor não afeta as propriedades mecânicas e físicas dos materiais dentários.

Formulation and characterization of antibacterial orthodontic adhesive

ABSTRACT Objective: The objective of this study was to formulate experimental orthodontic bracket adhesives and test their mechanical properties, fluoride release and antibacterial activity. Methods: Four experimental antibacterial orthodontic bracket adhesives were prepared with different compositions of synthesized antibacterial monomers replacing total 5% of dental monomers in the control Transbond XT (3M): 5%C11, 3.5%C11+1.5%C2, 5%C16, and 3.5%C16+1.5%C2. Transbond XT alone was used as control. These groups were used to bond premolar brackets to extracted premolars. Shear bond strength (SBS) was tested using an Instron machine. For antibacterial test, disk specimens (10mm diameter, 1mm thick, n=4) were fabricated and incubated with cultures of cariogenic Streptococcus mutans for 48h, and following gentle sonication, S. mutans biofilms in colony-forming-units (CFU) on the disks were enumerated by plating on agar medium. The data were analyzed using ANOVA and Tukey test (α=0.05). Results: All experimental groups had similar shear bond strength (no significant difference) to the control. All experimental groups showed significant inhibitory effect against S. mutans biofilm formation, when compared to the control, but there was no significant difference between experimental groups. Conclusion: Antibacterial orthodontic adhesive can be fabricated to have similar mechanical properties but better caries-inhibitory effect than current adhesive.

RESUMO Objetivo: o objetivo do presente estudo foi formular, experimentalmente, adesivos para colagem de braquetes ortodônticos e testar as suas propriedades mecânicas, sua liberação de flúor e sua atividade antibacteriana. Métodos: quatro adesivos ortodônticos antibacterianos foram preparados experimentalmente usando monômeros sintéticos antibacterianos com diferentes composições, substituindo-se 5% do monômero do grupo controle (Transbond XT, 3M) por: 5%C11; 3,5%C11 + 1,5%C2; 5%C16; ou 3,5%C16 + 1,5%C2. O Transbond XT original foi utilizado como controle. Esses diferentes adesivos foram usados para colar braquetes de pré-molares em pré-molares extraídos. A resistência da colagem ao cisalhamento (RCC) foi testada utilizando-se uma máquina Instron. Para os testes antibacterianos, amostras em formato de disco (10 mm de diâmetro, 1 mm de espessura, n = 4) foram fabricadas e incubadas por 48 horas com culturas cariogênicas de Streptococcus mutans. Após leve sonicação, os discos contendo os biofilmes de S. mutans em unidades formadoras de colônia (UFC) foram colocados em placas com meio de cultura ágar e numerados. Os dados foram analisados utilizando-se ANOVA e teste de Tukey (α?#8197;= 0,05). Resultados: todos os grupos experimentais apresentaram RCC semelhante (sem diferença significativa) ao grupo controle. Todos os grupos experimentais apresentaram significativo efeito inibitório contra a formação do biofilme de S. mutans, em comparação ao grupo controle, porém sem diferença significativa entre os grupos experimentais. Conclusão: adesivos ortodônticos antibacterianos podem ser produzidos para alcançar propriedades mecânicas semelhantes às dos adesivos atuais, porém com melhores efeitos inibitórios de cáries.

Evaluation of acidulated dentifrice influence on fluoride releasing from glass-ionomer cements / Avaliação da influência de creme dental acidulado na liberação de flúor de cimentos de ionômero de vidro

