Shrinkage stress and elastic modulus assessment of bulk-fill composites

Abstract Bulk-fill composites were introduced in dentistry to accelerate clinical procedures while providing adequate outcomes. Concerns regarding the use of bigger composite increments rely on the polymerization shrinkage and shrinkage stress, which may generate gaps on the adhesive interface and result in a reduced success rate. Objective: To evaluate the polymerization shrinkage stress of different bulk-fill resin composites and their elastic modulus. Materials and Methods: Fourteen specimens were made for each of the nine different resin composites (seven with 12 mm3 and seven with 24 mm3): Surefill SDR flow (SDR), X-tra Base (XB), Filtek Bulk Fill Flowable (FBF), Filtek Z350XT Flow (Z3F); Tetric Evo Ceram Bulk Fill (TBF), X-tra Fil (XF), Filtek Bulk Fill (FBP), Admira Xtra Fusion (ADM) and Filtek Z350 XT (Z3XT). Linear shrinkage stress was evaluated for 300 s with the aid of a linear shrinkage device adapted to a Universal Testing Machine. For each composite group, seven additional specimens (2x2x25 mm) were made and Young's modulus was evaluated with a 3-point bending device adapted in a Universal Testing Machine with 0.5 mm/min crosshead speed and 50 KgF loading cell. Results: For 12 mm3 specimens, three-way ANOVA showed that only SDR and TBF generated lower stress after 20 s. Considering 300 s, TBF, SDR, and XF generated the lowest stress, followed by ADM, FBP, XB, and FBF, which were similar to Z3XT. Z3F generated the highest stress values for all time points. Considering 24 mm3 specimens after 20 s, all bulk fill composites generated lower stress than Z3XT, except XB. After 300 s, SDR, FBP, and ADM generated the lowest stress, followed by TBF and XF. For elastic modulus, one-way ANOVA showed that FBF, SDR, Z3F, and ADM presented the lowest values, followed by XB and TBF. FBP, Z3XT, and XF presented the highest elastic modulus among the evaluated composites. Conclusions: Bulk-fill resin composites presented equal to lower shrinkage stress generation when compared to conventional composites, especially when bigger increments were evaluated. Bulk-fill composites showed a wide range of elastic modulus values, but usually similar to "regular" composites.

Marginal and internal fit of zirconia copings obtained using different digital scanning methods

Abstract The objective of this study was to evaluate the marginal and internal fit of zirconia copings obtained with different digital scanning methods. A human mandibular first molar was set in a typodont with its adjacent and antagonist teeth and prepared for an all-ceramic crown. Digital impressions were made using an intraoral scanner (3Shape). Polyvinyl siloxane impressions and Type IV gypsum models were also obtained and scanned with a benchtop laboratory scanner (3Shape D700). Ten zirconia copings were fabricated for each group using CAD-CAM technology. The marginal and internal fit of the zirconia copings was assessed by the silicone replica technique. Four sections of each replica were obtained, and each section was evaluated at four points: marginal gap (MG), axial wall (AW), axio-occlusal edge (AO) and centro-occlusal wall (CO), using an image analyzing software. The data were submitted to one-way ANOVA and Tukey's test (α = 0.05). They showed statistically significant differences for MG, AO and CO. Regarding MG, intraoral scanning showed lower gap values, whereas gypsum model scanning showed higher gap values. Regarding AO and CO, intraoral digital scanning showed lower gap values. Polyvinyl siloxane impression scanning and gypsum model scanning showed higher gap values and were statistically similar. It can be concluded that intraoral digital scanning provided a lower mean gap value, in comparison with conventional impressions and gypsum casts scanned with a standard benchtop laboratory scanner.

