RESUMEN
Besides high-power light-emitting diodes (LEDs) with dimensions in the range of mm, micro-LEDs (µLEDs) are increasingly gaining interest today, motivated by the future applications of µLEDs in augmented reality displays or for nanometrology and sensor technology. A key aspect of this miniaturization is the influence of the structure size on the electrical and optical properties of µLEDs. Thus, in this article, investigations of the size dependence of the electro-optical properties of µLEDs, with diameters in the range of 20 to 0.65 µm, by current-voltage and electroluminescence measurements are described. The measurements indicated that with decreasing size leakage currents in the forward direction decrease. To take advantage of these benefits, the surface has to be treated properly, as otherwise sidewall damages induced by dry etching will impair the optical properties. A possible countermeasure is surface treatment with a potassium hydroxide based solution that can reduce such defects.
RESUMEN
The combination of inorganic semiconductors with organic thin films promises new strategies for the realization of complex hybrid optoelectronic devices. Oxidative chemical vapor deposition (oCVD) of conductive polymers offers a flexible and scalable path towards high-quality three-dimensional inorganic/organic optoelectronic structures. Here, hole-conductive poly(3,4-ethylenedioxythiophene) (PEDOT) grown by oxidative chemical vapor deposition is used to fabricate transparent and conformal wrap-around p-type contacts on three-dimensional microLEDs with large aspect ratios, a yet unsolved challenge in three-dimensional gallium nitride technology. The electrical characteristics of two-dimensional reference structures confirm the quasi-metallic state of the polymer, show high rectification ratios, and exhibit excellent thermal and temporal stability. We analyze the electroluminescence from a three-dimensional hybrid microrod/polymer LED array and demonstrate its improved optical properties compared with a purely inorganic microrod LED. The findings highlight a way towards the fabrication of hybrid three-dimensional optoelectronics on the sub-micron scale.
RESUMEN
In this paper, a superior-quality InN/p-GaN interface grown using pulsed metalorganic vapor-phase epitaxy (MOVPE) is demonstrated. The InN/p-GaN heterojunction interface based on high-quality InN (electron concentration 5.19 × 1018 cm-3 and mobility 980 cm²/(V s)) showed good rectifying behavior. The heterojunction depletion region width was estimated to be 22.8 nm and showed the ability for charge carrier extraction without external electrical field (unbiased). Under reverse bias, the external quantum efficiency (EQE) in the blue spectral region (300â»550 nm) can be enhanced significantly and exceeds unity. Avalanche and carrier multiplication phenomena were used to interpret the exclusive photoelectric features of the InN/p-GaN heterojunction behavior.
RESUMEN
We study the photoluminescence emission from planar and 3D InGaN/GaN LED structures, excited using a femtosecond laser with fluences close to sample's damage threshold. For a typical laser system consisting of a titanium-sapphire regenerative amplifier, which is pumping an optical parametric amplifier delivering output pulses of a few tens of MW pulse power with â¼100 fs pulse duration, 1 kHz repetition rate and a wavelength of 325 nm, we determine the damage threshold of the InGaN/GaN LEDs to be about 0.05 J/cm2. We find that the relative intensity of the GaN photoluminescence (PL) and InGaN PL changes significantly close to the damage threshold. The changes are irreversible once the damage threshold is exceeded. As the damage threshold is approached, the InGaN luminescence band blue-shifts by several tens of meV, which is attributed to band filling effects. The PL decay time reduces substantially, by about 30%, when the excitation energy density is increased by approximately two orders of magnitude. The results are comparable for 2D and 3D LED structures, where in the latter case m-plane QWs exhibit different recombination dynamics because of the absence of the quantum confined Stark effect.
RESUMEN
Vertically aligned gallium nitride (GaN) nanowire (NW) arrays have attracted a lot of attention because of their potential for novel devices in the fields of optoelectronics and nanoelectronics. In this work, GaN NW arrays have been designed and fabricated by combining suitable nanomachining processes including dry and wet etching. After inductively coupled plasma dry reactive ion etching, the GaN NWs are subsequently treated in wet chemical etching using AZ400K developer (i.e., with an activation energy of 0.69 ± 0.02 eV and a Cr mask) to form hexagonal and smooth a-plane sidewalls. Etching experiments using potassium hydroxide (KOH) water solution reveal that the sidewall orientation preference depends on etchant concentration. A model concerning surface bonding configuration on crystallography facets has been proposed to understand the anisotropic wet etching mechanism. Finally, NW array-based vertical field-effect transistors with wrap-gated structure have been fabricated. A device composed of 99 NWs exhibits enhancement mode operation with a threshold voltage of 1.5 V, a superior electrostatic control, and a high current output of >10 mA, which prevail potential applications in next-generation power switches and high-temperature digital circuits.
RESUMEN
Nitride-based three-dimensional core-shell nanorods (NRs) are promising candidates for the achievement of highly efficient optoelectronic devices. For a detailed understanding of the complex core-shell layer structure of InGaN/GaN NRs, a systematic determination and correlation of the structural, compositional, and optical properties on a nanometer-scale is essential. In particular, the combination of low-temperature cathodoluminescence (CL) spectroscopy directly performed in a scanning transmission electron microscope (STEM), and quantitative high-angle annular dark field imaging enables a comprehensive study of the nanoscopic attributes of the individual shell layers. The investigated InGaN/GaN core-shell NRs, which were grown by metal-organic vapor-phase epitaxy using selective-area growth exhibit an exceptionally low density of extended defects. Using highly spatially resolved CL mapping of single NRs performed in cross-section, we give a direct insight into the optical properties of the individual core-shell layers. Most interesting, we observe a red shift of the InGaN single quantum well from 410 to 471 nm along the nonpolar side wall. Quantitative STEM analysis of the active region reveals an increasing thickness of the single quantum well (SQW) from 6 to 13 nm, accompanied by a slight increase of the indium concentration along the nonpolar side wall from 11% to 13%. Both effects, the increased quantum-well thickness and the higher indium incorporation, are responsible for the observed energetic shift of the InGaN SQW luminescence. Furthermore, compositional mappings of the InGaN quantum well reveal the formation of locally indium rich regions with several nanometers in size, leading to potential fluctuations in the InGaN SQW energy landscape. This is directly evidenced by nanometer-scale resolved CL mappings that show strong localization effects of the excitonic SQW emission.