Objetivo: Avaliar a influência da exposição a um creme dental acidulado sobre a liberação de flúorde Cimentos de Ionômero de Vidro (CIV). Material e Métodos: Confeccionou-se 27 corpos de prova divididos em 3 grupos: G1 (Maxion - R), G2 (KetacMolar 3M/ESPE) e G3 (Vittremer 3M/ESPE), subdividido em subgrupos (n = 3): A (exposição ao creme dental flúor acidulado – pH 4,5 / 7 h / 37ºC), B (exposição ao creme dental fluoretado não acidulado / 7 h / 37 ºC) e C (controle - exposição à saliva artificial). Após exposição aos cremes dentais,os corpos de prova foram imersos em saliva artificial e aferidas a liberação de flúor nos períodos de tempo:1 e 14 dias. Os dados obtidos foram submetidos a análise de variância, utilizando o pacote SPSS (Statiscal Package for Social Science). Aplicou-se seo Teste ANOVA com 5% de probabilidade, para comparação das médias e do comportamento de cada material. Resultados: A exposição ao creme dental ácido apresentou valores de liberação de flúor (ppm/mm2) que variaram, em suas médias, de 1 e 14 dias:G1A (0,269 a 0,204); G2A (0,394 a 0,038); G3A(0,080 a 0,123). Foi estatisticamente significante a relação entre os subgrupos para G1 em T1 e G3 emT1 e T14. Conclusão: a exposição ao creme dental acidulado influenciou positivamente a liberação de flúor do CIV híbrido testado e não impactou a liberação deste íon nos CIVs convencionais.

Objectives: To evaluate the acidulated dentifrice influence on fluoride releasing from glass-ionomercements. Methods: 27 specimens were constructed,divided into 3 groups: G1 (Maxion - R), G2 (KetacMolar 3M/ESPE) and G3 (Vittremer 3M/ESPE), and subdivided into 3 subgroups (n = 3): A (exposure to acidulated fluoride dentifrice – pH 4.5 / 7h /37 ºC), B (exposure to non-acidulated fluoridedentifrice / 7h / 37 ºC), C (control - exposure toartificial saliva). After exposing, the specimens were immersed into artificial saliva and the fluoridere leasing measured at the following time periods:1 to 14 days. Data were subjected to analysis ofvariance using the Statistical Package for Social Science (SPSS). ANOVA test was applied with levelof significance of 5% to compare the means and the behavior of each material. Results: The exposure to acidulated dentifrice showed fluoride releasing means values (ppm/mm2) that varied from 1 and 14days : G1A (0.269 to 0.204); G2A (0.394 to 0.038);G3A (0.080 to 0.123). The relationship among the G1 subgroups at T1 and G3 subgroups at T1and T14 was statistically significant. Conclusion:The acidulated dentifrice positively influenced onfluoride releasing of hybrid GIC but not on that ofconventional GICs.

Orthodontic cements: immediate protection and fluoride release / Cimentos ortodônticos: proteção imediata e liberação de flúor

OBJECTIVES: The objective of the authors was to evaluate fluoride release of 3 glass ionomer cements with immediate protection of fluoride varnish (Cavitine, SS White), divided into 3 groups: Group M (Meron, VOCO), Group V (Vidrion C, SS White) and Group KC (Ketac-Cem, 3M ESPE). METHODS: Fluoride release was measured during 60 days by means of an ion-selective electrode connected to an ion analyzer. After 4 weeks, the test specimens were exposed to a solution of 0.221% sodium fluoride (1000 ppm of fluoride). RESULTS: Results showed that the cements reached a maximum peak of fluoride release in a period of 24 h. There was a statistically significant difference between the amount of fluoride released after the applications of fluoride among the groups from the 31st to 60th day (p> 0.05). CONCLUSION: The Vidrion C and Meron cements showed better performance to uptake and release fluoride when compared with Ketac-Cem cement.

OBJETIVO: o objetivo desse estudo foi avaliar a liberação de flúor dos seguintes três cimentos de ionômero de vidro, com proteção imediata de verniz fluoretado (Cavitine, S. S. White): Meron / VOCO (Grupo M); Vidrion C / S. S. White (Grupo V); e Ketac Cem / 3M ESPE (Grupo KC). MÉTODOS: a liberação de flúor foi medida durante 60 dias, através de eletrodo íon seletivo conectado a um analisador de íons. Após quatro semanas, os corpos de prova foram expostos a uma solução de fluoreto de sódio a 0,221% (1.000ppm de flúor). RESULTADOS: os resultados evidenciaram que os cimentos atingiram o pico máximo de liberação de flúor com 24h após a presa inicial. Houve diferença estatisticamente significativa entre os grupos, quanto à quantidade de flúor liberado após as aplicações de flúor, do 31º ao 60° dia (p > 0,05). CONCLUSÃO: os cimentos Meron e Vidrion apresentaram maior capacidade de captação e liberação de flúor, em comparação ao cimento Ketac Cem.