Influence of different fillers on the properties of an experimental vinyl polysiloxane

Abstract The aim of the study was to evaluate the effect of the incorporation of different fillers on an experimental vinyl polysiloxane (VPS) at two different concentrations, 20% and 40%. Different fillers were added to an experimental VPS. The study was developed in two stages: (i) incorporation of fillers in different concentrations: (a) 20 wt% fillers, and (b) 40 wt%. The fillers were added to experimental VPS and mixed with a speed mixer; (ii) characterization of experimental VPS; after the base paste and catalyst paste were mixed, the experimental VPS was used to make specimens specifically for each test, which were stored at 23°C for 24 hours. The tests were designed according to the specific standardization for the analysis of tensile strength, detail reproduction, Shore A hardness, and elastic recovery. For analysis of filler size pattern, scanning electron microscopy at 1500× magnification was used. The aerosil OX-50 40% (AE), and pure aluminum hydroxide 40% (PAH) groups presented the highest tensile strength and Shore A hardness values. However, those were the only groups that did not present continuous detail reproduction of an intersection of 20 μm line. The elastic recovery was not statistically significant. The undesirable characteristics of VPS (lowest Shore A hardness and tensile strength) were observed when it was added to the composition of acrylic polymer (AP) and fiberglass (FG) in both concentrations, 20% and 40%. In groups AE and PAH, agglomerates of nanofillers were shown in SEM micrography, while the other groups presented different shapes and fillers sizes.

Uso de la herramienta Google Trends para estimar la incidencia de enfermedades tipo influenza en Argentina / Using Google Trends to estimate the incidence of influenza-like illness in Argentina / Uso da ferramenta Google Trends para estimar a incidência de síndrome gripal na Argentina

El objetivo del presente estudio fue hallar un modelo para estimar la incidencia de enfermedades tipo influenza (ETI), a partir de los términos de búsqueda relacionados recolectados por el Google Trends (GT). Los datos de vigilancia de ETI para los años 2012 y 2013 se obtuvieron del Sistema Nacional de Vigilancia de la Salud de Argentina. Las búsquedas de Internet se obtuvieron de la base de datos del GT, usando 6 términos: gripe, fiebre, tos, dolor de garganta, paracetamol e ibuprofeno. Se desarrolló un modelo de regresión de Poisson a partir de datos del año 2012, y se validó con datos del 2013 y resultados de la herramienta Google Flu Trends (GFT). La incidencia de ETI del sistema de vigilancia presentó fuertes correlaciones con las estimaciones de ETI del GT (r = 0,927) y del GFT (r = 0,943). Sin embargo, el GFT sobreestimó el pico de incidencia por casi el doble, mientras que el modelo basado en el GT subestimó el pico de incidencia por un factor de 0,7. Estos resultados demuestran la utilidad del GT como un complemento para la vigilancia de la influenza.

The aim of this study was to find a model to estimate the incidence of influenza-like illness (ILI) from the Google Trends (GT) related to influenza. ILI surveillance data from 2012 through 2013 were obtained from the National Health Surveillance System, Argentina. Internet search data were downloaded from the GT search engine database using 6 influenza-related queries: flu, fever, cough, sore throat, paracetamol, and ibuprofen. A Poisson regression model was developed to compare surveillance data and internet search trends for the year 2012. The model's results were validated using surveillance data for the year 2013 and results of the Google Flu Trends (GFT) tool. ILI incidence from the surveillance system showed strong correlations with ILI estimates from the GT model (r = 0.927) and from the GFT tool (r = 0.943). However, the GFT tool overestimates (by nearly twofold) the highest ILI incidence, while the GT model underestimates the highest incidence by a factor of 0.7. These results demonstrate the utility of GT to complement influenza surveillance.