Liberação de flúor dos compósitos Superbond® e Ultrabond®: estudo in vitro / Release of fluoride composites Superbond® and Ultrabond®: study in vitro

O objetivo do presente trabalho foi verificar a hipótese que não há diferença no desempenho de compósitos ortodônticos entre si quanto à liberaçãode flúor. Foram analisados dois compósitos ortodônticos: Grupo SB (Superbond, OrthoSource) e Grupo UB (Ultrabond, Aditek) e um cimento de ionômero de vidro (CIV) convencional ortodôntico: Grupo S (Sumo, OrthoSource), como controle. A liberação de flúor foi medida durante 28 dias (1h, 24h, 1, 3, 7, 14, 21 e 28 dias), através de eletrodo íon seletivo conectado. Houve diferença estatística entre os grupos SB e UB com o grupo S em todos os tempos avaliados (p < 0.05). Pode-se concluir com a realização desse trabalho que os compósitos Superbond e Ultrabond apresentaram um desempenho semelhante entre si, porém pouco expressiva comparado ao CIV.

Técnica do tratamento restaurador atraumatico em estudantes de escola municipal do Rio de Janeiro: avaliação in vitro da influência da proteção superficial e do tempo de entrada em serviço na resistência a tração diametral do cimento de ionômero de vidro utilizado / Atraumatic restorative treatment realized in schoolchildren in municipal school – RJ – Brazil: in vitro evaluated of cohesive resistence and diametral traccion of the glass ionomer used

Tratamento restaurador atraumático tornou-se uma opção real para o tratamento da cárie dentária em saúde pública no Brasil. O presente estudo teve como objetivo avaliar durabilidade, resistência e eficácia de 70 restaurações em 31 alunos (entre 6 a 12 anos de idade na Escola Municipal Rotary, RJ - Brasil). Depois de CPO-D e ceo-exame de acordo com critérios da OMS, todos os alunos com selecionados receberam TRA com VITRO MOLAR ® - DFL, juntamente com instruções de saúde bucal. Os critérios de exclusão foram a presença de cavidades muito profundas e exposição pulpar, casos em que os alunos foram encaminhados para o Postos de Saúde Municipal. In vitro avaliou-se a influência do tempo de entrada em serviço e do tipo de cobertura protetora utilizada na resistência coesiva do Cimento de Ionômero de Vidro utilizado, por meio de ensaios de tração diametral. Confeccionou-se para o teste de tração diametral 6 espécimes para cada variante, 72 no total, com dimensões de 4 mm de diâmetro por 8 mm de comprimento, divididos entre os grupos: grupo1 – sem protetor (controle); grupo2 – vaselina sólida; grupo3 – verniz para unhas. Realizou-se ensaios mecânicos em uma máquina universal de ensaios EMIC DL 500 MF, após a confecção e estocagem individual dos espécimes em potes plásticos contendo 5 ml de água deionizada, que formaram os subgrupos descritos a seguir: a - 20 minutos; b - 2 horas; c - 24 horas; d - 7 dias. Os dados obtidos foram tratados por ANOVA e por Student Newman-Keuls (p<0,05). Ao se avaliar a influência dos diferentes protetores de superfície no CIV utilizado no presente trabalho observou-se que, os protetores de superfície tiveram influência no comportamento do material (p=0,000), com o verniz para unhas mostrando um desempenho superior ao da vaselina sólida. Quanto ao tempo, não foi possível verificar ruptura do material no prazo de 20 minutos, pois os corpos de prova sofriam deformação elástica catastrófica não sendo adequado para a finalidade...