O objetivo deste estudo foi encontrar um modelo para estimar a incidência da síndrome gripal com base nos termos de busca relacionados recolhidos pelo Google Trends (GT). Os dados de monitoramento de síndrome gripal entre 2012 e 2013 foram obtidos no Sistema Nacional de Vigilância de Saúde da Argentina. As pesquisas na Internet foram feitas baseando-se no banco de dados do GT usando 6 termos: gripe, febre, tosse, dor de garganta, paracetamol e ibuprofeno. Um modelo de regressão de Poisson foi desenvolvido valendo-se de dados de 2012. O modelo foi ajustado e validado com dados de 2013 e comparado com os resultados da ferramenta Google Flu Trends (GFT). A incidência de síndrome gripal mostrou uma forte correlação com estimativas do GT (r = 0,927) e GFT (r = 0,943). No entanto, o GFT superestimou o pico de incidência por quase o dobro, e o modelo baseado no GT subestimou o pico de incidência por um fator de 0,7. Esses resultados demonstram a utilidade do GT como um suplemento para a vigilância da influenza.

A comparative evaluation of tray spacer thickness and repeat pour on the accuracy of monophasic polyvinyl siloxane impression material: In vitro study.

Purpose: This study was aimed to determine the effect of various tray spacer thickness and subsequent repeated pours on the accuracy and dimensional stability of the impression made from monophasic polyvinyl siloxane material. Materials and Methods: Custom trays with different spacer thickness (2, 4 and 6 mm) were used for making an impression of a master model simulating 3 unit fixed partial denture with monophasic polyvinyl siloxane material. These impressions were poured with die stone and repoured. Distance between the reference points were measured and subjected to statistical analysis. Result: Casts obtained from 1 st , 2 nd and 3 rd pour of the impression in 2, 4 and 6 mm spacer thickness tray have similar dimensional accuracy amongst each other and with the master model except in molar diameter and inter-abutment distances of cast obtained from 6 mm spacer thickness tray. Conclusion: The vertical distance of stone dies were decreased, whereas horizontal distance increased as the thickness of impression material is increased. There were statistically non-significant changes occurring among the repeated pours in 2, 4 and 6 mm spacer thickness. Clinical Implication: 2 and 4 mm spacer thickness are acceptable for making an impression for three unit fixed partial denture with monophasic polyvinyl siloxane material and it was not affected by two subsequent (1 st and 2 nd ) repeated pours.

Impact of filler size and distribution on roughness and wear of composite resin after simulated toothbrushing

OBJECTIVES: Nanofilled composite resins are claimed to provide superior mechanical properties compared with microhybrid resins. Thus, the aim of this study was to compare nanofilled with microhybrid composite resins. The null hypothesis was that the size and the distribution of fillers do not influence the mechanical properties of surface roughness and wear after simulated toothbrushing test. MATERIAL AND METHODS: Ten rectangular specimens (15 mm x 5 mm x 4 mm) of Filtek Z250 (FZ2), Admira (A), TPH3 (T),Esthet-X (EX), Estelite Sigma (ES), Concept Advanced (C), Grandio (G) and Filtek Z350 (F) were prepared according to manufacturer's instructions. Half of each top surface was protected with nail polish as control surface (not brushed) while the other half was assessed with five random readings using a roughness tester (Ra). Following, the specimens were abraded by simulated toothbrushing with soft toothbrushes and slurry comprised of 2:1 water and dentifrice (w/w). 100,000 strokes were performed and the brushed surfaces were reanalyzed. Nail polish layers were removed from the specimens so that the roughness (Ra) and the wear could be assessed with three random readings (µm). Data were analyzed by ANOVA and Tukey's multiple-comparison test (α=0.05). RESULTS: Overall outcomes indicated that composite resins showed a significant increase in roughness after simulated toothbrushing, except for Grandio, which presented a smoother surface. Generally, wear ofnanofilled resins was significantly lower compared with microhybrid resins. CONCLUSIONS: As restorative materials suffer alterations under mechanical challenges, such as toothbrushing, the use of nanofilled materials seem to be more resistant than microhybrid composite resins, being less prone to be rougher and worn.

Effect of five brands of latex gloves on the setting time of polyvinyl siloxane putty impression materials.