Atraumatic restorative treatment (ART) has become a real option for caries treatment in public health in Brazil. The present study aimed to evaluate the durability, the resistance, and the effectiveness of ART restorations in vivo in 31 students (ages 6 to 12 yrs old at the Municipal Rotary School, RJ - Brazil). After DMF-T and dmf-t examination according to WHO criteria, all students with dental cavities received ART with VITRO MOLAR® - DFL, along with oral health instruction. In vitro were evaluated the influence of time of entry into service and the type of protective covering used in the cohesive strength of the cement Glass Ionomer used by diametral tensile (TD).The glass iomer was manipulates according manufacture instructions and divided in three groups 1-without protector(control) G2-with solid vaseline and G3- nails varnish. Exclusion criteria were the presence of very deep cavities and exposed pulp exposition, in which cases the students were referred to the Municipality Health Care. For the traction tests, it was confectioned 6 specimens measuring 4 mm of diameter and 8 mm of lengths, individually storage in plastic tubs with 5ml of deodenized water. The mechanic trials were done in a universal machine EMIC DL 500 MF. Data were analyzed by ANOVA and Student Newman-Keuls (p<0,05). The influence of different protectors in the Glass Inomer,in the present work, it was observed that they had few influence in the material behavior, most f the time similar to the control group and the material suffer distortion when under a 20 minutes traction. The restorations were clinically observed after 6, 12, and 24 mos. In total, 72 restorations were made in 31 students. After 6 months, 5 restorations were fractured and 3 presented with some material lost. At 12 months, 8 more restorations were lost, only 1 was fractured, and 7 had lost some material. After 24 months, 12 more restorations were lost, 3 had lost some material. Although not...

Técnica do tratamento restaurador atraumatico em estudantes de escola municipal do Rio de Janeiro: avaliação in vitro da influência da proteção superficial e do tempo de entrada em serviço na resistência a tração diametral do cimento de ionômero de vidro utilizado / Atraumatic restorative treatment realized in schoolchildren in municipal school – RJ – Brazil: in vitro evaluated of cohesive resistence and diametral traccion of the glass ionomer used

Tratamento restaurador atraumático tornou-se uma opção real para o tratamento da cárie dentária em saúde pública no Brasil. O presente estudo teve como objetivo avaliar durabilidade, resistência e eficácia de 70 restaurações em 31 alunos (entre 6 a 12 anos de idade na Escola Municipal Rotary, RJ - Brasil). Depois de CPO-D e ceo-exame de acordo com critérios da OMS, todos os alunos com selecionados receberam TRA com VITRO MOLAR ® - DFL, juntamente com instruções de saúde bucal. Os critérios de exclusão foram a presença de cavidades muito profundas e exposição pulpar, casos em que os alunos foram encaminhados para o Postos de Saúde Municipal. In vitro avaliou-se a influência do tempo de entrada em serviço e do tipo de cobertura protetora utilizada na resistência coesiva do Cimento de Ionômero de Vidro utilizado, por meio de ensaios de tração diametral. Confeccionou-se para o teste de tração diametral 6 espécimes para cada variante, 72 no total, com dimensões de 4 mm de diâmetro por 8 mm de comprimento, divididos entre os grupos: grupo1 – sem protetor (controle); grupo2 – vaselina sólida; grupo3 – verniz para unhas. Realizou-se ensaios mecânicos em uma máquina universal de ensaios EMIC DL 500 MF, após a confecção e estocagem individual dos espécimes em potes plásticos contendo 5 ml de água deionizada, que formaram os subgrupos descritos a seguir: a - 20 minutos; b - 2 horas; c - 24 horas; d - 7 dias. Os dados obtidos foram tratados por ANOVA e por Student Newman-Keuls (p<0,05). Ao se avaliar a influência dos diferentes protetores de superfície no CIV utilizado no presente trabalho observou-se que, os protetores de superfície tiveram influência no comportamento do material (p=0,000), com o verniz para unhas mostrando um desempenho superior ao da vaselina sólida. Quanto ao tempo, não foi possível verificar ruptura do material no prazo de 20 minutos, pois os corpos de prova sofriam deformação elástica catastrófica não sendo adequado para a finalidade ...