Addition silicone impression materials have been used as impression material for more than 20 years. Although they are among the most expensive impression materials, they became popular during the past decade as they have excellent physical properties. Prevention of infection is an important aspect in dental treatment since dental professionals are routinely exposed to the wide variety of microorganisms present in saliva. Gloves are the most common protective measure used during dental treatment. The gloves are mostly made of latex. In this study, we examine how the setting time of three types polyvinyl putty materials were affected by the use of five different brands of latex gloves and one brand of vinyl gloves. Each material was first mixed without wearing gloves according to the manufacturer's instructions. After the stipulated mixing time, the setting time was measured using the Vicat needle. The setting time is measured from the time of mixing till the time that the needle does not produce any indentation on the surface of the material. The putty material was then mixed with gloved hands (using the five different brands of latex gloves in turn) and the setting time was measured. Then the material was mixed with washed gloved hands, and the setting time was measured again. Finally, the material was mixed with vinyl gloved hands and the setting time was measured. The following conclusions were drawn from the study: Reprosil™ and Express™ showed significant variation in the setting time with the latex gloved hands. There was no significant variation in the setting time when material was mixed with unwashed vs washed gloved hands. Vinyl gloves did not significantly affect the setting time of any of the putty impression materials.

Effects of sulfur-based hemostatic agents and gingival retraction cords handled with latex gloves on the polymerization of polyvinyl siloxane impression materials

OBJECTIVES: This study investigated the possible interactions between three addition silicone materials (Express®, Aquasil Ultra® and Adsil®), three hemostatic agents (ferric sulfate, StatGel FS®; aluminum sulfate, GelCord®; and aluminum chloride, Hemostop®) and gingival retraction cords previously handled with latex gloves to determine whether direct contact with medicaments or indirect contamination by latex in conditions similar to those found in clinical practice inhibit or affect the setting of the impression materials. MATERIAL AND METHODS: A portable device for the simultaneous test of several specimens was specifically developed for this study. Polymerization inhibition was analyzed by examination of the impressions and the molded surface. Ten trials were performed for each addition silicone material used in the study, at a total of 240 study samples. RESULTS: All the samples tested (N=240) were nonreactive regardless of the type of combination used. CONCLUSIONS: Aluminum sulfate, ferric sulfate and aluminum chloride hemostatic solutions did not show any inhibitory potential on the addition silicone samples under study, and there were no changes in polymerization as a result of contact between addition silicone and retraction cords handled with latex gloves.

Dimensional accuracy and detail reproduction of two hydrophilic vinyl polysiloxane impression materials tested under different conditions.

Background and Objectives: A limitation of vinyl polysiloxane (VPS) impression materials is hydrophobicity, and manufacturers have added surfactants and labeled these new products as "hydrophilic." The purpose of this investigation was to evaluate and compare the dimensional accuracy and surface detail reproduction of two hydrophilic VPS impression materials under dry, moist, and wet conditions. Materials and Methods: Ten impressions were made under dry, moist, and wet conditions respectively, with monophase, and regular body VPS impression material using a stainless steel metal die similar to that described in American Dental Association (ADA) specification 19, with lines scribed on it. Dimensional accuracy was measured by comparing the average length of the middle horizontal line in each impression to the same line on the metal die, by using a measuring microscope. The surface detail was evaluated. A one-way analysis of variance and Student t-test were used to compare mean dimensional changes (α = 0.05). Results: Conditions (dry, moist, and wet) did not cause significant adverse effects on the dimensional accuracy of either material. The mean dimensional changes were 0.00084% (+0.00041%) for monophase and 0.00119% (+0.00033%) for regular body. Monophase material was satisfactory in detail reproduction 100% of the time in dry conditions, 90% in moist, and only 20% in wet conditions. The regular body showed 100% satisfactory impressions in dry, 80% in moist, and 10% in wet conditions. With the additional smooth surface evaluation, only under dry conditions impressions with clinically acceptable surface quality were produced. Conclusions: Dimensional changes for both materials were well within ADA standards of minimal shrinkage value of 0.5%.

A comparative study to evaluate the discrepancy in condylar guidance values between two commercially available arcon and non-arcon articulators: A clinical study.

Aim: The purpose of this study was comparative evaluation of sagittal condylar values of arcon and non-arcon articulators with cephalometric readings and to determine the amount of discrepancy in sagittal condylar guidance values between arcon and non-arcon articulators using same protrusive record. Materials and Methods: Twenty subjects in the age group of 19-35 years, free from temporomandibular joint dysfunction, and occlusal disharmony, with healthy dentition participated in the study. Hanau H2 (non-arcon type) and Hanau Wide-Vue (arcon type) articulators were programmed for sagittal condylar guidance values using the same protrusive record made in polysiloxane bite registration material with edge to edge degree of protrusion. The resultant values for both the articulators on either side were compared with values obtained from tracing of digital lateral cephalogram using Kodak Dental imaging Window software 6.6.3.0-C program. The tabulated data were subjected to statistical analysis, ANOVA (Fishers 'F' test) for group comparison, Tukey's HSD test for inter-comparison, student's unpaired 't' test for intra-group comparison, and level of significance (P) was calculated using the same. Results: The mean sagittal condylar guidance values of the three different groups were found to be very highly significant (P=0.001) and highly significant (P=0.002) on the right and left sides respectively. There was a very highly significant difference (P=0.001) and highly significant difference (P=0.003) between the arcon and non-arcon group on the right and left side respectively. No significant difference was found between the arcon and cephalometric group (P=0.284 right, P=0.853 left) and a statistically significant difference was found between the non-arcon and cephalometric group (P=0.049 right, P=0.015 left). On intragroup comparison there was no statistically significant difference in sagittal condylar values on the right and left sides. Conclusion: The mean difference in the sagittal condylar guidance values obtained from non-arcon and arcon articulators shows a low level of reproducibility, and no significant difference found in mean sagittal condylar values obtained from arcon articulator and cephalometric tracings indicates replication of sagittal condylar guidance value from image of articular eminence.

Surface energy and wettability of polymers light-cured by two different systems

OBJECTIVE: This study evaluated the surface energy and wettability of composite resins polymerized by different light-curing units to ascertain the good wetting of tooth surfaces to achieve adhesion. MATERIAL AND METHOD: Filtek Z350 (3M ESPE), Admira (VOCO) and Grandio (VOCO) resins were selected for the testing procedures. The resins were light cured using LED and Halogen devices. Contact angles were measured goniometrically (Ramé-Hart F100) using water and glycerol as test liquids. Surface energy values were calculated with a software program (DROPimage Standard) that uses the harmonic mean method applied to the acid-base theory. The data were analyzed statistically by ANOVA and Tukey's test with a significance of 0.05. RESULTS AND CONCLUSIONS: No statistically significant differences were found between the values of surface energy. The measured wettability differed statistically in most combinations as a function of the type of composite resin, type of light-curing unit, and the test liquid.

Inorganic particle analysis of dental impression elastomers

The aim of this study was to determine quantitatively and qualitatively the inorganic particle fraction of commercially available dental elastomers. The inorganic volumetric fraction of two addition silicones (Reprosil Putty/Fluid and Flexitime Easy Putty/Fluid), three condensation silicones (Clonage Putty/Fluid, Optosil Confort/Xantopren VL and Silon APS Putty/Fluid), one polyether (Impregum Soft Light Body) and one polysulfide (Permlastic Light Body) was accessed by weighing a previously determined mass of each material in water before and after burning samples at 600ºC, during 3 h. Unsettled material samples were soaked in acetone and chloroform for removal of tthe organic portion. The remaining filler particles were sputter-coated with gold evaluation of their morphology and size, under scanning electron microscopy (SEM). Flexitime Easy Putty was the material with the highest results for volumetric particle fraction, while Impregum Soft had the lowest values. Silon 2 APS Fluid presented the lowest mean filler size values, while Clonage Putty had the highest values. SEM micrographs of the inorganic particles showed several morphologies - lathe-cut, spherical, spherical-like, sticks, and sticks mixed to lathe-cut powder. The results of this study revealed differences in particle characteristics among the elastometic materials that could lead to different results when testing mechanical properties.