Atraumatic restorative treatment (ART) has become a real option for caries treatment in public health in Brazil. The present study aimed to evaluate the durability, the resistance, and the effectiveness of ART restorations in vivo in 31 students (ages 6 to 12 yrs old at the Municipal Rotary School, RJ - Brazil). After DMF-T and dmf-t examination according to WHO criteria, all students with dental cavities received ART with VITRO MOLAR® - DFL, along with oral health instruction. In vitro were evaluated the influence of time of entry into service and the type of protective covering used in the cohesive strength of the cement Glass Ionomer used by diametral tensile (TD).The glass iomer was manipulates according manufacture instructions and divided in three groups 1-without protector(control) G2-with solid vaseline and G3- nails varnish. Exclusion criteria were the presence of very deep cavities and exposed pulp exposition, in which cases the students were referred to the Municipality Health Care. For the traction tests, it was confectioned 6 specimens measuring 4 mm of diameter and 8 mm of lengths, individually storage in plastic tubs with 5ml of deodenized water. The mechanic trials were done in a universal machine EMIC DL 500 MF. Data were analyzed by ANOVA and Student Newman-Keuls (p<0,05). The influence of different protectors in the Glass Inomer,in the present work, it was observed that they had few influence in the material behavior, most f the time similar to the control group and the material suffer distortion when under a 20 minutes traction. The restorations were clinically observed after 6, 12, and 24 mos. In total, 72 restorations were made in 31 students. After 6 months, 5 restorations were fractured and 3 presented with some material lost. At 12 months, 8 more restorations were lost, only 1 was fractured, and 7 had lost some material. After 24 months, 12 more restorations were lost, 3 had lost some material. Although not ...

Fluoride release frompolyacid modified composites (compomers) in artificial saliva and lactic acid / Liberação de flúor por compósitos poliácidos modificados (compômeros) em saliva artifical e ácido lático

OBJECTIVES: The aim of this study was to assess the effect of different extraction media and time on the amount and pattern of fluoride release from compomers. MATERIAL AND METHOD: 42 specimens (n = 7 per group) in disc forms (7 mm diameter, 2 mm thickness) from three different compomers (were placed in artificial saliva (pH = 7.0) and lactic acid (pH = 5.2). The amount of the fluoride in these solutions were measured at 1st, 7th, 14th, 21th and 28th day time intervals by means of the fluoride ion selective electrode. The fluoride amount was calculated by concentration (ppm). The amount and the pattern of fluoride release was dependent on both the material, the storage medium and time. RESULTS: Fluoride release was evident for all the compomers but the rate of release varied considerably between the materials. Significant differences were also found between the different types of compomer (p < 0.01). A time dependent increase in the fluoride content was observed for all the compomers in both media. For all the tested materials, the fluoride release was higher in the lactic acid (p < 0.01). The amount of fluoride release was the most from Compoglass followed by Dyract AP and Glasiosite at 28th days, in both artificial saliva and lactic acid respectively. The least amount of fluoride release was observed at the first day.

OBJETIVOS: O objetivo deste estudo foi determinar o efeito de diferentes meios e tempo na quantidade e padrão de liberação de flúor por compômeros. MATERIAL E MÉTODO: 42 espécimes (n = 7 por grupo) em discos (7 mm de diâmetro, 2 mm de espessura), três compômeros diferentes, foram colocados em saliva artificial (pH 7,0) e ácido lático (pH 5,2). A quantidade de flúor nas soluções foram medidas a intervalos semanais, do 1º ao 28º dias (quatro semanas) por meio de eletrodos seletivos para íons flúor. A quantidade de flúor foi calculdada por concentração(ppm). A quantidade e o padrão da liberação de flúor variou consideravelmente tanto do material, do meio de armazenamento e tempo. RESULTADOS: A liberação de flúor foi evidente por todos os compômeros, mas a taxa de liberação variou consideravelmente entre os diferentes tipos de compômeros (p < 0.01). Um aumento relacionado com o tempo no conteúdo de flúor foi observado para todos os compômeros em ambos os meios. Para todos os materiais testados, a liberação de flúor foi maior no ácido lático (p < 0.01). A quantidade de liberação de flúor foi maior pelo Compoglass®, seguido pelo Duract AP® e Glasiosite® aos 28 dias, tanto na saliva artificial como no ácido lático respectivamente. A menor liberação de flúor foi observada no primeiro dia.