O objetivo desse estudo foi determinar quantitativamente e qualitativamente a fração de partículas inorgânicas de elastômeros dentais disponíveis comercialmente. A fração volumétrica de dois silicones por adição (Reprosil Denso/Fluído e Flexitime Denso/Fluído), três silicones por condensação (Clonage Denso/Fluído, Optosil/Xantopren, e Silon 2 APS Denso/Fluído), um poliéter (Impregum Soft Light) e um polissulfeto (Permlastic Light Body) foi determinada pela pesagem prévia de uma determinada massa de cada material em água antes e após a queima das amostras a 600ºC, por 3 h. Amostras de material não polimerizado foram imersas em acetona e clorofórmio para a remoção da parte orgânica. As partículas de carga remanescentes foram cobertas com uma camada de ouro para avaliação da sua morfologia e tamanho, em microscopia eletrônica de varredura. O material Flexitime Denso foi o material com maior fração volumétrica de partículas de carga, enquanto que o Impregum teve menor fração volumétrica. Silon 2 APS Fluído apresentou partículas de carga de menor tamanho, enquanto que o Clonage Denso apresentou as maiores partículas. A observação em MEV. mostrou partículas de carga com vários tipos de morfologia (esféricas, irregulares, semi-esféricas, retangulares e mistura de retangulares/irregulares). Os resultados desse estudo mostraram diferenças nas partículas de carga dos materiais, as quais podem levar a diferentes resultados em suas propriedades mecânicas.

A comparative study of inter-abutment distance of dies made from full arch dual-arch impression trays with those made from full arch stock trays: An in vitro study.

Objectives: The dual-arch impression technique is convenient in that it makes the required maxillary and mandibular impressions, as well as the inter-occlusal record in one procedure. The accuracy of inter-abutment distance in dies fabricated from dual-arch impression technique remains in question because there is little information available in the literature. Materials and Methods: This study was conducted to evaluate the accuracy of inter-abutment distance in dies obtained from full arch dual-arch trays with those obtained from full arch stock metal trays. Results and Conclusion: The metal dual-arch trays showed better accuracy followed by the plastic dual-arch and stock dentulous trays, respectively, though statistically insignificant. The pouring sequence did not have any effect on the inter-abutment distance statistically, though pouring the non-working side of the dual-arch impression first showed better accuracy.

Effect of conventional and experimental gingival retraction solutions on the tensile strength and inhibition of polymerization of four types of impression materials

In the present study, two types of tests (tensile strength test and polymerization inhibition test) were performed to evaluate the physical and chemical properties of four impression materials [a polysulfide (Permlastic), a polyether (Impregum), a condensation silicone (Xantopren) and a polyvinylsiloxane (Aquasil) ,3; when polymerized in contact with of one conventional (Hemostop) and two experimental (Vislin and Afrin) gingival retraction solutions. For the tensile strength test, the impression materials were mixed and packed into a steel plate with perforations that had residues of the gingival retraction solutions. After polymerization, the specimens were tested in tensile strength in a universal testing machine. For the polymerization inhibition test, specimens were obtained after taking impressions from a matrix with perforations that contained 1 drop of the gingival retraction solutions. Two independent examiners decided on whether or not impression material remnants remained unpolymerized, indicating interference of the chemical solutions. Based on the analysis of the results of both tests, the following conclusions were reached: 1. The tensile strength of the polysulfide decreased after contact with Hemostop and Afrin. 2. None of the chemical solutions inhibited the polymerization of the polysulfide; 3. The polyether presented lower tensile strength after polymerization in contact with the three gingival retraction agents; 4. The polyether had its polymerization inhibited only by Hemostop; 5. None of the chemical solutions affected the tensile strength of the condensation silicone; 6. Only Hemostop inhibited the polymerization of the condensation silicone; 7. The polyvinylsiloxane specimens polymerized in contact with Hemostop had significantly lower tensile strength; 8. Neither of the chemical solutions (Afrin and Vislin) affected the tensile strength of the polyvinylsiloxane and the condensation silicone; 9. Results of ...

Comparative analysis of the shrinkage stress of composite resins

The aim of this study was to compare the shrinkage stress of composite resins by three methods. In the first method, composites were inserted between two stainless steel plates. One of the plates was connected to a 20 kgf load cell of a universal testing machine (EMIC-DL-500). In the second method, disk-shaped cavities were prepared in 2-mm-thick Teflon molds and filled with the different composites. Gaps between the composites and molds formed after polymerization were evaluated microscopically. In the third method, the wall-to-wall shrinkage stress of the resins that were placed in bovine dentin cavities was evaluated. The gaps were measured microscopically. Data were analyzed by one-way ANOVA and Tukey's test (alpha=0.05). The obtained contraction forces were: Grandio = 12.18 ± 0.428N; Filtek Z 250 = 11.80 ± 0.760N; Filtek Supreme = 11.80 ± 0.707 N; and Admira = 11.89 ± 0.647 N. The gaps obtained between composites and Teflon molds were: Filtek Z 250 = 0.51 ± 0.0357 percent; Filtek Supreme = 0.36 ± 0.0438 percent; Admira = 0.25 ± 0.0346 percent and Grandio = 0.16 ± 0.008 percent. The gaps obtained in wall-to-wall contraction were: Filtek Z 250 = 11.33 ± 2.160 µm; Filtek Supreme = 10.66 ± 1.211µm; Admira = 11.16 ± 2.041 µm and Grandio = 10.50 ± 1.224 µm. There were no significant differences among the composite resins obtained with the first (shrinkage stress generated during polymerization) and third method (wall-to-wall shrinkage). The composite resins obtained with the second method (Teflon method) differed significantly regarding gap formation.

Effect of microwave disinfection on denture base adaptation and resin surface roughness

This study evaluated the effect of disinfection methods [chemical disinfection (immersion in 100 ppm chloride solution) or microwave disinfection (690 W for 6 min)] on the internal adaptation of denture bases and resin surface roughness. For the adaptation test, 18 maxillary denture bases were obtained from stone casts duplicated from a metallic master model and submitted to the following treatments: 1) control (no disinfection), 2) chemical disinfection or 3) microwave disinfection. Disinfection procedures were performed twice (T1, T2) with a 7-day interval between them. Internal adaptation was measured at baseline (T0) and after T1 and T2 by weighing a vinyl polysiloxane film reproducing the gap between the resin base and the master model. For surface roughness measurement, 60 rectangular (5x10x40 mm) resin specimens were either mechanically or chemically polished and then submitted to the disinfection treatments. Surface roughness (Ra) was recorded after polishing (T0) and after T1 and T2. Data were analyzed by ANOVA GLM for repeated measures and Bonferroni correction at 5 percent significance level. Bases submitted to microwave disinfection had gradual increase of misfit, while bases immersed in chloride solution did not differ from the control group. Surface roughness increased in the mechanical polishing groups with microwave disinfection and decreased in the chemical polishing groups.