Liberação de flúor de cimentos ortodônticos com e sem proteção imediata / Fluoride release of orthodontic cements with and without immediate protection

O objetivo do autor foi avaliar a liberação de flúor de três cimentos de ionômero de vidro, com e sem proteção imediata de verniz fluoretado (Cavitine, SSWhite), divididos em seis grupos: Grupos M(sv) e M(cv) (Meron, Voco), V(sv) e V(cv) (Vidrion C, DFL), KC(sv) e KC(cv) (Ketac-Cem, 3M Espe) sem (sv) e com (cv), proteção, respectivamente. A liberação de flúor foi medida durante 33 dias, através de eletrodo íon seletivo conectado a um analisador de íons. Os resultados evidenciaram que a proteção imediata influenciou no tempo de 1h. Os cimentos Vidrion C e Meron apresentaram um desempenho melhor.

Avaliação in vitro da resistência ao cisalhamento e liberação de flúor de dois cimentos de ionômero de vidro reforçado por resina / In vitro evaluation of shear bond strength and fluoride release from two resin-reinforced glass ionomer cements

O objetivo deste estudo foi avaliar os cimentos de ionômero de vidro reforçados com resina Fuji Ortho LC e Fuji Ortho Band (GC América Corporation, Tokyo, Japan) quanto a resistência ao cisalhamento e liberação de flúor. Para avaliação da resistência ao cisalhamento utilizou-se 60 incisivos inferiores permanentes bovinos divididos em três grupos (n = 15). No Grupo 1, 2 e 3, as colagens foram realizadas com Transbond XT, Fuji Ortho LC e Fuji Ortho Band respectivamente. Após a colagem realizou-se o ensaio de cisalhamento de toda amostra à velocidade de 0,5 mm por minuto. A liberação de flúor dos materiais foram medidas durante 28 dias (1h, 24 h, 3, 7, 14, 21 e 28 dias) através de eletrodo íon seletivo conectado a um analisador de íons. Os resultados demonstraram que quanto a resistência ao cisalhamento (MPa) houve diferenças estatísticas entre os grupos 1 e 3, 2 e 3 (p > 0,05). Quanto a liberação de flúor os resultados evidenciaram diferença estatisticamente significante entre os grupos 1 e 3 e 2 e 3 em todos os tempos (p = 0.00) e entre os grupos 1 e 2 na avaliação de 3 dias de liberação de flúor (p = 0.00). Baseado nos resultados obtidos conclui-se que os materiais Transbond XT e Fuji Ortho possuem melhor resistência ao cisalhamento por??m menor liberação de flúor quando comparado ao Fuji Ortho Band.

The objective of this study was to evaluate two resin-reinforced glass ionomer cements, Fuji Ortho LC and Fuji Ortho Band (GC América Corporation, Tokyo, Japan) in terms of shear bond strength and fluoride release. Sixty bovine permanent lower incisors were divided into three groups (n = 15). In Groups 1, 2, and 3 the bonding procedures were performed with Transbond XT, Fuji Ortho LC, and Fuji Ortho Band materials respectively. Next, the samples were submitted to bond strength testing at crosshead speed of 0.5 mm/minute. Fluoride release from such materials was measured during 28 days (1h, 24 h, 3, 7, 14, 21, and 28 days) by means of selective ion electrodes connected to an ion analyser. With respect to the shear bond strength (MPa), the results demonstrated statistical differences between groups 1 and 3 as well as between groups 2 and 3. With respect to the fluoride release, the results showed statistically significant results between groups 1 and 3 as well as between groups 2 and 3 for all time periods (p = 0.00). Also, the 3-day evaluation showed statistical differences between groups 1 and 2 regarding fluoride release (p = 0.00). Based on the results obtained in the present study, one can conclude that Transbond XT and Fuji Ortho materials have a better shear bond strength than the Fuji Ortho Band one, although the latter releases less fluoride.