Este estudo avaliou o efeito de métodos de desinfecção [desinfecção química (imersão em solução clorada 100 ppm) ou desinfecção por microondas (690 W por 6 min)] na adaptação interna de bases de próteses totais e na rugosidade superficial da resina. Para o teste de adaptação, 18 bases superiores foram duplicadas a partir de um modelo-mestre metálico e submetidas aos seguintes tratamentos: 1) controle (sem desinfecção), 2) desinfecção química ou 3) desinfecção por microondas. Os procedimentos de desinfecção foram realizados duas vezes (T1, T2) com intervalo de 7 dias. A adaptação interna foi medida no baseline (T0), após T1 e T2 por pesagem de um filme de silicona de adição que reproduzia o espaço entre base de resina e modelo-mestre. Para a rugosidade superficial, 60 espécimes retangulares (5x10x40 mm) receberam polimento mecânico ou químico e foram submetidos aos tratamentos de desinfecção. A rugosidade superficial (Ra) foi registrada após o polimento (T0) e após T1 e T2. Os dados foram analisados por ANOVA GLM para medições repetidas e teste de Bonferroni com nível de significância de 5 por cento. As bases submetidas à desinfecção por microondas tiveram aumento gradual de desadaptação, enquanto que as bases imersas em solução clorada não diferiram do grupo controle. A rugosidade superficial aumentou nos grupos de polimento mecânico e desinfecção por microondas e diminuiu nos grupos de polimento químico.

Microhardness of resin-based materials polymerized with LED and halogen curing units

O objetivo deste estudo foi avaliar a microdureza de materiais resinosos polimerizados com unidades de fotoativação LED (diodos emissores de luz) e halógena. Vinte espécimes cilíndricos (3,0 mm de diâmetro e 2,0 mm de altura) foram preparados para cada material testado (Z100, Definite e Dyract). Os espécimes foram fotoativados na face superior (topo), utilizando duas unidades de fotoativação (Ultraled and Curing Light 2500), com tempos de 40 s e 60 s. As medidas de dureza foram realizadas nas superfícies do topo e da base de cada espécime. A análise estatística foi realizada por ANOVA e teste de Tukey (p<0,05). Não houve diferença significante na dureza na face superior entre as unidades LED e halógena para a Z100 e o Dyract. Por outro lado, a dureza foi menor quando a Definite foi polimerizada com o LED do que com a unidade halógena. Na base, a dureza de todos os materiais foi menor com o LED do que com a unidade halógena. A Z100 apresentou maior dureza que o Dyract e que a Definite independentemente da unidade de fotoativação. Não houve diferença significante na dureza entre os dois tempos de fotoativação para a face superior. Na base, a dureza foi maior quando os materiais foram polimerizados por 60 s. O LED não foi capaz de produzir a mesma dureza que a unidade halógena nos materiais resinosos testados.

Surface roughness of composite resins after finishing and polishing

This study evaluated the effect of surface finishing methods on the average surface roughness of resin composites. Seven composites and two polishing systems were used. One hundred and twenty-six conical specimens of each material were prepared in stainless steel molds against a polyester strip. Forty-two of them remained intact and were used as controls. Each half of the remaining samples was polished with either diamond burs or diamond burs + aluminum oxide discs. The results showed no statistical difference in average surface roughness (Ra, µm) between the polyester strip and aluminum oxide discs (p>0.05). However, finishing with diamond burs showed a statistically higher average roughness for all composites (p<0.05). Statistical differences were detected among materials (p<0.05) in the use of diamond burs

Amine and diamine polysiloxanes and their application

The amine and diamine polysiloxane ligands were prepared directly through hydrolytic condensation of[MeO][2-]Si-[CH[2]][3-]X [X=NH2 [X=NH2 or NH [CH2]2NH2 with a mixture of CH[2]=CH--Si [OMe][3]and Si [OEt][4]or indirectly by the reaction between the chloro-polysiloxane S- [CH2] 3-C1-[S represents the silocane matrix] and ethylenediamine. The vinyltrimethoxysilane used as a reactant where less cross-linking than those used Si [OEt] 4 alone, thus increased their capacity. These ligands are readily formed stable metal complexes of the type [S-[CH[2]]3-X][n]MC1[2][where n=2, M=Cu or Ni;n=3, M=Co]. With CU2+, Ni2+, Co2+ and Mn[2+ions, it was not usually possible that all the amine groups are accessible for coordination to the metal ion